CN118056892A - 新型润滑剂脱模剂组合物 - Google Patents
新型润滑剂脱模剂组合物 Download PDFInfo
- Publication number
- CN118056892A CN118056892A CN202211452979.7A CN202211452979A CN118056892A CN 118056892 A CN118056892 A CN 118056892A CN 202211452979 A CN202211452979 A CN 202211452979A CN 118056892 A CN118056892 A CN 118056892A
- Authority
- CN
- China
- Prior art keywords
- phthalate
- composition
- use according
- disodium
- sodium
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种新型润滑剂脱模剂组合物，描述了一种组合物在挤压金属处理中的用途。所述组合物包含至少一种苯二甲酸钠盐和/或苯二甲酸钾盐以及任选地至少一种碱土金属的苯二甲酸盐。
Description
技术领域
本发明涉及一种润滑剂脱模剂组合物在金属挤压处理中的用途。
背景技术
金属材料的挤压是通过塑性变形获得具有恒定横截面的部件的处理，例如板、管、型材和棒材。
挤压处理用于如铝、铜、铅和钢等金属材料的工业生产。必须加工和转化的材料通常呈糊状，呈托盘或粉末形式，并通过压入模具中而被压缩，以获得所需的产品，实际上外形是随后使用的。
模制是通过压缩坯料形式的金属材料进行的，通过专门设计的模具为被处理的材料提供所需形状。金属必须处于糊状熔化或软化状态，这样可以发生塑性成形通道。
一旦获得金属材料，例如铝，将其带到温度为440至500℃之间的加热炉中；然后用活塞将产品压在钢模上，挤压材料沿着辊子表面移动，并在此冷却。因为坯料的最后部分，对应于几十毫米(靠近活塞)，是型材和杂质的潜在缺陷来源，因此不会被挤出，而是循环结束时通过自动剪切装置切割，然后通过重熔而再利用(坯料底部)。由于胚料的高温，金属胚料倾向于附着在挤压机的活塞头并保持与所述活塞头的焊接状态，它可以锁定活塞，从而造成挤压机损坏。
已经引入了多种解决方案来防止坯料始终粘附在活塞头上，例如，使用润滑油和油和/或蜡基的糊剂(添加或不添加如石墨、铝和其他的固体颜料)。然而，这种类型的产品需要用垫板或刷子手动涂抹。由于高温，这些产品可以导致滴漏(损失和工作环境的污染)，并且总是会产生相当稠密的烟雾和蒸汽。此外，所述产品是可燃的并能够起火。
第二种解决方案涉及炭黑层的使用，由于燃烧时间短，炭黑层会沉积在处理过的表面上。然而，由于燃烧，使用所述产品是危险的，并且如果吸入可以是有害的。
氮化硼是一种合成陶瓷材料，在工作温度下不会发生变化。如果以某种方法沉积以完美地覆盖整个处理过的表面，该产品特别有效。由于它事实上不能在表面上迁移，任何未覆盖的区域都会在压脚和胚料之间产生金属化和胶合。此外，非常轻的粉末会扩散到环境中并且可以被吸入。
此外，水性产品在非常热的表面(>200℃)上喷涂时，会出现发暖现象(或莱顿弗罗斯特效应(Leidenfrost effect))，从而在喷涂的液滴和金属之间立即形成蒸汽屏障，防止液态金属和薄膜沉积的直接接触。这些材料的涂抹不可避免地导致不完整和不均匀的滴漏和成膜，这意味着这些产品属于不普遍的类别，尽管它仍然在使用。
为此，人们强烈感觉到需要克服上述技术问题，避免上述缺点。
发明内容
本发明涉及一种组合物在挤压金属处理中的用途。所述组合物包含至少一种苯二甲酸钠盐和/或苯二甲酸钠钾盐以及任选地至少一种碱土金属的苯二甲酸盐。
优选地，该组合物包含邻苯二甲酸二钠。该组合物优选粒度为5至120μm之间的粉末形式。根据实施方式，该组合物施用在挤压机1的活塞10的头部100的至少一个表面101上和/或金属坯料20的至少一个表面201上。优选地，该组合物在挤压处理开始之前施用，以便在挤压处理结束时有利于活塞10的头部100的至少一个表面101与坯料20分离。
附图说明
图1表示用于挤压金属的挤压机1的示意图。
具体实施方式
本发明涉及一种组合物在挤压金属处理中的用途。所述组合物包含至少一种苯二甲酸钠盐和/或苯二甲酸钾盐和任选地至少一种碱土金属的苯二甲酸盐。
根据实施方式，该组合物是粉末形式。优选地，该组合物是粒度为10至150μm之间，更优选5至120μm之间的粉末形式。
根据实施方式，苯二甲酸钠盐在苯二甲酸一钠和/或苯二甲酸二钠之间选择。优选地，苯二甲酸二钠选自邻苯二甲酸二钠和对苯二甲酸二钠。根据优选的实施方式，苯二甲酸二钠是邻苯二甲酸二钠。
根据进一步的实施方式，苯二甲酸钾盐选自苯二甲酸一钾或苯二甲酸二钾。
优选地，碱土金属的苯二甲酸盐选自邻苯二甲酸钙或镁盐或间苯二甲酸盐或对苯二甲酸盐。根据实施方式，组合物包含至少一种固体颜料，优选地，所述至少一种固体颜料选自滑石、云母、氮化硼、氮化石墨或其他矿物。
根据优选的实施方式，该组合物包含邻苯二甲酸二钠，任选地与至少一种碱土金属的苯二甲酸盐混合。
根据实施方式，该组合物包含浓度为20至75％重量/重量之间，优选30至60％重量/重量之间的苯二甲酸钠盐或苯二甲酸钾盐。
根据实施方式，该组合物包含浓度为20至75％重量/重量之间，优选30至60％重量/重量之间的至少一种碱土金属的苯二甲酸盐。
根据优选的实施方式，该组合物由苯二甲酸二钠组成。
根据实施方式，该组合物施用在挤压机1的活塞10的头部100的至少一个表面101上和/或金属坯料20的至少一个表面201上。优选地，该组合物在挤压处理开始之前施用，以便在挤压处理结束时有利于活塞10的头部100的表面101与坯料20分离。优选地，挤压处理是挤压有色金属(更优选由铝或铜或其与其他金属的合金制成)的处理。
根据实施方式，该组合物施加在挤压机1的活塞10的头部100的至少一个表面101上和/或在金属坯料20的至少一个表面201上，使用本领域专家已知的系统和方法。优选地，组合物通过喷涂的方式施用，优选使用静电型喷涂系统。
申请人惊奇地发现，根据本发明的组合物能够防止坯料20的金属粘附在活塞10的头部100上或防止在其上保持焊接以及因此的活塞10锁定，或防止在缩回时由于挤压机1的工具破损而造成损坏。因此，该组合物可以定义为润滑剂脱模剂。
根据本发明的组合物具有400至450℃之间的熔点，略低于或等于挤压处理的温度。由于这个原因，在将其施用到挤压机1的活塞10的头部100的至少一个表面101和/或金属坯料20的至少一个表面201上之后，由于坯料20或活塞10的头部100的高温，它开始熔化并在处理过的表面上自发扩散。活塞10的头部100和坯料20之间的后续压缩导致覆盖整个接触表面的薄膜完全拉伸，形成完整且连续的屏障膜。
此外，根据本发明的组合物的用途降低了相对于氮化硼的消耗，因为该产品不会产生粉末的静态积聚，而是总是覆盖表面而不论施加的量有多小。
为了尽可能减少昂贵的氮化硼的消耗，使用粒度为2至30μm，平均值约10μm，以保证5至15m2/g的覆盖能力。根据本发明的组合物包含具有更大粒度的苯二甲酸钠盐或苯二甲酸钾盐，在20和100微米之间，这是由于增加了覆盖能力的熔融特性。这意味着在喷涂分配过程中，与苯二甲酸钠盐或苯二甲酸钾盐相比，氮化硼倾向于在周围空间中更强烈和更快地扩散，另一方面，由于静电荷，苯二甲酸钠盐或苯二甲酸钾盐会到达待处理的表面，而不会进一步扩散到空气中。以这种方式，组合物很少扩散到处理过的表面之外，避免影响挤压机1、挤压机外围设备和周围环境。最重要的是，机器附近的操作员吸入的量较小。最后，这减少了由于根据本发明的组合物获得的型材40的包含物和条纹而导致的缺陷。
Claims (12)
1.一种组合物在挤压有色金属处理中的用途，
所述组合物包含至少一种苯二甲酸钠盐或苯二甲酸钾盐和任选的碱土金属的苯二甲酸盐，
并且，所述组合物呈粉末形式。
2.根据权利要求1所述的用途，其中，
所述组合物包含浓度为20至75％重量/重量之间，优选30至60％重量/重量之间的至少一种苯二甲酸钠盐或苯二甲酸钾盐。
3.根据权利要求1或2所述的用途，其中，
所述组合物包含浓度为20至75％重量/重量之间，优选30至60％重量/重量之间的碱土金属的苯二甲酸盐。
4.根据权利要求1至3中任一项所述的用途，其中，
所述苯二甲酸钠盐选自苯二甲酸一钠或苯二甲酸二钠。
5.根据权利要求1至4中任一项所述的用途，其中，
所述苯二甲酸钾盐选自苯二甲酸一钾或苯二甲酸二钾。
6.根据权利要求1至5中任一项所述的用途，其中，
所述苯二甲酸二钠选自邻苯二甲酸二钠和对苯二甲酸二钠。
7.根据权利要求6所述的用途，其中，
所述苯二甲酸二钠是邻苯二甲酸二钠。
8.根据权利要求1所述的用途，其中，
所述组合物由苯二甲酸二钠组成。
9.根据权利要求1至8中任一项所述的用途，其中，
所述组合物具有10至150μm之间的粒度。
10.根据权利要求9所述的用途，其中，
所述组合物具有5至120μm之间的粒度。
11.根据权利要求1至10中任一项所述的用途，其中，
将所述组合物施用在挤压机(1)的活塞(10)的头部(100)的至少一个表面(101)上和/或在有色金属的坯料(20)的至少一个表面(201)上。
12.根据权利要求1至11中任一项所述的用途，其中，
所述组合物还包含至少一种固体颜料，优选地，所述至少一种固体颜料选自滑石、云母、氮化硼、氮化石墨或其他矿物。