CN1206033A - Heat insulating waterproof plastic-steel paint - Google Patents
Heat insulating waterproof plastic-steel paint Download PDFInfo
- Publication number
- CN1206033A CN1206033A CN 97108165 CN97108165A CN1206033A CN 1206033 A CN1206033 A CN 1206033A CN 97108165 CN97108165 CN 97108165 CN 97108165 A CN97108165 A CN 97108165A CN 1206033 A CN1206033 A CN 1206033A
- Authority
- CN
- China
- Prior art keywords
- powder
- parts
- aqueous solution
- organizes
- pva
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The heat-insulating and waterproof plastic-steel paint for building roofing consists of separately packed two components, A and B, in the ratio of 5 to 6-10. Component A is liquid comprising acrylate emulsion, PVA water solution and water solution of polyacrylamide; and Component B is solid powder comprising magnesium chloride, silice white, china clay powder, barium sulfate, talcum powder and mica powder. Compared with available technology, the present invention has the features of low cost, high waterproof performance, high heat insulating effect and others, and it may be also used as the middle layer paint for the outer wall of high-rise building.
Description
The present invention relates to a kind of building coating, particularly a kind of roof insulation waterproof plastic-steel paint.
Existing roof insulation waterproof paint all exists and uses that to deposit life not long, constructional difficulties, cost height, weak points such as bad renovation.
The objective of the invention is to overcome the deficiencies in the prior art part and a kind of novel roof insulation waterproof plastic-steel paint is provided.
Technical scheme of the present invention is: heat insulating waterproof plastic-steel paint by two groups of materials of the A that comprises respectively, B by 5: 6～10 mixed and stir and make, A group material is a liquid, B group material is a pressed powder, A group material is made up of acrylic acid ester emulsion, PVA (10%) aqueous solution and poly-two alkene acid amides (0.05～0.1%) aqueous solution, and B group material is made up of magnesium oxide, white carbon black, china clay in powder, barium sulfate, talcum powder and mica powder;
The proportioning of A, two groups of materials of B is as follows:
A organizes material: acrylic ester emulsion 50-80 part
PVA (10%) aqueous solution 10-20 part
Polyacrylamide (0.05-0.1%) aqueous solution 10-30 part
B organizes material: magnesium oxide 25-40 part
White carbon black 15-25 part
China clay in powder 15-30 part
Barium sulfate 15-25 part
Talcum powder 30-40 part
Mica powder 10-20 part;
The blending process of A, two groups of materials of B is as follows:
A organizes material: by proportioning with acrylic acid ester emulsion, PVA (10%) aqueous solution and polyacrylamide (0.05-0.1%) aqueous solution and stir;
B organizes material: magnesium oxide, white carbon black, china clay in powder, barium sulfate, talcum powder and mica powder are mixed and stir by proportioning, be transported in the container of band vibratory screening apparatus again and carefully mix.
Heat insulating waterproof plastic-steel paint provided by the invention is owing to adopt as above technical scheme, compared with prior art, have that cost is low, weathering resistance good, strong adhesion, water resistance are good, good heat-insulation effect, "dead" pollution, nontoxic, environmentally safe, easy construction, be beneficial to the roofing renovation, use the longevity
Embodiment:
The proportioning of A, two groups of materials of B is:
A organizes material: 70 parts of acrylic ester emulsions
10 parts of PVA (10%) aqueous solution
20 parts of polyacrylamide (0.05-0.1%) aqueous solution
B organizes material: 30 parts in magnesium oxide
18 parts of white carbon blacks
22 parts of chinies clay in powder
20 parts in barium sulfate
25 parts of talcum powder
15 parts of mica powders
To prepare and directly on the rigid roofing of cleaning, scrape about 2 mm thick behind two groups of material mixings of packing respectively by said ratio, treat that it does the best effect that can reach insulating water-proof after about 2 hours.
Claims (2)
1, a kind of heat insulating waterproof plastic-steel paint, it is characterized in that by two groups of materials of A, B of packing respectively by 5: 6～10 mixed and stir and make, A group material is a liquid, B group material is a pressed powder, A group material is made up of acrylic acid ester emulsion, PVA (10%) aqueous solution and polyacrylamide (0.05-0.1%) aqueous solution, and B group material is made up of magnesium oxide, white carbon black, china clay in powder, barium sulfate, talcum powder and mica powder;
The proportioning of A, two groups of materials of B is as follows:
A organizes material: acrylic ester emulsion 50-80 part
PVA (10%) aqueous solution 10-20 part
Polyacrylamide (0.05-0.1%) aqueous solution 10-30 part
B organizes material: magnesium oxide 25-40 part
White carbon black 15-25 part
China clay in powder 15-30 part
Barium sulfate 15-25 part
Talcum powder 30-40 part
Mica powder 10-20 part;
The blending process of A, two groups of materials of B is as follows:
A organizes material: by proportioning with acrylic acid ester emulsion, PVA (10%) aqueous solution and poly-two alkene acid amides (0.05-0.1%) aqueous solution and stir;
B organizes material: connect proportioning and magnesium oxide, white carbon black, china clay in powder, barium sulfate, talcum powder and mica powder are mixed and stir, be transported in the container of band vibratory screening apparatus again and carefully mix.
2, coating as claimed in claim 1 is characterized in that the proportioning of A, two groups of materials of B is:
A organizes material: 70 parts of acrylic ester emulsions
10 parts of PVA (10%) aqueous solution
20 parts of polyacrylamide (0.05-0.1%) aqueous solution
B organizes material: 30 parts in magnesium oxide
18 parts of white carbon blacks
22 parts of chinies clay in powder
20 parts in barium sulfate
25 parts of talcum powder
15 parts of mica powders