CN1226106C - Building of regenerated resource walling - Google Patents
Building of regenerated resource walling Download PDFInfo
- Publication number
- CN1226106C CN1226106C CNB031100120A CN03110012A CN1226106C CN 1226106 C CN1226106 C CN 1226106C CN B031100120 A CNB031100120 A CN B031100120A CN 03110012 A CN03110012 A CN 03110012A CN 1226106 C CN1226106 C CN 1226106C
- Authority
- CN
- China
- Prior art keywords
- building
- walls
- wall body
- coarse aggregate
- aggregate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
The present invention relates to a field of resources science, environmental protection and buildings, which is an ecological building wall body mainly aiming to eliminate building rubbish. The ecological building wall body is a building wall body material prepared from treated building rubbish aggregate, clean sand, fly ash, cement, hydrated lime powders, calcined gypsum powders, fibrous materials, additives and molding water and is used for bearing or non-bearing wall body engineering of internal walls, external walls, thermal insulation walls, earth-retaining walls, enclosure walls, etc. of industrial buildings and civil buildings.
Description
The present invention relates to resources science, environmental protection and building field, be a kind of be the construction wall of primary raw material with the building waste.
Along with the economic sustained and rapid development of China, the level of urbanization improves constantly, the extension in city is enlarging, quantity is increasing, this cultivated land resource that China is originally lacked has relatively constituted great threat, and the sintered clay tile product that uses is is at present occupied the arable land in a large number, makes this problem seriousization that more become, for a large amount of building wastes that pull down and remove a building for reconstruction in the old town and the Xincheng District construction produces, existing processing method be the soot landfill or pour to field, stream, the roadside in suburb nearby.Processing is not only being polluted environment but also destroy and wasted resource like this, also is unfavorable for the sustainable development of architectural engineering.
The present invention is intended to building waste is carried out harmless treatment, makes it to become the circular regeneration resource, produces a kind of non-autoclaved and unburned environmental protection, energy-conservation, high-strength wall material.
Its technical scheme is achieved as follows:
One, the raw material of finished product is formed
1, rubbish coarse aggregate raw material
Building waste is sorted, select brick output, watt, the block waste material of inoganic solids with big intensity such as porcelain, stone, concrete, through cleaning, broken, screening, fully mixing, be processed into the good rubbish coarse aggregate raw material of grating then.Its main particle diameter is determined according to the concrete purposes of finished product.The rubbish coarse aggregate raw material for preparing should be sprinkled water before using and be preserved moisture.
2, rubbish mixing fine aggregate raw material
Building waste fine aggregate and the flyash of particle diameter≤5mm after the fragmentation fully are hybridly prepared into rubbish mixing fine aggregate raw material by a certain percentage, also can add a certain amount of clean sand according to purposes.
3, inorganic gel raw material
According to the different purposes of finished product, adopt the proper ratio of inorganic coagulation materials such as cement, gypsum, lime to form, also can use wherein one or both.
4, auxiliary material
SILICA FUME
5, additive
Additive can adopt concrete early strength agent, air-entrainment, water reducer or other type according to the different purposes of finished product, also can not use Concrete Additive according to purposes.
6, moulding water
Moulding water is following two kinds, and preferentially selects first kind for use.
(1) the middle water after Sewage Plant is handled wherein should strict control to the harmful chemical analysis of inorganic gel raw material setting and harden.And take effective measures and prevent to saltout, have peculiar smell and through disinfecting.
(2) clean water.Its quality standard reaches the requirement of relevant concrete water.
Two, the production routine of finished product
Rubbish coarse aggregate raw material with moisture-keeping maintaining, be immersed in 1: 1 the Portland cement SILICA FUME slurries of the weight ratio of mud, also can be immersed in the weight ratio of mud and be and treat the certain fate of maintenance after the initial set in 1: 1 the common silicate cement pulverized fuel ash slurry, make and strengthen rubbish coarse aggregate raw material.
The thick collagen material of mixed intensified rubbish, rubbish mixing fine aggregate raw material, inorganic gel raw material, additive, moulding water, in order to increase toughness, improve nailability and can and prevent that the crack from occurring, can add the good fibrous material of a certain amount of tensile property, and stir, pressure injection is gone into the moulding of mould vibration compacting, and maintenance is to finished product.The use of this materials for wall also can method cast-in-place by the job site and maintenance realize.
Three, the base stock of finished product
This finished product at base stock is:
Rubbish coarse aggregate raw material, rubbish fine aggregate raw material, finished cement, additive, moulding water.
Other composition can require to determine increase and decrease according to purposes.
If the more low-grade finished product of preparation, the rubbish coarse aggregate raw material that is adopted does not need to finish the intensive treatment program.
Four, the specification of finished product
The main specifications of this finished product is cube building block or cuboid sheet material.
This finished product is made hollow type or solid type according to purposes.
Five, these finished product characteristics
Through test and investigation proof, this finished product body of wall has following characteristics:
(1) solved urban development and building waste contaminated environment and plough to reduce between contradiction.
(2) heat insulation, insulation, sound insulation value can be adjusted to excellent by the mode of adding additive.
(3) intensity is high also can regulate.
(4) nailability is strong.
(5) form of construction work is convenient various.
(6) cheap.
Six, scale and benefit
The mode that this invention can take the heavy construction soot to focus on and process stirring moulding suitability for industrialized production streamline realizes, if factory is near sewage treatment plant, middle water after then can utilizing Sewage Plant to handle according to product purpose is done the environmental protection and energy saving benefit like this and can be obtained bringing into play biglyyer.
Claims (2)
1, a kind of manufacture method of strengthening aggregate building regenerated resources materials for wall, it is characterized in that building waste is sorted, select brick output, watt, porcelain, stone, concrete, coarse aggregate through cleaning, fragmentation, screening, generation after abundant the mixing, be immersed in the weight ratio of mud and be in 1: 1 the Portland cement SILICA FUME slurries, the construction refuse regenerated coarse aggregate of reinforcement is made in maintenance after treating initial set, makes intensifying regenerating aggregate concrete walling material then.
2, the reinforcement of the described coarse aggregate of claim 1 also can be immersed in coarse aggregate the weight ratio of mud and is in 1: 1 the Portland cement pulverized fuel ash slurry and finish.