CN108192514B - 一种热塑性弹性体止水带及其制备方法 - Google Patents
一种热塑性弹性体止水带及其制备方法 Download PDFInfo
- Publication number
- CN108192514B CN108192514B CN201711457702.2A CN201711457702A CN108192514B CN 108192514 B CN108192514 B CN 108192514B CN 201711457702 A CN201711457702 A CN 201711457702A CN 108192514 B CN108192514 B CN 108192514B
- Authority
- CN
- China
- Prior art keywords
- water stop
- parts
- styrene
- mixture
- adhesive layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种热塑性弹性体止水带及其制备方法，涉及止水带的技术领域。本发明的止水带包括止水带本体，止水带本体包括以下重量份的原料：聚丙烯30～50份，三元乙丙橡胶20～30份，线性低密度聚乙烯5～10份，超高分子量聚乙烯5～10份，苯乙烯‑异戊二烯共聚物5～15份，阻燃剂5～10份，填充剂10～20份，抗老化剂0.1～0.5份；本发明的止水带还可以带有自粘层，本发明还给出上述止水带的制备方法。本发明的止水带耐高低温，可以通过热风焊接对接，焊接强度高，止水效果好，不含增塑剂，使用寿命长，解决了金属止水带易生锈、橡胶止水带难焊接以及塑料止水带增塑剂迁移的问题，施工方便，全方位解决了水的渗漏问题。
Description
技术领域
本发明属于止水带的技术领域，特别是指一种热塑性弹性体止水带及其制备方法。
背景技术
在基建工程、地下设施和隧道等工程施工过程中，因混凝土收缩和膨胀等原因而引起变形导致混凝土结构产生一定的裂缝，严重时会造成渗水、漏水和窜水等事故。为避免这一事故的发生，通常会采取裂缝控制措施，例如：在混凝土浇筑过程中，在施工缝、接缝和变形缝内埋入止水带。
根据止水带的主要材质可将其分为金属止水带、橡胶止水带和塑料止水带。其中，金属止水带最大的缺点是容易生锈，后期难以处理；橡胶止水带主要使用三元乙丙橡胶(EPDM)，采用螺杆挤出、微波热空气硫化工艺，具有良好的弹性、耐磨性、耐老化性和抗撕裂性能，适应变形能力强，防水性能好，温度使用范围为-45℃～+60℃，但当温度超过70℃以及受强烈的氧化作用或受油类等有机溶剂侵蚀时，便不能使用橡胶止水带，橡胶止水带由于其自身特点决定其无法采用焊接的方法进行搭接边的对接；塑料止水带主要是指软质聚氯乙烯(PVC)止水带，具有较高的抗拉强度、伸长率、硬度较大，价格低，但塑料止水带易老化，耐低温性能差，当温度低至6℃，塑料止水带将变脆脆弱，承受接缝容易破裂，造成止水失效，同时，塑料止水带往往会加入大量增塑剂以增加止水带的弹性，因此，其在使用过程中会因增塑剂的迁移会导致止水带性能下降。
发明内容
本发明提供一种热塑性弹性体止水带及其制备方法，解决了现有技术中橡胶止水带无法焊接对接以及聚氯乙烯塑料止水带存在增塑剂迁移的问题。
本发明的一种热塑性弹性体止水带，其主要是通过以下技术方案加以实现的：包括止水带本体，所述止水带本体包括以下重量份的原料：
本发明的止水带本体由聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂组成，各组分相互作用，相互协同，充分发挥不同组分的增韧、增强以及抗老化作用，所得止水带本体具有韧性高、耐高低温、抗老化、可热风焊接、无增塑剂迁移止水效果好以及止水效果持久的优点；聚丙烯添加增强了止水带的拉伸强度，提高了止水带的刚性；三元乙丙橡胶和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的添加提高了止水带的柔软度，降低了止水带的压缩永久变形，有利于施工；线性低密度聚乙烯和超高分子量聚乙烯的添加提升了止水带的韧性和撕裂强度，增强了止水带的力学性能，延长了止水带的使用寿命，方便施工。
作为一种优选的实施方案，所述聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的熔融指数在190℃和2.16Kg条件下均为0.5～10g/10min。苯乙烯-异戊二烯-苯乙烯嵌段共聚物简称SIS，具有这种熔融指数的聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的混合使用，使止水带加工制备过程中容易混合均匀，得到的止水带产品质量更加均一，稳定性更好。
作为一种优选的实施方案，所述阻燃剂复配阻燃剂，所述复配阻燃剂为氢氧化镁和氢氧化铝按照重量比为2:1组成的混合物。阻燃剂的添加提高了止水带的阻燃性能，使其使用安全放心；复配阻燃剂提高了止水带的阻燃等级，提高了阻燃效果，这种复配的阻燃剂原料来源方便，价廉易得，阻燃效果好；并且，不含卤素，具有环保、无毒和无烟的优点。
作为一种优选的实施方案，所述填充剂为纳米碳酸钙、滑石粉和硅藻土按照重量比为1:1:1组成的混合物。硅藻土属于多孔性的填料，在一定程度上可以吸附纳米碳酸钙和滑石粉，起到均匀分散的作用，有利于止水带性能的提高；填充剂在止水带中起骨架结构的作用，增加止水带的强度和刚性，采用这三种填充剂组成的复合填充剂，其耐高温效果好，同时，还可以耐受低温，提高了止水带的综合性能。
作为一种优选的实施方案，所述抗老化剂为抗氧剂1010、抗氧剂1076和抗氧剂168按照重量比为2:0.5:0.5的混合物。抗老化剂的添加提高了止水带的抗老化性能和耐候性能，延长了止水带的使用寿命；本发明采用三种抗老化剂复合的形式，抗氧剂168是辅助抗氧剂，与主抗氧剂1010和主抗氧剂1076并用，起到协同作用，大大提高止水带的抗氧化性能，不仅增强了止水带的抗老化性能，而且，增强了止水带的止水性能。
作为一种优选的实施方案，所述止水带的单侧或双侧上设有自粘层。在止水带上增强自粘层，可以将止水带之间粘贴到混凝土上，使其施工更加便利，提高了其使用性能。
作为一种优选的实施方案，所述自粘层包括以下重量份的原料：
本发明的止水带还可以采用上述配方的自粘层，这种自粘层中苯乙烯-异戊二烯-苯乙烯嵌段共聚物、聚异丁烯、天然胶乳、萜烯树脂和环烷油相互作用，相互协同，相容性好，溶解性好，具有良好的粘结性能，不易脱落；这种配方的止水带中含有苯乙烯-异戊二烯-苯乙烯嵌段共聚物组分，与止水带中的这一组分相同，这样促进自粘层与止水带之间的融合，进一步提高自粘层与止水带之间的粘结力。
作为一种优选的实施方案，所述聚异丁烯为聚异丁烯混合物，所述聚异丁烯混合物为聚异丁烯1300和聚异丁烯2400按照重量比为1:2组成的混合物。聚异丁烯1300是指分子量为1300的聚异丁烯，也简称PIB1300；同样，聚异丁烯2400是指分子量为2400的聚异丁烯，也简称PIB2400；这两种聚异丁烯是高粘度的液体，加入以后可以增加自粘层的粘度，PIB2400和PIB1300相比，前者的自粘层强度较大，后者的初粘性更好，两者共混，可以平衡两种性能。
本发明的一种热塑性弹性体止水带的制备方法，其主要是通过以下技术方案加以实现的：包括以下步骤：
1)取聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂，混合均匀，得到混合料；
2)将步骤1)所得的混合料加入到双螺杆挤出机中，共混挤出，挤出机温度控制区段为8段，每区段温度设定范围均为180～200℃，机头温度为190～195℃，螺杆转速为200～400转/分，冷却定型，得止水带本体；
3)将步骤2)所得的止水带本体与自粘层复合，得具有自粘层的止水带。
本发明的止水带的制备方法简单，操作方便，对设备没有特殊要求，反应温度低，能耗少，成本低，环保，安全，易于实现产业化。本发明的止水带可以添加自粘层，也可以不添加自粘层，该自粘层可以是现有的粘结剂形成的自粘层，也可以是本发明的配方的粘结剂形成自粘层。自粘层上可以附上隔离纸，使用时，将隔离纸撕下之后，直接与混凝土进行粘结即可。
作为一种优选的实施方案，所述步骤3)中自粘层的制备方法为：取苯乙烯-异戊二烯-苯乙烯嵌段共聚物30～50份、聚异丁烯20～30份、天然胶乳20～30份、萜烯树脂5～10份和环烷油5～15份，加入双螺杆挤出机中，挤出机温度控制区段为5段，每区段温度设定范围均为170～190℃，机头温度为180～185℃，螺杆转速为100～300转/分，得自粘层。本发明的自粘层原料直接放入双螺杆挤出机进行共混挤出，工艺流程短，操作方便，提高了生产效率，所得止水带上自粘层的厚度一般在1mm左右，粘贴效果好，粘贴强度高，不易脱落，方便施工。
与现有技术相比，本发明的有益效果是：本发明的止水带本体由聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂组成，各组分相互作用，相互协同，充分发挥不同组分的增韧、增强以及抗老化作用，所得止水带本体具有韧性高、耐高低温、抗老化、可焊接、止水效果好以及止水效果持久的优点；聚丙烯添加增强了止水带的拉伸强度，提高了止水带的刚性；三元乙丙橡胶和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的添加提高了止水带的柔软度，降低了止水带的压缩永久变形，有利于施工；线性低密度聚乙烯和超高分子量聚乙烯的添加提升了止水带的韧性和撕裂强度，增强了止水带的力学性能，延长了止水带的使用寿命，方便施工；该止水带的单侧或双侧可以增设自粘层，从而得到具有自粘层的止水带，可以直接通过自粘层与混凝土粘结，具有良好的黏结性能；本发明的止水带制备方法简单，操作方便，对设备没有特殊要求，反应温度低，能耗少，成本低，易于实现产业化。
具体实施方式
下面将结合本发明的具体实施例对本发明的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
本发明的一种热塑性弹性体止水带，包括止水带本体，所述止水带本体包括以下重量份的原料：
优选地，所述聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的熔融指数在190℃和2.16Kg条件下均为0.5～10g/10min。
具体地，所述阻燃剂复配阻燃剂，所述复配阻燃剂为氢氧化镁和氢氧化铝按照重量比为2:1组成的混合物。
进一步地，所述填充剂为纳米碳酸钙、滑石粉和硅藻土按照重量比为1:1:1组成的混合物。
更优选地，所述抗老化剂为抗氧剂1010、抗氧剂1076和抗氧剂168按照重量比为2:0.5:0.5的混合物。
更进一步地，所述止水带的单侧或双侧上设有自粘层。
更具体地，所述自粘层包括以下重量份的原料：
再次优选地，所述聚异丁烯为聚异丁烯混合物，所述聚异丁烯混合物为聚异丁烯1300和聚异丁烯2400按照重量比为1:2组成的混合物。
本发明的一种热塑性弹性体止水带的制备方法，包括以下步骤：
1)取聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂，混合均匀，得到混合料；
2)将步骤1)所得的混合料加入到双螺杆挤出机中，共混挤出，挤出机温度控制区段为8段，每区段温度设定范围均为180～200℃，机头温度为190～195℃，螺杆转速为200～400转/分，冷却定型，得止水带本体；
3)将步骤2)所得的止水带本体与自粘层复合，得具有自粘层的止水带。
具体地，所述步骤3)中自粘层的制备方法为：取苯乙烯-异戊二烯-苯乙烯嵌段共聚物30～50份、聚异丁烯混合物20～30份、天然胶乳20～30份、萜烯树脂5～10份和环烷油5～15份，加入双螺杆挤出机中，挤出机温度控制区段为5段，每区段温度设定范围均为170～190℃，机头温度为180～185℃，螺杆转速为100～300转/分，得自粘层。
实施例一
本发明的一种热塑性弹性体止水带包括止水带本体，其制备方法包括以下步骤：
1)按照如下重量份称取止水带本体的原料：
2)将聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂，混合均匀，得到混合料；
3)将步骤2)所得的混合料加入到双螺杆挤出机中，共混挤出，挤出机温度控制区段为8段，每区段温度设定范围均为180～200℃，机头温度为190℃，螺杆转速为300转/分，冷却定型，得止水带本体。
实施例二
本发明的一种热塑性弹性体止水带包括止水带本体，其制备方法包括以下步骤：
1)按照如下重量份称取止水带本体的原料：
其中，聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的熔融指数在190℃和2.16Kg条件下分别为0.5、0.5、0.5、0.5、0.5g/10min，复配阻燃剂为氢氧化镁和氢氧化铝按照重量比为2:1组成的混合物，复合填充剂为纳米碳酸钙、滑石粉和硅藻土按照重量比为1:1:1组成的混合物，复合抗老化剂为抗氧剂1010、抗氧剂1076和抗氧剂168按照重量比为2:0.5:0.5的混合物；
2)将聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂，在高速捏合机中混配均匀，捏合机转速为800转/分，温度为60℃，混合时间为10分钟，然后，冷却至室温，得到混合料；
3)将步骤2)所得的混合料加入到双螺杆挤出机中，共混挤出，挤出机温度控制区段为8段，每区段温度设定范围均为180～200℃，机头温度为195℃，螺杆转速为200转/分，螺杆直径为35mm，长径比L/D为43，冷却定型，得止水带本体；
4)将步骤3)所得的止水带本体与自粘层复合，得具有自粘层的止水带。
实施例三
本发明的一种热塑性弹性体止水带包括止水带本体，其制备方法包括以下步骤：
1)按照如下重量份称取止水带本体的原料：
2)将聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂，在高速捏合机中混配均匀，捏合机转速为800转/分，温度为60℃，混合时间为9分钟，然后，冷却至室温，得到混合料；
3)将步骤2)所得的混合料加入到双螺杆挤出机中，共混挤出，挤出机温度控制区段为8段，每区段温度设定范围均为180～200℃，机头温度为192℃，螺杆转速为400转/分，螺杆直径为35mm，长径比L/D为43，冷却定型，得止水带本体；
4)按照如下重量份称取自粘层的原料：
5)取苯乙烯-异戊二烯-苯乙烯嵌段共聚物、聚异丁烯混合物、天然胶乳、萜烯树脂和环烷油，加入双螺杆挤出机中，挤出机温度控制区段为5段，每区段温度设定范围均为170～190℃，机头温度为180℃，螺杆转速为100转/分，螺杆直径为25mm，长径比L/D为43，得自粘层；
6)将步骤3)所得的止水带本体与步骤5)所得自粘层复合，得具有自粘层的止水带。
实施例四
本发明的一种热塑性弹性体止水带包括止水带本体，其制备方法包括以下步骤：
1)按照如下重量份称取止水带本体的原料：
其中，聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的熔融指数在190℃和2.16Kg条件下分别为5、2、4、6、4g/10min，复配阻燃剂为氢氧化镁和氢氧化铝按照重量比为2:1组成的混合物，复合填充剂为纳米碳酸钙、滑石粉和硅藻土按照重量比为1:1:1组成的混合物，复合抗老化剂为抗氧剂1010、抗氧剂1076和抗氧剂168按照重量比为2:0.5:0.5的混合物；
2)将聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂，在高速捏合机中混配均匀，捏合机转速为800转/分，温度为60℃，混合时间为8分钟，然后，冷却至室温，得到混合料；
3)将步骤2)所得的混合料加入到双螺杆挤出机中，共混挤出，挤出机温度控制区段为8段，每区段温度设定范围均为180～200℃，机头温度为193℃，螺杆转速为300转/分，螺杆直径为35mm，长径比L/D为43，经口模挤出的止水带本体经水槽，冷却定型，得止水带本体；
4)按照如下重量份称取自粘层的原料：
其中，聚异丁烯混合物为聚异丁烯1300和聚异丁烯2400按照重量比为1:2组成的混合物；
5)取苯乙烯-异戊二烯-苯乙烯嵌段共聚物、聚异丁烯混合物、天然胶乳、萜烯树脂和环烷油，加入双螺杆挤出机中，挤出机温度控制区段为5段，每区段温度设定范围均为170～190℃，机头温度为185℃，螺杆转速为200转/分，螺杆直径为25mm，长径比L/D为43，得自粘层；
6)将步骤3)所得的止水带本体经过风道吹干后，与步骤5)所得自粘层复合，自粘层厚度为1mm，然后，将自粘层覆以隔离纸进行包装，存放，得具有自粘层的止水带。
实施例五
本发明的一种热塑性弹性体止水带包括止水带本体，其制备方法包括以下步骤：
1)按照如下重量份称取止水带本体的原料：
其中，聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的熔融指数在190℃和2.16Kg条件下分别为10、10、10、10、10g/10min，复配阻燃剂为氢氧化镁和氢氧化铝按照重量比为2:1组成的混合物，复合填充剂为纳米碳酸钙、滑石粉和硅藻土按照重量比为1:1:1组成的混合物，复合抗老化剂为抗氧剂1010、抗氧剂1076和抗氧剂168按照重量比为2:0.5:0.5的混合物；
2)将聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂，在高速捏合机中混配均匀，捏合机转速为800转/分，温度为60℃，混合时间为10分钟，然后，冷却至室温，得到混合料；
3)将步骤2)所得的混合料加入到双螺杆挤出机中，共混挤出，挤出机温度控制区段为8段，每区段温度设定范围均为180～200℃，机头温度为195℃，螺杆转速为300转/分，螺杆直径为35mm，长径比L/D为43，经口模挤出的止水带本体经水槽，冷却定型，得止水带本体；
4)按照如下重量份称取自粘层的原料：
其中，聚异丁烯混合物为聚异丁烯1300和聚异丁烯2400按照重量比为1:2组成的混合物；
5)取苯乙烯-异戊二烯-苯乙烯嵌段共聚物、聚异丁烯混合物、天然胶乳、萜烯树脂和环烷油，加入双螺杆挤出机中，挤出机温度控制区段为5段，每区段温度设定范围为170～190℃，机头温度为183℃，螺杆转速为200转/分，螺杆直径为25mm，长径比L/D为43，得自粘层；
6)将步骤3)所得的止水带本体经过风道吹干后，与步骤5)所得自粘层复合，自粘层厚度为1mm，然后，将自粘层覆以隔离纸进行包装，存放，得具有自粘层的止水带。
将实施例一至实施例五所得的止水带中的止水带本体分别进行性能测试实验，实验参照国家标准GB18173.2-2014《高分子防水材料第2部分：止水带》中规定的方法进行，测试结果如表1所示。
表1不同止水带性能测试结果
由表1可以看出，本发明的方法制备的热塑性弹性体止水带均达到了国家标准GB18173.2-2014对止水带各项性能指标的要求，而且，本发明的止水带本体拉伸强度高，压缩永久变形小，撕裂强度大，脆性温度低，耐热空气老化，48h臭氧老化过程中均无裂纹出现；因此，本发明的止水带本体具有韧性高、耐高低温、抗老化、可焊接、止水效果好以及止水效果持久的优点。与目前市场上现有止水带相比，本发明制备的止水带不仅可以进行热风焊接，提高止水效果，而且，没有增塑剂的迁移问题，是一种环境友好型止水带。
与现有技术相比，本发明的有益效果是：本发明的止水带本体由聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂组成，各组分相互作用，相互协同，充分发挥不同组分的增韧、增强以及抗老化作用，所得止水带本体具有韧性高、耐高低温、抗老化、可焊接、止水效果好以及止水效果持久的优点；聚丙烯添加增强了止水带的拉伸强度，提高了止水带的刚性；三元乙丙橡胶和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的添加提高了止水带的柔软度，降低了止水带的压缩永久变形，有利于施工；线性低密度聚乙烯和超高分子量聚乙烯的添加提升了止水带的韧性和撕裂强度，增强了止水带的力学性能，延长了止水带的使用寿命，方便施工；该止水带的单侧或双侧可以增设自粘层，从而得到具有自粘层的止水带，可以直接通过自粘层与混凝土粘结，具有良好的黏结性能；本发明的止水带制备方法简单，操作方便，对设备没有特殊要求，反应温度低，能耗少，成本低，易于实现产业化。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (6)
1.一种热塑性弹性体止水带，其特征在于：包括止水带本体，所述止水带的单侧或双侧上设有自粘层，所述止水带本体包括以下重量份的原料：
聚丙烯 30~50份，
三元乙丙橡胶 20~30份，
线性低密度聚乙烯 5~10份，
超高分子量聚乙烯 5~10份，
苯乙烯-异戊二烯-苯乙烯嵌段共聚物 5~15份，
阻燃剂 5~10份，
填充剂 10~20份，
抗老化剂 0.1~0.5份；
所述阻燃剂为复配阻燃剂，所述复配阻燃剂为氢氧化镁和氢氧化铝按照重量比为2:1组成的混合物，所述填充剂为纳米碳酸钙、滑石粉和硅藻土按照重量比为1:1:1组成的混合物，所述抗老化剂为抗氧剂1010、抗氧剂1076和抗氧剂168按照重量比为2:0.5:0.5的混合物。
2.根据权利要求1所述的热塑性弹性体止水带，其特征在于：
所述聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯和苯乙烯-异戊二烯-苯乙烯嵌段共聚物的熔融指数在190℃和2.16Kg条件下均为0.5~10g/10min。
3.根据权利要求1或2所述的热塑性弹性体止水带，其特征在于：所述自粘层包括以下重量份的原料：
苯乙烯-异戊二烯-苯乙烯嵌段共聚物 30~50份，
聚异丁烯 20~30份，
天然胶乳 20~30份，
萜烯树脂 5~10份，
环烷油 5~15份。
4.根据权利要求3所述的热塑性弹性体止水带，其特征在于：
所述聚异丁烯为聚异丁烯混合物，所述聚异丁烯混合物为聚异丁烯1300和聚异丁烯2400按照重量比为1:2组成的混合物。
5.根据权利要求1~4中任意一项所述的热塑性弹性体止水带的制备方法，其特征在于，包括以下步骤：
1）取聚丙烯、三元乙丙橡胶、线性低密度聚乙烯、超高分子量聚乙烯、苯乙烯-异戊二烯-苯乙烯嵌段共聚物、阻燃剂、填充剂和抗老化剂，混合均匀，得到混合料；
2）将步骤1）所得的混合料加入到双螺杆挤出机中，共混挤出，挤出机温度控制区段为8段，每区段温度设定范围均为180~200℃，机头温度为190~195℃，螺杆转速为200~400转/分，冷却定型，得止水带本体；
3）将步骤2）所得的止水带本体与自粘层复合，得具有自粘层的止水带。
6.根据权利要求5所述的热塑性弹性体止水带的制备方法，其特征在于，所述步骤3）中自粘层的制备方法为：
取苯乙烯-异戊二烯-苯乙烯嵌段共聚物30~50份、聚异丁烯混合物20~30份、天然胶乳20~30份、萜烯树脂5~10份和环烷油5~15份，加入双螺杆挤出机中，挤出机温度控制区段为5段，每区段温度设定范围均为170~190℃，机头温度为180~185℃，螺杆转速为100~300转/分，得自粘层。