CN117841219A - 一种无纺布生产用高熔指亲水母粒加工工艺 - Google Patents
一种无纺布生产用高熔指亲水母粒加工工艺 Download PDFInfo
- Publication number
- CN117841219A CN117841219A CN202311508512.4A CN202311508512A CN117841219A CN 117841219 A CN117841219 A CN 117841219A CN 202311508512 A CN202311508512 A CN 202311508512A CN 117841219 A CN117841219 A CN 117841219A
- Authority
- CN
- China
- Prior art keywords
- raw materials
- master batch
- temperature
- zone
- melting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种无纺布生产用高熔指亲水母粒加工工艺，包括以下步骤：准备原材料以及加工设备，对各项原材料进行筛分、清洗和烘干，同时将各项原材料分区放置，通过称重设备对其称重，按照一定配比进行称重放置；将各项原材料按照份数比例加入混料锅内，然后开启混料锅，混料的时间3分钟，然后将混合物倒入密炼机当中密炼，待物料呈现团状后放料，然后加入硅藻土，再继续搅拌3min—5min，制得预混料；然后将混合料投入高低速搅拌机中搅拌后冷却，搅拌时间为30分钟，冷却时间为5‑10分钟。本发明制备出的母粒能够吸收原材料内部所含的水分，利于加工，降低能耗，提高了成品塑料的质量。
Description
技术领域
本发明涉及金属结构件制造技术领域，更具体的说，它涉及一种无纺布生产用高熔指亲水母粒加工工艺。
背景技术
世界资源永远是人类的一大热门话题，节约资源的口号以慢慢深入到人心，因此再生料的觉醒也是必然的，这样人们通过资源的回收利用，才能真正的做到环保节能。由于塑料的无法自然降解性，所以再生塑料更是环保节能的重点，并且价格便宜，根据不同的需要，只需要加工某个方面的属性，能够制造出对应的产品即可，这样不会让资源流失，脱水母粒是用来在塑料加工成型过程中，解决塑料中的水分，使用脱水母粒，不用对塑料进行烘干。现有的脱水母粒流动性差，且分散性差，而且在流延膜生产中容易产生晶点，且容易在塑料加工中发生堵网的情况，此外，丙纶亲水母粒是一种高吸水树脂与聚丙烯树脂及其它亲水材料进行相容改性而成的母粒，母粒生产的亲水无纺布是一种替代后整理亲水无纺布理想产品。传统的亲水母粒浓度普遍较低，见效较慢。因此有待提出一种浓度高、亲水效果好、见效快的母粒及工艺。
发明内容
(一)解决的技术问题
针对现有技术中存在的问题，本发明提供了一种无纺布生产用高熔指亲水母粒加工工艺，以解决背景技术中提到的技术问题。
(二)技术方案
为实现上述目的，本发明提供如下技术方案：一种无纺布生产用高熔指亲水母粒加工工艺，包括以下步骤：
步骤一：准备原材料以及加工设备，对各项原材料进行筛分、清洗和烘干，同时将各项原材料分区放置，通过称重设备对其称重，按照一定配比进行称重放置；
步骤二：将各项原材料按照份数比例加入混料锅内，然后开启混料锅，混料的时间3分钟，然后将混合物倒入密炼机当中密炼，待物料呈现团状后放料；
步骤三：将步骤二中中加入硅藻土，再继续搅拌3min—5min，制得预混料；
步骤四：将步骤三中的混合料投入高低速搅拌机中搅拌后冷却，搅拌时间为30分钟，冷却时间为5-10分钟，冷却温度为20摄氏度；
步骤五：将步骤四中制得的预混料喂入双螺杆挤出机中，再经挤出、水冷、切粒及干燥，即制得吸水母粒。
本发明进一步设置为，所述原材料包括基体树脂、抗氧剂1010、抗氧剂168、分散剂、硬酯酸盐、润滑剂和弹性体聚丙烯。
本发明进一步设置为，所述的分散剂为硬脂酸单甘油酯或乙撑基双硬脂酰胺。
本发明进一步设置为，所述粉体载体为硅灰石、滑石粉、碳酸钙、碳酸钙晶须、高岭土、蒙脱土、重晶石、云母中的一种或两种以上的混合物。
本发明进一步设置为，所述步骤二中的密炼机密炼容积为50-250L，密炼时间为15-30分钟，密炼机设定温度180-290℃。
本发明进一步设置为，所述双螺杆挤出机有十二个区，一区温度为0℃，二区温度为50℃，三区温度为80℃，四区温度为120℃，五区温度为160℃，六区温度为175℃，七区温度为175℃八区温度为170℃，九区温度为160℃，十区温度为155℃，十一区温度为155℃，十二区温度为150℃。
本发明进一步设置为，所述润滑剂为PE蜡、EVA蜡、硬脂酸钙、亚乙基二硬脂酸胺中的一种或两种以上的混合物。
本发明进一步设置为，所述抗氧剂为抗氧剂1010、抗氧剂168或硫代二丙酸双十八醇酯中的一种或两种以上的混合物。
(三)有益效果
与现有技术相比，本发明提供了一种无纺布生产用高熔指亲水母粒加工工艺，具备以下有益效果：
本发明生成的母粒为高浓度的亲水母粒，一般亲水母粒在无纺布制品生产时亲水剂添加量在2-4％的情况下需要3-7天甚至更长的时间才会具有亲水效果，该配方工艺生产的母粒同等的添加量能把亲水效果提前至1-3天左右，此外，本发明制备出的母粒能够吸收原材料内部所含的水分，利于加工，降低能耗，提高了成品塑料的质量，另外，亲水母粒中添加了较多量的抗氧剂，因此兼具有老化母粒的作用，能减少因回料的再次重复性使用而导致的氧化裂解等问题，从而减少了刺激性气味的产生。
附图说明
图1为本发明中的整体流程图。
具体实施方式
需要说明的是，在不冲突的情况下，本申请中的实施例及实施例中的特征可以相互结合。下面将参考附图并结合实施例来详细说明本发明。
需要指出的是，除非另有指明，本申请使用的所有技术和科学术语具有与本申请所属技术领域的普通技术人员通常理解的相同含义。
本发明中，在未作相反说明的情况下，使用的方位如“上、下”通常是针对附图所示的方向而言，或者是针对竖直、垂直或重力方向上而言的；同样地，为便于理解和描述，“左、右”通常是针对附图所示的左、右；“内、外”是指相对于各部件本身的轮廓的内、外，但上述方位词并不用于限制本发明。
实施例1：
请参阅图1，一种无纺布生产用高熔指亲水母粒加工工艺，包括以下步骤：
步骤一：准备原材料以及加工设备，对各项原材料进行筛分、清洗和烘干，同时将各项原材料分区放置，通过称重设备对其称重，按照一定配比进行称重放置，原材料包括基体树脂30-50份、抗氧剂1010 5-10份、抗氧剂168 5-10、分散剂10-20份、硬酯酸盐10-20份、润滑剂10-20份和弹性体聚丙烯10-20份；
步骤二：将各项原材料按照份数比例基体树脂30份、抗氧剂1010 5份、抗氧剂1685、分散剂10份、硬酯酸盐20份、润滑剂20份和弹性体聚丙烯20份加入混料锅内，然后开启混料锅，混料的时间3分钟，然后将混合物倒入密炼机当中密炼，待物料呈现团状后放料；
步骤三：将步骤二中中加入硅藻土，再继续搅拌3min，制得预混料；
步骤四：将步骤三中的混合料投入高低速搅拌机中搅拌后冷却，搅拌时间为30分钟，冷却时间为5分钟，冷却温度为20摄氏度；
步骤五：将步骤四中制得的预混料喂入双螺杆挤出机中，再经挤出、水冷、切粒及干燥，即制得吸水母粒。
双螺杆挤出机有十二个区，一区温度为0℃，二区温度为50℃，三区温度为80℃，四区温度为120℃，五区温度为160℃，六区温度为175℃，七区温度为175℃八区温度为170℃，九区温度为160℃，十区温度为155℃，十一区温度为155℃，十二区温度为150℃
实施例2：
一种无纺布生产用高熔指亲水母粒加工工艺，包括以下步骤：
步骤一：准备原材料以及加工设备，对各项原材料进行筛分、清洗和烘干，同时将各项原材料分区放置，通过称重设备对其称重，按照一定配比进行称重放置，原材料包括基体树脂30-50份、抗氧剂1010 5-10份、抗氧剂168 5-10、分散剂10-20份、硬酯酸盐10-20份、润滑剂10-20份和弹性体聚丙烯10-20份；
步骤二：将各项原材料按照份数比例基体树脂50份、抗氧剂1010 5份、抗氧剂1685、分散剂10份、硬酯酸盐12份、润滑剂12份和弹性体聚丙烯16份加入混料锅内，然后开启混料锅，混料的时间3分钟，然后将混合物倒入密炼机当中密炼，待物料呈现团状后放料；
步骤三：将步骤二中中加入硅藻土，再继续搅拌6min，制得预混料；
步骤四：将步骤三中的混合料投入高低速搅拌机中搅拌后冷却，搅拌时间为30分钟，冷却时间为5分钟，冷却温度为20摄氏度；
步骤五：将步骤四中制得的预混料喂入双螺杆挤出机中，再经挤出、水冷、切粒及干燥，即制得吸水母粒。
在本发明进一步的实施例中，所述原材料包括基体树脂、抗氧剂1010、抗氧剂168、分散剂、硬酯酸盐、润滑剂和弹性体聚丙烯。
在本发明进一步的实施例中，所述的分散剂为硬脂酸单甘油酯或乙撑基双硬脂酰胺。
在本发明进一步的实施例中，所述粉体载体为硅灰石、滑石粉、碳酸钙、碳酸钙晶须、高岭土、蒙脱土、重晶石、云母中的一种或两种以上的混合物。
在本发明进一步的实施例中，所述步骤二中的密炼机密炼容积为50-250L，密炼时间为15-30分钟，密炼机设定温度180-290℃。
在本发明进一步的实施例中，所述润滑剂为PE蜡、EVA蜡、硬脂酸钙、亚乙基二硬脂酸胺中的一种或两种以上的混合物。
在本发明进一步的实施例中，所述抗氧剂为抗氧剂1010、抗氧剂168或硫代二丙酸双十八醇酯中的一种或两种以上的混合物。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (8)
1.一种无纺布生产用高熔指亲水母粒加工工艺，其特征在于，包括以下步骤：
步骤一：准备原材料以及加工设备，对各项原材料进行筛分、清洗和烘干，同时将各项原材料分区放置，通过称重设备对其称重，按照一定配比进行称重放置；
步骤二：将各项原材料按照份数比例加入混料锅内，然后开启混料锅，混料的时间3分钟，然后将混合物倒入密炼机当中密炼，待物料呈现团状后放料；
步骤三：将步骤二中中加入硅藻土，再继续搅拌3min—5min，制得预混料；
步骤四：将步骤三中的混合料投入高低速搅拌机中搅拌后冷却，搅拌时间为30分钟，冷却时间为5-10分钟，冷却温度为20摄氏度；
步骤五：将步骤四中制得的预混料喂入双螺杆挤出机中，再经挤出、水冷、切粒及干燥，即制得吸水母粒。
2.根据权利要求1所述的一种无纺布生产用高熔指亲水母粒加工工艺，其特征是：所述原材料包括基体树脂、抗氧剂1010、抗氧剂168、分散剂、硬酯酸盐、润滑剂和弹性体聚丙烯。
3.根据权利要求1所述的一种无纺布生产用高熔指亲水母粒加工工艺，其特征是：所述的分散剂为硬脂酸单甘油酯或乙撑基双硬脂酰胺。
4.根据权利要求1所述的一种无纺布生产用高熔指亲水母粒加工工艺，其特征是：所述粉体载体为硅灰石、滑石粉、碳酸钙、碳酸钙晶须、高岭土、蒙脱土、重晶石、云母中的一种或两种以上的混合物。
5.根据权利要求1所述的一种无纺布生产用高熔指亲水母粒加工工艺，其特征是：所述步骤二中的密炼机密炼容积为50-250L，密炼时间为15-30分钟，密炼机设定温度180-290℃。
6.根据权利要求2所述的一种无纺布生产用高熔指亲水母粒加工工艺，其特征是：所述双螺杆挤出机有十二个区，一区温度为0℃，二区温度为50℃，三区温度为80℃，四区温度为120℃，五区温度为160℃，六区温度为175℃，七区温度为175℃八区温度为170℃，九区温度为160℃，十区温度为155℃，十一区温度为155℃，十二区温度为150℃。
7.根据权利要求2所述的一种无纺布生产用高熔指亲水母粒加工工艺，其特征是：所述润滑剂为PE蜡、EVA蜡、硬脂酸钙、亚乙基二硬脂酸胺中的一种或两种以上的混合物。
8.根据权利要求1所述的一种无纺布生产用高熔指亲水母粒加工工艺，其特征是：所述抗氧剂为抗氧剂1010、抗氧剂168或硫代二丙酸双十八醇酯中的一种或两种以上的混合物。