CN117924939A - 一种耐低温性能好的止水带 - Google Patents
一种耐低温性能好的止水带 Download PDFInfo
- Publication number
- CN117924939A CN117924939A CN202311786001.9A CN202311786001A CN117924939A CN 117924939 A CN117924939 A CN 117924939A CN 202311786001 A CN202311786001 A CN 202311786001A CN 117924939 A CN117924939 A CN 117924939A
- Authority
- CN
- China
- Prior art keywords
- water stop
- rubber
- low temperature
- temperature resistance
- raw materials
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐低温性能好的止水带，包含以下各成分的重量百分比原料：橡胶基原料50％、抗老化剂7％、填料18％、加工助剂10％、硫化剂7％、阻燃剂3％和加工油料5％。本发明采用低苯基硅橡胶和三乙丙橡胶都具有良的耐候性，能够抵紫外线、高温、寒等不利气候条件的侵和损害，保持密封能长时间稳定，苯基硅橡胶和三元丙橡胶具有较高的学稳定性，对很多化学质具有优异的耐腐和耐侵蚀能力，能在复杂的环境中保密封效果，低苯基硅橡胶和三元乙丙橡胶都具有良好的弹性和拉伸性能，能够承受一定的形和应力，适应不同表面形状和尺寸的需求，实现有效的密封效果。
Description
技术领域
本发明涉及止水带技术领域，更具体为一种耐低温性能好的止水带。
背景技术
胶止水带是一种具有弹性和耐久性的密封材料，常用于防水和密封应用。它通常由胶或聚合物材料制成具有良好的抗水、油和抗化学品的特点。
橡胶止水带可以广应用于建筑、工程、道系统、水池、浴室及其他需要防水密封的所。它能够有效地防水、气体、灰尘和音的渗入，保持环的干燥和清洁。同时，它还可以提供一定的抗和防护功能。使用橡胶水带时，一般需要先洁和处理被密封的表面，然后将止水带固定在需要密封的地方。可以使用胶水、胶带或者机械方式将止水带定好，并确保密封完。需要注意的是，不同场合和应用可能需要不材质、尺寸和厚度的橡胶止水带。
传统的橡胶止水带的抗撕裂能力和脑膜等力学性能不足，无法保证止水带的使用寿命。因此，需要提供一种新的技术方案给予解决。
发明内容
本发明的目的在于提供一种耐低温性能好的止水带，解决了传统的橡胶止水带的抗撕裂能力和脑膜等力学性能不足，无法保证止水带的使用寿命的问题。
为实现上述目的，本发明提供如下技术方案：一种耐低温性能好的止水带，包含以下各成分的重量百分比原料：橡胶基原料40％～60％、抗老化剂5％～10％、填料10％～25％、加工助剂5％～16％、硫化剂5％～10％、阻燃剂2％～5％和加工油料3％～6％。
作为本发明的一种优选实施方式，包含以下各成分的重量百分比原料：橡胶基原料50％、抗老化剂7％、填料18％、加工助剂10％、硫化剂7％、阻燃剂3％和加工油料5％。
作为本发明的一种优选实施方式，所述橡胶基原料包括低苯基硅橡胶和三元乙丙橡胶，所述低苯基硅橡胶是由聚二甲基硅氧烷作为基础聚合物，经过苯基衍生物的取代反应制得，所述三元乙丙橡胶乙烯、丙烯和一小部分非共聚单体通过聚合反应而制成，所述低苯基硅橡胶和三元乙丙橡胶的比例为：3～7:2～8。
作为本发明的一种优选实施方式，所述填料为碳黑、硅灰、活性白土、陶瓷微珠和纤维填料中的一种或多种组合。
作为本发明的一种优选实施方式，所述抗老化剂为酚类抗氧剂、有机磷类氧剂和光稳定剂中的一种。
作为本发明的一种优选实施方式，所述加工助剂为硫酸镁、硫酸锌、弹性体助剂和分散剂中的一种。
作为本发明的一种优选实施方式，所述阻燃剂为氯化石蜡、六偏磷酸酯、氧化铝、硅酸铝、氧化镁、硼砂和氯化铝中的一种或混合物。
作为本发明的一种优选实施方式，所述分散剂为硬脂酸钙、蒙脱土和烷偶联剂中的一种。
与现有技术相比，本发明的有益效果如下：
本发明采用低苯基硅橡胶和三乙丙橡胶都具有良的耐候性，能够抵紫外线、高温、寒等不利气候条件的侵和损害，保持密封能长时间稳定，苯基硅橡胶和三元丙橡胶具有较高的学稳定性，对很多化学质具有优异的耐腐和耐侵蚀能力，能在复杂的环境中保密封效果，低苯基硅橡胶和三元乙丙橡胶都具有良好的弹性和拉伸性能，能够承受一定的形和应力，适应不同表面形状和尺寸的需求，实现有效的密封效果，低苯基硅橡胶和三元乙丙橡胶在防水应用方面表出色，能够有效阻隔分的渗透和泄漏，持被密封区域的干燥，低基硅橡胶和三元乙橡胶制成的止水带常具有较低的挥发性有机物含量，符合环保标准，对人体和环境安全可靠。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本发明提供一种耐低温性能好的止水带，包含以下各成分的重量百分比原料：橡胶基原料50％、抗老化剂7％、填料18％、加工助剂10％、硫化剂7％、阻燃剂3％和加工油料5％。
进一步改进的，所述橡胶基原料包括低苯基硅橡胶和三元乙丙橡胶，所述低苯基硅橡胶是由聚二甲基硅氧烷作为基础聚合物，经过苯基衍生物的取代反应制得，所述三元乙丙橡胶乙烯、丙烯和一小部分非共聚单体通过聚合反应而制成，所述低苯基硅橡胶和三元乙丙橡胶的比例为：5:5。
进一步改进的，所述填料为碳黑、硅灰的组合，碳黑和硅灰可以显著提高橡胶材料的耐磨性能和强度。
进一步改进的，所述抗老化剂为酚类抗氧剂，较高的抗化剂含量可以提供更的耐候性能和耐低温性能。
进一步改进的，所述加工助剂为硫酸镁，硫酸镁通常用作加工助剂的酸化反应催化剂，可以促进橡胶硫化过程中的交联反应。
进一步改进的，所述阻燃剂为氧化铝、硅酸铝和氯化铝中的混合物，通过与橡胶材一起混炼或涂覆的方式来提供阻燃性能。
进一步改进的，所述分散剂为烷偶联剂，确保材料在橡胶中的均匀分布。
与现有技术相比，本发明的有益效果如下：
本发明采用低苯基硅橡胶和三乙丙橡胶都具有良的耐候性，能够抵紫外线、高温、寒等不利气候条件的侵和损害，保持密封能长时间稳定，苯基硅橡胶和三元丙橡胶具有较高的学稳定性，对很多化学质具有优异的耐腐和耐侵蚀能力，能在复杂的环境中保密封效果，低苯基硅橡胶和三元乙丙橡胶都具有良好的弹性和拉伸性能，能够承受一定的形和应力，适应不同表面形状和尺寸的需求，实现有效的密封效果，低苯基硅橡胶和三元乙丙橡胶在防水应用方面表出色，能够有效阻隔分的渗透和泄漏，持被密封区域的干燥，低基硅橡胶和三元乙橡胶制成的止水带常具有较低的挥发性有机物含量，符合环保标准，对人体和环境安全可靠。
实施例2
本发明提供一种耐低温性能好的止水带，包含以下各成分的重量百分比原料：橡胶基原料40％、抗老化剂10％、填料15％、加工助剂16％、硫化剂10％、阻燃剂4％和加工油料5％。
进一步改进的，所述橡胶基原料包括低苯基硅橡胶和三元乙丙橡胶，所述低苯基硅橡胶是由聚二甲基硅氧烷作为基础聚合物，经过苯基衍生物的取代反应制得，所述三元乙丙橡胶乙烯、丙烯和一小部分非共聚单体通过聚合反应而制成，所述低苯基硅橡胶和三元乙丙橡胶的比例为：3:7。
进一步改进的，所述填料为陶瓷微珠和纤维填料的组合，陶瓷微珠是一种轻质、高硬度的填料，它可以提高材料的抗压强度和耐磨性，纤维填料可以是玻璃纤维、碳纤维、防火纤维，可以增加材料的强度和韧性。
进一步改进的，所述抗老化剂为光稳定剂，增加了止水带的抗老化效果。
进一步改进的，所述加工助剂为弹性体助剂，可以改善橡胶的可塑性和加工性能。
进一步改进的，所述阻燃剂为硼砂，通过与橡胶材一起混炼的方式来提供阻燃性能。
进一步改进的，所述分散剂为硬脂酸钙，确保材料在橡胶中的均匀分布。
与现有技术相比，本发明的有益效果如下：
本发明采用低苯基硅橡胶和三乙丙橡胶都具有良的耐候性，能够抵紫外线、高温、寒等不利气候条件的侵和损害，保持密封能长时间稳定，苯基硅橡胶和三元丙橡胶具有较高的学稳定性，对很多化学质具有优异的耐腐和耐侵蚀能力，能在复杂的环境中保密封效果，低苯基硅橡胶和三元乙丙橡胶都具有良好的弹性和拉伸性能，能够承受一定的形和应力，适应不同表面形状和尺寸的需求，实现有效的密封效果，低苯基硅橡胶和三元乙丙橡胶在防水应用方面表出色，能够有效阻隔分的渗透和泄漏，持被密封区域的干燥，低基硅橡胶和三元乙橡胶制成的止水带常具有较低的挥发性有机物含量，符合环保标准，对人体和环境安全可靠。
实施例3
本发明提供一种耐低温性能好的止水带，包含以下各成分的重量百分比原料：橡胶基原料60％、抗老化剂5％、填料10％、加工助剂5％％、硫化剂10％、阻燃剂5％和加工油料5％。
进一步改进的，所述橡胶基原料包括低苯基硅橡胶和三元乙丙橡胶，所述低苯基硅橡胶是由聚二甲基硅氧烷作为基础聚合物，经过苯基衍生物的取代反应制得，所述三元乙丙橡胶乙烯、丙烯和一小部分非共聚单体通过聚合反应而制成，所述低苯基硅橡胶和三元乙丙橡胶的比例为：6:4。
进一步改进的，所述填料为活性白土，活性白土是一种颗粒状的填料，它可以增加材料的硬度、强度和耐磨性。
进一步改进的，所述抗老化剂为有机磷类氧剂，增加了止水带的抗老化效果。
进一步改进的，所述加工助剂为硫酸锌，硫酸锌也是一种常用的加助剂，它可以加速橡胶的硫化反应，提高硫化速度。
进一步改进的，所述阻燃剂为氯化石蜡，通过与橡胶材一起混炼的方式来提供阻燃性能。
进一步改进的，所述分散剂为蒙脱土，确保材料在橡胶中的均匀分布。
与现有技术相比，本发明的有益效果如下：
本发明采用低苯基硅橡胶和三乙丙橡胶都具有良的耐候性，能够抵紫外线、高温、寒等不利气候条件的侵和损害，保持密封能长时间稳定，苯基硅橡胶和三元丙橡胶具有较高的学稳定性，对很多化学质具有优异的耐腐和耐侵蚀能力，能在复杂的环境中保密封效果，低苯基硅橡胶和三元乙丙橡胶都具有良好的弹性和拉伸性能，能够承受一定的形和应力，适应不同表面形状和尺寸的需求，实现有效的密封效果，低苯基硅橡胶和三元乙丙橡胶在防水应用方面表出色，能够有效阻隔分的渗透和泄漏，持被密封区域的干燥，低基硅橡胶和三元乙橡胶制成的止水带常具有较低的挥发性有机物含量，符合环保标准，对人体和环境安全可靠。
对比实施例1
一种耐低温的止水带橡胶材料，包括以下重量比的成分：三元乙丙橡胶70份，低苯基硅橡胶30份，甲基丙烯酸锌3份，硫化活性剂1份，防老剂1份，炭黑60份，过氧化物交联剂5份，增塑剂1份。
其中，所述三元乙丙橡胶的乙烯丙烯比为50/50。
并且，硫化活性剂为氧化锌。
又，所述防老剂为防老剂D。
并且，所述炭黑为炭黑N220。
进一步的，所述过氧化物交联剂为过氧化物交联剂BIBP。
此外，所述增塑剂为癸二酸二辛酯。
并且，所述低苯基硅橡胶的苯基含量为C6H5/Si＝6～11％。
上述耐低温的止水带橡胶材料的制备方法包括以下步骤：
①按照以下重量比称取原料：三元乙丙橡胶70份，低苯基硅橡胶30份，甲基丙烯酸锌3份，硫化活性剂1份，防老剂1份，炭黑60份，过氧化物交联剂5份，增塑剂1份；
②将三元乙丙橡胶投入密闭式炼胶机进行塑炼，密炼机温度95±5℃，压力0.5MPa，塑炼5分钟；
③在塑炼后的三元乙丙橡胶中加入低苯基硅橡胶，密炼机温度85±5℃，压力0.5MPa，混炼3分钟
④向三元乙丙橡胶和低苯基硅橡胶的混炼胶料中加入甲基丙烯酸锌、防老剂、炭黑、过氧化物交联剂、增塑剂，继续混炼2分钟；加入硫化活性剂，继续混炼1分钟；
⑤将加入硫化活性剂后的混炼胶料冷却2h后置于开炼机上，打三角包薄通，混炼均匀，下片；
⑥将步骤⑤得到的片状胶料进行硫化，之后取出冷却至室温，即得所述耐低温的止水带橡胶材料。其中，所述硫化条件为在10MPa、170℃条件下硫化10min。
耐低温的止水带橡胶材料采用的三元乙丙橡胶是乙烯、丙烯和少量的非共轭二烯烃的共聚物，是乙丙橡胶的一种，因其主链是由化学稳定的饱和烃组成，只在侧链中含有不饱和双键，故其耐臭氧、耐热、耐候等耐老化性能优异，适用温度范围广，最低使用温度-40～-60℃。
硅橡胶是指分子主链以Si-O键为主，而侧基为有机基团(主要是甲基)的一类线形聚合物，是一种兼具无机和有机性质的高分子弹性体。由于其主链的Si-O键键能比一般橡胶分子主链的C-C键键能高得多，硅橡胶具有优异的耐热性、弹性、耐寒性，优良的脱模性、电气性、透气性、导热性、防水性及良好的温度稳定性。苯基的引入可提高硅橡胶的耐高、低温性能，硅橡胶耐低温性能良好，一般在-55℃下仍能工作，引入苯基后，可达-73℃。
本发明所述的耐低温的止水带橡胶材料采用的低苯基硅橡胶是在乙烯基硅橡胶的分子链中，引入二苯基硅氧链节或甲基苯基硅氧链节而得。该低苯基硅橡胶的苯基含量为C6H5/Si＝6～11％，通过采用具有良好耐低温性能的低苯基硅橡胶和三元乙丙橡胶进行复配，得到的橡胶材料制成的止水带不仅具有良好的抗撕裂、耐磨等力学性能，还具有较好的耐老化、耐高温，特别是具有较好的耐低温性能，
对实施例1、2、3和对比实施例进行性能对比表格如下：
表1
有上述对比表格可以看出，实施例1、2和3所制成的耐低温止水带，相较于传统的止水带，其防水性能、耐高温性、耐低温性、耐老化性和耐磨性都有一定的提高，而实施例2中所制成的产品性能最好.
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言，显然本发明不限于上述示范性实施例的细节，而且在不背离本发明的精神或基本特征的情况下，能够以其他的具体形式实现本发明。因此，无论从哪一点来看，均应将实施例看作是示范性的，而且是非限制性的，本发明的范围由所附权利要求而不是上述说明限定，因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
最后应说明的几点是：首先，在本申请的描述中，需要说明的是，除非另有规定和限定，术语“安装”、“相连”、“连接”应做广义理解，可以是机械连接或电连接，也可以是两个元件内部的连通，可以是直接相连，“上”、“下”、“左”、“右”等仅用于表示相对位置关系，当被描述对象的绝对位置改变，则相对位置关系可能发生改变。
最后应说明的是：以上所述仅为本发明的优选实施例而已，并不用于限制本发明，尽管参照前述实施例对本发明进行了详细的说明，对于本领域的技术人员来说，其依然可以对前述各实施例所记载的技术方案进行修改，或者对其中部分技术特征进行等同替换。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.一种耐低温性能好的止水带，其特征在于：包含以下各成分的重量百分比原料：橡胶基原料40％～60％、抗老化剂5％～10％、填料10％～25％、加工助剂5％～16％、硫化剂5％～10％、阻燃剂2％～5％和加工油料3％～6％。
2.根据权利要求1所述一种耐低温性能好的止水带，其特征在于：包含以下各成分的重量百分比原料：橡胶基原料50％、抗老化剂7％、填料18％、加工助剂10％、硫化剂7％、阻燃剂3％和加工油料5％。
3.根据权利要求2所述一种耐低温性能好的止水带，其特征在于：所述橡胶基原料包括低苯基硅橡胶和三元乙丙橡胶，所述低苯基硅橡胶是由聚二甲基硅氧烷作为基础聚合物，经过苯基衍生物的取代反应制得，所述三元乙丙橡胶乙烯、丙烯和一小部分非共聚单体通过聚合反应而制成，所述低苯基硅橡胶和三元乙丙橡胶的比例为：3～7:2～8。
4.根据权利要求2所述一种耐低温性能好的止水带，其特征在于：所述填料为碳黑、硅灰、活性白土、陶瓷微珠和纤维填料中的一种或多种组合。
5.根据权利要求2所述一种耐低温性能好的止水带，其特征在于：所述抗老化剂为酚类抗氧剂、有机磷类氧剂和光稳定剂中的一种。
6.根据权利要求2所述一种耐低温性能好的止水带，其特征在于：所述加工助剂为硫酸镁、硫酸锌、弹性体助剂和分散剂中的一种。
7.根据权利要求2所述一种耐低温性能好的止水带，其特征在于：所述阻燃剂为氯化石蜡、六偏磷酸酯、氧化铝、硅酸铝、氧化镁、硼砂和氯化铝中的一种或混合物。
8.根据权利要求6所述一种耐低温性能好的止水带，其特征在于：所述分散剂为硬脂酸钙、蒙脱土和烷偶联剂中的一种。