CN103467005B - A kind of air-entrained concrete building block containing benzene emulsion - Google Patents
A kind of air-entrained concrete building block containing benzene emulsion Download PDFInfo
- Publication number
- CN103467005B CN103467005B CN201310335624.4A CN201310335624A CN103467005B CN 103467005 B CN103467005 B CN 103467005B CN 201310335624 A CN201310335624 A CN 201310335624A CN 103467005 B CN103467005 B CN 103467005B
- Authority
- CN
- China
- Prior art keywords
- building block
- benzene emulsion
- powder
- entrained concrete
- concrete building
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of air-entrained concrete building block containing benzene emulsion, it is obtained by the raw material of following weight parts: expanded vermiculite 17-19, bamboo charcoal powder 1-2, peanut oil oleic acid 0.1-0.2, potassium silicate 0.1-0.2, calcium lignin sulphonate 0.1-0.2, Sunmorl N 60S 0.1-0.2, barium stearate 0.01-0.02, urea 0.1-0.3, sodium carbonate 0.3-0.4, dicalcium powder 1-2, light calcium carbonate powder 2-4, benzene emulsion 2-4, cement 5-7, zinc powder 0.06-0.08, rapeseed oil 0.1-0.2, Chinese medicine compound 3-5, wilkinite 3-5.
Description
Technical field
The present invention relates to aerated bricks field, is exactly a kind of air-entrained concrete building block containing benzene emulsion.
Background technology
Aerated bricks is the air-entrained concrete building block produced by autoclave at high temperature apparatus and process." aerated bricks " can be understood as simplify an or general title.Its product scope contained should be wanted greatly a bit, namely to adopt the brick product comprising other various explained hereafter of steam pressure.
The materials for wall mainly common brick that construction market was used in the past, present many advanced areas have been completely forbidden common brick and have been used.
Existing aerated bricks Development Technology is slow, cannot meet the market requirement of diversification.
Summary of the invention
The object of the present invention is to provide a kind of air-entrained concrete building block containing benzene emulsion.
Above-mentioned purpose is realized by following scheme:
A kind of air-entrained concrete building block containing benzene emulsion, it is characterized in that: it is obtained by the raw material of following weight parts: expanded vermiculite 17-19, bamboo charcoal powder 1-2, peanut oil oleic acid 0.1-0.2, potassium silicate 0.1-0.2, calcium lignin sulphonate 0.1-0.2, Sunmorl N 60S 0.1-0.2, barium stearate 0.01-0.02, urea 0.1-0.3, sodium carbonate 0.3-0.4, dicalcium powder 10-12, light calcium carbonate powder 12-14, benzene emulsion 2-4, cement 5-7, zinc powder 0.06-0.08, rapeseed oil 0.1-0.2, Chinese medicine compound 3-5, wilkinite 13-15.
Described a kind of air-entrained concrete building block containing benzene emulsion, is characterized in that:
Preparation method is:
(1) get Cushaw stem 1-2 part, Leaf of Matrimonyvine 3-5 part, pachyrhizus leaf 1-2 part, root of large-flowered skullcap 2-4 part, safflower 2-4 part, after mixing, dry, abrasive dust, obtain Chinese medicine compound, for subsequent use;
(2) peanut oil oleic acid, potassium silicate, calcium lignin sulphonate, Sunmorl N 60S, barium stearate, urea, sodium carbonate are mixed by weight, add again and be equivalent to above-mentioned raw materials gross weight 3-5 water doubly, at 25-35 DEG C, stir 20-30 minute, obtain modification liquid for subsequent use;
(3) by Chinese medicine compound, modification liquid and all the other raw material blendings, then add suitable quantity of water, pour into the mold shaping, after at 40-50 DEG C precuring 3-5 hour, the demoulding, cutting, obtain building block base;
(4) building block base is put into reactor steam press maintenance 15-17 hour, put finished product in storage and get final product.
Beneficial effect of the present invention is: the present invention can be good at the intensity increasing aerated bricks, adds benzene emulsion, when not increasing unit weight, keeps intensity.
Embodiment
A kind of air-entrained concrete building block containing benzene emulsion, it is obtained by the raw material of following weight parts (kg): expanded vermiculite 17, bamboo charcoal powder 2, peanut oil oleic acid 0.2, potassium silicate 0.2, calcium lignin sulphonate 0.2, Sunmorl N 60S 0.2, barium stearate 0.02, urea 0.1, sodium carbonate 0.4, dicalcium powder 10, light calcium carbonate powder 14, benzene emulsion 4, cement 7, zinc powder 0.08, rapeseed oil 0.2, Chinese medicine compound 5, wilkinite 15.
Described a kind of air-entrained concrete building block containing benzene emulsion,
Preparation method is:
(1) get Cushaw stem 1.5 parts (kg), Leaf of Matrimonyvine 4 parts, 1 part, pachyrhizus leaf, the root of large-flowered skullcap 3 parts, 4 parts, safflower, after mixing, dry, abrasive dust, obtain Chinese medicine compound, for subsequent use;
(2) peanut oil oleic acid, potassium silicate, calcium lignin sulphonate, Sunmorl N 60S, barium stearate, urea, sodium carbonate are mixed by weight, then add the water being equivalent to above-mentioned raw materials gross weight 4 times, stir 30 minutes at 30 DEG C, obtain modification liquid for subsequent use;
(3) by Chinese medicine compound, modification liquid and all the other raw material blendings, then add suitable quantity of water, pour into the mold shaping, after precuring 3 hours at 48 DEG C, the demoulding, cutting, obtains building block base;
(4) building block base is put into reactor steam press maintenance 15 hours, put finished product in storage and get final product.
The volume-weighted average of this building block is 520kg/m
3, good heat insulating, has a large amount of pores and micropore at block interiors, thus has good thermal and insulating performance, and mean value ultimate compression strength is 8.7MPa.
Claims (1)
1. the air-entrained concrete building block containing benzene emulsion, is characterized in that: it is obtained by the raw material of following weight parts: expanded vermiculite 17-19, bamboo charcoal powder 1-2, peanut oil oleic acid 0.1-0.2, potassium silicate 0.1-0.2, calcium lignin sulphonate 0.1-0.2, Sunmorl N 60S 0.1-0.2, barium stearate 0.01-0.02, urea 0.1-0.3, sodium carbonate 0.3-0.4, dicalcium powder 10-12, light calcium carbonate powder 12-14, benzene emulsion 2-4, cement 5-7, zinc powder 0.06-0.08, rapeseed oil 0.1-0.2, Chinese medicine compound 3-5, wilkinite 13-15;
The described air-entrained concrete building block preparation method containing benzene emulsion is:
(1) get Cushaw stem 1-2 part, Leaf of Matrimonyvine 3-5 part, pachyrhizus leaf 1-2 part, root of large-flowered skullcap 2-4 part, safflower 2-4 part, after mixing, dry, abrasive dust, obtain Chinese medicine compound, for subsequent use;
(2) peanut oil oleic acid, potassium silicate, calcium lignin sulphonate, Sunmorl N 60S, barium stearate, urea, sodium carbonate are mixed by weight, add again and be equivalent to above-mentioned raw materials gross weight 3-5 water doubly, at 25-35 DEG C, stir 20-30 minute, obtain modification liquid for subsequent use;
(3) by Chinese medicine compound, modification liquid and all the other raw material blendings, then add suitable quantity of water, pour into the mold shaping, after at 40-50 DEG C precuring 3-5 hour, the demoulding, cutting, obtain building block base;
(4) building block base is put into reactor steam press maintenance 15-17 hour, put finished product in storage and get final product.