CN1110698A - Multifunctional ash calcium powder - Google Patents
Multifunctional ash calcium powder Download PDFInfo
- Publication number
- CN1110698A CN1110698A CN 94111729 CN94111729A CN1110698A CN 1110698 A CN1110698 A CN 1110698A CN 94111729 CN94111729 CN 94111729 CN 94111729 A CN94111729 A CN 94111729A CN 1110698 A CN1110698 A CN 1110698A
- Authority
- CN
- China
- Prior art keywords
- coatings
- replace
- water
- urea
- salt
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The filler for building material is made up of first-class calcium lime, talc powder, ammonium alum, aluminium sulfate, silicon oxide, urea, salt and water through mixing. The filling material can be used in various water-soluble coatings, can be used in 106, 107 and 801 coatings to replace light calcium, can be used in scrub resistant coatings to replace attapulgite and wollastonite powder, and can be used in ceramic simulating coatings to replace heavy calcium. The invention has excellent scrubbing resistance and lower cost than other paint fillers.
Description
The present invention is a kind of material of construction, especially for the multifunction filler of making stopping composition in the building coating.
The stopping composition of existing building coating generally adopts fine particle calcium carbonate, coarse whiting, talcum powder and mica powder etc., and it cooperatively interacts, and can be used as the coating stopping composition.Its shortcoming is a not scrubbing resistance of the coating made, and hardness is low, the cost height.
The objective of the invention is to overcome above-mentioned the deficiencies in the prior art, the stopping composition of a kind of multifunction filler as coating is provided, make the coating over-all properties preferable, have scrubbing resistance, hardness height, advantage that cost is low.
Solution of the present invention is: a kind of multifunction filler is characterized in following ratio (weight percent, down together) preparation each component:
One-level unslaked lime 55%～75%;
Talcum powder 7%～13%;
Tschermigite 0.5%～0.9%;
Tai-Ace S 150 0.5%～0.8%;
Silicon oxide 0.9%～1.7%;
Urea 0.4%～0.7%;
Salt 0.1%～0.3%;
Water 15%～30%.
By the multifunction filler of above proportioning, its production technique adopts: lime is smashed, and choosing is fallen to overdo and is had not been cooked or heated long enough lime; After lime of selecting for use and tschermigite, urea, salt, Tai-Ace S 150 are mixed, be piled into taper shape, add water make it the heating clear up; After clearing up cooling, cross the mesh screen choosing, then with talcum powder, silicon oxide, mixing; Break into powder, pack at last.
The present invention's advantage compared with prior art: stopping composition of the present invention can be used in the various water soluble paint.Be used for 106,107,801 coating and replace fine particle calcium carbonate, be used for rubbing-resistant paint and replace attapulgite and wollastonite powder, be used for porcelain-imitated coating and replace coarse whiting.The advantage that the present invention gives prominence to is that scrub performance is fine, cooperates with the PVA emulsion, and the scrubbing resistance number of times is above 300 times; Cooperate with the PVAC emulsion, the scrubbing resistance number of times is above 500 times.Cost of the present invention is low, hardness is high.Its every technical indicator is as follows.
Whiteness 〉=90 degree, colloid index 〉=12%, Calcium of intensifiens 〉=65%, potassium oxide 〉=1.6%, aluminum oxide 〉=2.0%, moisture content≤1.5%, opacifying power＜110 gram/m
2, system porcelain-imitated coating hardness 〉=4.5H.
The present invention can further specify in conjunction with the embodiments.
Embodiment 1, multifunction filler are prepared each component in following ratio:
One-level unslaked lime 62.7%;
Talcum powder 11%;
Tschermigite 0.5%;
Tai-Ace S 150 0.6%;
Silicon oxide 1.2%;
Urea (agricultural) 0.6%;
Salt 0.1%;
Water 23.3%.
The stopping composition that adopts said ratio to make is filled in the coating, has higher hardness and good scrub resistance.
Embodiment 2, multifunction filler are prepared each component in following ratio:
One-level unslaked lime 67.1%;
Talcum powder 8.5%;
Tschermigite 0.6%;
Tai-Ace S 150 0.7%;
Silicon oxide 1.4%;
Urea (agricultural) 0.5%;
Salt 0.2%;
Water 21%.
Stopping composition by this proportioning is filled in the coating, has good scrub resistance.
Claims (2)
1, a kind of multifunction filler is characterized in that in following ratio (weight percent, down together) preparation each component:
One-level unslaked lime: 55%～75%;
Talcum powder: 7%～13%;
Tschermigite: 0.5%～0.9%;
Tai-Ace S 150: 0.5%～0.8%;
Silicon oxide: 0.9%～1.7%;
Urea: 0.4%～0.7%;
Salt: 0.1%～0.3%;
Water: 15%～30%.
2, multifunction filler according to claim 1 is characterized in that each component content is:
One-level unslaked lime: 62.7%;
Talcum powder: 11%; Urea (agricultural): 0.6%;
Tschermigite: 0.5%; Salt: 0.1%;
Tai-Ace S 150: 0.6%; Water: 23.3%.
Silicon oxide: 1.2%;