CN1184093A - 速溶颗粒钙镁磷肥及生产方法 - Google Patents
速溶颗粒钙镁磷肥及生产方法 Download PDFInfo
- Publication number
- CN1184093A CN1184093A CN96120924A CN96120924A CN1184093A CN 1184093 A CN1184093 A CN 1184093A CN 96120924 A CN96120924 A CN 96120924A CN 96120924 A CN96120924 A CN 96120924A CN 1184093 A CN1184093 A CN 1184093A
- Authority
- CN
- China
- Prior art keywords
- calcium magnesium
- phosphate fertilizer
- magnesium phosphate
- fertilizer
- fast dissolved
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于农用化肥生产技术领域。其以粉状钙镁磷肥作为基料,配加腐植酸作为基本结合剂,并在造粒过程中加入有微量元素和作为结合包覆剂的易溶于水的无机盐。本发明产品的主要成分含量枸溶性P2O5≥12.0%,MgO>14%,SiO2>20%,颗粒强度≥8牛顿,成品粒度1~5mm,水中裂解≤1分钟,裂解率≥94%。其主要特点是适宜大面积播种,并减少施肥时的损失,扩大了适用范围,可作为底肥、追肥使用,微量元素丰富,并可以改良土壤。
Description
本发明属于农用化肥生产技术领域,主要提出一种速溶颗粒钙镁磷肥及生产方法。
钙镁磷肥(简称FMP)是一种多元素化肥,是我国的磷肥主要品种之一,据统计1991年我国FMP实物产量663万吨,折纯P2O5100.5万吨;据联合国粮农组织(FAO)统计,我国耕地和多年生作物面积0.97亿公顷,每公顷施肥水平N191.6Kg,P2O553.4Kg、K2O17Kg,FMP平均至全国每公顷耕地可施P2O510.8Kg,仅占53.4Kg的20.3%,从这一点出发FMP仍有巨大生命力。
FMP能供应植物生长所必需的多种养份,除磷外FMP通常还含有K2O、MgO、CaO及少量Mn、Fe、Zn、B等元素;长期施用实践证明,增产效果显著。据统计,每亩地施用50~100KgFMP,一般每斤FMP增产2-4斤;除施用粮食作物外,对豆类、菜类、棉花、果树的增产、对提高瓜果、甘庶的甜度和品级有明显效果,FMP是农作物不可缺少的肥料品种之一,不仅适合我国情况,而且很可能成为21世纪世界关注的化肥之一。
FMP是由磷矿石及熔剂(蛇纹石、白云石、橄榄石等)在高温下(1450℃以上)熔融而得的玻璃体,熔体经水淬骤冷、烘干、磨细而得成品。以此工艺生产的FMP呈粉末状,细变80~60%,但其在长期施用实践中,存在一些问题:
1、由于FMP呈粉末状,施肥主要靠人工作业完成,劳动条件差,且肥料飘洒损失大,不适宜大面积机耕需要。
2、粉状FMP所含营养元素在土壤中移动性很小,据研究,植物根系可利用土壤中元素的半径P=2.5mm,CaMg=5mm,NaK=7.5mm。因此粉状FMP必须施于耕作层内植物根系能够伸及的地方,只能作底肥,不能追肥。
本发明的目的正在此基础上提出,即提出一种以粉状FMP为基料的速溶颗粒钙镁磷肥及生产方法,从而解决现有磷肥施用中所存在的问题。
本发明是在总结研究FMP的特性和生产方法,并分析土壤对所施肥料元素要求的基础上提出;其出发点是提出的磷肥改变常规的松散粉末状,即提出颗粒状磷肥,从而使其具有可施播性,人工施肥时不飘洒,减少粉尘污染并改善劳动条件,尤其更适宜于具有发展趋势的大面积机播的需要。为了提高土壤对有效元素的需求,扩大其作用范围,可作为底肥和追肥施用。
本发明在研制中解决的关键问题之一是成粒技术,其它工业方面颗粒状产品成粒,均可加有带粘结特性的原料,以便与基料混合成粒;而本发明提出的磷肥产品则要考虑其成粒后,如粘结性物质包覆,则在施加土壤后,粘结状颗粒不易或很难溶解,则影响其使用效果,也可以说基本无有效果,本发明提出的颗粒状磷肥并要求其可速溶解于土壤中;由此本发明经过长时间、多次的实验、选择,提出天然半有机质的腐植酸作为基本粘结包覆剂,其具有较强的吸附力及松散性,具有结合基料的作用,同时又可以改良土壤,提高肥料的肥效和刺激作物增长。
同时本发明在造粒过程中添加有微量元素,其可为钼酸铵和硫酸铜,因此除含有P2O5外,还含有腐植酸、Cu、Mo、B、Zn等微量元素。腐植酸在发酵过程中产生大量碳酸,有利于枸溶性磷的溢出,因此本发明提出的颗粒状磷肥既可作底肥,也可追肥。
本发明提出的颗粒状磷肥造粒过程中的结合包覆剂还选用有易溶于水的无机盐,使成球后湿态强度低、干态强度大。
附图提供了本发明的生产过程。
结合生产过程框图,对生产方法加以具体说明:
由于在加工过程中将加入添加剂和其它微肥,从而使P2O5含量降低,为了使本发明产品中有效五氧化二磷达到合格即不低于12%的要求,基料中有效P2O5含量要求不少于14%,也可据用户对本发明产品中P2O5要求的高低确定基料中P2O5的含量。
配料时腐植酸如腐植酸钙与基料(即粉状FMP)的加入比例为5-10∶100。
造粒在成球盘内进行,成球盘结构与现有技术的成球盘相同,但其盘的倾斜角度较大,一般在65~70℃之间,这是考虑粉状钙镁磷肥属玻璃体,成球难度大,加大其倾斜角度,是为了使粒子成有效滚动外,还可有重心滚动的因素,以利于成球。由于成球盘倾斜角度较大,为使盘中的加入物料有足够的量,提高盘边高度,设计盘边高(h)与成球盘直径φ的相对关系为(h)1∶5~6(φ)。
造粒时加入微量元素,微量元素可选择钼酸铵和硫酸铜,也可为其它微量元素,钼酸铵浓度约万分之五到万分之八;硫酸铜浓度为万分之四到万分之六。
造粒时加入的结合包覆剂有易溶于水的无机盐,其作为结合剂成球后湿态强度低,干态强度大,可达几十牛顿,配制过程将其溶于水并搅拌均匀后过滤加入配有微量元素的容器内混合,与基料和腐植酸混料共同造粒。
本发明提出的颗粒产品水分不大于0.5%,这是考虑如水分稍大,则刚烘干的球水溶性极好,但一段时间后将溶解性很差,降低肥效。
本发明生产过程中烘干机角度不大于1.5度,以考虑减慢湿粒在烘干机管内的速度,防止其破裂。烘干机管内设置的扬料板为斜置,即相对管子的旋转方向向下倾斜,以此保证扬料板刮勺有粒球并随管子逐渐向上旋转时慢慢将粒球倾洒,而不致将粒球带上高处后倾洒使刚成球的湿粒破碎。同样出于这种考虑,进料烘干初始时应实施间断运转,逐步升温。同时烘干以低温相应延长时间为宜,烘干最佳温度应<100℃为宜,这是因为如果温度过高,则烘干后的粒球不会溶解而失去肥效。延长烘干时间的作法可采取加长烘干机长度,这样将会加大生产投资;也可实行间隔运行。
本发明产品筛分可采用不同的方式,但正品球一般按复肥标准1.0~4.75mm。
返料粉碎其细度不小于80%,即通过60目筛。
本发明产品的主要技术指标为:
枸溶性 P2O5≥12.0% MgO>14%
SiO2>20%
颗粒强度≥8牛顿 成品粒度1~5mm
水中裂解≤1分钟 裂解率≥94%
由于速溶颗粒FMP粒度均匀、强度高、水溶性好,且在生产中加入了腐植酸及其它元素,因此它除了粉状FMP的优点外,还具有:
1、适宜大面积机播,无粉尘污染,改善了劳动环境,减小了施肥时造成的FMP损失。
2、造粒时加入了丰富的腐植酸,腐植酸发酵过程中产生大量碳酸,有利于枸溶性磷的溢出,因此扩大了适用范围,既可作底肥,也可追肥。
3、微量元素更丰富,除含有P2O5外,还含有腐植酸、Cu、Mo、B、Zn、S等微量元素。
4、可以改良土壤。
Claims (10)
1、速溶颗粒钙镁磷肥,其以粉状钙镁磷肥作为基料,配加腐植酸作为基本结合包覆剂,并在选粒过程中加入有微量元素和作为结合包覆剂的易溶于水的无机盐;
速溶颗粒钙镁磷肥及生产方法,特征是将粉状钙镁磷肥作基料与作为基本结合剂的腐植酸混合配料,将作为结合剂的易溶于水的无机盐溶水搅拌均匀后过滤入配有微量元素的容器内混合,与基料和腐植酸的混料共同造粒;形成的颗粒状磷肥经烘干、冷却、筛分后构成本发明产品。
2、根据权利要求1所述的速溶颗粒钙镁磷肥,其特征在于所采用的微量元素可为钼酸铵。
3、根据权利要求1所述的速溶颗粒钙镁磷肥,其特征在于所采用的微量元素可为硫酸铜。
4、根据权利要求1所述的速溶颗粒钙镁磷肥,其特征在于作为基料的粉状钙镁磷肥中有效五氧化二磷的含量不少于14%。
5、根据权利要求1所述的速溶颗粒钙镁磷肥生产方法,其特征在于配料时腐植酸与作为基料的粉状钙镁磷肥加入比例为5~10∶100。
6、根据权利要求1所述的速溶颗粒钙镁磷肥生产方法,其特征在于造粒的成球盘倾斜角度在60°~70°之间,盘边高h与成球盘直径φ的比例为1∶5~6。
7、根据权利要求1所述的速溶颗粒钙镁磷肥生产方法,其特征在于烘干过程中的烘干机角度<1.5°,烘干机管内设置的扬料板为斜置,相对管子的旋转方向向下倾斜。
8、根据权利要求1所述的速溶颗粒钙镁磷肥生产方法,其特征在于进料烘干初始实施间断运转,逐步升温;烘干最佳温度<100℃。
9、根据权利要求1所述的速溶颗粒钙镁磷肥,其特征在于产品中水分不大于0.5%。
10、根据权利要求1所述的速溶颗粒钙镁磷肥,其特征在于产品中成分含量为:枸溶性P2O5≥12.0%,MgO>14%,SiO2>20%。