CN1190319C - Decorative wall leather and its making method - Google Patents

Decorative wall leather and its making method Download PDF

Info

Publication number
CN1190319C
CN1190319C CN 02134040 CN02134040A CN1190319C CN 1190319 C CN1190319 C CN 1190319C CN 02134040 CN02134040 CN 02134040 CN 02134040 A CN02134040 A CN 02134040A CN 1190319 C CN1190319 C CN 1190319C
Authority
CN
China
Prior art keywords
parts
pvc
wall
mould inhibitor
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN 02134040
Other languages
Chinese (zh)
Other versions
CN1404989A (en
Inventor
李文
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sichuan Jinlu Group Co Ltd
Original Assignee
Sichuan Jinlu Group Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sichuan Jinlu Group Co Ltd filed Critical Sichuan Jinlu Group Co Ltd
Priority to CN 02134040 priority Critical patent/CN1190319C/en
Publication of CN1404989A publication Critical patent/CN1404989A/en
Application granted granted Critical
Publication of CN1190319C publication Critical patent/CN1190319C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The present invention discloses wall leather formed by compounding a surface composition and a bottom composition by a scratching technology. The present invention is characterized in that the surface composition has the components by weight of 100 parts of PVC base material, 30 to 60 parts of diisodecyl phthalate, 0 to 25 parts of chlorinated paraffin, 1 to 2 parts of barium-zinc liquid composite stabilizer, 0 to 3 parts of azobisformamide, 0 to 5 parts of antimonic oxide, and 0.2 to 1.5 parts of oil soluble mildew preventing agent for dry films; the bottom composition has the components of 100 parts of PVC base material, 40 to 62 parts of diisodecyl phthalate, 0 to 25 parts of chlorine paraffin, 1.5 to 3.5 parts of barium-zinc liquid composite stabilizer, 2 to 6 parts of azobisformamide, 3 to 8 parts of antimonic oxide, and 0.2 to 2 parts of oil soluble mildew preventing agent for dry films. The technology comprises working procedures such as mixture, filtration, primary scratching and drying, secondary scratching, drying, foaming and molding, peeling, printing, embossing, edge cutting, product inspection and package. The wall leather has the advantages of fire retardance performance, mildew prevention, moisture prevention, sound absorption, good sound isolation performance, no toxicity, no discoloration, aging resistance, long service life, short production technical process, high working efficiency and low product cost, and is a substitute product for traditional wall paper and wall cloth.

Description

A kind of decorative wall leather and manufacture method thereof
Technical field
The present invention relates to a kind of production technique of decorative material for wall surface, exactly relate to the producing and manufacturing technique of a kind of wall with the artificial leather material.
Background technology
What traditional decorative material for wall surface was used is wallpaper or wall paper, and they are to be coated with the product that the PVC plastics generate on paper substrate or fabricbase, be subjected to paper and cloth to influence flame retardant properties not high, the moistureproof and mildewproof poor effect is subjected to environmental restraint very big in the use; The low thin thickness of this product foaming is attached on the metope firmly firmly, can not sound-absorbing, sound insulation; Product structure is to be combined into one by the different layers of material of the coefficient of expansion, produces adverse consequencess such as alice, foaming and shape and color change in causing using; And it is, very easily aging because of thin, the anti-light ability of product.And existing common wall leather on the market, owing to be the cloth sill, no fire retardant and mould inhibitor, fire prevention mildew-resistant moisture effect is very poor.
Summary of the invention
The objective of the invention is to: overcome the existing shortcoming that exists with the wallpaper wall paper of decorating, for the user provides a kind of flame retardant resistance, mildew-resistant moistureproofness good, foaming is high, the sound-absorbing sound-proofing properties well and do not remove from office with wall by alice, non-foaming, nondiscoloration, soft outward appearance foofaraw.
Another object of the present invention provides the manufacture method of this wall leather.
The objective of the invention is to realize by the enforcement following technical proposals:
A kind of decorative wall leather composition, be composited by blade coating technology by table, the ends two layer composition, wherein in skin combined thing and foundation composition, all include heavy calcium carbonate filling, organic silicone oil viscosity-depression agent and the organic and mineral dye of non-azo heavy metal free, it is characterized in that:
(1) upper layer composition component (meter by weight) includes:
PVC base-material 100
Wherein: emulsion pvc (K=70-80) 100~0
Emulsion pvc (K=62-67) 0~100
Softening agent
Di Iso Decyl Phthalate 30~60
Chlorinity is 52% clorafin 0~25
One package stabilizer
Barium one Zn liquid composite stabilizing agent 1~2
Whipping agent
Cellmic C 121 0~3
Fire retardant
The weisspiessglanz 0~5 that contains antimony 95%
Mould inhibitor
Oil soluble dry film mould inhibitor 0.2~1.5
(2) foundation composition component (meter by weight) includes:
PVC base-material 100
Wherein: emulsion pvc (K=70-80) 60~0
Emulsion pvc (K=62-67) 40~100
Softening agent
Di Iso Decyl Phthalate 40~62
Chlorinity is 52% clorafin 0~25
One package stabilizer
Barium one Zn liquid composite stabilizing agent 1.5~3.5
Whipping agent
Cellmic C 121 2~6
Fire retardant
The weisspiessglanz 3~8 that contains antimony 95%
Mould inhibitor
Oil soluble dry film mould inhibitor 0.2~2
Wherein: emulsion pvc (K=70-80) is meant the polyvinyl chloride (PVC) RESINS of molecular-weight average between 82000-95000 of producing with emulsion method; Emulsion pvc (K=62-67), be meant that the polyvinyl chloride (PVC) RESINS K value of molecular-weight average between 50000-69000 of producing with emulsion method is to represent the index of polyvinyl chloride (PVC) RESINS molecular weight size, K=70-80 represents that the molecular-weight average of this resin is between 82000-95000; K=62-67 represents that the molecular-weight average of this resin is between 50000-69000.
Wall of the present invention leather manufacture method has batching in regular turn, filters, peels off, stamp, embossing, side cut, inspection after construction and each operation of the packing of product, it is characterized in that: filtering between operation and the stripping process, also once blade coating oven dry and secondary blade coating are dried foamed process in regular turn.
Each operation technology contents is as follows:
A, burden process:
Respectively upper layer, bottom raw material are complied with component, the ratio of prescription, allotment being mixed and made into two kinds of uniform pasty state material.During modulation, earlier liquid starting material is mixed, adding mixed solid material at least at twice under constantly stirring, churning time is no less than 30 minutes at least, make the thickener temperature not the end in 50 ℃.
B, filtration operation:
Two kinds of thickeners that prepare are filtered, and upper layer is crossed 150 order mesh screens with thickener, and bottom is crossed 100 order mesh screens with thickener.
C, a blade coating baking operation: the upper layer thickener after will filtering, be evenly coated on the special-purpose separate-type paper carrier with the PU/PVC spreadometer, coat-thickness 0.18~0.23mm enters behind the loft drier under 160 ℃~180 ℃ temperature its oven dry.
D, secondary blade coating oven dry foaming operation: the bottom thickener after will filtering with the PU/PVC spreadometer, be evenly coated in and be coated with on the refrigerative surface layer adhesive face, coat-thickness 0.38~0.42mm enters drying baker its oven dry is foamed.
E, stripping process: promptly be shaped to work in-process wall leather after the dope layer cooling on the separate-type paper, can on separate-type paper, it be peeled off.
F, revenue stamp process: on work in-process wall leather, use the required color pattern of press printing, 100 ℃~140 ℃ of stamp temperature.
G, embossing operation: the work in-process that will print carry out embossing on the special-purpose embossing machine of far infrared, the embossing temperature is 80 ℃~150 ℃, and embossing pressure is 5~25N/cm 2
H, side cut operation: excision wall leather burr.
I, inspection after construction operation:
According to inspecting standard;
Outward appearance: 30m length is one, and every at most allows two sections, every section minimum length must not the end in 3m; Product does not allow the continuous regular defective, and the allowable defect maximum must not surpass 3mm 2, per ten meters can not be more than 2.
The invention has the advantages that:
1. decoration of the present invention is removed from office with wall, good flame resistance, and the mildew-resistant humidity resistance is good, and sound-absorbing, sound insulation be good, not alice, non-foaming, nondiscoloration, length of anti-aging life-span, toxicological harmless, use is not subjected to environmental restraint, is the substitute products of traditional wallpaper, wall paper.
2. processing method of the present invention, Production Flow Chart is short, work efficiency is high, product cost is low.Owing in technology,, directly make matrix with raw material PVC without paper substrate or fabricbase, concoct other function raw material, adopt secondary blade coating technology, the wall that makes it to generate leather avoids producing composite intermediate layer, internal structure has guaranteed the tensile strength and the anti-fire ability of product for completely becoming one.Owing to be the defective that homogenous product has overcome the shrinking percentage unanimity.
Description of drawings
Fig. 1 is wall leather manufacturing process flow diagram of the present invention
Embodiment
A kind of decorative wall leather composition, interior table, the ends two layer composition are composited by blade coating technology, the preferred feedstock component (by weight) of its used formation upper layer composition:
PVC base-material 100
Wherein: emulsion pvc (K=70~80) 70
Emulsion pvc (K=62~67); 30
Di Iso Decyl Phthalate 35
Chlorinity is 52% clorafin 20
Barium-Zn liquid composite stabilizing agent 2
Cellmic C 121 2
Water-ground limestone 20
The weisspiessglanz 3 that contains antimony 95%
Oil soluble dry film mould inhibitor 1
Organic silicone oil 1
Organic and the mineral dye 20 of non-azo heavy metal free
The preferred feedstock component (parts by weight) of used formation foundation composition:
PVC base-material 100
Wherein: emulsion pvc (K=70~80) 0
Emulsion pvc (K=62~67) 100
Di Iso Decyl Phthalate 40
Chlorinity 52% clorafin 25
Barium-zinc liquid meets stablizer 2
Cellmic C 121 4
Water-ground limestone 40
The weisspiessglanz 5 that contains antimony 95%
Oil soluble dry film mould inhibitor 1
Organic silicone oil 1
Organic and the mineral dye 10 of non-azo heavy metal free
The method of manufacturing technology of wall leather of the present invention is described identical with preamble.

Claims (2)

1, a kind of decorative wall leather composition, be composited by blade coating technology by table, the ends two layer composition, wherein in skin combined thing and low layer composition, all include heavy calcium carbonate filling, organic silicone oil viscosity-depression agent and the organic and mineral dye of non-azo heavy metal free, it is characterized in that:
1. upper layer composition component (meter by weight) includes:
PVC base-material 100
Wherein: emulsion pvc (K=70-80) 100~0
Emulsion pvc (K=62-67) 0~100
Softening agent
Di Iso Decyl Phthalate 30~60
The clorafin 0~25 of chlorinity 52%
One package stabilizer
Barium one Zn liquid composite stabilizing agent 1~2
Whipping agent
Cellmic C 121 0~3
Fire retardant
The weisspiessglanz 0~5 that contains antimony 95%
Mould inhibitor
Oil soluble dry film mould inhibitor 0.2~1.5
2. foundation composition component (meter by weight) includes:
PVC base-material 100
Wherein: emulsion pvc (K=70-80) 60~0
Emulsion pvc (K=62-67) 40~100
Softening agent
Di Iso Decyl Phthalate 40~62
The clorafin 0~25 of chlorinity 52%
One package stabilizer
Barium one Zn liquid composite stabilizing agent 1.5~3.5
Whipping agent
Cellmic C 121 2~6
Fire retardant
The weisspiessglanz 3~8 that contains antimony 95%
Mould inhibitor
Oil soluble dry film mould inhibitor 0.2~2.
2, a kind of processing method of making the described decorative wall leather of claim 1, include in regular turn: prepare burden, filter, peel off, stamp, embossing, side cut, inspection after construction and each operation of the packing of product, it is characterized in that: filtering between operation and the stripping process, also once blade coating oven dry and secondary blade coating are dried foamed process in regular turn.
CN 02134040 2002-11-12 2002-11-12 Decorative wall leather and its making method Expired - Fee Related CN1190319C (en)