CN117625321A - 一种防腐蚀清洗剂及其制备方法 - Google Patents
一种防腐蚀清洗剂及其制备方法 Download PDFInfo
- Publication number
- CN117625321A CN117625321A CN202311578850.5A CN202311578850A CN117625321A CN 117625321 A CN117625321 A CN 117625321A CN 202311578850 A CN202311578850 A CN 202311578850A CN 117625321 A CN117625321 A CN 117625321A
- Authority
- CN
- China
- Prior art keywords
- acid
- percent
- cleaning agent
- catalyst
- anticorrosive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种防腐蚀清洗剂及其制备方法，属于日用化工用品技术领域，由以下质量百分比原料组成：酸性改性纤维溶液30.0％～40.0％；催化剂0.2％～0.5％；保护剂：2.0％～5.0％；助洗剂5.0％～8.0％；其余为去离子水，所述的酸性改性纤维溶液由植物纤维经改性用酸酸化改性而制成，所述的催化剂为果酸钙和碱金属或碱土金属的卤化物，按质量百分比1:1比例配制，所述的植物纤维为原棉、落棉、头道绒等，所述的改性用酸是由正磷酸和辅助酸复配使用，主要应用于硬物表面清洗。
Description
技术领域
本发明属于日用化工用品技术领域，具体涉及一种防腐蚀清洗剂及制备方法。
背景技术
瓷面清洗剂是现代家庭卫生间必备的清洁用品，其特点是专门为卫生间内顽固污垢而设计的，能够迅速有效的分解卫生间内墙壁的磁瓦、洗手盆和厕盆表面的顽固污垢，无需费力擦洗，光亮且不损伤陶瓷的表面，对金属基本无腐蚀性。
市面上洁厕液大多由无机酸组成，使用时异味比较重，对人体刺激性较大，对瓷面、水泥和金属的腐蚀性都比较大。
申请人有着多年关于清洁剂领域的研发经验，通过不断地实验和改进配方，终于研究出一款更贴合人们生活的新清洁剂，主要应用于瓷面清洁方面。
发明内容
本发明的目的是提供一种新发明思路，克服现有技术中所存在的缺陷。将植物纤维在催化剂的作用下，在一定温度下通过酸性改性，形成纤细的酸性纤维，均匀的分布在清洗剂中，利用酸性改性纤维的易吸附、毛细渗透、溶胀等作用辅以其它助洗剂快速去除瓷面的顽固污垢，对瓷面、水泥和金属无损伤，无异味。给使用者提供一种安全有效地全新使用体验。
一种防腐蚀清洗剂，其特征在于，由以下质量百分比原料组成：酸性改性纤维溶液30.0％～40.0％；催化剂0.2％～0.5％；保护剂：2.0％～5.0％；助洗剂5.0％～8.0％；其余为去离子水。
酸性改性纤维是由植物纤维经酸化改性而制成，其中植物纤维可以是原棉、落棉、头道绒和麻等纤维质。
改性用酸是由正磷酸和辅助酸复配使用，其中辅助酸可以为乙醇酸，乙二酸、乳酸等液体有机酸二种或几种复配。改性用酸不能用无机强酸，会使植物纤维碳化，失去效能，只能用中等强度的酸，经过多次试验得出磷酸效果最好。辅助用酸采用有机酸复配而成，可以增强酸化纤维在液体中的分散度。
植物纤维：6.0％～8.0％，改性用酸：正磷酸(含量≧85％)：6.0％～8.0％、辅助酸：12.0％～14.0％，其余为去离子水。
催化剂为果酸钙和碱金属或碱土金属的卤化物，按质量百分比1:1比例配制，在植物纤维酸化过程中，可以有效的帮助植物纤维纤细化并分散开。
保护剂是柠檬酸、苹果酸、氨基磺酸、酒石酸等有机酸中的一种或几种和双氧水溶于酒精制备而成，具体按质量百分比比例配制：有机酸:双氧水:酒精＝2:1:7。可以提供鳌和离子和缓冲酸性的效果，降低腐蚀，提高清洗后瓷面的亮度。
酸性改性纤维的制备方法，将按配比称量好的正磷酸加入反应罐中，再加入尽量撕碎开的植物纤维，使植物纤维充分浸泡润湿，升温至80～90℃保温30min，加入余下的1/3热去离子水、催化剂，保温80～90℃搅拌60～90min，再加入辅助酸和其余的去离子水，搅拌冷却至室温。
助洗剂为表面活性剂、增稠剂和香精防腐剂的混合物。
具体制备方法，按配比将称好的各组分，按序将去离子水、酸性改性纤维溶液、保护剂、助洗剂加入搅拌罐，室温搅拌30min，搅拌均匀即可。制得的成品PH值：4-5。
本发明具有以下有益效果：
本发明的防腐蚀清洗剂，利用酸性改性纤维的特性，渗透进污垢与瓷面接触界面，产生溶胀作用，使得污垢尤其是固体污垢产生松动分散，与瓷面分离，可以轻易地用水冲洗干净。与市面上的酸性洁厕液，作用机理完全不同，在快速去除污垢后，不再侵蚀基体，对瓷面、水泥和金属基本无损伤，且不产生异味。
具体实施方式
为了充分说明本发明的特性以及实施本发明的方式，下面给出实施例。
实施例1
一种防腐蚀清洗剂，由以下质量百分比的原料组成：酸性改性纤维溶液30.0％，催化剂0.2％；保护剂5.0％；助洗剂8.0％；其余为去离子水。
制备方法如下：
步骤a：酸性改性纤维溶液的制备方法，将正磷酸加入反应罐中，再加入撕碎开的植物纤维，使植物纤维充分浸泡润湿，升温至80～90℃保温30min，加入其余的1/3热去离子水、催化剂，保温80～90℃搅拌60～90min。再加入辅助酸和其余的去离子水，搅拌冷却至室温备用。
步骤b：催化剂的制备方法，果酸钙和碱金属或碱土金属的卤化物，按质量百分比1:1比例配制。
步骤c：保护剂的制备方法，将柠檬酸、苹果酸、氨基磺酸、酒石酸等有机酸中的一种或几种和双氧水溶于酒精中搅拌均匀。具体按质量百分比比例配制：有机酸:双氧水:酒精＝2:1:7。备用。
步骤d：助洗剂的制备方法，助洗剂为表面活性剂、增稠剂和香精防腐剂的混合物。
步骤e：将按配比称好的各组分，按序将去离子水、酸性改性纤维溶液、保护剂、助洗剂加入搅拌罐，室温搅拌30min，搅拌均匀即可。
实施例2
一种防腐蚀清洗剂，由以下质量百分比的原料组成：酸性改性纤维溶液33.0％，催化剂0.3％；保护剂6.0％；助洗剂7.0％；其余为去离子水。
制备方法：与实施例1相同。
实施例3
一种防腐蚀清洗剂，由以下质量百分比的原料组成：酸性改性纤维溶液35.0％，催化剂0.3％；保护剂6.0％；助洗剂5.0％；其余为去离子水。
制备方法：与实施例1相同。
实施例4
一种防腐蚀清洗剂，由以下质量百分比的原料组成：酸性改性纤维溶液38.0％，催化剂0.4％；保护剂7.0％；助洗剂7.0％；其余为去离子水。
制备方法：与实施例1相同。
实施例5
一种防腐蚀清洗剂，由以下质量百分比的原料组成：酸性改性纤维溶液40.0％，催化剂0.5％；保护剂8.0％；助洗剂8.0％；其余为去离子水。
制备方法：与实施例1相同。
金属腐蚀性测试
参照GB/T3810.13陶瓷砖试验方法中8.1测定实施例样品对瓷砖的腐蚀性，参照QB/T 2117通用水基金属净洗剂中测试实施例和对比例样品对金属的腐蚀性，测试结果如表1所示。
表1腐蚀性测试结果
从表1的数据可以看出，与市面上采购样品中性瓷面清洗剂对比例1和强酸性瓷面清洗剂对比例2相比本发明的瓷面清洁剂对瓷砖和金属均无腐蚀性。
去垢力测试方法
参照HG/T5533水垢酸性清洗剂中3.4、3.5测试实施例和对比例样品对碳酸盐型水垢的溶垢率和溶垢量进行测试，测试结果如表2所示。
从测试结果可以看出，与市面上采购样品中性瓷面清洗剂对比例1和强酸性瓷面清洗剂对比例2相比，本发明的清洁剂具有较高的溶垢率及溶垢量，在PH值4～5的条件中具有良好的去垢效果。
本发明包括但不限于以下实施例，凡是在本发明精神的原则之下进行的任何等同替换或局部改进，都将视为在本发明的保护范围之内。
Claims (9)
1.一种防腐蚀清洗剂，其特征在于，由以下质量百分比原料组成：酸性改性纤维溶液30.0％～40.0％；催化剂0.2％～0.5％；保护剂：2.0％～5.0％；助洗剂5.0％～8.0％；其余为去离子水。
2.根据权利要求1所述的一种防腐蚀清洗剂，其特征在于，所述的酸性改性纤维溶液由植物纤维经改性用酸酸化改性而制成。
3.根据权利要求1所述的一种防腐蚀清洗剂，其特征在于，所述的催化剂为果酸钙和碱金属或碱土金属的卤化物，按质量百分比1:1比例配制。
4.根据权利要求2所述的一种防腐蚀清洗剂，其特征在于，所述的植物纤维为原棉、落棉、头道绒等。
5.根据权利要求2所述的一种防腐蚀清洗剂，其特征在于，所述的改性用酸是由正磷酸和辅助酸复配使用。
6.根据权利要求1所述的一种防腐蚀清洗剂，其特征在于，所述的保护剂是有机酸中的一种或几种和双氧水溶于酒精制备而成，具体按质量百分比比例配制：有机酸:双氧水:酒精＝2:1:7。
7.根据权利要求5所述的一种防腐蚀清洗剂，其特征在于，所述的辅助酸为乙醇酸，乙二酸、乳酸等液体有机酸二种或几种。
8.根据权利要求5所述的一种防腐蚀清洗剂，其特征在于，所述的酸性改性纤维溶液组成质量百分比为：植物纤维：6.0％～8.0％；正磷酸(含量≧85％)6.0％～8.0％；辅助酸12.0％～14.0％，其余为无离子水。
9.根据权利要求1-9任一项所述的一种防腐蚀清洗剂的制备方法，其特征在于，包括以下步骤：
步骤a：酸性改性纤维溶液的制备方法，将正磷酸加入反应罐中，再加入撕碎开的植物纤维，使植物纤维充分浸泡润湿，升温至80～90℃保温30min，加入其余的1/3热去离子水、催化剂，保温80～90℃搅拌60～90min，再加入辅助酸和其余的水，搅拌冷却至室温备用。
步骤b：催化剂的制备方法，果酸钙和碱金属或碱土金属的卤化物，按质量百分比1:1比例配制；
步骤c：保护剂的制备方法，将柠檬酸、苹果酸、氨基磺酸、酒石酸等有机酸中的一种或几种和双氧水溶于酒精中搅拌均匀，具体按质量百分比比例为：有机酸:双氧水:酒精＝2:1:7。备用；
步骤d：助洗剂的制备方法，助洗剂为表面活性剂、增稠剂和香精防腐剂的混合物；
步骤e：将按配比称好的各组分，按序将无离子水、酸性改性纤维溶液、保护剂、助洗剂加入搅拌罐，室温搅拌30min，搅拌均匀即可，制得的成品PH值：4～5。