CN1218854A - Terry knitting fabric, and its producing method and sewing method - Google Patents
Terry knitting fabric, and its producing method and sewing method Download PDFInfo
- Publication number
- CN1218854A CN1218854A CN98103227A CN98103227A CN1218854A CN 1218854 A CN1218854 A CN 1218854A CN 98103227 A CN98103227 A CN 98103227A CN 98103227 A CN98103227 A CN 98103227A CN 1218854 A CN1218854 A CN 1218854A
- Authority
- CN
- China
- Prior art keywords
- cloth
- sewing
- stringer
- looped pile
- pile part
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to provide a pile knit fabric which can be sewn together at a high speed, a process for producing the fabric and a method for the sewing of the fabric. A wale loop part 14 for forming a wale W of a ground cloth of a pile knit fabric 11 is fellable erected in a state deformable to be escaped from a sewing needle when brought into contact with a sewing machine needle 5 approaching from above and below. The wale loop part 14 for forming the wale W of a ground cloth is fellably raised to form a pile knit fabric 11 by shrinking the knit cloth by heat-treatment. The pile knit fabrics are sewn together using a sewing machine needle of JIS No.23 (the diameter is 1.6 mm) to 19 (the diameter is 1.2 mm) at a sewing speed of >=1,500 spm.
Description
The present invention relates to a kind ofly can carry out the at a high speed knitted loop cloth of sewing, and preparation method thereof and bind.Described knitted loop cloth can be made into chair cover or analog, is used for seat, the outer surface of conventional chair or analog.
Usually, to shown in Figure 6, knitted loop cloth 1 is made at the knitting state of flat pin by filling 2 and pile yarns 3, and pile yarns 3 are cut into the clipping shape as Fig. 4.In addition, as knitted loop cloth, have a position in a uncut pile shape, wherein, the sinker loop that is made of pile yarns 3 is not sheared.
After using knitted loop cloth 1 to make in the cover for seat, cloth is cut into preliminary dimension, the sheet stock that is cut into is stitched together by Sewing machines.In order to improve output, can under the high-speed state that improves Sewing machines speed, carry out sewing operation.At this moment, the sewing needle of Sewing machines will adopt bodkin, with stand high-speed sewing (as, JIS#19 (diameter 1.2mm) or thicker pin).
In addition, for knitted loop cloth 1, when utilizing the tailor-tacking swage to carry out high speed when sewing, sewing needle 5 can produce collision with stringer looped pile part 4, this stringer looped pile partly comprises the filling 2 of the institutional framework that forms a column cloth, and stringer looped pile part 4 may be sewed pin 5 and cut off.Owing to cut off filling 2, suturing part branch does not enlarge from notch, thereby causes the linear slit fracture.Therefore, in order to prevent the not increase of sutured portion, coat gum in the back of stringer looped pile part to form a back-up coat or to comprise knitted fabric by adhering to one usually, nonwoven fabric or analog are realized at interior back-up coat reinforcing.
But the most of knitted loop cloth 1 that is in the cloth back is made of pile yarns 3.Therefore, therefore the institutional framework of the cloth that need strengthen, so just possibly can't prevent the increase by the not sutured portion of filling cut-off parts generation by pile yarns 3 and reinforcing indirectly at cloth back covering filling 2.In addition, owing to will finish the reinforcing operation, also existence can cause the problem that cost of manufacture increases.
In addition, with regard to knitted loop cloth, filling 2 is set at the whole back of cloth, even also can not prevent the expansion by the not sutured portion of filling cut-off parts generation under the situation of cloth through the reinforcing operation.
Therefore, result according to be sewed under high speed for the stringer looped pile part 4 that obtains comprising filling 2 that pin 5 cuts off former thereby the test of many times of carrying out, the inventor has found to adopt can sew at a high speed stringer looped pile part and the knitted loop cloth of not counted out, and preparation method thereof and bind, under the condition of not reinforcing operation, also can finish at a high speed sewing.
For the knitted loop cloth of under the situation of not reinforcing cloth, sewing at a high speed, device that the present invention according to claim 1 adopts, in knitted loop cloth, make the stringer looped pile part of the institutional framework that forms column cloth upright, so that can lodge, and make cloth be suitable for distortion,, can break away from from sewing needle with when the sewing needle with the Sewing machines of sending to from the above and below contacts.For further removing the obstacle that the stringer looped pile partly is out of shape,, also can adopt the material that is added with smoothing preparation for the filling of the institutional framework that forms cloth and/or the pile yarns of formation pile part.
According to the present invention, when the sewing needle of the Sewing machines of sending to from the above and below partly contacts with the stringer looped pile that forms the column cloth tissue, stringer looped pile part can be out of shape with the sewing needle from the Sewing machines sent to and be broken away from, and therefore, the sewing needle of Sewing machines can not cut off stringer looped pile part.In addition, when use was stained with the filling of smoothing preparation, with respect to the sewing needle of the Sewing machines of sending to, the contact resistance of stringer looped pile part was weakened.Thereby can finish the distortion of stringer looped pile part more glibly.In addition, when having adopted the pile yarns that are stained with smoothing preparation, be easy to slide, and the distortion or the motion that are easy to the stringer looped pile part that breaks away from from the sewing needle of the Sewing machines sent to can be finished more glibly at the pile yarns of stringer looped pile part.
In order to be manufactured on the knitted loop cloth that to sew at a high speed under the situation of not reinforcing cloth, device that the present invention according to claim 3 adopts, a kind of method of making claim 1 or 2 described knitted loop cloths is provided, wherein make the stringer looped pile part that forms a column cloth institutional framework upright, so that by making the cloth that has been made into experience heat treatment so that cloth shrinks and can lodge.In this case, in order to promote stringer looped pile part upright, can adopt percent thermal shrinkage to carry out knitting greater than the filling of pile yams.In addition,,, knitted cloth should be placed on the conveyer belt, under the situation that is not subjected to any external force, heat-treat so that make the whole zone lodging of cloth in order to make stringer looped pile part upright.In addition, in order to improve the DIMENSIONAL STABILITY of cloth, make cloth by heat treatment through after shrinking, when on cloth, finishing the HEAT SETTING operation, along cloth vertically apply tentering tension force, its degree should be able to keep stringer looped pile part upright so that can lodge.
According to the present invention, knitted loop cloth can be provided, wherein when by make cloth through Overheating Treatment so that cloth shrinks when the stringer looped pile is partly lodged, make the stringer looped pile part of the institutional framework stringer that forms cloth upright.In addition, when being arranged on the conveyer belt and when under tension-free state, heat-treating, can making stringer looped pile part upright, can make its evenly lodging in the whole zone of cloth simultaneously by making.In addition, when after heat treatment, when carrying out the HEAT SETTING operation, can obtain to have the cloth of good DIMENSIONAL STABILITY with respect to cloth.
In order under the situation of not reinforcing cloth, to carry out the high speed sewing, device of the present invention according to claim 3, in sewing up the described knitted loop cloth of claim 1, the sewing needle (diameter is 1.6mm) that utilizes the Sewing machines of JIS#23 can be to sew more than or equal to the Sewing machines sewing velocity of 1500spm (the stroke number of per minute) to #19 (diameter is 1.2mm).
According to the present invention, promptly use the tailor-tacking swage to sew up cloth of the present invention at a high speed, the stringer looped pile of the institutional framework that forms column cloth partly is out of shape with the sewing needle from the Sewing machines sent to breaks away from, so just can not cut off under the stringer looped pile situation partly and finish sewing operation at the sewing needle of Sewing machines.
Fig. 1 is an embodiment of knitted loop cloth of the present invention, and wherein, near the cut state of clipping that has amplified cloth institutional framework surface is exaggerated, and understands the clipping of right half part with the surface view linear list;
Fig. 2 is the sectional view along Fig. 1 center line A-A, is depicted as the state that clipping is not cut;
Fig. 3 is the sectional view along Fig. 1 center line B-B, is depicted as the state that clipping is not cut;
Fig. 4 is not through reinforcing the conventional loop knitted cloth of operation, has wherein amplified the state after near the clipping the institutional framework surface of cloth has been cut off and has removed, and understands the clipping of right half part with the surface view linear list;
Fig. 5 is the sectional view along Fig. 4 center line A-A, is depicted as the state that clipping is not cut;
Fig. 6 is the sectional view along Fig. 4 center line B-B, is depicted as the state that clipping is not cut;
According to following embodiment shown in the drawings the present invention is illustrated.The embodiment that Fig. 1 to Fig. 3 has described knitted loop cloth of the present invention (hereinafter, be called " cloth of the present invention "), wherein Fig. 1 is a surface view, this view has amplified the state that clipping has been cut off and removed near the cloth weave, and linear expression the clipping of right half part, Fig. 2 is the sectional view along Fig. 1 center line A-A, is depicted as the state that clipping is not cut off, Fig. 3 is the sectional view along Fig. 1 center line B-B, is depicted as the state that clipping is not cut off.
As Figure 1-3, cloth 11 of the present invention is woven under the plain stitch state by filling 2 and pile yarns 3, and forms the clipping shape by the pile part 13 that shearing contains pile yarns 3.The characteristics of cloth 11 of the present invention are corresponding stringer looped pile part 14, and this part comprises the filling 2 of the institutional framework stringer w that forms corresponding cloth.Promptly, moving towards direction C along the institutional framework of cloth in filling 14a and sinker loop part 15 is intertwined under the situation as its basic side each other continuously, corresponding stringer looped pile part 14 can be upright to the face side distortion, as shown in Figure 2, when the sewing needle 5 most advanced and sophisticated 5a that make stringer looped pile part 14 with the Sewing machines that is used to sew up cloth contact, shown in double dot dash line among the figure, stringer looped pile part 14 can be deformed descending along the lodging direction, so that stringer looped pile part 14 breaks away from from sewing needle 5 by the promotion of the sewing needle 5 sent to.
Because stringer looped pile part 14 can be upright along lodging direction-agile shape ground, so can be along three-dimensional (with respect to the fore-and-aft direction in the space of stringer looped pile part 14 occupied row in stringer looped pile part 14, left and right directions and above-below direction) produce distortion, this will help the disengaging with sewing needle 5.Be deformed into from Sewing machines sewing needle after 5 most advanced and sophisticated disengagings, the compressing of the inclined-plane 5b by sewing needle in Sewing machines 5 most advanced and sophisticated near is moved stringer looped pile part 14 along continuous straight runs, and therefore, the sewing needle 5 that stringer looped pile part 14 can not be sewed machine excises.Stringer looped pile part 14 relies on suitable elasticity upright, therefore, has firmly formed the distortion that can break away from from sewing needle 5 reposefully, and sewing needle 5 pushings of depositing Sewing machines down and the motion on the horizontal direction that produces.
When the sewing needle 5 most advanced and sophisticated 5a of Sewing machines send to the cloth surface from the cloth back, this distortion and the motion that also can produce stringer looped pile part 14 equally.Promptly, when the sewing needle 5 most advanced and sophisticated 5a at Sewing machines send to the cloth surface from the cloth back, it is contacted with corresponding stringer looped pile part 14, though this explanation is omitted, but, corresponding stringer looped pile part 14 will produce distortion, and be separated with sewing needle 5, locate corresponding stringer looped pile part 14 further at this by the promotion of the sewing needle 5 sent to or analog, raise and along continuous straight runs moves by the promotion of the inclined-plane 5b sewing needle 5 front ends that are in the Sewing machines of further sending near, therefore, corresponding stringer looped pile part 14 can not be sewed sewing needle 5 cut-outs of machine.
Therefore, even the surface of two-layer cloth 11 of the present invention is overlapped mutually, by the sewing needle 5 of Sewing machines, sew from the cloth rear side, the sewing needle 5 of the Sewing machines that stringer looped pile part 14 also can not be sent to cuts off.
In addition, the sewing needle 5 of Sewing machines can be from the above and below be sent to around ground-tint part (ground portion) 14a of the stringer looped pile part 14 that is intertwined with sinker loop looped pile part 15 or its.But, twine part by make filling 2 and pile yarns 3 in conjunction with and suitably be intertwined securely and form, and link to each other with sinker loop looped pile part 15 on being in yielding both sides, therefore, twine part and be easy to whole mobile.So, twine part when contact when making with the most advanced and sophisticated 5a of the sewing needle 5 of Sewing machines, twining part can be moved, and breaks away from from sewing needle 5 by the promotion of the sewing needle 5 sent to, can not be sewed sewing needle 5 cut-outs of machine.
Equally, the sewing needle 5 of Sewing machines can be sent to from the above and below towards sinker loop looped pile part 15.But, sinker loop looped pile part 15 is easy to be moved, therefore, and when the most advanced and sophisticated 5a that makes sinker loop looped pile part 15 with the sewing needle 5 of Sewing machines contacts, promotion by the sewing needle 5 sent to makes sinker loop looped pile part 15 break away from from sewing needle 5, and the sewing needle 5 that can not be sewed machine cuts off.
Above-mentioned winding part and sinker loop part 15 produce and move, so that be separated with sewing needle 5, this situation is similar to conventional loop knitted cloth 1 shown in Figure 6 to Fig. 4.
But as shown in Figure 5 and Figure 6, the corresponding stringer looped pile part 4 of conventional loop knitted cloth 1 remains on lodging state as shown in Figure 5 and Figure 6, and can not rise to the degree of lodging again.Therefore, when the corresponding stringer looped pile part 4 that makes conventional loop knitted cloth 1 contacts with the most advanced and sophisticated 5a of the Sewing needles of sending at a high speed 5, corresponding stringer looped pile part 4 can not be out of shape at once breaking away from from sewing needle 5, and the shearing of the sewing needle 5 most advanced and sophisticated 5a by Sewing machines is cut off.The cut-out of stringer looped pile part 4 can cause the fracture of seam, and the fracture of seam is caused by above-mentioned cloth institutional framework.
In addition, though saved explanation, cloth 11 of the present invention also can be made of uncut pile, at this place, the pile of pile yarns 3 part is not sheared, they or constitute by length/undercoat suede that the terry height size differs from one another, or cut/hang down lint by the height at the plush place of being cut off and constitute.The cloth 11 of the present invention also multiple pile yarns 3 of available different colours is made.
In addition, though saved explanation, at cloth 11 of the present invention, by the traditional fabrication method known to the public, can sidepiece is provided with a cushion in the back, this cushion is urethane foams or the analog with suitable thickness.And cloth 11 of the present invention can be made refractory process by the preparation method known to the public.
The yarn that is made of polyester filament or staple fibre can be used for the filling 2 and the pile yarns 3 of cloth 11 of the present invention.Select 20 to 1000 deniers' (being preferably 50 to 400 deniers) filling 2 and pile yarns 3, adhere to the polyester-based elasticity macromolecule resin that lumps together with smoothing preparation, silicone or analog are used to filling 2 and/or pile yarns 3, can further improve the slip of sewing needle 5 in the Sewing machines with this.
In the first step, form knitted loop cloth at plain stitch state same as the prior art.At this moment, carry out weaving operation greater than the filling 2 of pile yarns 3, can use without the filling 2 of crossing heat setting processing and reach the pile yarns 3 that in dry heat is handled, passed through heat setting in order to utilize percent thermal shrinkage.
In second step, to heat-treating in the knitted loop cloth that in the first step, prepares, and make the institutional framework of the cloth that comprises filling 2 wrinkling, when the looped pile part 14 that makes the institutional framework stringer w that forms cloth is upright, make it also have the lodging ability, thereby obtain cloth 11 of the present invention.The terry knitting that will obtain in the first step under tension-free state is arranged on net formula conveyer belt or the similar device and heat-treats, on cloth, do not apply external tension this moment, so that make the stringer looped pile part 14 can be evenly upright on the whole zone of cloth, also has the ability of lodging simultaneously.Make cloth finish heat treatment by about 80 ℃-150 ℃ heater, its time of staying is about 10 seconds-10 minutes.The temperature and the time of staying should change according to the heating system (as the hot gas heating system, radiation heating system or similar device) of heater and be determined by test of many times.
In addition, make stringer looped pile part 14 upright by finish heat treatment under tension-free state, the major reason that has the lodging ability simultaneously again is usually by content decision as described below.The filling 2 of this former because thermal contraction and have a thermal strain of 3 generations of pile yarns of littler percent thermal shrinkage at ground-tint part (ground portion) 14a of stringer looped pile part 14 poor by adding hot work, can make stringer looped pile part 14 upright, wherein said ground-tint part is permanent by twining filling 2 and pile yarns 3 to combine securely.
In the 3rd step, make the cloth of the present invention 11 that in second step, obtains improve the DIMENSIONAL STABILITY of cloth through the HEAT SETTING operation.According to the HEAT SETTING operation, catch the cloth of the present invention 11 both sides acies that move along cloth moving direction C with pin formula stenter, and on the stringer direction w of cloth, apply tentering tension force, make cloth pass through heater inside.The degree of tentering tension force and heating is set to and can keeps stringer looped pile part 14 upright, also has the lodging ability simultaneously.
In addition, in this step, the processing of also will preventing fires sometimes, promptly before adding the HEAT SETTING operation by the sprayed coating system, dip coating system or similar device apply the fire prevention composition and the fire prevention composition are being added in the hot work dry on cloth 11 of the present invention.
In the 4th step, on the back of cloth 11 of the present invention, be provided with comprise that the urethane foams with suitable thickness or the bed course of analog, cloth of the present invention have made and experienced the HEAT SETTING operation in the 3rd step.In the operation that bed course is set, mat surface is heated fusing and fuses bed course back at cloth 11 of the present invention, or bed course is adhered to the back of cloth 11 of the present invention by adhesive or analog.
Certainly, also can omit for the 3rd step and the 4th step according to the final use of cloth 11 of the present invention.
By the above portion that makes 11, its sewing operation can utilize #23 sewing needle 5 (diameter is 1.6mm) to the sewing needle of #19 (diameter is 1.2mm), sew with the Sewing machines speed more than or equal to 1500spm.According to cloth 11 of the present invention, even when utilizing the tailor-tacking swage to carry out sewing operation at a high speed, the stringer looped pile part 14 that forms the institutional framework stringer w of cloth also can be out of shape, break away from sewing needle 5 from the Sewing machines sent to, therefore, under the situation of the sewing needle 5 cut-out stringer looped pile parts 14 that can not be sewed machine, can finish sewing operation.In addition, according to cloth of the present invention, owing to can utilize the tailor-tacking swage to carry out sewing operation at a high speed in this way, therefore, utilize finedraw swage, also carry out sewing operation easily with low speed less than 1500spm less than #19 (diameter is 1.2mm).
(embodiment)
The inventor has carried out test that conventional loop knitted cloth and cloth of the present invention are compared under the following conditions, and has obtained following result:
1, for the knitted loop cloth test specimen:
A, usual conditions
(1) filling 2 is the 200 denier's long filaments that comprise polyester, and without Overheating Treatment but passed through the processing of smoothing preparation, this smoothing preparation comprises polyester-based elasticity macromolecule resin.
(2) pile yarns 3 are 200 deniers' polyester filament, and it has passed through the heat treatment in the yarn dyeing step.
(3) described cloth is made of clipping at the knitting state of flat pin, comprises following " a " and " b ".
A, the mesh number of the institutional framework moving direction of cloth be 23/inch and the institutional framework of cloth longitudinally the mesh number be 42/inch.
B, be 21/inch at the mesh number of the institutional framework line direction of cloth, the institutional framework of cloth longitudinally the mesh number be 43/inch.
The content of B, each test specimen:
(1) test specimen 1 (traditional cloth)
This cloth is without the heat treatment of above-mentioned second step.
(2) test specimen 2 (cloth of the present invention)
Just blow the heat treatment that 150 ℃ hot-air carried out for second step from cloth with 1 minute the time of staying towards cloth by heater inside.
2, sewing condition
A, usual conditions
The polyester filament of suture for using for Sewing machines, its rugosity is JIS-L2511#8, comprises 2 * 3 compound silks of 167 dtexs, and the sewing pitch is 5mm.
The content of B, corresponding stitching condition
(1) sewing condition 1
The sewing needle 5 of Sewing machines is JIS#19, and the speed of Sewing machines is 750spm.
(2) sewing condition 2
The sewing needle 5 of Sewing machines is JIS#23, and the speed of Sewing machines is 750spm.
(3) sewing condition 3
The sewing needle 5 of Sewing machines is JIS#23, and the speed of Sewing machines is 1500spm.
3, cloth mesh long duration test method
Answer the stacked surface of test specimen layer mutually opposed two-phase (combination of above-mentioned " a " and " b " in conjunction with these two types), and sew up these sheet stocks from behind, each test specimen of each type has corresponding 4 sheet stocks, and described sheet stock is when being sewn, and is 1500m along the stitch length of moving direction.
4, result of the test
(1) for test specimen 1 (traditional cloth):
1, stitching condition 1
In each sheet stock, in the institutional framework of cloth, average 1.5 place's yarns are cut off.
2, stitching condition 2
In each sheet stock, on the institutional framework of cloth, average 20 place's yarns are cut off.
3, stitching condition 3
In each sheet stock, on the institutional framework of cloth, average 80 place's yarns are cut off.
(2) for test specimen 2 (cloth of the present invention):
In each sheet stock, the cloth with respect in any sewing condition 1,2 and 3 does not produce the yarn breakpoint in the institutional framework of cloth.
For knitted loop cloth of the present invention, because the tailor-tacking swage that the stringer looped pile partly is out of shape with the Sewing machines of sending to from high speed breaks away from, therefore produced good effect, state the sewing needle that stringer part is not sewed machine cuts off and under the situation of not reinforcing cloth, also can not produce sewing and breaking in this place.
The preparation method of knitted loop cloth of the present invention has produced good effect, at this place by very simple processing just can obtain to utilize the tailor-tacking swage of Sewing machines, with the knitted loop cloth of sewing at a high speed, in this processing procedure, described cloth is retracted by heat treatment.
The bind of knitted loop cloth of the present invention has produced good effect, and the filling that can produce the sewing fracture is not cut off, and utilizes the tailor-tacking swage of Sewing machines to carry out the high speed sewing to knitted loop cloth, thereby has improved sewing efficiency greatly.
Claims (6)
1, a kind of knitted loop cloth is characterized in that: make the looped pile part of the institutional framework that forms column cloth upright, when contacting with the Sewing needles of sending to from the above and below, it can lodge and deform break away from from Sewing needles.
2, knitted loop cloth according to claim 1 is characterized in that: for the filling of the institutional framework that forms cloth and/or the pile yarns of formation pile part, adopt the material that has added smoothing preparation.
3, a kind of method that is used to make claim 1 or 2 described knitted loop cloths is characterized in that: the cloth that has been made into makes cloth shrink through Overheating Treatment, makes the looped pile part of the institutional framework stringer that forms cloth upright, so that can lodge.
4, the method for making knitted loop cloth according to claim 3 is characterized in that: making knitted cloth place on the conveyer belt and not applying on the cloth under the state of the tension force that is produced by external force, heat-treat.
5, according to the method for claim 3 or 4 described making knitted loop cloths, it is characterized in that: make the heat treatment of cloth experience and after shrinking, on described cloth, carry out the HEAT SETTING operation, apply tentering tension force simultaneously in the vertical, its degree can make and keep stringer looped pile part upright, and has the lodging ability.
6, the method for making knitted loop cloth according to claim 1 and 2, it is characterized in that: utilize the sewing needle of JIS#23 (diameter is 1.6mm), to sew more than or equal to the Sewing machines sewing velocity of 1500spm (the stroke number of per minute) to #19 (diameter is 1.2mm).