CN118355100A - 含有水溶性胶囊的包装 - Google Patents
含有水溶性胶囊的包装 Download PDFInfo
- Publication number
- CN118355100A CN118355100A CN202280080803.5A CN202280080803A CN118355100A CN 118355100 A CN118355100 A CN 118355100A CN 202280080803 A CN202280080803 A CN 202280080803A CN 118355100 A CN118355100 A CN 118355100A
- Authority
- CN
- China
- Prior art keywords
- package
- water
- unit dose
- weight
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种包装,其包含至少50重量%的可生物降解材料和多个单位剂量洗涤剂小袋,并且其中所述单位剂量洗涤剂小袋包含平均3至15g洗涤剂组合物。
Description
本发明涉及包含大批量洗衣或机器餐具洗涤水溶性胶囊(其由水溶性膜制成)的产品,其容纳在可生物降解包装中。
WO 02/20361公开了一种用于容纳和分配制品形式的单位剂量的洗衣添加剂的制品或包装。该包装包括多个洗衣添加剂制品、用于防止洗涤制品在分配或使用之前暴露于湿气的装置以及具有用于将多个制品包裹在容器中的隔室和封闭件的容器。容器可以是桶、托盘、罐、瓶子、小袋、袋子、盒或其一些组合,并且优选由聚合物材料制成。任选地,容器可具有用于将容器隔室细分成子隔室的分隔装置,使得容器可在单独的隔室中容纳多种不同的添加剂。任选地,但优选地,容器封闭件具有儿童防护特征以及在封闭件处于关闭位置时用于观察包装的内容物的窗口或其它装置。用于防止制品暴露于湿气的装置可以简单地是围绕容器封闭件的密封,或者它可以包括用于每个洗衣添加剂制品的单独的密封。用于单个制品的密封优选为其中形成有用于接收洗衣添加剂制品的凹部的托盘和在凹部上方粘附至托盘以将制品密封在其内的聚合物膜。
WO 2016/198978公开了一种儿童防护容器,该容器包括:限定了内部容积并且表现出由自由边缘界定的通道开口的由片材制成的壳体、由片材制成的配置用于限定该壳体的关闭状态和打开状态的封闭系统,该封闭系统包括可相对于壳体自由边缘活动的具有封闭部分的拉片。容器包括由片材制成的安全装置,其呈现:由拉片承载的第一钩挂部分,与壳体接合的第二钩挂部分。该第一钩挂部分和第二钩挂部分构造成用于在封闭系统的封闭状态下彼此稳定接合并且用于限定安全状态:第一钩挂部分和第二钩挂部分在安全状态下配置成用于防止封闭系统从关闭状态切换至打开状态。
US2021/047072(P&G)公开了包括容器和至少一个水溶性单位剂量制品的消费品。
US2020/240068(P&G)公开了一种用于单一单位剂量洗涤剂的包装,该包装具有外壳和内部结构。外壳和内部结构包括可生物降解的材料。内部结构具有能够容纳一个或多个单一单位剂量洗涤剂制品的一个或多个分开的区段。该一个或多个分开的区段中的至少一个包括从面向该外壳的内表面的表面延伸的突起。
WO 2021/11037(Unilever)公开了一种基材处理产品,其包括包含至少一个纤维或纸浆材料层和至少一个聚合物材料层的包装,所述聚合物材料选自聚乳酸、聚羟基链烷酸酯、聚酯、聚对苯二甲酸己二酸丁二醇酯、基于纤维素的材料、基于淀粉的材料、基于甘蔗的材料及其混合物,并且所述包装容纳多个水溶性胶囊,每个水溶性胶囊在密封隔室内包含基材处理组合物,所述密封隔室填充至隔室体积的至少60%,所述包装包括(i)容纳或更多个所述水溶性囊的接收器和闭合件;(ii)儿童防护封闭机构,其包括在所述接收器上的第一锁定构件和存在于所述闭合件上的第二锁定构件,由此所述构件互锁;其中所述基材处理组合物在25摄氏度和21sec-1的剪切速率下的粘度范围为200mPa.s-2000mPa.s,其中水溶性胶囊包含水溶性膜,所述水溶性膜包含聚乙烯醇、改性聚乙烯醇、聚乙酸乙烯酯、羧甲基纤维素或羟丙基甲基纤维素,并且其中基材处理组合物的水含量基于组合物的总重量计在0.01重量%-15重量%的范围内。
EP-A-1256623(P&G)公开了包含至少第一和第二水溶性或水分散性小袋的试剂盒,所述小袋包含至少第一和第二组合物,每种组合物包含至少一种不同的成分。
水溶性胶囊是非常方便的,然而,某些组合物需要在其上印刷以向消费者指示方向和其它信息。
水溶性胶囊是非常方便的,然而,某些组合物需要在其上印刷以向消费者指示用法和其它信息。
还期望通过将儿童防护特征并入包装中来限制对胶囊的接触,特别是对于儿童而言。目前的胶囊通常包装在塑料桶或塑料袋中。它是水和所包含的制剂不透的。刚性包装目前可以回收利用,然而在环境上需要减少塑料的使用。可堆肥或可生物降解的材料提供了环境优势,然而由于其本身性质(倾向于生物降解),使用这类材料存在问题。如果胶囊从例如不完全的密封中泄漏,包装可能通过可生物降解材料在与泄漏的制剂直接接触的情况下的过早降解而弱化。包装的机械性能受到损害。在大批量胶囊的重量及水分可能从胶囊渗出的情况下,任何儿童防护封闭件的完整性可能受到损害。因此,儿童可能可更容易接触包装,这是不期望的。
此外,尽管塑料容器通常是紧密密封的并因此表现出非常低的湿气透过率,但是纸浆或纤维容器倾向于具有高的水透过性质。这意味着水渗入和/或渗出的可能性高得多,因此对这种基于纤维或纸浆的容器内部的单位剂量产品的物理性能有影响。特别的特征是含有具有5至15%水的洗涤剂组合物的单位剂量产品在储存时倾向于粘着在这类容器的内侧表面。当储存在纸基容器中时,这种粘着是由受水透过负面影响的外表面引起的。通过在内侧进行印刷,我们发现该特性显著降低。印刷的位置在可生物降解的包装如纸浆或纤维中的单位剂量产品的性能中起作用,这是出乎意料但受欢迎的。
因此,在第一方面,提供了一种包含至少50重量%的可生物降解材料和多个单位剂量洗涤剂小袋的包装,并且其中所述单位剂量洗涤剂小袋包含单位剂量小袋重量的平均3至9.5g,优选5至8g洗涤剂组合物。
我们惊讶地发现,通过减小洗涤剂胶囊的尺寸并代之以使用具有平均3-9.5g洗涤剂组合物的小袋,可以提供更稳定的液体单位剂量洗涤剂产品,这意味着在可生物降解的包装中观察到改进的性能。
“包含至少50重量%的可生物降解材料”是指形成容器的材料包含至少50重量%的可生物降解的材料。这并不意味着包括任一容器的任何内容物。例如,第二容器中的洗涤剂小袋不包括在第二容器的可生物降解材料含量的计算中。
该效果特别适用于包含可生物降解材料如纤维素基材料,例如纸、纸浆和纸板的容器,以及适用于其中小袋包含1-25重量%水的情况。
如整个本说明书(包括权利要求书)中所使用的,定义以下术语:
当冠词“一”和“一个”在权利要求中使用时,应理解为是所要求保护或所描述的一个或多个。
在酶组合物的情况中,“环境活性的”旨在意指在不超过40℃,优选地不超过30℃,更优选地不超过25℃,最优选地不超过15℃但总是大于1℃的温度下是活性的,并且“活性的”指有效地实现污渍去除,其也在本文中定义。
“可生物降解的”是指物质被微生物完全分解为二氧化碳、水、生物质和无机材料。
“儿童防护封闭机构”是指通过其减少对水溶性胶囊的接触的任何机构,使得婴儿和儿童不能容易地取出水溶性胶囊。这优选地包含需要个体进行多个认知和操作步骤以打开的任何合适布置,从而防止儿童无意中接触胶囊。
“可堆肥的”是指满足以下三个要求的材料:(1)能够在固体废物堆肥设施中进行处理;(2)如果经过如此处理,最后成为最终的堆肥;和(3)如果在土壤中使用堆肥,材料将最终在土壤中生物降解。
“酶”包括酶变体(例如通过重组技术产生的)。这种酶变体的实例公开于例如EP251446(Genencor)、WO91/00345(Novo Nordisk)、EP525610(Solvay)和WO94/02618(Gist-Brocades NV)中。
“基本上不含某组分”指没有将任何量的该组分有意地掺入组合物中。
“膜”指水溶性材料,且可以是片状材料。材料的长度和宽度可以远超过材料的厚度,然而膜可以具有任何厚度。
“可再生的”指可由天然来源产生或可由天然来源衍生的材料,其通过陆地、水生或海洋生态系统的植物(例如农作物、可食用和不可食用的草、林产品、海藻或藻类)或微生物(例如细菌、真菌或酵母)的作用而定期(例如,每年地或多年地)更新。
“可再生资源”指可在100年时间段内更新的自然资源。该资源可以自然地或经由农业技术更新。可再生资源包括植物、动物、鱼类、细菌、真菌和林业产品。它们可以是天然存在的、杂交的或遗传工程化的生物体。花费超过100年来形成的自然资源如原油、煤和泥炭不被认为是可再生资源。
“热成型”指其中通过加热使膜变形的过程,并且特别地,其可以包括以下步骤:使第一膜片进行模制过程以在膜中形成包围,例如在膜中形成凹陷。优选地,这包括在变形之前加热。变形步骤优选地是通过将膜放置在空腔上并在空腔内施加真空或负压(以将膜保持在空腔中)来实现的。然后可以填充凹陷。然后该方法可包括将第二片覆盖在经填充的凹陷上,并将其围绕凹陷的边缘密封到第一片膜上以形成平坦的密封网,从而形成可以是单位剂量产品的胶囊。第二膜可以在制造期间热成型。或者,第二膜可以不在制造期间热成型。优选地,第一水溶性膜在单位剂量制品的制造期间热成型,并且第二水溶性膜不在单位剂量制品的制造期间热成型。
“单位剂量”指适合于处理一次洗衣负载的组合物的量,例如,约3g至约9.5g,或5g至约8g。
“水溶性”指在20℃下,制品(膜或包装)溶于水中。
除非另有说明,否则所有组分或组合物含量均是关于该组分或组合物的活性部分,并且不包括可存在于这样的组分或组合物的可商购来源中的杂质,例如残留溶剂或副产物。
除了在实施例和比较实验中,或在另外明确指出的情况下,否则所有数字都应理解为由词语“约”修饰。
除非另有说明,否则本文中包含的所有百分比(表示为“%”)和比率均按重量计。除非另有说明,否则本文所有条件均为20℃和在大气压下。除非另有特别地说明,否则所有聚合物分子量均按照重均数分子量(weight average number molecular weight)确定。
以“x至y”格式表示的数字范围应理解为包括x和y。当针对特定特征以“x至y”格式描述多个优选范围时,应理解还预期组合不同端点的所有范围。在规定值或量的任何范围时,任何特定的上限值或量都可以与任何特定的下限值或量相关联。
包装材料
包装包括可生物降解材料。可生物降解材料可包括可生物降解聚合物。包装可包括完全可生物降解的材料,使得包装整体上可以被微生物如细菌、真菌、酵母和藻类;环境热、湿气或其它环境因素完全物质分解为二氧化碳、水、生物质和无机材料。优选地各容器的90-99.9重量%,更优选96-99.9重量%由纸浆或纤维材料如纸、卡片或纸板组成。剩余部分包含阻隔材料和/或信息标签。然而,优选的是,任何标签还包含如本文所述的可生物降解材料,优选纸或其它纤维基或纸浆基材料。
如果需要,可生物降解性的程度可根据例如ASTM测试方法5338.92来确定。
合适的可生物降解材料包括来自纤维素或衍生物的纸、卡片或纸板;并且可以任选地包含木质素或衍生物;可生物降解的塑料,例如生物塑料,其优选为氧-生物降解塑料,其中生物降解由同时或连续的氧化和细胞介导的现象产生(不同于氧降解,其是由“大分子的氧化裂解”产生的降解,使得塑料破碎但除非经过很长的时间,否则不生物降解)。该材料也可以是可堆肥的。
可生物降解材料包括生物聚合物,如聚乳酸(PLA),其可以来自例如玉米淀粉、木薯、甘蔗等;聚羟基烷酸酯(PHA),包括聚-3-羟基丁酸酯(PHB或PH3B)、聚羟基戊酸酯(PHV)和聚羟基己酸酯(PHH)。PHA共聚物,称为聚(3-羟基丁酸酯-共-3-羟基戊酸酯)(PHBV);可生物降解聚酯,例如聚己内酯(PCL)、聚丁二酸丁二醇酯(PBS)、聚乙烯醇(PVA);聚己二酸对苯二甲酸丁二醇酯(PBAT);纤维素基材料,例如乙基纤维素、醋酸纤维素(真)玻璃纸(Cellophane)(由木材、棉花或麻制成);淀粉或淀粉基材料(来自马铃薯、大米、玉米等);甘蔗渣,及其任何组合或混合物。例如,PCL可与淀粉混合以改善PCL的生物降解性。
可生物降解材料可包括任何可生物降解的聚烯烃。
可生物降解的石油基塑料包括:聚乙醇酸(PGA)、热塑性聚合物和脂肪族聚酯;聚琥珀酸丁二醇酯(PBS),其是具有与丙烯相当的性质的热塑性聚合物树脂;聚己内酯(PCL),因为它具有提供可生物降解性能的可水解酯键。已经表明厚壁菌和变形菌可以降解PCL。青霉属菌株26-1可降解高密度PCL;尽管不如耐热曲霉属菌株ST-01快。梭菌属物种可以在厌氧条件下降解PCL;聚己二酸对苯二甲酸丁二醇酯(PBAT),其是可生物降解的无规共聚物。
最优选的可生物降解材料包括来自纤维素或衍生物的纸、卡片或纸板。
优选地,可生物降解的材料是根据14C或放射碳方法(EU:EN 16640或CEN/TS16137,国际:ISO 16620-2,US:ASTM 6866)的生物基的。优选地,可生物降解材料由可再生资源制成。
包装材料可以包括外层以提供额外的保护或光泽(对于具有无光泽涂饰的可生物降解材料,例如纸板)。该层优选包括可生物降解聚合物涂层或清漆或膜。优选地,外层包含上述生物聚合物中的任一种。优选地,外层至少存在于容器的一些或全部的内表面上。
术语纤维或纸浆材料包括纸或纸板:具体而言。优选地,纤维或纸浆材料为片材的形式并形成为坯料,该坯料被折叠以形成可闭合的容器。可闭合的容器可由单件坯料形成或可含有多个部件。
可用于制造包装的材料可以表现出100-500g/m2,优选200-400g/m2的克重。在其实施方案变型中,用于制造容器的片状纸材料可在第一和/或第二主要展开表面的至少部分上被涂层(例如膜)覆盖,其目的是在具有泄漏保护的容器的内部和外部之间保持水转移的平衡。有利地但非以限制性的方式,涂层可包括在限定容器的纸材料的一侧或两侧(内侧和/或外侧)上的挤出涂层,其值可例如在10至50微米的涂层材料的范围内。涂层塑料材料可以例如选自以下材料:LDPE、HDPE、PP、PE。
优选的阻隔材料包括选自聚乳酸、聚羟基链烷酸酯、聚酯、聚己二酸对苯二甲酸丁二醇酯、纤维素基材料、淀粉基材料、甘蔗基材料及其混合物的聚合物材料。
在优选的实施方案中,可生物降解材料包含至少两层,更优选至少三层。
可生物降解材料优选包含漂白层,并且该漂白层包含可生物降解材料的外层。外层是指漂白层是物理上的最外层。第二层包含非漂白层,其也在外部但与漂白层相对。因此,可生物降解材料优选在相对侧上包含漂白和未漂白层。在漂白层和未漂白层之间优选是由消费后回收利用的材料组成的填料层,并且其也优选是纸基的。
纤维素纤维长度
优选地,用于本发明的可生物降解材料是纸基的。纸基是指它来源于含纤维素的天然来源如树。纸基或纸浆基产品的物理性质主要取决于在加工过程中从木质素分离的纤维素纤维的性质。这可能受到纤维素来源的影响,即哪种类型的树是原始来源,以及已经进行了什么处理。通常倾向是将纸表征为回收使用的或原生的、非回收的,然而,这是误导性的,因为在本发明的情况中纤维素纤维的物质性是其性能的关键。例如,硬木纤维通常具有良好的平滑性和成型性并且具有短纤维。典型的硬木来源包括桉树、桦树、枫树、山毛榉和橡树。相反,软木纤维具有良好的强度和硬度,并且包括源自松木、云杉和冷杉的那些。
因此,在至少一层可生物降解材料是纸基的情况下,优选的是纸中纤维素的重均纤维长度为至少2mm,更优选3至5mm。
纤维素纤维长度根据TAPPI(纸浆和造纸工业的技术协会)称为T271om-18的测试进行表征,其是设计用于通过使用偏振光的自动光学分析仪测量纸浆和纸的纤维长度的方法。该测试是经批准的美国国家标准(ANSI)。
在包装包含配合的基部和盖部构件的情况下,优选地,基部含有具有至少2mm,更优选地3至5mm的重均纤维长度的纸基层。我们惊讶地发现,当包装设计用于储存液体洗涤剂胶囊时,这种优异的纤维长度提供了改进的性能,特别是在泄漏事件中水封闭的情况下。当包装设计需要具有儿童安全特征时,这是特别重要的,因为较差的水封闭可能导致包装薄弱并因此更容易接近内容物。
当包装包括单独的盖部部件时,优选的是盖包括重均纤维素纤维长度为1-5mm的纸。
在优选的实施方案中,盖部包含80%,更优选95%重量的具有1-5mm重均纤维素纤维长度的盖部纸。
在优选的实施方案中,基部包含80%,更优选95%重量的重均纤维素纤维长度为至少2mm的基部纸。
印刷
单位剂量产品被印刷以向消费者提供有用的信息。当形成时,印刷基本上在胶囊或产品的内部。通常,在制造产品之前在膜卷上进行印刷,使得经印刷的表面是在形成最终产品时面向洗涤剂组合物的表面。
印刷的区域可覆盖整个膜或其部分。印刷的区域可包含单一颜色或可能包括多种颜色,甚至三种颜色。印刷的区域可以包括白色、黑色和红色。印刷的区域可包含颜料、染料、上蓝剂或其混合物。印刷可作为膜表面上的层存在或可至少部分地渗入膜中。除了膜的内表面之外,印刷的区域可存在于单位剂量制品的外侧,即与液体洗衣洗涤剂组合物接触。
优选地,膜包含酞菁基颜料。这种颜料用于印刷到膜上。优选的颜料包括可从SunChemical商购获得的F UVDB354,并且是酞菁基颜料。其被称为CAS147-14-8。
单位剂量制品可包含至少两个膜,或甚至至少三个膜,其中膜密封在一起。印刷的区域可存在于一个膜上,或多个膜上,例如两个膜上,或甚至三个膜上。
印刷的区域可以使用标准技术实现,例如柔版印刷或喷墨印刷。优选地,通过柔版印刷(在其中膜被印刷)实现印刷区域,然后模制成单位剂量制品。
容器容纳有多个水溶性胶囊,每个水溶性胶囊包含在密封的隔室内的洗涤剂组合物,所述密封的隔室优选填充至隔室体积的至少60%。
优选地,容器包括10个或更多个所述单位剂量产品和封闭件。
通过这种布置,具有基质处理液体的性能水平的水溶性胶囊可以快速填充并以大批量包装以降低制造成本,但可以使用可生物降解材料进行包装并仍使泄漏胶囊的有害影响最小化。考虑到形成胶囊膜的组合物以及用于可生物降解包装的聚合物的相似性,这是令人惊讶的。
所选择的粘度范围确保填充时间不会减慢制造时间,从而使胶囊成本过高。同时,申请人已经发现,如果液体增稠到如本发明的第一方面中所规定的粘度,这使得胶囊密封区域的飞溅最小化,并且还使得在高速填充胶囊时可能也影响密封完整性的波纹(在制剂中)的形成最小化。
容器
容器优选具有300N的最小压缩强度。选择材料的厚度(或纸厚)以向包装提供必要的结构刚性。
容器可包括任何合适的刚性结构,如桶或纸箱或盒子、管状结构或瓶子。然而,优选的容器由形成为容器的坯料形成。优选地,容器包括基部、相对的成对壁和可封闭的盖部。优选地,盖部与基部一体或由单独的部件形成。
这类结构的壁可以是发泡的或模制的。它可以包括层压结构(例如按层累加)。它可以包括胶合、压缩和/或包围在刚性壁中的纤维性材料如纤维/纸浆。可以引入开槽,例如瓦楞纸板。对于纸板,克重优选为至少200gsm(克/平方米),优选至少225gsm。
优选地,第一容器包含瓦楞纸板材料。
该结构可以在提供功能性接受器的竖起的结构和有助于运输和以后处置方便性的扁平结构之间折叠,使得多个包装可以被扁平化和堆叠以准备运输到生物降解位点。
可生物降解的容器可包含纤维和/或纸浆材料和聚合物材料的组合。一个实例可以是包含与一种或多种聚合物材料(所有材料都是可生物降解的)组合的一个或多个纤维和/或纸浆层的材料。可以有夹在聚合物材料层之间一个或多个纤维和/或纸浆层。材料可以是原生的或回收的。
包装形状优选为类立方形。这意味着它具有基本上均匀的长度、深度和高度。优选地,长度比深度长,使得其通过交替两个相对的小侧壁和两个相对的长侧壁而形成。这两组相对侧壁的底部边缘被附接到基部以形成在顶部开放的容器。顶部可由任何常规的盖部如铰接的盖部或单独的盖部封闭。
在包装包含单独的盖部和基部的情况下,优选的是盖部包括顶部片材和悬垂的相对壁的对,使得其类似于立方体的五个侧面。类似地,优选的是基部包括底片和直立的相对壁的对,使得其也类似于立方体的五个侧面。
以这种方式,盖部和基部配合以形成封闭的第二容器,其中当盖部和基部可伸缩地配合时,盖部和基部中每一个的相对壁的对提供针对外部的双重保护。优选地,当基部和盖部可伸缩地接合以关闭包装时,盖部提供最外的表面。
优选地,包装的盖部包括在最外层上的漂白层和在最内层上的未漂白层。在这样的构型中,对于盖部构成的五个侧面,漂白层呈现包装的最外表面。优选地,该最外层包含印刷的部分。
优选地,漂白层还包含如下所述的阻隔材料。更优选地,最内表面包括未漂白层,并且最优选地未用阻隔材料处理。
优选地包装的基部包含在最内层上的漂白层和在最外层上的未漂白层。在这种构型中,对于基部构成的五个侧面,漂白层呈现了包装的最内表面。这种最内层与至少一些洗衣单位剂量产品物理接触。
优选地,漂白层还包含如下所述的阻隔材料。更优选地基部的最内表面包含未漂白层,并且最优选地还用阻隔材料进行处理。
优选地,包装的盖部包括至少一个孔,在盖部和基部的分离过程中,来自容器外部的空气可以通过该孔进入容器,并且其中容器内部的芳香剂可以离开容器。
孔优选地在侧壁上比侧壁的底部边缘更靠近盖部的顶表面。这允许更多的空气进入容器中的顶部空间,并因此当盖部从基部抽出时产生更多的空气流进入容器中。此外,当容器关闭时,更多的空气从基部和盖部之间的空间排出。这类似地在关闭时通过孔从容器内部排出更多的空气。结果是在打开和关闭容器时芳香剂云从容器中更多地排出。优选地,盖部具有顶部片和与其附接的两对相对壁,并且所述相对侧壁中的至少一个包括一对孔。
包装的盖部和基部优选地可伸缩地接合。这意味着每一个的尺寸使得当两者被拉开或被压向彼此时一个在另一个内滑动。优选地,当两者接合时,盖在基部外部滑动。
优选地,包装的基部和盖部包括侧壁,其延伸大致相似的距离,使得当处于闭合构型时,盖部形成容器的顶部和侧部,其中基部仅在其底部可见,基部的侧壁在盖部的侧壁的内侧,因此对于大部分是不可见的。
优选地,包装基部的侧壁比盖部侧壁上的孔之间的距离延伸得更远,使得当处于封闭构型时,基部的侧壁关闭孔。
更优选地,孔被定位成使得盖部和基部可以被部分拉开并且孔通过基部侧壁保持关闭。这意味着基部侧壁进一步延伸,使得孔的最上部和超过孔的最上部的距离确定了在孔通过出现在基部侧壁的边缘上方而暴露之前基部和盖部可被拉开的量。
当用于制造包含单位剂量洗涤剂小袋的完全包装时,包装优选在50-55%的相对湿度下,优选在20-23℃的温度下储存。
在制造过程中,包装优选由坯料形成为如上所述的可封闭的容器。用单位剂量洗涤剂小袋填充包装,然后封闭。湿度和温度条件对于控制包装制造后储存期间水迁移进出容器和小袋是重要的。如果条件不适当,过多的水可能离开或进入小袋,导致小袋失效。
然而,我们发现,使用可生物降解的包装,产品故障,特别是小袋的粘连被减少,特别是在使用所声称的较小的小袋尺寸时。
多个包装可以堆叠在货盘上,并且优选收缩包裹用于运输和存储。
阻隔材料
包装优选包括用于改善的性能的阻隔材料。更优选地,阻隔材料在包装的外部而不是在内部。
阻隔材料优选用于提供湿度控制,并且通常根据最终用途施用在板表面的一侧或两侧上
分散体阻隔
在没有传统涂覆层的情况下,分散体是新的阻隔选择。表面用水基分散技术处理。这使得板在其使用过程中耐液体和油脂,同时它在如纸的回收过程中分解,从而在回收产品时提供高产量的回收纤维。
Green PE涂层
PE Green是传统PE(聚乙烯)的完全可再生的选择,并提供优异的湿度保护。PEGreen由可再生的、基于植物的原材料制成,因此可获得100%可再生和可回收的阻隔包装。在转换时,它以与PE相同的方式进行,因此易于被用户引入到生产中。
PE涂层
PE,或聚乙烯,是最常用的阻隔涂层。聚烯烃阻隔,例如LDPE和HDPE聚合物,提供优异的湿度保护。
可生物降解的涂层
可生物降解的涂层是特制的聚合物,其提供湿度、氧气和油脂阻隔和密封性。我们的可生物降解的涂层是可堆肥的。然而,也可以容易地回收利用生物聚合物涂覆的纸板,这通常是优选的使用终止选项。
生物聚合物可以由天然作物或化石原料生产。但是关键在于在最后生物聚合物涂覆的纸板分解成腐殖质和CO2。如果选择我们的生物聚合物涂覆的纸板,则可以得到可回收的产品,或者它可以被收集在进入工业堆肥中的其它可堆肥废物中。
PET涂层
PET提供阻隔并执行其它功能。提供耐热性的黑色或白色PET涂层充当优异的油脂阻隔并且具有固体WVTR(水蒸气透过率)特性。
PP涂层
PP或聚丙烯涂层为微波炉提供耐热性,并且还适于深度冷冻。良好的密封性能保证了使用中的性能。
然而,优选的是阻隔材料包含小于5重量%,更优选小于1重量%,并且优选基本上0重量%的PE、PP或PET。
在优选的实施方案中,阻隔包含水基分散体。
水基阻隔涂层密封基材表面并保护包装免受外部和内部影响。包装保持有吸引力并且可以不受限制地实现其功能。根据产品的不同,我们的阻隔涂层在包装的使用期限内提供了对脂肪、水、水蒸气、乳制品、醇、油或碱的充分保护。由于其通用性,它们用于广泛的应用。阻隔涂层可用于包装转换器和打印机或造纸工业。
优选地,包装的基部包括水基分散体阻隔。
优选地,基部上的阻隔材料施用至内表面。
优选地,盖部包括小于1重量%的阻隔材料,更优选水基分散体阻隔。
更优选地,分散体阻隔部件包含热塑性弹性体(TPE)。所述TPE优选分散在阻隔部件中。
含TPE的阻隔材料的优点是其分散在阻隔部件中,使得层不是需要的。分散体一次性施用。
替代的阻隔部件可包括多层方式。这些阻隔包括可从Weilburger以品牌商购的那些。实例描述于WO2018/069413中。优选地,这些将通过数字印刷、墨斗阻尼单元、柔版印刷、在线-离线涂覆单元和卷筒纸胶印以及凹版印刷来施用。
这类阻隔材料可以主要作为湿层施加。分散体优选是水性分散体,特别是PTFE分散体、全氟烷氧基(PFA)聚合物分散体和/或氟化乙烯-丙烯(FEP)、六氟丙烯的共聚物。
当以潮湿形式施用层时,形成表面膜,其然后可固化。第一层可具有树脂以改善对基材的粘附。示例性的合适树脂为,但不限于聚酰胺酰亚胺、聚苯硫醚(PPS)、聚醚砜(PES)、聚醚醚酮(PEEK)、有机硅树脂和/或聚砜。这种树脂在作为层施用的湿组合物(特别是分散体)中的比例优选为组合物的约3至8重量%。
第二聚合物以液体形式施用到第一层上。该分散体可含有本文提及的其它成分。分散体优选为水性分散体,特别是PTFE分散体、全氟烷氧基(PFA)聚合物分散体和/或氟化乙烯-丙烯(FEP、六氟丙烯和四氟乙烯的共聚物)分散体。作为层施用的湿组合物(特别是分散体)中的第二聚合物的比例优选为约40-60重量%。在施用第二层之前,第一层可以已经干燥、部分干燥或未干燥。在有利的变体中,只要第一层仍然是潮湿的,将第二层施用至第一层上,特别是只要第一层仍然是潮湿的。
优选地,第二容器的盖部和基部都包括多层阻隔材料,如以上所述的那些。
优选地,阻隔材料施用至盖部和/或基部的外部。更优选地,阻隔材料施用至盖部外表面的至少50%,更优选70%,特别优选90%,最优选95%。
更优选地,将阻隔材料施用至基部外表面的至少50%,更优选70%,特别优选90%,最优选95%。
更优选地,基部包括外表面和内表面上的阻隔材料。
粘合剂
优选地,将包装折叠成形并借助于粘合剂保持其形状。粘合剂在本领域中是常见的,但优选地,我们是指热熔粘合剂、反应性热熔粘合剂、热固性粘合剂、压敏粘合剂、接触胶粘合剂。优选地,粘合剂是热熔压敏粘合剂。
优选地,热熔压敏粘合剂适于增粘和粘结到构成包装的一系列材料上。
总含量
优选地,阻隔材料和粘合剂占总包装加粘合剂和阻隔材料(即,无单位剂量小袋)的0.1-5重量%。更优选地,阻隔材料和粘合剂占总容器加粘合剂和阻隔材料的1-3重量%,并且最优选1.5-2.5重量%。
优选地,阻隔材料和粘合剂占盖部加粘合剂和阻隔材料的0.1-5重量%。更优选地,阻隔材料和粘合剂占盖部加粘合剂和阻隔材料的1-3重量%,和最优选0.9-1.4重量%。
优选地,阻隔材料和粘合剂占基部加粘合剂和阻隔材料的0.1-5重量%。更优选地,阻隔材料和粘合剂占基部加粘合剂和阻隔材料的1-3重量%,最优选1.5-2.6重量%。
优选地,阻隔材料占总第二容器加阻隔材料和粘合剂,减去小袋的0.1-5重量%。更优选地,阻隔材料占总第二容器加阻隔材料和粘合剂的1-3重量%,和最优选1.5-2.5重量%。
优选地,阻隔材料占盖部加阻隔材料和粘合剂的0.1-5重量%。更优选地,阻隔材料占盖部加阻隔材料和粘合剂的1-3重量%,最优选1.4-2.2重量%。
优选地,阻隔材料占基部加阻隔材料和粘合剂的0.1-5重量%。更优选地,阻隔材料占基部加阻隔材料和粘合剂的0.3-3重量%,和最优选0.5-1.5重量%。
优选地,粘合剂占总包装加粘合剂和阻隔材料的0.1-5重量%。更优选地,粘合剂占总包装加粘合剂和阻隔材料的1-3重量%,最优选1.5-2.5重量%。
优选地,粘合剂占盖部加粘合剂和阻隔材料的0.1-5重量%。更优选地,粘合剂占盖部加粘合剂和阻隔材料的1-3重量%,最优选1.2-2.1重量%。
优选地,粘合剂占基部加粘合剂和阻隔材料的0.1-5重量%。更优选地,粘合剂占基部加粘合剂和阻隔材料的1-3重量%,最优选1.5-2.6重量%。
优选地,盖部加基部包含0至5重量%的选自PP、PE和PET的聚烯烃。更优选地,基部加盖部包含0-1重量%,最优选0重量%的PP、PE和PET。
具有漂白的外表面的包装的盖部和具有漂白的内表面的基部意味着当盖部和基部协同接合时,两个未漂白的表面彼此接触。这利于两者之间的滑动,特别是在潮湿环境中。
COBB值
COBB测试(T441 om-20,TAPPI)测量施胶和波纹纤维板的吸水性。“Cobb值”是在1cm水下1m2基材在特定时间内吸收的水的质量。
优选地,未添加阻隔材料的包装的盖部的Cobb60,对于漂白的表面为5至80g/m2,更优选6至50g/m2,且对于未漂白的表面为5至100g/m2,更优选10至30g/m2。
优选地,添加阻隔材料的包装的盖部的Cobb60,对于漂白的表面为0.1至1.5g/m2,更优选0.3至1.0g/m2。
优选地,未添加阻隔材料的包装的盖部的Cobb1800,对于漂白的表面为80至200g/m2,更优选90-150g/m2,且对于未漂白的表面为8至200g/m2,更优选100-130g/m2。
优选地,添加阻隔材料的第二容器的盖部的Cobb1800,对于漂白的表面为80-200g/m2,更优选90-150g/m2。
优选地,未添加阻隔材料的包装的基部的Cobb60,对于漂白的表面为0.5至15g/m2,更优选1-10g/m2,且对于未漂白的表面为5-80g/m2,更优选10-30g/m2。
优选地,添加阻隔材料的包装的基部的Cobb60,对于漂白的表面为0.1-1.5g/m2,更优选0.3-1.0g/m2。
优选地,未添加阻隔材料的包装的基部的Cobb1800,对于漂白的表面为80-200g/m2,更优选90-150g/m2,且对于未漂白的表面为8-200g/m2,更优选80-120g/m2。
优选地,添加阻隔材料的包装的基部的Cobb1800,对于漂白的表面为0.5-20g/m2,更优选2-15g/m2。
我们惊讶地发现,当包装设计用于储存液体洗涤剂胶囊时,特别是在泄漏事件中水封闭的情况下,这种优异的纤维长度提供了改进的性能。当包装设计需要具有儿童安全特征时,这是特别重要的,因为较差的水封闭可能导致包装薄弱并因此更容易接触到内容物。
优选地,用于包装的盖部和基部的纸板的深度为200至800微米。
优选地,包装包括吸收垫。优选地,在将单位剂量制品放置在包装内部之前,将这种吸收垫在基部放置在包装的底部。
儿童防护封闭件
包装优选包括儿童防护封闭机构,其包括在接受器上的第一锁定构件和在封闭件上存在的第二锁定构件,由此构件互锁。
儿童防护封闭件通过特定结构获得,以将封闭件固定在适当位置(关闭接受器),直到进行特定操作以解开封闭件。
封闭件可包括具有相应锁定构件的顶部和盖部,所述锁定构件在它们从接受器上的锁定构件释放之前必须沿特定定向对齐,或者需要执行一定顺序的步骤或动作来激活它们的释放,如下所述。
接受器和封闭件可以各自包括至少一个,优选至少两个这样的锁定构件,以及包装通过多对锁定构件的锁定进行关闭,每对锁定构件包括与接受器上的一个锁定构件相互接合的封闭件上的一个锁定构件。优选地,每对锁定构件可独立于任何至少一个其它锁定构件对进行操作,使得一个锁定构件对的解锁不会自动地解锁另一锁定构件对。优选地,至少一个对在包装上的位置处与另一对间隔开,因此例如,它们可以位于对角相对的位置处,例如位于或邻近大致正方形/矩形封闭件的对角相对的边缘/角处和/或位于圆形封闭件的边缘上的径向相对的位置处。
优选地,该锁定构件或每个锁定构件包含弹性部分,使得该弹性部分弹入和/或弹出与相应锁定构件的锁定接合。
锁定构件可以选自任何突起和对应的凹陷、卡子、夹子、闩锁、翼片、条带、钩和环紧固件、棘齿装置或凸耳(在螺纹上)、滑动装置、按钮、拉片、键、磁体或其他锁定部件。锁定构件可以被偏置,例如加载在锁定位置的弹簧(与相应的锁定构件接合),使得必须使用压力来将它们彼此释放。
接受器和封闭件可以通过铰链彼此附接,或者它们可以相对于彼此滑动并且甚至可以是单体的(例如,具有活动铰链),使得封闭件与接受器是一体的。本发明对于这样的装置是特别优选的,因为使接受器软化可导致变形并在封闭件上施加应力。
特定操作可包括对封闭件的双重和/或协同动作。优选地,儿童防护封闭件包含需要双重和/或协同动作以打开所述封闭件的锁定构件。因此,例如,所需的动作可以是本领域技术人员已知的按压-转动或按压-拉动机构。例如,只有当封闭件或其一部分被同时挤压(径向)和旋转,或被推动(包装的轴向)和旋转时,封闭件才可以被打开。儿童防护封闭件可包括抓握或挤压封闭件的两侧并同时旋转以移除封闭件。封闭件可以通过作为锁定构件的相应携带内螺纹的棘齿或楔形凸耳保持在该接受器上,并且防止封闭件从颈部开口旋开,除非封闭件和/或颈部直径地挠曲而由此这些锁定构件在径向方向上移开并且允许封闭件旋开。
锁定构件可能需要双重和/或协同动作来解锁。例如,包装例如按压并滑动,或按压并拉动。可能需要可移除的锁定键来锁定和/或解锁所述互锁构件。
包装可以包含滑动机构,由此封闭件或其部分相对于接受器滑动,或者接受器在封闭件内滑动(例如,作为托盘包装装置,由此胶囊堆叠在托盘部分上),并且提供至少一个配置成相对于包装件的外部锁定内部滑动部分的锁定机构。可对锁定机构进行偏置,使得必须施用压力以释放托盘。在一些实施方式中,内套筒包括用于将内套筒从外套筒内部移除的拉片。
锁定构件可在空间上布置以防止儿童接触。例如,至少2个对可以彼此分开对应于成人手的拇指和食指之间的平均跨度的距离。只有当所有两个对被同时释放时,才可能打开包装容器的盖。
对于盒构型,优选地,锁定构件位于盒子的对角相对的角处。
儿童防护封闭件可产生如“咔哒”的听觉反馈以向使用者发出封闭件就位的信号。
抗撕裂部件
优选地,包装包含尺寸稳定的抗撕裂平面材料(例如层压材料),如用于制造抗撕裂包装结构的尺寸稳定的抗撕裂纸板层压材料。尺寸稳定的抗撕裂纸板层压材料可包括具有第一和第二相对侧的抗撕裂的可生物降解的聚合物芯层。尺寸稳定的抗撕裂纸板层压材料还包括用第一粘合介质粘合到所述抗撕裂聚合物芯层的第一侧上的第一纸板层。尺寸稳定的抗撕裂纸板层压材料还包括用第二粘合介质粘合到抗撕裂聚合物芯层的第二侧上的第二纸板层。抗撕裂聚合物芯层具有至少1密耳的厚度和如通过Elmendorf撕裂传播测试所测量的,纵向上至少350克力和横向上至少400克力的抗撕裂性。此外,第一和第二纸板层在结构上基本相同。
优选地,抗撕裂聚合物芯层具有大约3密耳的厚度和如通过Elmendorf撕裂传播测试所测量的,在纵向上约1700克力和横向上约400克力的抗撕裂性。
单位剂量产品
优选的单位剂量小袋、其构成部件及其制造方法都描述于WO2015/153157中。详细地说,水溶性单位剂量制品包含至少两个水溶性膜和至少一个内部隔室,其中所述隔室由膜包围并且具有内部空间,并且其中所述隔室在内部空间内包含清洁组合物。
单位剂量制品具有高度、宽度和长度。任何这些尺寸的最大值是指单位剂量制品相对侧上两点之间的最大距离。换句话说,单位剂量制品可不具有直侧边,因此可具有可变的长度、宽度和高度,这取决于在何处进行测量。因此,应该在彼此分隔最远的任意两点处测量最大值。
优选地,一旦将单位剂量制品加入到1L烧杯中的950ml的20-21摄氏度的去离子水中,单位剂量制品在10秒和5分钟之间破裂,其中用5cm磁力搅拌棒以350rpm搅拌水。对于破裂,我们在此是指膜可见地断裂或裂开。在膜断裂或裂开后不久,可以看到内部液体洗涤剂组合物离开单位剂量制品进入周围的水中。
水溶性膜
单位剂量制品的膜可溶于或可分散于水中,并且优选具有至少50%,优选至少75%或甚至至少95%的水溶解度,如通过本文所述的方法使用最大孔径20微米的玻璃过滤器后测量的:
向预称重的400ml烧杯中添加50克±0.1克的膜材料,并添加245ml±1ml的蒸馏水。将其在设定为600rpm的磁力搅拌器上剧烈搅拌30分钟。然后,将混合物通过具有如上定义的孔径(最大20微米)的折叠定性烧结玻璃过滤器进行过滤。水通过任何常规方法从收集的滤液中干燥掉,并测定剩余材料的重量(其为溶解或分散的部分)。然后,可以计算百分溶解度或分散性。
优选的膜材料优选为聚合物材料。膜材料可以例如通过聚合物材料的浇铸、吹塑、挤出或吹塑挤出获得,如本领域已知的。
适合用作小袋材料的优选的聚合物、共聚物或其衍生物选自聚乙烯醇、聚乙烯吡咯烷酮、聚环氧烷、丙烯酰胺、丙烯酸、纤维素、纤维素醚、纤维素酯、纤维素酰胺、聚乙酸乙烯酯、聚羧酸和盐、聚氨基酸或肽、聚酰胺、聚丙烯酰胺、马来酸/丙烯酸的共聚物、多糖(包括淀粉和明胶)、天然树胶(例如黄原胶和卡拉胶)。更优选的聚合物选自聚丙烯酸酯和水溶性丙烯酸酯共聚物、甲基纤维素、羧甲基纤维素钠、糊精、乙基纤维素、羟乙基纤维素、羟丙基甲基纤维素、麦芽糊精、聚甲基丙烯酸酯,并且最优选选自聚乙烯醇、聚乙烯醇共聚物和羟丙基甲基纤维素(HPMC),以及它们的组合。优选地,小袋材料中聚合物(例如PVA聚合物)的含量为至少60%。聚合物可以具有任何重均分子量,优选约1000-1000000,更优选约10000-300000,还更优选约20000-150000。
聚合物的混合物也可用作膜材料。根据其应用和所需的要求,这可能有利于控制隔室或小袋的机械和/或溶解性质。合适的混合物包括例如其中一种聚合物具有比另一种聚合物更高的水溶性和/或一种聚合物具有比另一种聚合物更高的机械强度的混合物。具有不同重均分子量的聚合物的混合物也是合适的,例如重均分子量为约10000-40000,优选约20000的PVA或其共聚物与重均分子量为约100000-300000,优选约150000的PVA或其共聚物的混合物。本文中还合适的是聚合物共混组合物,例如包含可水解降解的和水溶性的聚合物共混物,如聚丙交酯和聚乙烯醇,其通过将聚丙交酯和聚乙烯醇混合获得,通常包含约1-35重量%的聚丙交酯和约65-99重量%的聚乙烯醇。本文优选使用的是约60%至约98%水解的,优选约80%至约90%水解的聚合物,以改善材料的溶解特性。
优选的膜材料是聚合物材料。如本领域已知的,膜材料可以例如通过聚合物材料的浇铸、吹塑、挤出或吹塑挤出获得。适合用作小袋材料的优选的聚合物、共聚物或其衍生物选自聚乙烯醇、聚乙烯吡咯烷酮、聚环氧烷、丙烯酰胺、丙烯酸、纤维素、纤维素醚、纤维素酯、纤维素酰胺、聚乙酸乙烯酯、聚羧酸和盐、聚氨基酸或肽、聚酰胺、聚丙烯酰胺、马来酸/丙烯酸的共聚物、多糖(包括淀粉和明胶)、天然树胶(例如黄原胶和卡拉胶)。更优选的聚合物选自聚丙烯酸酯和水溶性丙烯酸酯共聚物、甲基纤维素、羧甲基纤维素钠、糊精,乙基纤维素、羟乙基纤维素、羟丙基甲基纤维素、麦芽糊精、聚甲基丙烯酸酯,并且最优选选自聚乙烯醇、聚乙烯醇共聚物和羟丙基甲基纤维素(HPMC),以及它们的组合。优选地,小袋材料中聚合物例如PVA聚合物的含量为至少60%。聚合物可以具有任何重均分子量,优选约1000-1000000,更优选约10000-300000,还更优选约20000-150000。聚合物的混合物也可用作小袋材料。根据其应用和所需的要求,这可以有利于控制隔室或小袋的机械和/或溶解性质。合适的混合物包括例如其中一种聚合物具有比另一种聚合物更高的水溶性和/或一种聚合物具有比另一种聚合物更高的机械强度的混合物。具有不同重均分子量的聚合物的混合物也是合适的,例如重均分子量为约10000-40000,优选约20000的PVA或其共聚物与重均分子量为约100000-300000,优选约150000的PVA或其共聚物的混合物。本文还合适的是聚合物共混组合物,例如包含可水解降解的和水溶性的聚合物共混物,例如聚丙交酯和聚乙烯醇,其通过混合聚丙交酯和聚乙烯醇获得,通常包含约1-35重量%的聚丙交酯和约65-99重量%的聚乙烯醇。优选本文使用的是约60%至约98%水解的,优选约80%至约90%水解的聚合物,以改善材料的溶解特性。优选的膜在冷水中表现出良好的溶解性,这意味着直接来自水龙头的未加热的水。优选地,这样的膜在低于25摄氏度,更优选低于21摄氏度,更优选低于15摄氏度的温度下表现出良好的溶解性。良好的溶解性是指膜表现出至少50%,优选至少75%或甚至至少95%的水溶性,如在使用上述具有20微米最大孔径的玻璃过滤器之后通过本文所述的方法测量的。
优选的膜是由Monosol以商品编号M8630、M8900、M8779、M8310供应的那些。
自然地,不同的膜材料和/或不同厚度的膜可用于制造本发明的隔室。选择不同膜的益处是所得隔室可表现出不同的溶解度或释放特性。
本文的膜材料还可包含一种或多种添加剂成分。例如,添加增塑剂例如甘油、乙二醇、二甘醇、丙二醇、山梨醇及其混合物可能是有益的。其它添加剂可包括水和待递送至洗涤水的功能性洗涤剂添加剂(包括水),例如有机聚合物分散剂等。
膜可以包含印刷的区域。印刷的区域可覆盖整个膜或其部分。印刷的区域可包括单一颜色或可包括多种颜色,甚至三种颜色。印刷的区域可包含颜料、染料、上蓝剂或其混合物。印刷可作为膜表面上的层存在或可至少部分地渗入膜中。单位剂量制品可包含至少两个膜,或甚至至少三个膜,其中膜密封在一起。印刷的区域可存在于一个膜上,或多于一个膜上,例如两个膜上,或甚至三个膜上。
印刷的区域可以使用标准技术实现,例如柔版印刷或喷墨印刷。优选地,通过柔版印刷(在其中膜被印刷)实现印刷的区域,然后将其模制成开放隔室的形状。然后用洗涤剂组合物填充该隔室,并将第二膜置于该隔室上并与第一膜密封。印刷的区域可以在膜的任一侧上。
印刷的区域可以是纯美学的或可以向消费者提供有用的信息。
印刷的区域可以是不透明的、半透明的或透明的。
液体洗衣洗涤剂组合物
单位剂量小袋或胶囊包含洗衣洗涤剂组合物,优选液体或粉末状洗涤剂组合物,并且最优选液体洗涤剂组合物。液体组合物可以是不透明的、半透明的或透明的。每个隔室可以包含相同或不同的组合物。单位剂量制品包含液体组合物,然而,其也可在不同隔室中包含不同组合物。组合物可以是任何合适的组合物。组合物可以是固体、液体、分散体、凝胶、糊剂、流体或其混合物的形式。组合物在不同的隔室中可以是不同的形式。组合物的非限制性实例包括清洁组合物、织物护理组合物、自动餐具洗涤组合物和硬表面清洁剂。更特别地,组合物可以是洗衣、织物护理或餐具洗涤组合物,包括预处理或浸泡组合物和其它漂洗添加剂组合物。洗衣洗涤剂组合物可在主洗过程中使用或可用作预处理或浸泡组合物。
洗衣洗涤剂组合物包括织物洗涤剂、织物软化剂、2合1洗涤剂和软化、预处理组合物等。洗衣洗涤剂组合物可包含表面活性剂、助洗剂、螯合剂、染料转移抑制剂、分散剂、酶和酶稳定剂、催化材料、漂白活化剂、聚合物分散剂、粘土污垢去除/抗再沉积剂、增白剂、抑泡剂、染料、附加的香料和香料递送体系、结构弹性化剂、织物软化剂、载体、助水溶剂、加工助剂和/或颜料,以及它们的混合物。组合物可为包含选自以下的成分的洗衣洗涤剂组合物:调色染料、表面活性剂、聚合物、香料、包封的香料材料、结构化剂以及它们的混合物。
液体洗衣洗涤剂组合物可包含选自以下的成分:漂白剂、漂白催化剂、染料、色调染料、清洁聚合物(包括烷氧基化聚胺和聚乙烯亚胺)、去污聚合物、表面活性剂、溶剂、染料转移抑制剂、螯合剂、酶、香料、包封的香料、聚羧酸盐、结构化剂以及它们的混合物。
表面活性剂可选自阴离子表面活性剂、阳离子表面活性剂、两性离子表面活性剂、非离子表面活性剂、两性表面活性剂或它们的混合物。优选地,织物护理组合物包含阴离子表面活性剂、非离子表面活性剂或它们的混合物。
阴离子表面活性剂可选自直链烷基苯磺酸盐、烷基乙氧基化物硫酸盐及其组合。
适用于本发明的阴离子表面活性剂可包括通常用于液体洗涤剂产品中的任何常规阴离子表面活性剂类型。这些包括烷基苯磺酸及其盐以及烷氧基化或非烷氧基化烷基硫酸盐物质。
适用于本发明的非离子表面活性剂包括醇烷氧基化物非离子表面活性剂。醇烷氧基化物是对应于以下通式的物质:R1(CmH2mO)nOH,其中R1为C8-C16烷基,m为2至4,且n为约2至12的范围。在一个方面,R1是烷基,其可以是伯烷基或仲烷基,包含约9至15个碳原子,或约10至14个碳原子。在一个方面,烷氧基化脂肪醇也是每分子含有平均约2至12个环氧乙烷部分或每分子约3至10个环氧乙烷部分的乙氧基化物质。
用于本发明洗衣洗涤剂组合物中的调色染料可包含聚合物或非聚合物染料、颜料或它们的混合物。优选地,调色染料包含聚合物染料,其包含发色团组分和聚合物组分。发色团组分的特征在于暴露于光时其吸收蓝色、红色、紫色、紫红色或其组合的波长范围内的光。在一个方面,发色团组分在水和/或甲醇中表现出约520纳米至约640纳米的最大吸收光谱,和在另一方面,在水和/或甲醇中表现出约560纳米至约610纳米的最大吸收光谱。
尽管可以使用任何合适的发色团,但染料发色团优选选自苯并二呋喃、甲川、三苯甲烷、萘酰亚胺、吡唑、萘醌、蒽醌、偶氮、噁嗪、吖嗪、呫吨、三苯并二噁嗪和酞菁染料发色团。单-和双-偶氮染料发色团是优选的。
调色染料可包含染料聚合物,所述染料聚合物包含与至少三个连续重复单元中的一个或多个共价结合的发色团。应当理解,重复单元本身不需要包含发色团。染料聚合物可包含至少5个,或至少10个,或甚至至少20个连续重复单元。
重复单元可以衍生自有机酯(如二羧酸苯酯)与氧化烯氧基和聚氧化烯氧基的组合。重复单元可以衍生自烯烃、环氧化物、氮丙啶、包括包含改性纤维素如羟烷基纤维素的单元的碳水化合物;羟丙基纤维素;羟丙基甲基纤维素;羟丁基纤维素;和羟丁基甲基纤维素或其混合物。重复单元可以衍生自烯烃或环氧化物或其混合物。重复单元可以是C2-C4亚烷氧基,有时称为烷氧基,优选衍生自C2-C4亚烷基氧。重复单元可以是C2-C4烷氧基,优选乙氧基。
为了本发明的目的,至少三个连续重复单元形成聚合物组分。聚合物组分可以通过连接基团直接或间接地与发色团共价结合。合适的聚合物组分的实例包括具有多个重复单元的聚氧化烯链。在一个方面,聚合物组分包括具有2至约30个重复单元,2至约20个重复单元,2至约10个重复单元或甚至约3或4至约6个重复单元的聚氧化烯链。聚氧化烯链的非限制性实例包括环氧乙烷、环氧丙烷、缩水甘油氧化物、环氧丁烷及其混合物。
染料可以未纯化的混合物的形式引入洗涤剂组合物中,其是有机合成途径的直接结果。因此,除了染料聚合物之外,如对于任何聚合步骤的结果所预期的,还可以存在少量未反应的起始材料、副反应的产物和包含不同链长的重复单元的染料聚合物的混合物。
组合物可包含一种或多种提供清洁性能和/或织物护理益处的洗涤剂酶。合适的酶的实例包括但不限于半纤维素酶、过氧化物酶、蛋白酶、纤维素酶、木聚糖酶、脂肪酶、磷脂酶、酯酶、角质酶、果胶酶、角质素酶、还原酶、氧化酶、酚氧化酶、脂加氧酶、木质素酶、支链淀粉酶、鞣酸酶、戊聚糖酶、苹果酸酶(malanase)、β-葡聚糖酶、阿拉伯糖苷酶、透明质酸酶、软骨素酶、漆酶和淀粉酶,或其混合物。典型的组合是常规可应用的酶如蛋白酶、脂肪酶、角质酶和/或纤维素酶与淀粉酶结合的组合。
本发明的洗衣洗涤剂组合物可包含一种或多种漂白剂。除漂白催化剂以外的合适漂白剂包括光漂白剂、漂白活化剂、过氧化氢、过氧化氢源、预形成的过酸及其混合物。通常,当使用漂白剂时,本发明的组合物可包含按所述清洁组合物的重量计约0.1%至约50%或甚至约0.1%至约25%的漂白剂。
组合物可以包含增白剂。合适的增白剂是二苯乙烯类,例如增白剂15。其它合适的增白剂是疏水性增白剂和增白剂49。增白剂可为微粉化的颗粒形式,具有在3至30微米,或3微米至20微米,或3至10微米的范围内的重均粒度。增白剂可以是α或β结晶形式。
本文的组合物还可任选地含有一种或多种铜、铁和/或锰螯合剂。如果使用,螯合剂通常占本文组合物的约0.1重量%至约15重量%,或甚至占本文组合物的约3.0重量%至约15重量%。
组合物可以包含碳酸钙晶体生长抑制剂,如选自以下的一种:1-羟基乙烷二膦酸(HEDP)及其盐;N,N-二羧甲基-2-氨基戊烷-1,5-二酸及其盐;2-膦酰基丁烷-1,2,4-三羧酸及其盐;及其任何组合。
本发明的组合物还可以包含一种或多种染料转移抑制剂。合适的聚合物染料转移抑制剂包括但不限于聚乙烯吡咯烷酮聚合物、聚胺N-氧化物聚合物、N-乙烯基吡咯烷酮和N-乙烯基咪唑的共聚物、聚乙烯噁唑烷酮和聚乙烯基咪唑,或其混合物。当存在于本文的组合物中时,染料转移抑制剂以清洁组合物的约0.0001重量%、约0.01重量%、约0.05重量%至清洁组合物的约10重量%、约2重量%或甚至约1%重量的水平存在。
洗衣洗涤剂组合物可包含一种或多种聚合物。合适的聚合物包括羧酸酯聚合物、聚乙二醇聚合物、聚酯去污聚合物如对苯二甲酸酯聚合物、胺聚合物、纤维素聚合物、染料转移抑制聚合物、染料锁定聚合物(如通过咪唑和表氯醇任选地以1:4:1的比率缩合产生的缩合低聚物)、六亚甲基二胺衍生聚合物及其任何组合。
其它合适的纤维素聚合物可具有0.01至0.99的取代度(DS)和使得DS+DB为至少1.00或DB+2DS-DS2为至少1.20的嵌段度(degree of blockiness)(DB)。取代的纤维素聚合物可具有至少0.55的取代度(DS)。取代的纤维素聚合物可具有至少0.35的嵌段度(DB)。取代的纤维素聚合物可具有1.05至2.00的DS+DB。合适的取代纤维素聚合物是羧甲基纤维素。
另一种合适的纤维素聚合物是阳离子改性的羟乙基纤维素。
合适的香料包括香料微胶囊、聚合物辅助的香料递送体系,包括席夫碱香料/聚合物复合物、淀粉包封的香料香调、负载香料的沸石、释香香料香调以及它们的任何组合。合适的香料微胶囊是基于三聚氰胺甲醛的,通常包含被包含三聚氰胺甲醛的壳包封的香料。这类香料微胶囊可能非常适于在壳中包含阳离子和/或阳离子前体材料,如聚乙烯基甲酰胺(PVF)和/或阳离子改性的羟乙基纤维素(catHEC)。
合适的抑泡剂包括硅氧烷和/或脂肪酸如硬脂酸。
液体洗衣洗涤剂组合物可为有色的。液体洗衣洗涤剂组合物的颜色可与制品的膜上的任何印刷区域相同或不同。单位剂量制品的每个隔室可具有不同的颜色。优选地,液体洗衣洗涤剂组合物包含具有至少16的平均烷氧基化度的非直接染料。
单位剂量制品的至少一个隔室可包含固体。如果存在,固体可以以单位剂量制品的至少5重量%的浓度存在。
第二水溶性膜可包含至少一个开放或封闭的隔室。
在一个实施方案中,开放小袋的第一网状物与封闭小袋的第二网状物组合,优选地其中第一网状物和第二网状物通过合适的方式被放在一起并密封在一起,并且优选地其中第二网状物是转鼓式设置。在这样的设置中,小袋在转鼓的顶部被填充,并且优选地随后用一层膜密封,封闭的小袋下降以与优选地在水平成型表面上形成的小袋(优选地开放小袋)的第一网状物会合。已经发现,将转鼓单元放置在水平成型表面单元上方是特别合适的。
优选地,切割所得到的封闭小袋的网状物以产生单个单位剂量制品。
本领域技术人员将认识到为了制造根据本发明的单位剂量制品所需的模具的适当尺寸。
优选地,为了消费者的价值和方便,容器含有足够数目的胶囊,其为10个或更多个胶囊,更优选20个或更多个胶囊,甚至更优选30个或更多个胶囊,甚至更优选40个或更多个胶囊,并且更优选50个或更多个胶囊。容器中可以有不超过70个胶囊,优选不超过60个胶囊。
胶囊堆叠或堆积在包装中。每个包装有更多数量的胶囊降低了制造成本和对于消费者的价格,但是增加了包装的重量和不在包装内的任何堆叠或堆积物的顶部的每个胶囊所经受的重力。通过使泄漏最少,本发明对于这种胶囊特别有利。
优选地,每个胶囊中洗涤剂组合物的平均质量(m)在3g<m≤15g,优选地3g<m<9.5g和更优选地5g-8g的范围内。该包装在一个包装中包含至少20个胶囊,优选至少30个胶囊,更优选至少40个,甚至更优选至少50个且至多100个胶囊。随着增加每个胶囊的重量,胶囊施用在包装上的力也因此增加。因此保持刚性越来越重要。
每个胶囊可包含至少两片水溶性膜,所述至少两片膜通过围绕胶囊周边延伸的密封(称为密封网)密封在一起。
优选地,胶囊进一步包含内部密封,该内部密封分隔胶囊以提供所述至少两个隔室。这可以增加每个胶囊的密封面积,并进而增加填充期间密封污染的风险。本发明对于这种胶囊是特别有利的。
所有隔室填充有液体或凝胶。然而,另外的隔室也可用凝胶、粉末或其任何组合填充。因此,例如,一些胶囊可以具有容纳液体的隔室和容纳粉末的隔室,或者可以具有液体-凝胶、凝胶-粉末组合(每种形式在不同隔室中,例如液体、凝胶、粉末)。
适用于本发明的可分割成不同组分的组合物包括旨在用于洗衣(基材清洁、软化和/或处理)或机器餐具洗涤的那些。
多隔室胶囊可包含处理组合物的不同部分,当组合时,其构成完全的处理组合物。这意味着处理组合物的各部分的制剂在其物理形式(例如粘度)、其组成或优选其颜色/不透明度方面是不同的。
优选通过成型,更优选热成型一片或多片水溶性膜来制造胶囊。在成型或热成型期间,在膜中形成凹陷。然后填充凹陷,将通常较薄的第二片材叠放在填充的凹陷上并围绕凹陷的边缘将其密封至第一片膜以形成平坦的密封网。粘度高于本发明范围的基材处理组合物在填充后需要更长的时间才能沉降到胶囊凹陷中。如果它们在第二片材叠加和密封时还没有沉降,则较薄的第二片材可在堆积制剂(其可包含膜)上拉伸。这种拉伸可通过加剧薄膜中的针孔而产生泄漏。因此,本发明的粘度范围对于这种胶囊是特别有利的。
在单位剂量的产品或胶囊的腔室堆叠的情况下,即它们不是并排的而是放置在另一腔室的顶部上,产品将包含至少三个膜,其中一个腔室由形成在第一腔室顶部上的另一腔室密封(slead)。
此外,当在模具中真空从第一片膜释放时,通常第一膜的松弛然后导致所施用的第二片材凸出。
多隔室胶囊是通过热成型过程产生的。这样的过程可以有利地包括以下步骤以形成胶囊:
(a)将第一片水溶性聚乙烯醇膜置于具有空腔组的模具上,每个组包括至少两个并排布置的空腔;
(b)对膜进行加热并施用真空以将膜模制到空腔中并且将其保持在适当位置以便在膜中形成相应的凹陷;
(c)将各自可具有不同颜色/不透明度(以及不同的处理功能)的基材处理组合物的不同部分填充到侧凹陷和中心凹陷中,所述部分一起形成完全的洗涤剂组合物;
(d)跨所形成的凹陷将第二片膜密封到第一片膜上以产生具有位于彼此连接的相对位置上并且被连续的内部密封网分开的隔室的多隔室胶囊;
(e)在胶囊之间进行切割以使得形成一系列多隔室的隔室胶囊,每个胶囊在多个隔室(一个中心隔室和两个侧隔室)中含有处理组合物的一部分。
密封可通过任何合适的方法进行,例如热密封、溶剂密封或UV密封或超声密封或其任何组合。特别优选的是水密封。可以通过在将第二片膜密封到第一片膜以形成密封区域之前将水分施用至第二片膜来进行水密封。
优选的热成型方法使用其上载有成型空腔的旋转鼓。使用这种旋转鼓的真空热成型机可获自Cloud LLC。根据本发明的胶囊还可以通过在空腔部分的线性阵列上热成型来制造。适用于该类型的工艺的机器可获自Hoefliger。下面的实例描述集中于旋转工艺。本领域技术人员将理解如何在不付出创造性劳动的情况下适应于采用线性阵列工艺。
苦味剂
本发明的小袋优选包括苦味剂。苦味剂通常是已知的。苦味剂可以是针对包装所描述的那些中的任何一种。
苦味剂通常被掺入到水溶性包装的外表面内或膜涂覆在其上。另外地或可选地,苦味剂作为施用至水溶性包装的外表面的粉末涂层中的粉末状苦味剂包括在水溶性包装中。
在特定的实施方案中,苦味剂被掺入(包括在)水溶性基质中。例如,通过在形成水溶性基质之前将苦味剂溶解在水溶性聚合物溶液中,可以将苦味剂掺入到包括在水溶性基质中的水溶性聚合物的基质(matrix)中。基于苦味剂和水溶性基质的重量,苦味剂可以以100至5000ppm,优选200至3000ppm,更优选500至2000ppm的范围存在于水溶性基质材料中。例如,可将1mg的苦味剂掺入1g的水溶性基质中以提供1000ppm的苦味剂。
苦味剂在水溶性基质表面上的膜涂覆可以通过已知技术进行,如将苦味剂溶液喷雾或印刷到水溶性基质的表面上。
苦味剂可以包括在一个或多个印刷区域中的水溶性基质外表面上的粉末涂层中、涂膜在其上和/或包含在其中。当苦味剂包括在印刷区域中的在水溶性基质的外表面上的粉末涂层中、涂覆在其上和/或包括在其中时,对UV固化油墨印刷物的质量可能没有不利影响。特别地,当苦味剂被掺入到印刷区域中的水溶性基质中时,对UV固化油墨印刷物的质量没有不利影响。在一些实施方案中,苦味剂均匀地掺入水溶性基质中。这样,可以简化将苦味剂包含到水溶性基质中和水溶性基质的印刷中。
芳香剂
单位剂量洗涤剂组合物包含芳香剂。
优选地,芳香剂选自2-甲基戊酸乙酯(母菊酯)、柠檬烯、二氢月桂烯醇、二甲基苄基碳酸乙酸酯、乙酸苄酯、香叶醇、甲基壬基乙醛、六氢化-4,7-亚甲基-1H-茚-5-酚乙酸酯(乙酸三环癸烯酯)、仙客来醛、β-紫罗兰酮、水杨酸己酯、吐纳麝香、[2-(环己氧基)乙基]苯、八氢四甲基苯乙酮(OTNE)及其混合物。
然而,优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂2-甲基戊酸乙酯(母菊酯)。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂柠檬烯。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂二氢月桂烯醇。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂二甲基苄基碳酸乙酸酯。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂乙酸苄酯。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂香叶醇。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂甲基壬基乙醛。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂六氢化-4,7-亚甲基-1H-茚-5-酚乙酸酯(乙酸三环癸烯酯)。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂仙客来醛。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂β-紫罗兰酮。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂水杨酸己酯。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂吐纳麝香。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂[2-(环己氧基)乙基]苯。
优选地,芳香剂包含0.5至30重量%,更优选2至15重量%和特别优选6至10重量%的芳香剂八氢四甲基苯乙酮(OTNE)。
此类芳香剂是已知的并且描述于EP-A-1 407 754中。
香料优选包含倍半萜或类倍半萜组分,其选自长叶环烯、法尼醇、2,3-二氢金合欢醇、α-金合欢烯(farnescene)、β-金合欢烯、朱栾倍半萜、α-桉叶油醇、α-摩勒烯、表-α-cardinol、β-芹子烯、α-芹子烯、大根香烯D、大根香烯B、澳白檀醇、β-倍半菲兰烯、α-姜黄烯、α-红没药烯、α-红没药醇、β-檀香醇、viridifloral、香附烯、长叶烯、库贝醇、马兜铃烯、香橙烯、蛇麻烯环氧化物、羟基菖蒲烯、愈创木醇、quinanol E、quinanol D、quinanol C、quinanol B、quinanol A、脱氢-jinkoh-eremol、7β-H-9(10)-烯-11,12-环氧-8-氧代艾里莫芬烷、nookatone、α-蛇麻烯、8,12-环氧艾里莫芬-9,11-二烯、neopetasane、β-沉香呋喃、α-沉香呋喃、α-雪松醇、虎尾草醇、榄香醇、(+)-(4S,5R)-卡拉酮、琼脂螺醇、(+)-(4S,5R)-二氢卡拉酮、4,15-二羟基二氢-β-沉香呋喃、E-橙花叔醇、10-表-桉叶油醇、芹子-3,11-二烯-14-醇、(5S,7S,10S)-(-)-芹子-3,11-二烯-9-酮及其混合物。
其他
本文所述的单位剂量产品适用于基材处理方法,合适地适用于洗衣或机器餐具洗涤方法。因此,本发明的另一方面提供了如本文所述的单位剂量产品或胶囊在清洁方法中的用途,所述清洁方法合适地为洗衣或机器餐具洗涤方法。合适地,该方法包括通过解锁儿童防护封闭件来打开包装,从包装中取出一个或多个胶囊,在洗涤循环开始之前将胶囊放置在洗衣机的滚筒或进料抽屉或任何进料装置中。
胶囊尤其适用于(基材)洗涤机和餐具洗涤机以及其它应用。它们也可用于手工洗衣或餐具洗涤操作。在使用中,根据本发明的胶囊优选且方便地直接放入将形成洗涤液的液体中或放入将引入该液体的区域中。胶囊在与液体接触时溶解,从而从单独的隔室释放洗涤剂组合物并使它们形成所需的洗涤液。
优选地,一旦将单位剂量制品添加到1L烧杯中的20-21℃的950ml去离子水中,胶囊在10秒,优选30秒至5分钟之间破裂,其中用5cm磁力搅拌棒以350rpm搅拌水。对于破裂,我们在本文中是指观察到膜可见地破裂或分裂。在膜破裂或分裂后不久,可以看到内部液体基质组合物离开制品进入周围的水中。
本文描述了许多提议和方面,这些提议和方面旨在被组合以实现改进的或累积的益处。因此,任何一个方面可以与任何其他方面组合。类似地,与任何方面相关联的任选特征可适用于其它方面的任何一个。
Claims (11)
1.一种包装,所述包装包含至少50重量%的可生物降解材料和多个单位剂量洗涤剂小袋,并且其中所述单位剂量洗涤剂小袋包含平均3至15g洗涤剂组合物。
2.如权利要求1所述的包装,其中所述单位剂量洗涤剂小袋包含平均3至9.5g,优选5至8g洗涤剂组合物。
3.如权利要求1或2所述的包装,其中所述洗涤剂组合物包含非水性溶剂。
4.如前述任一项权利要求所述的包装,其中所述可生物降解材料包括阻隔涂层。
5.如前述任一项权利要求所述的包装,其中所述阻隔涂层包括水基阻隔涂层。
6.如权利要求3-4中任一项所述的包装,其中所述阻隔涂层包含热塑性弹性体。
7.如前述任一项权利要求所述的包装,其中所述单位剂量洗涤剂小袋包含0重量%至5重量%的水。
8.如前述任一项权利要求所述的包装,其中所述单位剂量洗涤剂小袋包含苦味剂。
9.如前述任一项权利要求所述的包装,其中所述单位剂量洗涤剂小袋包含酞菁基颜料。
10.如前述任一项权利要求所述的包装,其中所述单位剂量洗涤剂小袋包含基于膦酸的螯合剂。
11.如前述任一项权利要求所述的包装,其中所述洗涤剂组合物包含芳香剂组分,其选自2-甲基戊酸乙酯(母菊酯)、柠檬烯、二氢月桂烯醇、二甲基苄基碳酸乙酸酯、乙酸苄酯、香叶醇、甲基壬基乙醛、六氢化-4,7-亚甲基-1H-茚-5-酚乙酸酯(乙酸三环癸烯酯)、仙客来醛、β紫罗兰酮、水杨酸己酯、吐纳麝香、[2-(环己氧基)乙基]苯、八氢四甲基苯乙酮(OTNE)及其混合物。