CN1187408A - 树脂碾米砂辊的制造方法 - Google Patents

树脂碾米砂辊的制造方法 Download PDF

Info

Publication number
CN1187408A
CN1187408A CN97109318A CN97109318A CN1187408A CN 1187408 A CN1187408 A CN 1187408A CN 97109318 A CN97109318 A CN 97109318A CN 97109318 A CN97109318 A CN 97109318A CN 1187408 A CN1187408 A CN 1187408A
Authority
CN
China
Prior art keywords
rice milling
resin
resin roller
abrasive material
hours
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN97109318A
Other languages
English (en)
Inventor
王瑞武
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiang Qiuyuan
Original Assignee
Jiang Qiuyuan
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiang Qiuyuan filed Critical Jiang Qiuyuan
Priority to CN97109318A priority Critical patent/CN1187408A/zh
Publication of CN1187408A publication Critical patent/CN1187408A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种树脂碾米砂辊的制造方法,它以磨料、结合剂和填充料加工而成,其结合剂是三种不同组分的树脂,以本发明制造的产品,具有自锐性能好,动力消耗低,台时产量高,碾米能力强,且有效地解决了碎米问题,节约大量粮食。

Description

树脂碾米砂辊的制造方法
本发明涉及一种磨具制造，具体地说是一种用于粮食加工的磨具制造。
磨具，作为粮食加工的核心部件，在很长的时期里，用的是铁辊和陶瓷砂辊，很不理想：耗电量高，自锐性差，特别是碎米率高，往往达百分之十几，损耗了大量粮食，成为影响粮食丰产丰收的重要环节。
本发明的目的在于提供一种动力消耗低、台时产量高，自锐性能好，碎米少的粮食加工部件树脂碾米砂辊。
为达上述目的，本发明所采取的技术方案是：一种树脂碾米砂辊，以磨料、结合剂和填充料加工而成，其特征在干结合剂是树脂，其配比是(重量百分数)：
磨  料：70～90
结合剂：5～20
石膏粉：2～10
其中的磨料，可以用黑色碳化硅，亦可以将黑色碳化硅和棕刚玉掺合使用。磨料的粒度则根据粮食加工的需要，在16#～100#之间选用。
其配方中的结合剂是由树脂1，树脂2和树脂3构成，其重量百分比是：
树脂1：1～5
树脂2：3～10
树脂3：1～5
一种树脂碾米砂辊，其特征在干，它是按以下加工工艺完成的：配混料—模压成型—干燥—加工—硬化—检验
上述加工工艺中的投料，按照砂辊单重加上2～20％的耗料，其成型密度为2～3克/厘米3。
其加工工艺中干燥的过程为：时间10～15小时，最高温度110～130度保持2～6小时，其余为升降温时间。
其加工工艺中硬化的过程为：时间12～18小时，最高温度170～200度保持2～6小时，其余为升降温时间。
本发明由于采用的是树脂结合剂，且又根据粮食加工的实际情况，视一机出白或量多机出白，加工大米或是杂粮而选用不同粒度的磨料制造成砂辊，因此，满足了粮食加工的需要，碾白能力强，砂粒可以适时脱落，始终保持良好的自锐性，降低能耗，提高产量，有效地解决了碎米问题，实现增产增收，为国家节约大量粮食。
以下结合实施例对本发明作进一步的说明。
以一种规格为150×70×212×2(外径×内径×长×只)的砂辊为例，通过计算坯体体积乘以成型密度，得到头尾两节的单重均为6.93公斤，按每10公斤混合料加200克耗料进行投料，为便干称量和搅拌混料，加大投料总量，比如将投料总量定为27公斤，则可以根据头尾两节砂辊的不同功用选用磨料，头节选用粒度较粗的磨料，使之保持良好的碾削效果，尾节则可以选用粒度稍细的磨料，使之碾削时而不致于损伤米粒。按比例可以采取以下配方(单位公斤)：
头  节                     尾  节
黑碳化硅24#：    12.12    36#         12.08
棕刚玉24#～30#：6.615    36#～40#   9.88
      46#～60#  3.3
树脂1：           0.6                   0.66
树脂2：           1.94                  1.87
树脂3：           1.10                  1.10
石膏粉：          1.32                  1.40
总重：            27                    27
然后将搅拌均匀的混合料分2～3次投料，进行模压成型，然后进入干燥工序进行干燥处理，成型坯体在干燥炉中，经过7小时逐步升温至120度，保温4小时，降温4小时出炉，加工外形及槽形，而后进入硬化炉，经过9小时逐步升温至190度保温4小时而后逐步降温出炉，进行质检，确定优劣，整个生产加工过程完成。

Claims (7)

1、一种树脂碾米砂辊，以磨料、结合剂和填充料加工而成，其特征在干结合剂是树脂，其配比是(重量百分数)：
磨  料：70～90
结合剂：5～20
石膏粉：2～10
2、根据权利要求1所述的树脂碾米砂辊，其特征在干：磨料可以用黑色碳化硅，亦可以将黑色碳化硅和棕刚玉掺合使用。磨料的粒度在16#～100#之间选用。
3、根据权利要求1所述的树脂碾米砂辊，其特征在于：结合剂是三种树脂，其重量百分比是：
树脂1    1～5
树脂2    3～10
树脂3    1～5
4、一种树脂碾米砂辊，其特征在于：它是按以下加工工艺完成的：配混料—模压成型—干燥—加工—硬化—检验。
5、根据权利要求4所述的树脂碾米砂辊，其特征在于：投料是按照砂辊单重加上2～20％的耗料，其成型密度为2～3克/厘米3。
6、根据权利要求4所述的树脂碾米砂辊，其特征在干干燥过程为：时间10～15小时，最高温度110～130度保持2～6小时，其余为升降温时间。
7、根据权利要求4所述的树脂碾米砂辊，其特征在于硬化过程为：时间12～18小时，最高温度170～200度保持2～6小时，其余为升降温时间。
CN97109318A 1997-11-27 1997-11-27 树脂碾米砂辊的制造方法 Pending CN1187408A (zh)