CN209482626U - A kind of superhigh tenacity concrete inorganic decorating board of the surface containing pattern - Google Patents
A kind of superhigh tenacity concrete inorganic decorating board of the surface containing pattern Download PDFInfo
- Publication number
- CN209482626U CN209482626U CN201821714631.XU CN201821714631U CN209482626U CN 209482626 U CN209482626 U CN 209482626U CN 201821714631 U CN201821714631 U CN 201821714631U CN 209482626 U CN209482626 U CN 209482626U
- Authority
- CN
- China
- Prior art keywords
- superhigh tenacity
- decorating board
- tenacity concrete
- inorganic decorating
- decorative panel
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The utility model relates to technical field of construction and decoration materials, disclose a kind of superhigh tenacity concrete inorganic decorating board of the surface containing pattern, be greater than 100 megapascal, flexural strength by compression strength adds arrangement of reinforcement is prefabricated to form greater than the superhigh tenacity concrete of 16 megapascal, the upper surface of the decorative panel has decorative pattern, four edges of the decorative panel include the installation bolt hole of perforation, wherein arrangement of reinforcement is criss-cross web, uses sealing structure glue connection between adjacent decorative panel.Technical solutions of the utility model have the characteristics that toughness height, decorative effect diversification, compact structure pore-free, mold turn around time is short, relative low price, fire resistance is good, resistant waterproof performance is good, durability is strong using the inorganic decorating board that superhigh tenacity concrete carries out vacuum defoamation preparation, are suitble to the development and application of green energy conservation ornament materials.
Description
Technical field
The utility model relates to technical field of construction and decoration materials, and it is tough to relate more specifically to a kind of superelevation of the surface containing pattern
Property concrete inorganic decorating board.
Background technique
Since China reforms and opens up to the outside world, with the rapid development of economic construction, the continuous improvement of living standards of the people, building dress
Decorations problem, which has been put on the agenda, to be come, and China's building decoration generally uses normal concrete or glass fiber reinforced cement instantly
(GRC) or lithotome produces, and all haves the defects that certain.For normal concrete since mechanical property is lower, the decoration of production is mixed
Solidifying soil component is than cumbersome；Although GRC can accomplish more frivolous, GRC mold consumption is big, and buckling deformation is big after installation,
The intensive level of industry is lower, cannot achieve big industrial intensive manufacture, compact structure is poor, later strength retraction, anti-pollution characteristic
Difference, at high cost, low efficiency；Although lithotome good decorating effect, itself brittleness is big, production of resources is limited, have radiation,
There is pollution to environment.Superhigh tenacity concrete be after high intensity, high performance concrete, in twentieth century end by French cloth she
The research of lattice (Bouygues) company is successfully a kind of by the good quartzy fine sand (being free of coarse aggregate) of gradation, cement, silica flour, silicon
The brittleness strong with superelevation, low of the compositions such as powder, high efficiency water reducing agent, fiber, excellent in te pins of durability and new with broad prospect of application
Type super high strength concrete.Superhigh tenacity concrete exquisite in texture, quality stabilization, excellent in te pins of durability, have good decorative performance,
There is good physical and mechanical property again simultaneously, structural ornament integration may be implemented, be more conducive to expanding architectural concrete
Application field.Superhigh tenacity concrete has good workability, is conducive to produce various special-shaped decoration elements, it is easy to accomplish
Industrialized production reaches economic and green dual purpose.
Superhigh tenacity concrete inorganic decorating board aiming at above-mentioned traditional decoration material deficiency and the novel nothing researched and developed
Machine dalle, with the spies such as toughness is high, brittleness is low, decorative effect is diversified, resistant waterproof performance is good, durability is good
Point, the scape in urban operating mechanism, residential quarters, gardens needed for can be widely applied to the various occasions such as house, business and urban construction etc.
It sees and creates, and can be used for the engineering such as hot environment of particular surroundings, which has a vast market application prospect, will lead not
Carry out the developing direction of inorganic decorating plate.
Utility model content
That utility model aims to solve traditional decoration concrete plate toughness is low, brittleness is big, component is heavy, resin
Ingredient causes serious pollution to the environment, mold consumption is more, shrinks the problems such as big, anti-pollution characteristic is poor, production efficiency is low, fire resistance is poor,
It is good, wear-resisting to provide few a kind of high tenacity, lower shrinkage, mold consumption, high production efficiency, decorative effect diversification, fire protecting performance
The utilization superhigh tenacity concrete that performance is good, resistant waterproof performance is good, cost of manufacture is cheap, endurance quality is good uses vacuum defoamation
Superhigh tenacity concrete inorganic decorating board and preparation method thereof of the surface of preparation containing pattern.
The above-mentioned purpose of the utility model is achieved by the following technical programs:
A kind of superhigh tenacity concrete inorganic decorating board of the surface containing pattern, the inorganic decorating board are greater than by compression strength
100 megapascal, flexural strength are greater than the superhigh tenacity concrete of 16 megapascal, electric flux less than 100 coulombs and add arrangement of reinforcement is prefabricated to form.
The superhigh tenacity concrete inorganic decorating board of the surface containing pattern using the preparation of superhigh tenacity concrete and its
Preparation method, the raw material including following parts by weight:
500~800 parts of the continuous grading colored aggregate of 3~8mm of partial size；
400~600 parts of the fine aggregate of 0.15~2.36mm of partial size；
Intensity is not less than 350~750 parts of cement of 32.5MPa；
200~450 parts of the admixture that 5~30 μm of average grain diameter；
5~20 parts of the organic fiber of 10~20mm of length；
20~50 parts of pigment powder；
15~25 parts of high performance additive；
Water-cement ratio 0.16~0.22.
In preferred embodiment, the length of the superhigh tenacity concrete inorganic decorating board is 500-2400mm, width 500-
1200mm, with a thickness of 15~30mm.
In preferred embodiment, the superhigh tenacity concrete inorganic decorating board is multilayered structure, and the web is centre
Layer, the web upper and lower surface are covered with concrete material layer.
In preferred embodiment, the position of the installation bolt hole is located at respectively at the 50mm of decorative panel both sides.
Compared with prior art, technical solutions of the utility model have the advantages that
(1) superhigh tenacity concrete inorganic decorating board tool of a kind of surface that technical solutions of the utility model are related to containing pattern
There are high-densit pore-free, superhigh tenacity, lower shrinkage, compression strength to be greater than 100 megapascal, flexural strength is greater than 16 megapascal, electricity is logical
Amount less than 100 coulombs, decorative effect diversification, fire protecting performance is good, resistant waterproof performance is good, wear-resisting property is good, durability is good etc.
Feature.
(2) superhigh tenacity concrete inorganic decorating board system of a kind of surface that technical solutions of the utility model are related to containing pattern
Mold dosage is few in Preparation Method, and mold turn around time is short, solves that traditional decoration concrete slab mold consumption is more, costly asks
Topic.
(3) ultra-high performance concrete of surface of a kind of surface containing pattern containing pattern that technical solutions of the utility model are related to
The raw material sources of inorganic decorating board extensively, it can be achieved that industrialized production, high production efficiency, belong to energy-saving and environment friendly product,
With economic and social benefits.
(4) a kind of superhigh tenacity concrete inorganic decorating board of the surface that technical solutions of the utility model are related to containing pattern can
It realizes decorative effect diversification and can solve the problems, such as the color difference that traditional decoration concrete slab has, improve the decoration of inorganic decorating board
Effect.
Detailed description of the invention
Fig. 1 is a kind of three-view diagram of superhigh tenacity concrete inorganic decorating board of surface containing pattern.
Fig. 2 is a kind of sectional view of superhigh tenacity concrete inorganic decorating board of surface containing pattern.
Fig. 3 is a kind of construction diagrams of superhigh tenacity concrete inorganic decorating board of surface containing pattern.
Specific embodiment
Hereinafter, will be made in conjunction with Figure of description and specific embodiment to the technical solution of the utility model and advantage
More detailed explanation and explanation.It should be understood that is presented in specification, specific embodiment and Figure of description is interior
Hold, just to clearly illustrate the technical solution of the utility model and its advantage, not to the protection of the utility model
Range is construed as limiting.Those skilled in the art reasonable can convert on the basis of specification disclosure for various
Technical solution after to variation, without departing from the spirit of the utility model, the technical solution after various change is included in this
Within the protection scope of utility model.
Illustrate the structure of the ultra-tough concrete inorganic decorating board of the utility model below with reference to Fig. 1-3.
Fig. 1 is the three-view diagram of the utility model inorganic decorating board.Decorative panel appearance is in cuboid, wherein being preferably dimensioned to be length
Degree is 500-2400mm, width 500-1200mm, with a thickness of 15-30mm.Four edges of decorative panel 1 include four perforations
Installation bolt hole 2, at each 50mm in decorative panel both sides, when installation, may be selected suitable reinforcer and passes through installation site
Bolt hole 2 is installed, mounting plate is fixed on metope or house basal plane, reinforcer can be expansion bolt, rivet, self-tapping screw.
Fig. 2 is the sectional view of inorganic decorating board, is sandwich inside decorative panel, and middle layer is web 3, plays reinforcement
The effect of muscle, the upper and lower surfaces of web respectively cover one layer of decorative panel concrete material layer, and three layers close compound.
Fig. 3 is the construction diagrams of inorganic decorating board.When decorative panel is constructed, for the effect for reinforcing adjacent decorative panel, prevent rainwater,
Dust enters the bonding for inside decorative panel and destroying decorative panel and metope, and structure sealant 4 is used when adjacent decoration plate splices
It is bonded.
The following examples more specifically describe the structure and composition and its system of the utility model inorganic decorating board
Preparation Method.
Although the content of the present invention includes specific embodiment, to those skilled in the art it is apparent that not
In the case where the utility model element or scope for deviateing present claims and its equivalent technical solutions, these embodiments can be done
Replacement or variation on various forms and in details out.Embodiment described herein should be considered only in descriptive sense, and
It is non-for the purpose of limitation.The description of feature and aspect in each example is deemed applicable in other embodiments
Similar features and aspect.Therefore, the scope of the utility model should not be by specifically describing to be limited, but by claim skill
The restriction of art scheme, and all changes in the range of present claims and its equivalent are interpreted included in originally practical
Within novel technical solution.
Embodiment 1
A kind of superhigh tenacity concrete inorganic decorating board of the surface containing pattern, the inorganic decorating board are greater than by compression strength
100 megapascal, flexural strength are greater than the superhigh tenacity concrete of 16 megapascal, electric flux less than 100 coulombs and add arrangement of reinforcement is prefabricated to form,
The upper surface of the decorative panel has decorative pattern, and four edges of the decorative panel include the installation bolt hole of perforation,
Middle arrangement of reinforcement is criss-cross web, uses sealing structure glue connection between adjacent decorative panel.
It is described using superhigh tenacity concrete preparation ultra-high performance concrete of surface of the surface containing pattern containing pattern without
Machine decorative panel and preparation method thereof, the raw material including following parts by weight:
500 parts of the continuous grading colour coarse aggregate of 3~8mm of partial size；
4000 parts of the fine aggregate of 0.15~2.36mm of partial size；
Intensity is not less than 350 parts of cement of 32.5MPa；
200 parts of the admixture that 5~30 μm of average grain diameter；
5 parts of the organic fiber of 10~20mm of length；
20 parts of pigment powder；
15 parts of high performance additive；
Water-cement ratio 0.16.
The arrangement of reinforcement is glass fiber reticular cloth.
The length of the decorative panel is 1500mm, width 600mm, thickness 20mm.
The preparation method of the inorganic decorating board is made according to the following steps:
S1 will be put on stainless steel bed die with pattern template and pave, and then retarder is sprayed on bed die, and 15~30 points
Stainless steel periphery frame is fixed on bed die with buckle by the peripheral frame that correspondingly-sized is assembled after removing with pattern template after clock
On, obtain the removable inorganic decorating board mold for being sprayed with retarder pattern；
S2 according to ultra-high performance concrete each raw material usage of mix calculation, by whole cement, admixture, pigment powder
First premix 2~4 minutes；
Premix obtained by water addition S2 step of the S3 by all colored coarse aggregate, fine aggregate, organic fiber and 40% weight is dry
It is stirred 1~2 minute in powder；
Whole additives and remaining 60% water are added in the mixture prewetted obtained by S3 step by S4, are sufficiently stirred 7
~9 minutes, obtain superhigh tenacity concrete mix；
The superhigh tenacity concrete mix that step S4 is obtained is poured into the removable inorganic decorating template die that S1 is obtained by S5
In tool, when being poured into the 1/3~1/2 of thickness, arrangement of reinforcement is spread, continues to be poured into design thickness, vibrate 5~10 seconds；
Step S5 is poured the decorative panel obtained after vibration and moves into vacuum chamber by S6, after carrying out vacuumizing and defoaming, by decorative panel
Vacuum chamber is removed, surface is closed flat；
Decorative panel overlay film made from step S6 is conserved 8~16 hours and is demoulded by S7, and washes away inorganic decorating with giant
Board finish obtains patterned superhigh tenacity concrete inorganic decorating board；
The superhigh tenacity concrete inorganic decorating board that S7 is obtained is put into 80~95 DEG C of dry heating curing kiln and conserves 36 by S8
~48 hours；
S9 polishes decorative panel bilayer made from step S8, has pattern plane to polish with a thickness of 0.2~0.5mm, no figure
The polishing of case face with a thickness of 0.5~1.0mm, will have pattern plane polish and sprayed surface protective agent obtain superhigh tenacity concrete without
Machine decorative panel.
The peripheral bezel height for the removable inorganic decorating board mold that the step S1 is obtained is 18~33mm.
The step S2 first premixes whole cement, admixture, pigment powder 2~4 minutes, fills pigment powder with cementitious material
Divide mixing, guarantee inorganic decorating board color uniformity, reduces color difference.
The superhigh tenacity concrete mix integral working that the step S4 is obtained is 550~700mm of extension.
The carry out vacuumizing and defoaming of the step S6, pressure are -0.07~-0.1 megapascal, and inclined heated plate is 5~10 seconds.
Vacuum defoamation improves the compactness of superhigh tenacity concrete inorganic decorating board of the surface containing pattern, makes superelevation of the surface containing pattern
The polishing of toughness concrete inorganic decorating board, surface of polished pore-free, improve decorative effect, mechanical property and endurance quality.
The step S7 obtains patterned superhigh tenacity concrete inorganic decorating board, and pattern depth is 0.5~
2.0mm。
The step S9 carries out sanding and polishing and sprayed protection agent to decorative panel, can solve the plaque surface accumulation of salt in the surface soil and table
The problems such as face is scraped off, and improve decorative panel resistant, wear-resisting property.
Embodiment 2
In addition to the formula of superhigh tenacity concrete inorganic decorating board of the surface containing pattern is different, other conditions are the same as embodiment 1.
A kind of superhigh tenacity concrete inorganic decorating board and preparation method thereof of the surface containing pattern, including following parts by weight
Raw material:
800 parts of the continuous grading colour coarse aggregate of 3~8mm of partial size；
600 parts of the fine aggregate of 0.15~2.36mm of partial size；
Intensity is not less than 750 parts of cement of 32.5MPa；
450 parts of the admixture that 5~30 μm of average grain diameter；
20 parts of the organic fiber of 10~20mm of length；
50 parts of pigment powder；
25 parts of high performance additive；
Water-cement ratio 0.22.
Embodiment 3
In addition to the formula of superhigh tenacity concrete inorganic decorating board of the surface containing pattern is different, other conditions are the same as embodiment 1.
A kind of superhigh tenacity concrete inorganic decorating board and preparation method thereof of the surface containing pattern, including following parts by weight
Raw material:
575 parts of the continuous grading colour coarse aggregate of 3~8mm of partial size；
450 parts of the fine aggregate of 0.15~2.36mm of partial size；
Intensity is not less than 450 parts of cement of 32.5MPa；
260 parts of the admixture that 5~30 μm of average grain diameter；
8.5 parts of the organic fiber of 10~20mm of length；
28 parts of pigment powder；
17.5 parts of high performance additive；
Water-cement ratio 0.17.
Embodiment 4
In addition to the formula of superhigh tenacity concrete inorganic decorating board of the surface containing pattern is different, other conditions are the same as embodiment 1.
A kind of superhigh tenacity concrete inorganic decorating board and preparation method thereof of the surface containing pattern, including following parts by weight
Raw material:
725 parts of the continuous grading colour coarse aggregate of 3~8mm of partial size；
550 parts of the fine aggregate of 0.15~2.36mm of partial size；
Intensity is not less than 650 parts of cement of 32.5MPa；
90 parts of the admixture that 5~30 μm of average grain diameter；
16.5 parts of the organic fiber of 10~20mm of length；
42 parts of pigment powder；
22.5 parts of high performance additive；
Water-cement ratio 0.21.
Embodiment 5
In addition to the formula of superhigh tenacity concrete inorganic decorating board of the surface containing pattern is different, other conditions are the same as embodiment 1.
A kind of superhigh tenacity concrete inorganic decorating board and preparation method thereof of the surface containing pattern, including following parts by weight
Raw material:
650 parts of the continuous grading colour coarse aggregate of 3~8mm of partial size；
500 parts of the fine aggregate of 0.15~2.36mm of partial size；
Intensity is not less than 550 parts of cement of 32.5MPa；
325 parts of the admixture that 5~30 μm of average grain diameter；
12.5 parts of the organic fiber of 10~20mm of length；
35 parts of pigment powder；
20 parts of high performance additive；
Water-cement ratio 0.19.
Comparative example 1
Especially in addition to colored coarse aggregate 400, other conditions are the same as embodiment 1.
Comparative example 2
Especially in addition to cement 300, other conditions are the same as embodiment 1.
Comparative example 3
Especially in addition to organic fiber 1, other conditions are the same as embodiment 1.
Comparative example 4
Other than water-cement ratio 0.15, other conditions are the same as embodiment 1.
Comparative example 5
Other than water-cement ratio 0.25, other conditions are the same as embodiment 1.
Compare case 6
Other than not having to carry out vacuum defoamation, other conditions are the same as embodiment 1.
Compare case 7
Other than not having to carry out the agent of sanding and polishing sprayed protection, other conditions are the same as embodiment 1.
Standard specimen progressive is fabricated to inorganic decorating board prepared by the above case study on implementation 1~5, comparison case 1~7
It can test, test result is as shown in table 1:
1 inorganic decorating board performance test results of table
From the point of view of table 1, colored 400 parts of the coarse aggregate of comparative example 1 compares, flexural strength, resistant waterproofness with embodiment 1
Can and fire resistance decline more, shrinking percentage and water absorption rate increase more；300 parts of 2 cement of comparative example, it is right with embodiment 1
Than flexural strength, resistant waterproof performance and fire resistance decline more, and shrinking percentage and water absorption rate increase more；Comparative example 3
It 1 part of organic fiber, is compared with embodiment 1, flexural strength, resistant waterproof performance and fire resistance decline more, shrinking percentage
Increase with water absorption rate more；4 water-cement ratio 0.15 of comparative example is compared with embodiment 1, flexural strength, resistant waterproof performance and resistance to
Fiery performance declines more, and shrinking percentage and water absorption rate increase more；5 water-cement ratio 0.25 of comparative example compares, bending resistance with embodiment 1
Qu Qiangdu, resistant waterproof performance and fire resistance decline more, and shrinking percentage and water absorption rate increase more；Comparative example 6 is without vacuum
Deaeration is compared with embodiment 1, and flexural strength decline is less, and shrinking percentage and water absorption rate increase more, resistant waterproofness and fire resisting
Performance decline is more；Comparative example 7 is compared with embodiment 1, and flexural strength, shrinking percentage and fire endurance are almost the same, water absorption rate
Increase it is less, resistant waterproof performance decline it is more.Colored coarse aggregate, water by a large number of experiments, selected by the utility model
Mud, water-cement ratio are optimal；The bending resistance of organic fiber raising decorative panel；Decorative panel compactness can be improved in vacuum defoamation,
To improve mechanical property, the resistant waterproof performance, fire resistance of decorative panel；Decoration can be improved in sanding and polishing sprayed protection agent
Resistant waterproof performance, wear-resisting property and the scoring resistance energy of plate surface reduce accumulation of salt in the surface soil phenomenon.
Obviously, above-described embodiment of this patent is only intended to clearly illustrate this patent example, and is not pair
The restriction of the embodiment of this patent.For those of ordinary skill in the art, may be used also on the basis of the above description
To make other variations or changes in different ways.There is no necessity and possibility to exhaust all the enbodiments.It is all this
Made any modifications, equivalent replacements, and improvements etc., should be included in patent claims within the spirit and principle of patent
Protection scope within.
Claims (3)
1. a kind of superhigh tenacity concrete inorganic decorating board of surface containing pattern, 100 megapascal, counter-bending strong are greater than by compression strength
The superhigh tenacity concrete that degree is greater than 16 megapascal adds arrangement of reinforcement is prefabricated to form, and four edges of the decorative panel include the peace of perforation
Bolt hole is filled, wherein arrangement of reinforcement is criss-cross web, uses sealing structure glue sticking, feature between adjacent decorative panel
It is, the length of the superhigh tenacity concrete inorganic decorating board is 500-2400mm, width 500-1200mm, with a thickness of 15
~30mm.
2. a kind of superhigh tenacity concrete inorganic decorating board of the surface according to claim 1 containing pattern, which is characterized in that
The superhigh tenacity concrete inorganic decorating board is multilayered structure, and the web is middle layer, following table on the web
Face is covered with concrete material layer.
3. a kind of superhigh tenacity concrete inorganic decorating board of the surface according to claim 1 containing pattern, which is characterized in that
The position of the installation bolt hole is located at respectively at the 50mm of decorative panel both sides.