CN1197810C - Ground tile having natural color and lustre and process for producing same - Google Patents
Ground tile having natural color and lustre and process for producing same Download PDFInfo
- Publication number
- CN1197810C CN1197810C CN 02133328 CN02133328A CN1197810C CN 1197810 C CN1197810 C CN 1197810C CN 02133328 CN02133328 CN 02133328 CN 02133328 A CN02133328 A CN 02133328A CN 1197810 C CN1197810 C CN 1197810C
- Authority
- CN
- China
- Prior art keywords
- parts
- commercially available
- lustre
- natural
- ground tile
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a ground tile having natural color and lustre, which is characterized in that a colored surface layer is prepared from the following raw material components (part by weight): 300 to 400 parts of broken granular stone materials, 100 to 120 parts of quartz sand, 20 to 30 parts of fine stone powder, 100 parts of polyester resins, 2 to 4 parts of curing agents, 1 to 3 parts of accelerating agents and 1 to 2 parts of affinity agents. The surface layer of the organic ground tile containing various natural fine and broken stone materials and the inorganic base layer of cement concrete are organically combined so that the present invention has the advantages of high strength, good abrasion resistance, convenient installation and repair and low cost without consuming precious and limited stone materials any longer. The color and the lustre which are displayed by the ground tile are the inherent colors of the natural stone materials, and the present invention not only has the advantages of natural color and lustre, various colors and no color degradation or environmental pollution, but also has good decoration and practicality, and is an ideal natural colored ground tile.
Description
Technical field
The present invention relates to a kind of colour floor brick, especially a kind of colour floor brick of All Pure Nature color and luster.
Background technology
Along with the raising of people's living standard, people also begin to pay attention to the improvement of urban environment and living environment when pursuing more good days, promptly constantly beautify and greening environment.And in beautifying the environment in cities and towns, can't do without using a large amount of floor tiles.With regard to existing floor tile, remove the concrete floor brick, outside the natural stone floor tile, the colored top layer floor tile that adheres to pigment and cement mixing on cement basic layer is arranged, and the multi color pattern ceramic tile that is fired into.As application number is 98124500 " a kind of colour floor brick and production method thereof ", and application number is 971001545 " a kind of colour floor tile and preparation method thereof " or the like.The color dullness of cement floor tile and natural stone floor tile, especially concerning the natural stone floor tile, its top layer easily collects dust, and because of the big defective that causes using of density difference distance, even more serious is to consume the limited natural rock of reserves; Colour floor brick on the surface, though solved the problem of color dullness because its color adds artificially, through after a while wind, Exposure to Sunlight, drench with rain and wear and tear, just can fade very soon, and expose the true qualities of cement, therefore, existing colour floor brick falls short of the reality; The ceramic tile of multi color pattern is the production cost height not only, and being greatly limited property and be difficult to repair in use.Therefore, floor tile on the market still can not satisfy the needs of real social life at present, is necessary prior art is improved.
Summary of the invention
The object of the present invention is to provide and a kind ofly never fade, the intensity height, cost is low and make full use of that depleted is thin, the colour floor brick of broken natural rock.
The present invention realizes by following technical proposal: described colour floor brick is made of cement basic layer and colored top layer, it is characterized in that colored top layer is formulated by the feed composition of following weight part:
Broken particle building stones 300-400 part,
Quartz sand 100-120 part,
Microlith powder 20-30 part,
100 parts in vibrin,
Solidifying agent 2-4 part,
Promotor 1-3 part,
Affinity agent 1-2 part.
Described solidifying agent adopts commercially available 50%HCH phthalic acid dibutyl ester to stick with paste, and perhaps the 50%BPO phthalic acid dibutyl ester is stuck with paste.
Described promotor is adopted commercially available cobalt naphthenate (containing cobalt amount＞1%), perhaps 10%N, accelerine or N, N-Diethyl Aniline.
Described affinity agent adopts commercially available phosphatidic acid.
Colour floor brick provided by the invention prepares by following processing method:
1, get the raw materials ready: various depleted are nonmetal carefully, metaling carries out fragmentation, makes the diameter of macrobead building stones be not more than 4mm;
2, mix to stir: will above-mentionedly get the raw materials ready and commercially available each auxiliary material mixes by following prescription:
Broken particle building stones 300-400 part,
Quartz sand 100-120 part,
Microlith powder 20-30 part,
100 parts in vibrin,
Solidifying agent 2-4 part,
Promotor 1-3 part,
Affinity agent 1-2 part;
3, top layer moulding: the above-mentioned compound that will stir is put into the mould of getting ready in advance, controls its thickness in the 60-100mm scope, after firmly tying, carries out the vibration that time of vibration was no less than for 120 seconds, must synthesize the colour floor brick top layer;
4, global formation: add the rapid hardening cement concrete that mixes in advance on above-mentioned colour floor brick top layer, control whole floor tile thickness in the 550-600mm scope, and be no less than the vibration in 35 seconds;
5, the dry demoulding: seasoning is after 4 hours, and the demoulding promptly gets the colour floor brick of natural colored.
Described rapid hardening cement is commercially available low basicity sulfate cement.
The present invention compared with prior art has following advantage and effect: because such scheme, organism floor tile top layer and the inorganic basic unit of cement concrete of containing various natural fine, metaling organically are combined into one, intensity height not only, wear resisting property is good, install, repair easy, and employed natural rock is, and depleted is thin, broken, powder, and its cost is lower, no longer consume valuable and limited stone material.In addition the shown color and luster that comes out of floor tile provided by the invention all is a natural rock inherent color, not only never fade in the use, the color and luster nature, color is various, and can not cause any pollution to environment, having ornamental preferably and practicality, therefore, is a kind of comparatively ideal natural colorful floor tile.
Embodiment
Embodiment 1
1, get the raw materials ready: various depleted are nonmetal carefully, metaling carries out fragmentation, makes the diameter of macrobead building stones be not more than 4mm;
2, mix to stir: will above-mentionedly get the raw materials ready and commercially available each auxiliary material mixes by following prescription:
300 parts of broken particle building stones,
100 parts of quartz sands,
20 parts in microlith powder,
100 parts in vibrin,
2 parts of phosphatidic acids
The 50%HCH phthalic acid dibutyl ester is stuck with paste 2 parts,
1 part of cobalt naphthenate (containing cobalt amount＞1%);
3, top layer moulding: the above-mentioned compound that will stir is put into the mould of getting ready in advance, after firmly tying, vibrates for 100 seconds, and making thickness is the synthetic colour floor brick top layer of 80mm;
4, global formation: add the rapid hardening cement concrete (C20) mix in advance on above-mentioned colour floor brick top layer, and carry out the vibration in 35 seconds, make thickness and be 40 square metres of the whole floor tiles of 550mm;
5, the dry demoulding: seasoning is after 4 hours, and the demoulding promptly gets the colour floor brick of natural colored.
Embodiment 2
Adopt the processing method identical, make 50 square metres natural colorful floor tile by following prescription with embodiment 1:
400 parts of broken particle building stones,
120 parts of quartz sands,
30 parts in microlith powder,
100 parts in vibrin,
2 parts of phosphatidic acids
The 50%BPO phthalic acid dibutyl ester is stuck with paste 4 parts,
10%N, 3 parts of accelerines.
Embodiment 3
Adopt the processing method identical, make 45 square metres natural colorful floor tile by following prescription with embodiment 1:
350 parts of broken particle building stones,
110 parts of quartz sands,
25 parts in microlith powder,
100 parts in vibrin,
1 part of phosphatidic acid
The 50%HCH phthalic acid dibutyl ester is stuck with paste 3 parts,
N, 2 parts of N-Diethyl Anilines.
Claims (3)
1, a kind of ground tile having natural color and lustre is characterized in that colored top layer is formulated by the feed composition of following weight part:
Particle diameter is less than broken particle building stones 300-400 part of 4mm,
Quartz sand 100-120 part,
Microlith powder 20-30 part,
100 parts in vibrin,
Solidifying agent 2-4 part,
Promotor 1-3 part,
Affinity agent 1-2 part,
Wherein solidifying agent is that commercially available 50%HCH phthalic acid dibutyl ester is stuck with paste, and perhaps the 50%BPO phthalic acid dibutyl ester is stuck with paste; Promotor is the commercially available cobalt naphthenate that contains cobalt amount＞1%, perhaps 10%N, accelerine or N, N-Diethyl Aniline; Affinity agent is commercially available phosphatidic acid.
2, a kind of production method of ground tile having natural color and lustre is characterized in that it comprises following processing method:
A, get the raw materials ready: nonmetal thin, the metaling of various depleted is carried out fragmentation, make the diameter of macrobead building stones be not more than 4mm;
B, mix to stir: will above-mentionedly get the raw materials ready and commercially available each auxiliary material mixes by following prescription:
Broken particle building stones 300-400 part,
Quartz sand 100-120 part,
Microlith powder 20-30 part,
100 parts in vibrin,
Solidifying agent 2-4 part,
Promotor 1-3 part,
Affinity agent 1-2 part,
Wherein solidifying agent is that commercially available 50%HCH phthalic acid dibutyl ester is stuck with paste, and perhaps the 50%BPO phthalic acid dibutyl ester is stuck with paste; Promotor is the commercially available cobalt naphthenate that contains cobalt amount＞1%, perhaps 10%N, accelerine or N, N-Diethyl Aniline; Affinity agent is commercially available phosphatidic acid;
C, top layer moulding: the above-mentioned compound that will stir is put into the mould of getting ready in advance, controls its thickness in the 60-100mm scope, after firmly tying, carries out the vibration that time of vibration was no less than for 120 seconds, must synthesize the colour floor brick top layer;
D, global formation: add the rapid hardening cement concrete that mixes in advance on above-mentioned colour floor brick top layer, control whole floor tile thickness in the 550-600mm scope, and be no less than the vibration in 35 seconds;
E, the dry demoulding: seasoning demoulding after 4 hours promptly gets the colour floor brick of natural colored.
3, the production method of ground tile having natural color and lustre according to claim 2 is characterized in that described rapid hardening cement is commercially available low basicity sulfate cement.