CN103467008B - A kind of air-entrained concrete building block adding bamboo carbon powder - Google Patents

A kind of air-entrained concrete building block adding bamboo carbon powder Download PDF

Info

Publication number
CN103467008B
CN103467008B CN201310335950.5A CN201310335950A CN103467008B CN 103467008 B CN103467008 B CN 103467008B CN 201310335950 A CN201310335950 A CN 201310335950A CN 103467008 B CN103467008 B CN 103467008B
Authority
CN
China
Prior art keywords
bamboo carbon
building block
carbon powder
air
entrained concrete
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310335950.5A
Other languages
Chinese (zh)
Other versions
CN103467008A (en
Inventor
强晓震
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Original Assignee
ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd filed Critical ANHUI ZHONGLONG BUILDING MATERIALS TECHNOLOGY Co Ltd
Priority to CN201310335950.5A priority Critical patent/CN103467008B/en
Publication of CN103467008A publication Critical patent/CN103467008A/en
Application granted granted Critical
Publication of CN103467008B publication Critical patent/CN103467008B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention discloses a kind of air-entrained concrete building block adding bamboo carbon powder, it is obtained by the raw material of following weight parts: bamboo carbon powder 5-7, flyash 10-15, cement 16-22, gypsum 8-10, rice hull carbon 2-4, acrylic fiber 0.2-0.4, organic silicon emulsion 0.4-0.6, sugar calcium water reducer 3-5, magnesium aluminometasilicate 0.3-0.5, polyisobutylene succinamide 0.001-0.003, three Risorex PGIS 22 0.002-0.004, isomeric alcohol polyethenoxy ether 0.002-0.003, cocoanut fatty acid diethanolamide 0.002-0.004, trevira 1-2, attapulgite modified 8-12, sugar calcium 0.001-0.003, calcium formiate 0.002-0.003, aluminium powder 0.02-0.06, oxidized paraffin wax soap 0.01-0.03.

Description

A kind of air-entrained concrete building block adding bamboo carbon powder
Technical field
The present invention relates to aerated bricks field, is exactly a kind of air-entrained concrete building block adding bamboo carbon powder.
Background technology
Aerated bricks is the air-entrained concrete building block produced by autoclave at high temperature apparatus and process." aerated bricks " can be understood as simplify an or general title.Its product scope contained should be wanted greatly a bit, namely to adopt the brick product comprising other various explained hereafter of steam pressure.
The materials for wall mainly common brick that construction market was used in the past, present many advanced areas have been completely forbidden common brick and have been used.
Existing aerated bricks Development Technology is slow, cannot meet the market requirement of diversification.
Summary of the invention
The object of the present invention is to provide a kind of air-entrained concrete building block adding bamboo carbon powder.
Above-mentioned purpose is realized by following scheme:
A kind of air-entrained concrete building block adding bamboo carbon powder, it is characterized in that: it is obtained by the raw material of following weight parts: bamboo carbon powder 5-7, flyash 10-15, cement 16-22, gypsum 8-10, rice hull carbon 2-4, acrylic fiber 0.2-0.4, organic silicon emulsion 0.4-0.6, sugar calcium water reducer 3-5, magnesium aluminometasilicate 0.3-0.5, polyisobutylene succinamide 0.001-0.003, three Risorex PGIS 22 0.002-0.004, isomeric alcohol polyethenoxy ether 0.002-0.003, cocoanut fatty acid diethanolamide 0.002-0.004, trevira 1-2, attapulgite modified 8-12, sugar calcium 0.001-0.003, calcium formiate 0.002-0.003, aluminium powder 0.02-0.06, oxidized paraffin wax soap 0.01-0.03,
Described attapulgite modified preparation method is: attapulgite is calcined 1-2 hour at 900-1000 DEG C, cool to 700-800 DEG C of insulation 1-2 hour, grinding, cross 100-200 mesh sieve, then add and be equivalent to the ethoxylated dodecyl alcohol of its weight 0.5-1.2%, the triethanolamine oleate of 0.1-0.5%, the aluminium nitride of 0.1-0.2% and appropriate water, stir 10-15 minute at 40-42 DEG C after, take out, dry, to obtain final product.
Described a kind of air-entrained concrete building block adding bamboo carbon powder, is characterized in that:
Preparation method is:
(1) get bamboo carbon powder by weight, then in concentration be 10-15% hydrochloric acid soln in soak 10-15 hour, take out,
Deionized water wash, dries, and crosses 100-200 mesh sieve, obtains modified bamboo powdered carbon for subsequent use;
(2) modified bamboo carbon dust, flyash, cement, gypsum, organic silicon emulsion, sugared calcium water reducer, magnesium aluminometasilicate are mixed by weight, 15-18 minute is stirred under 70-80 rev/min, take out, after mixing with the whole raw material of residue and suitable quantity of water again, join in double-shaft horizontal stirring tank, 200-300 rev/min is at the uniform velocity stirred 20-30 minute, again that the material be stirred is shaping with pouring into the mold, after at 40-50 DEG C precuring 3-5 hour, the demoulding, handling is cut to cutting part, obtains building block base;
(3) building block base is put into reactor steam press maintenance, put finished product in storage and get final product.
Beneficial effect of the present invention is: the present invention with the addition of bamboo carbon powder, adds porosity of the present invention, has good water-reduction while reducing unit weight.
Embodiment
A kind of air-entrained concrete building block adding bamboo carbon powder, it is obtained by the raw material of following weight parts (kg): bamboo carbon powder 7, flyash 15, cement 17, gypsum 8, rice hull carbon 3, acrylic fiber 0.4, organic silicon emulsion 0.5, sugar calcium water reducer 5, magnesium aluminometasilicate 0.3, polyisobutylene succinamide 0.003, three Risorex PGIS 22s 0.004, isomeric alcohol polyethenoxy ether 0.003, cocoanut fatty acid diethanolamide 0.004, trevira 2, attapulgite modified 12, sugared calcium 0.003, calcium formiate 0.003, aluminium powder 0.04, oxidized paraffin wax soap 0.03;
Described attapulgite modified preparation method is: calcined 2 hours at 900 DEG C by attapulgite, cool to 800 DEG C of insulations 1 hour, grinding, cross 100 mesh sieves, then add and be equivalent to the ethoxylated dodecyl alcohol of its weight 0.8%, the triethanolamine oleate of 0.5%, the aluminium nitride of 0.2% and appropriate water, stir at 42 DEG C after 15 minutes, take out, dry, to obtain final product.
Described a kind of air-entrained concrete building block adding bamboo carbon powder, preparation method is:
(1) get bamboo carbon powder by weight, then in concentration be 12% hydrochloric acid soln in soak 12 hours, take out,
Deionized water wash, dries, and crosses 100 mesh sieves, obtains modified bamboo powdered carbon for subsequent use;
(2) modified bamboo carbon dust, flyash, cement, gypsum, organic silicon emulsion, sugared calcium water reducer, magnesium aluminometasilicate are mixed by weight, stir 15 minutes under 70 revs/min, take out, then after mixing with the whole raw material of residue and suitable quantity of water, join in double-shaft horizontal stirring tank, 300 revs/min are at the uniform velocity stirred 30 minutes, again that the material be stirred is shaping with pouring into the mold, after precuring 5 hours at 47 DEG C, the demoulding, handling is cut to cutting part, obtains building block base;
(3) building block base is put into reactor steam press maintenance, put finished product in storage and get final product.
The volume-weighted average of this building block is 600-650kg/m 3, good heat insulating, has a large amount of pores and micropore at block interiors, thus has good thermal and insulating performance, and mean value ultimate compression strength is 8.7MPa.

Claims (2)

1. one kind is added the air-entrained concrete building block of bamboo carbon powder, it is characterized in that: it is obtained by the raw material of following weight parts: bamboo carbon powder 5-7, flyash 10-15, cement 16-22, gypsum 8-10, rice hull carbon 2-4, acrylic fiber 0.2-0.4, organic silicon emulsion 0.4-0.6, sugar calcium water reducer 3-5, magnesium aluminometasilicate 0.3-0.5, polyisobutylene succinamide 0.001-0.003, three Risorex PGIS 22 0.002-0.004, isomeric alcohol polyethenoxy ether 0.002-0.003, cocoanut fatty acid diethanolamide 0.002-0.004, trevira 1-2, attapulgite modified 8-12, sugar calcium 0.001-0.003, calcium formiate 0.002-0.003, aluminium powder 0.02-0.06, oxidized paraffin wax soap 0.01-0.03, described attapulgite modified preparation method is: attapulgite is calcined 1-2 hour at 900-1000 DEG C, cool to 700-800 DEG C of insulation 1-2 hour, grinding, cross 100-200 mesh sieve, then add and be equivalent to the ethoxylated dodecyl alcohol of its weight 0.5-1.2%, the triethanolamine oleate of 0.1-0.5%, the aluminium nitride of 0.1-0.2% and appropriate water, stir 10-15 minute at 40-42 DEG C after, take out, dry, to obtain final product.
2. a kind of air-entrained concrete building block adding bamboo carbon powder according to claim 1, is characterized in that: preparation method is:
(1) get bamboo carbon powder by weight, then in concentration be 10-15% hydrochloric acid soln in soak 10-15 hour, take out, deionized water wash, dry, cross 100-200 mesh sieve, obtain modified bamboo carbon dust for subsequent use;
(2) modified bamboo carbon dust, flyash, cement, gypsum, organic silicon emulsion, sugared calcium water reducer, magnesium aluminometasilicate are mixed by weight, 15-18 minute is stirred under 70-80 rev/min, take out, then after mixing with the whole raw material of residue and suitable quantity of water, join in double-shaft horizontal stirring tank, 200-300 rev/min is at the uniform velocity stirred 20-30 minute, again that the material be stirred is shaping with pouring into the mold, after at 40-50 DEG C precuring 3-5 hour, the demoulding, handling is cut to cutting part, obtains building block base;
(3) building block base is put into reactor steam press maintenance, put finished product in storage and get final product.
CN201310335950.5A 2013-08-05 2013-08-05 A kind of air-entrained concrete building block adding bamboo carbon powder Active CN103467008B (en)