CN103922655B - Ecological heat preservation wall brick preparation method - Google Patents
Ecological heat preservation wall brick preparation method Download PDFInfo
- Publication number
- CN103922655B CN103922655B CN201410138706.4A CN201410138706A CN103922655B CN 103922655 B CN103922655 B CN 103922655B CN 201410138706 A CN201410138706 A CN 201410138706A CN 103922655 B CN103922655 B CN 103922655B
- Authority
- CN
- China
- Prior art keywords
- carries out
- heat preservation
- mould
- ecological
- maintenance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of ecological heat preservation wall brick preparation method, comprise raw material disposal, material configuration, stir, enter the steps such as mould, compacting, maintenance, form removal cutting.Invention applies tangerine bar grass meal and polyurethane foams, and building waste, the raw material configurations such as flyash, cement, river sand form, and are applicable to different zones building construction, dissimilar building construction, different sites body of wall.
Description
Technical field
The present invention relates to a kind of ecological heat insulating wall brick masonry constructional method.
Background technology
Building construction wall body structure form has gone through Ni Caoqiang, brick wall, brick mix wall, reinforced concrete wall, the several Structure Stage of steel structure body wall.Body of wall is carried out reforms, the Chinese government attaches great importance to, and from 70 years last century, governments at all levels of China corrected this mechanism until the level People's Government of counties and cities all set up wall, really setting up of this mechanism has greatly promoted China's wall reform, and in wall reform, played good effect.But along with scientific technological advance, social progress, current applied brick mix structure wall, steel and concrete structure wall, steel structure body wall, is still not suitable with Future Social Development demand, needs to reform further.
Building construction body of wall is generally steel and concrete structure wall at present is both at home and abroad main body, and this wall cost is high, expends natural resources many, does not take measures on customs clearance, the weakness such as poor thermal insulation property.
Summary of the invention
The object of the present invention is to provide a kind of easy construction, effective ecological heat preservation wall brick preparation method.
Technical solution of the present invention is:
A kind of ecological heat preservation wall brick preparation method, comprises the following steps:
(1) raw material disposal: ecological heat preservation wall brick makes material except commodity cement, polyurethane foam agent material, and other material is equal, carries out processing; Straw grass through grinding and processing, grass meal silk after processing, filament length≤5mm, stem is thick≤2mm; Wood materials carries out carbonizing treatment, is carried out burning into wooden carbon by wood materials, and is pulverized by wooden carbon, particle diameter >=3mm after pulverizing; Earth is through baking process, and water ratio answers≤3%, then carries out process of milling, and after process, fineness is≤1mm; Reinforcing bar is rejected in building waste process, then pulverizes, particle diameter≤30mm after pulverizing;
(2) material configuration: by weight allocation ratio: ecological Cai Liao ︰ hot-resistant heat-preserving Cai Liao ︰ Jiao ties Cai Liao ︰ aggregate=40% ︰ 5% ︰ 30% ︰ 25%; Described ecomaterial is straw grass and charcoal, and the two weight ratio is 3:1; Described hot-resistant heat-preserving material is polyurethane foams; Described consolidating material is cement; Described aggregate is building waste;
(3) stir: adopt stirrer to enter dry mixing more than 5 times, guarantee fully to mix thoroughly, then press raw-material weight and water weight proportion 10 ︰ 3, grab agglomerating with hand, namely loose being advisable of loosing one's grip, carries out stirring more than 3 times;
(4) mould is entered: mould specification is selected to carry out selection according to brick body design specification and determined, transfers in mould by brick body mixing material;
(5) compacting: by application machine by material compaction;
(6) maintenance: carry out maintenance in a mold, curing time is 5-7 days;
(7) form removal cutting: maintenance expires, and carries out form removal, gently tears open.
Invention applies tangerine bar grass meal and polyurethane foams, and building waste, the raw material configurations such as flyash, cement, river sand form, and are applicable to different zones building construction, dissimilar building construction, different sites body of wall.
Below in conjunction with embodiment, the invention will be further described.
Embodiment
A kind of ecological heat preservation wall brick preparation method, comprises the following steps:
(1) raw material disposal: ecological heat preservation wall brick makes material except commodity cement, polyurethane foam agent material, and other material is equal, carries out processing; Straw grass through grinding and processing, grass meal silk after processing, filament length≤5mm, stem is thick≤2mm; Wood materials carries out carbonizing treatment, is carried out burning into wooden carbon by wood materials, and is pulverized by wooden carbon, particle diameter >=3mm after pulverizing; Earth is through baking process, and water ratio answers≤3%, then carries out process of milling, and after process, fineness is≤1mm; Reinforcing bar is rejected in building waste process, then pulverizes, particle diameter≤30mm after pulverizing;
(2) material configuration: by weight allocation ratio: ecological Cai Liao ︰ hot-resistant heat-preserving Cai Liao ︰ Jiao ties Cai Liao ︰ aggregate=40% ︰ 5% ︰ 30% ︰ 25%; Described ecomaterial is straw grass and charcoal, and the two weight ratio is 3:1; Described hot-resistant heat-preserving material is polyurethane foams; Described consolidating material is cement; Described aggregate is building waste;
(3) stir: adopt stirrer to enter dry mixing more than 5 times, guarantee fully to mix thoroughly, then press raw-material weight and water weight proportion 10 ︰ 3, grab agglomerating with hand, namely loose being advisable of loosing one's grip, carries out stirring more than 3 times;
(4) mould is entered: mould specification is selected to carry out selection according to brick body design specification and determined, transfers in mould by brick body mixing material;
(5) compacting: by application machine by material compaction;
(6) maintenance: carry out maintenance in a mold, curing time is 5-7 days;
(7) form removal cutting: maintenance expires, and carries out form removal, gently tears open.
When using this insulating brick insulated wall to build by laying bricks or stones, comprise the following steps:
(1) processing base level: to body of wall basis, by working design requirement, carry out body of wall based process, and carry out line location, cut height and fill out low, ensure that basal plane is smooth;
(2) mixing mortar: mortar material configuration selection 325 or 425 ordinary Portland cement, sand selects medium sand, and fineness mould degree controls 2.5, lime putty selected by adulterant, fine grinding quicklime, wet concentration clean water, proportioning is configured by weight: Shui Ni ︰ Sha ︰ Can He Liao ︰ water=3 ︰ 6 ︰ 1 ︰ 2;
(3) build by laying bricks or stones: building method, adopt full laid process.
(4) lacing wire: to nook, door/window corner place, arranges connecting lacing wire, guarantees resistance to overturning;
(5) brushing pitch: boil pitch, sprays at wall outer side hairbrush or spray gun the pitch that a layer thickness is 5mm;
(6) geotextile is pasted: when after pitch spraying, on metope, cover geotextile immediately;
(7) mortar plucking: adopt thermal insulation mortar plucking, thickness is 10mm; 425 silicate Portland cement 350kg selected by insulation plucking mortar, SILICA FUME 25-53kg, flyash 50kg, 40-70 order silica sand 250kg, 50-100 order silica sand 250kg, nanometer rubber powder 15kg, Vltra tears 2-3kg, anti-crack fiber 1kg, wood fibre 5kg is configured, stir, metope wharf's pavement quality.
Claims (1)
1. an ecological heat preservation wall brick preparation method, is characterized in that: comprise the following steps:
(1) raw material disposal: ecological heat preservation wall brick makes material except commodity cement, polyurethane foam agent material, and other material all carries out processing; Straw grass, through grinding and processing, becomes grass meal silk, filament length≤5mm after processing, and stem is thick≤2mm; Wood materials carries out carbonizing treatment, is carried out burning into wooden carbon by wood materials, and is pulverized by wooden carbon, particle diameter >=3mm after pulverizing; Earth is through baking process, and water ratio answers≤3%, then carries out process of milling, and after process, fineness is≤1mm; Reinforcing bar is rejected in building waste process, then pulverizes, particle diameter≤30mm after pulverizing;
(2) material configuration: by weight allocation ratio: ecological Cai Liao ︰ hot-resistant heat-preserving Cai Liao ︰ Jiao ties Cai Liao ︰ aggregate=40% ︰ 5% ︰ 30% ︰ 25%; Described ecomaterial is straw grass and wooden carbon, and the two weight ratio is 3:1; Described hot-resistant heat-preserving material is polyurethane foams; Described consolidating material is cement; Described aggregate is building waste;
(3) stir: adopt stirrer to enter dry mixing more than 5 times, guarantee fully to mix thoroughly, then press raw-material weight and water weight proportion 10 ︰ 3, grab agglomerating with hand, namely loose being advisable of loosing one's grip, carries out stirring more than 3 times;
(4) mould is entered: mould specification is selected to carry out selection according to brick body design specification and determined, transfers in mould by brick body mixing material;
(5) compacting: by application machine by material compaction;
(6) maintenance: carry out maintenance in a mold, curing time is 5-7 days;
(7) form removal cutting: maintenance expires, and carries out form removal, gently tears open.