CN1216002C - 钢渣水泥 - Google Patents

钢渣水泥 Download PDF

Info

Publication number
CN1216002C
CN1216002C CN031389422A CN03138942A CN1216002C CN 1216002 C CN1216002 C CN 1216002C CN 031389422 A CN031389422 A CN 031389422A CN 03138942 A CN03138942 A CN 03138942A CN 1216002 C CN1216002 C CN 1216002C
Authority
CN
China
Prior art keywords
cement
slag
steel slag
present
raw material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN031389422A
Other languages
English (en)
Other versions
CN1486951A (zh
Inventor
侯新凯
李虎森
李文卿
范莲花
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taiyuan Iron and Steel Group Co Ltd
Original Assignee
Taiyuan Iron and Steel Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taiyuan Iron and Steel Group Co Ltd filed Critical Taiyuan Iron and Steel Group Co Ltd
Priority to CN031389422A priority Critical patent/CN1216002C/zh
Publication of CN1486951A publication Critical patent/CN1486951A/zh
Application granted granted Critical
Publication of CN1216002C publication Critical patent/CN1216002C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

本发明公开了一种钢渣水泥，它是先将石灰石、粘土、砂岩、钢渣等原料按比例配合后，经过粉磨、煅烧制成水泥熟料，然后将水泥熟料与水渣、钢渣、添加剂等原料按比例配合共同粉磨即形成水泥。本发明在生产熟料和水泥时均使用了钢渣，提高了钢渣的用量，解决了环境污染和资源短缺问题，为工业废渣处理找到了一条有效途径，具有很高的社会效益和经济效益。本发明具有需水量小，后期强度高，与木质素及奈系减水剂适应性好等优点，并且其抗硫酸盐侵蚀、抗干燥收缩和抑制碱集料膨胀性能都较好。

Description

钢渣水泥
技术领域
本发明涉及一种建筑材料，特别是涉及一种钢渣水泥。
背景技术
GB1344-1999中规定的矿渣硅酸盐水泥和GB12958-1999中规定的复合硅酸盐水泥的生产工艺中均使用硫酸渣和铁矿石，掺量在3～5％，它们存在需水量大，后期强度低，与木质素及奈系减水剂适应性差等缺点，并且其抗硫酸盐侵蚀、抗干燥收缩和抑制碱集料膨胀性能都较差。它们不仅存在上述缺点，而且还存在资源短缺问题，没有很好地利用工业废渣，而另一方面钢铁企业的钢渣却通过掩埋的办法处理，既易对环境造成污染，又需占用大量的地方。
发明内容
本发明的目的旨在克服上述缺点，提供一种既能利用工业废渣，保护环境，又能改善复合水泥性能的钢渣水泥。
为达上述目的，本发明钢渣水泥是先将石灰石、粘土、砂岩、钢渣等原料按比例配合后，经过粉磨、煅烧制成水泥熟料，然后将水泥熟料与水渣、钢渣、添加剂等原料按比例配合共同粉磨即形成水泥，其中制备水泥熟料的各原料的重量份配比是：
石灰石675-735份                    粘土100-160份
砂岩85-95份                        钢渣75-85份
制备水泥的各原料的重量份配比是：
熟料375-425份                      水渣375-425份
钢渣160-180份                      添加剂25-35份。
上述的钢渣水泥，其特征在于：所述的添加剂为烧石膏、明矾石和元明粉中的一种或几种。
与现有技术相比，本发明具有如下优点：
1、本发明在生产熟料和水泥时均使用了钢渣，提高了钢渣的用量，解决了环境污染和资源短缺问题，为工业废渣处理找到了一条有效途径，具有很高的社会效益和经济效益。
2、本发明用钢渣作为煅烧水泥熟料的生料原料，易于配制硅酸率较高的熟料，可改善熟料的后期强度，而且还可利用钢渣的晶种作用，改善水泥熟料的易烧性，降低热耗。在高掺量矿渣水泥中引入适量的钢渣，激发矿渣的活性，使混合材总量达60～65％，水泥强度等级可达到42.5，与GB1344-1999中规定的矿渣硅酸盐水泥和GB12958-1999中规定的复合硅酸盐水泥相比，本发明具有需水量小，后期强度高，与木质素及奈系减水剂适应性好等优点，并且其抗硫酸盐侵蚀、抗干燥收缩和抑制碱集料膨胀性能都高于上述两种水泥。
3、本发明在不增加水泥生产设备、不改变水泥工艺条件的情况下，熟料产量提高36％，熟料强度提高10MPa，能耗降低25％，CO2排放量减少12％。若全国的水泥企业广泛应用，每年可消化利用钢渣2000万吨。
具体实施方式
实施例1：本实施例制备水泥熟料的各原料的重量份配比是：石灰石695kg、粘土135kg、砂岩89kg、钢渣81kg；制备水泥的各原料的重量份配比是：熟料425kg、水渣375kg、钢渣170kg、烧石膏12kg、明矾石6kg、元明粉12kg。
实施例2：本实施例制备水泥熟料的各原料的重量份配比是：石灰石700kg、粘土130kg、砂岩90kg、钢渣80kg；制备水泥的各原料的重量份配比是：熟料420kg、水渣380kg、钢渣170kg、烧石膏18kg、元明粉12kg。
实施例3：本实施例制备水泥熟料的各原料的重量份配比是：石灰石710kg、粘土120kg、砂岩92kg、钢渣78kg；制备水泥的各原料的重量份配比是：熟料400kg、水渣400kg、钢渣170kg、烧石膏30kg。
                                上述三个实施例熟料的物理性能
  序号   安定性 标稠用水   细度   凝结时间(h:m)     抗折强度(Mpa)   抗压强度(Mpa)
  ％   ％ 初凝 终凝     3d     28d     3d   28d
  1 合格 22.5  5.0  2:10  3:00   5.4   9.3   28.2   61.8
  2 合格 22.5  6.0  1:50  2:45   5.6   9.4   24.3   59.5
  3 合格 22.5  5.0  1:55  2:30   4.8   9.5   21.8   63.3
                               上述三个实施例的水泥性能
  序号   安定性 标稠用水   细度   凝结时间(h:m)     抗折强度(Mpa)     抗压强度(Mpa)
  ％   ％ 初凝 终凝     3d     28d     3d     28d
  1 合格 24.0  4.8  2:30  5:06     4.6     8.8     18.7     54.3
2 合格 25.3 6.0 1:59 5:14 3.6 8.6 17.0 53.2
3 合格 24.8 5.6 3:17 6:42 4.4 9.1 14.1 47.0

Claims (2)

1、一种钢渣水泥，其特征在于：它是先将石灰石、粘土、砂岩、钢渣原料按比例配合后，经过粉磨、煅烧制成水泥熟料，然后将水泥熟料与水渣、钢渣、添加剂原料按比例配合共同粉磨即形成水泥，其中制备水泥熟料的各原料的重量份配比是：
石灰石675-735               粘土100-160
砂  岩85-95                 钢渣75-85
制备水泥的各原料的重量份配比是：
熟料375-425               水渣375-425
钢渣160-180               添加剂25-35。
2、根据权利要求1所述的钢渣水泥，其特征在于：所述的添加剂为烧石膏、明矾石和元明粉中的一种或几种。
CN031389422A 2003-07-30 2003-07-30 钢渣水泥 Expired - Fee Related CN1216002C (zh)