CN102287052A - Construction method of ecological wall - Google Patents

Abstract

The invention discloses a construction method of an ecological wall. The construction method comprises the steps of processing materials, erecting a formwork and configuring reinforcement, feeding the materials, removing the formwork, applying a geotextile, brushing asphalt and the like. The construction method has the following beneficial effects: the wall is convenient to construct and has good quality and the wall per m<3> can save electrical energy by 4 degrees, cement amount by over 30kg and clay by 0.6m<3> compared with the brick body.

Description

The job practices of ecological wall

Technical field

The present invention relates to a kind of job practices of ecological wall.

Background technology

The construction of ecological wall generally adopts mud wall to pile up, and its stack manner has two kinds: a kind of is that water is folded: earth and water are are fully mixed and stirred, and its water content is about 20%, and with the special-purpose wall instrument of beating, the shovel mound is folded then; Another kind of for non-irrigated folded: as to be to draft body of wall width formwork erection, to add folded dried mud compacting.Tradition mud wall technology subject matter is to utilize problems such as clay resource is many, the body of wall life-span is short.

Summary of the invention

The object of the present invention is to provide a kind of easy construction, the job practices of the ecological wall that wall quality is good.

Technical solution of the present invention is:

A kind of job practices of ecological wall is characterized in that: comprise the following steps:

(1) material processed: material of main part pulverized be the particle of particle diameter for≤1cm; Fibrous material is processed into fineness less than 0.15mm, and length mixes material of main part, fibrous material, cementitious materials and the water part by weight by 6:2:1:1 then less than the particle of 10mm; Described material of main part is one or more in earth, cinder, the building waste; Described fibrous material is one or more in stalk, wood chip, the foam; Described cementitious materials is cement, lime or gypsum;

(2) formwork erection, configuration reinforcement: carry out formwork erection and configuration reinforcement by designing requirement;

(3) feed intake: the material that step (1) is prepared feeds intake, and the thickness that feeds intake is 30cm, tamps then or vibrates, and makes compactness greater than 98%;

(4) form removal: after body of wall forms 3d, carry out form removal;

(5) geotextiles of applying ointment or plaster: after the form removal, after the time body of wall more than 3 months is metalled run out, the geotextiles of on body of wall, applying ointment or plaster;

(6) brushing pitch: after geotextiles is applied ointment or plaster, be 0.5cm pitch, form the waterproofing course surface layer at the even brushing thickness of geotextiles.

Easy construction of the present invention, wall quality is good, and every cubic metre of body of wall is compared with the brick body and can be saved 4 degree electric energy, saves more than the cement consumption 30kg, saves 0.6 cubic metre of clay.

The specific embodiment

The invention will be further described below in conjunction with embodiment.

The specific embodiment

A kind of job practices of ecological wall comprises the following steps:

(1) material processed: material of main part pulverized be the particle of particle diameter for≤1cm; Fibrous material is processed into fineness less than 0.15mm, and length mixes material of main part, fibrous material, cementitious materials and the water part by weight by 6:2:1:1 then less than the particle of 10mm; Described material of main part is one or more in earth, cinder, the building waste; Described fibrous material is one or more in stalk, wood chip, the foam; Described cementitious materials is cement, lime or gypsum;

(2) formwork erection, configuration reinforcement: carry out formwork erection and configuration reinforcement by designing requirement;

(3) feed intake: the material that step (1) is prepared feeds intake, and the thickness that feeds intake is 30cm, tamps then or vibrates, and makes compactness greater than 98%;

(4) form removal: after body of wall forms 3d, carry out form removal;

(5) geotextiles of applying ointment or plaster: after the form removal, after the time body of wall more than 3 months or 3 months is metalled run out, the geotextiles of on body of wall, applying ointment or plaster;

(6) brushing pitch: after geotextiles is applied ointment or plaster, be 0.5cm pitch, form the waterproofing course surface layer at the even brushing thickness of geotextiles.

Claims (1)

1. the job practices of an ecological wall is characterized in that: comprise the following steps:

(1) material processed: material of main part pulverized be the particle of particle diameter for≤1cm; Fibrous material is processed into fineness less than 0.15mm, and length mixes material of main part, fibrous material, cementitious materials and the water part by weight by 6:2:1:1 then less than the particle of 10mm; Described material of main part is one or more in earth, cinder, the building waste; Described fibrous material is one or more in stalk, wood chip, the foam; Described cementitious materials is cement, lime or gypsum;

(2) formwork erection, configuration reinforcement: carry out formwork erection and configuration reinforcement by designing requirement;

(3) feed intake: the material that step (1) is prepared feeds intake, and the thickness that feeds intake is 30cm, tamps then or vibrates, and makes compactness greater than 98%;

(4) form removal: after body of wall forms 3d, carry out form removal;

(5) geotextiles of applying ointment or plaster: after the form removal, after the time body of wall more than 3 months is metalled run out, the geotextiles of on body of wall, applying ointment or plaster;

(6) brushing pitch: after geotextiles is applied ointment or plaster, be 0.5cm pitch, form the waterproofing course surface layer at the even brushing thickness of geotextiles.