CN117468243A - 一种保温隔热成品艺术漆及其制备方法和应用 - Google Patents
一种保温隔热成品艺术漆及其制备方法和应用 Download PDFInfo
- Publication number
- CN117468243A CN117468243A CN202311437220.6A CN202311437220A CN117468243A CN 117468243 A CN117468243 A CN 117468243A CN 202311437220 A CN202311437220 A CN 202311437220A CN 117468243 A CN117468243 A CN 117468243A
- Authority
- CN
- China
- Prior art keywords
- parts
- layer
- heat
- paint
- artistic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种保温隔热成品艺术漆及其制备方法,所述保温隔热成品艺术漆包括依次层叠设置的保温隔热层、无纺布层、防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层。本发明中提供的保温隔热成品艺术漆具有保温、隔热、抗开裂、防水、防污、可擦洗效果和耐候性优异的特点;同时还具有优异的附着性和阻燃性,所述保温隔热成品艺术漆在使用时可以有效降低人工操作的出错率,提高施工效率。
Description
技术领域
本发明属于艺术漆技术领域,具体涉及一种保温隔热成品艺术漆及其制备方法和应用。
背景技术
艺术漆是集多种墙面装饰工艺于一体的墙面装饰材料,具有耐老化、抗潮湿、耐擦洗、防水、防尘、防燃等功能。从美观度上来看,艺术漆具有色彩丰富,质感高级,可以搭配多种家居风格,且长久保色,历久弥新。但是,由于艺术漆对现场施工的专业性要求较高,因专业施工人员手艺水平不同,相同设计图纸的展现图案效果差异较大;还对墙面平整度要求极高及存在后期容易开裂、起皮等诸多问题;另外,施工面积大往往需要花费更多的施工时间及施工费用,此外还会产生更多的专业施工人员施工费,因此现场施工的艺术漆花费时间成本及费用成本较高,普通消费者较难承受。
CN112980263A公开了一种艺术漆墙布及其制备方法,所述艺术漆墙布包括:基材层;复合于所述基材层表面的加强层;复合于所述加强层表面的艺术漆层;复合于所述艺术漆层表面的图案层;复合于所述图案层表面的纹理层;复合于所述纹理层表面的防水保护层;其中,所述艺术漆层由包括以下质量份组分的艺术浆料形成:水性丙烯酸乳液15-50份;水6-9份;纳米云母粉3-10份;纳米二氧化钛1-10份;碳酸钙12-18份;短切纤维丝0.2-0.5份;甲氧基硅烷0.5-1份;成膜助剂0.5-0.7份;非离子表面活性剂0.5-1.5份;分散剂0.2-0.5份;光泽增强剂0-1份。该技术方案提供的艺术漆墙布具有艺术漆效果,相比于涂漆方式能够降低成本,而且本发明提供的艺术漆墙布具有优异的耐刮性、附着性及耐曲折性。
此外,现有技术中用于装饰的艺术漆缺少保温结构,使得艺术漆在上墙后,屋内或屋外的温度很容易通过墙布或艺术漆进行传递,保暖效果较差。
因此,针对上述技术问题,需要开发一种具有优异的保温、隔热、抗开裂、防水和防污的特点,且施工效率高、出错率低、成本低、装饰效果好的艺术漆。
发明内容
针对现有技术的不足,本发明的目的在于提供一种保温隔热成品艺术漆及其制备方法和应用。本发明中通过保温隔热层、无纺布层、防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层设置,制备得到的保温隔热成品艺术漆具有优异的保温、隔热、抗开裂、防水、防污、可擦洗效果和耐候性的特点,且施工效率高、出错率低、成本低、装饰效果好。
为达到此发明目的,本发明采用以下技术方案:
第一方面,本发明提供一种保温隔热成品艺术漆,所述保温隔热成品艺术漆包括依次层叠设置的保温隔热层、无纺布层、防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层。
本发明中,所述保温隔热成品艺术漆包括依次设置的保温隔热层、无纺布层、防护层、艺术漆基础层、艺术色彩层、艺术漆纹理层和疏水保护层,本发明通过将艺术漆制备成成品,使用时在墙面涂胶液,然后将所述保温隔热成品艺术漆直接贴在墙上即可,施工效率高;所述保温隔热成品艺术漆底面设置保温隔热层,能有效起到保温隔热作用;再设置无纺布层,无纺布层具防开裂作用,能有效防止墙体细微开裂导致的表面艺术漆开裂;再设置防护层,提高耐酸碱性和成型性;再设置艺术漆基础层,增强艺术漆的硬度,达到一定的耐磕碰性;再依次设置艺术漆色彩层和艺术漆纹理层,使得保温隔热成品艺术漆具有优异的装饰性;最后设置疏水保护层,疏水保护层的材料,具有优异的疏水性,设置在所述保温隔热成品艺术漆远离墙面的最外侧,能使保温隔热成品艺术漆具有优异的防水性、防污性和可擦洗性。
优选地,所述保温隔热层的制备原料包括水性树脂、气凝胶、隔热填料、助剂和水。
优选地,所述保温隔热层的制备原料包括按重量份数计的如下组分水性树脂30-45份(例如32份、32份、34份、36份、38份、40份、41份、42份或44份等)、气凝胶5-10份(例如5.5份、6份、6.5份、7份、7.5份、8份、8.5份、9份或9.5份等)、隔热填料3-5份(例如3.2份、3.4份、3.6份、3.8份、4份、4.2份、4.4份、4.6份或4.8份等)、助剂2-5份(例如2.5份、2.8份、3份、3.2份、3.5份、4份、4.2份、4.5份或4.8份等)和水30-42份(例如32份、33份、34份、35份、36份、37份、38份、39份、40份或41份等)。
本发明中,所述气凝胶的重量份数为5-10份,若气凝胶的质量份数过小,则保温隔热效果下降,若气凝胶的质量份数过大,则保温隔热层易开裂保温隔热效果下降。
优选地,所述水性树脂包括水性丙烯酸树脂。
优选地,所述气凝胶包括二氧化硅气凝胶。
优选地,所述隔热填料包括空心玻璃微珠。
优选地,所述助剂包括十二碳醇酯。
优选地,所述无纺布层包括水刺无纺布。
本发明中,所述水刺无纺布具有吸水性低、不易变型且手撕不坏的优势,能解决现有艺术漆开裂的问题,且具有多种规格,进而在实际使用时能确保一整面墙采用一整块无纺布,不需要拼接,并能遮盖墙面细微裂纹。
优选地,所述防护层的制备原料包括纳米活性炭。
本发明中,所述纳米活性炭是一种新型功能性纤维吸附材料,具有优异的吸附作用,且成型性好,耐酸碱性好,电导性与化学稳定性好等特点,其不仅比表面积大、孔径适中、分布均匀、吸附速度快,而且还具有不同的形态;本发明将防护层设置在无纺布层和艺术漆基础层之间,有效提高了保温隔热成品艺术漆的环保性、耐酸碱性和成型性。
优选地,所述艺术漆基础层和艺术漆纹理层的制备原料各自独立地包括按重量份数计的如下组分:水性丙烯酸乳液10-25份(例如11份、13份、15份、17份、20份、22份、23份或24份等)、聚四氟乙烯乳液5-10份(例如5.5份、6份、6.5份、7份、7.5份、8份、8.5份、9份或9.5份等)、贝壳粉5-20份(例如6份、8份、10份、12份、14份、16份或18份等)、水5-10份(例如5.5份、6份、6.5份、7份、7.5份、8份、8.5份、9份或9.5份等)、任选地钛白粉5-10份(例如5.5份、6份、6.5份、7份、7.5份、8份、8.5份、9份或9.5份等)、任选地高岭土5-15份(例如6份、7份、8份、9份、10份、11份、12份、13份或14份等)和任选地滑石粉5-10份(例如5.5份、6份、6.5份、7份、7.5份、8份、8.5份、9份或9.5份等)。
本发明中,所述艺术漆基础层和艺术漆纹理层的制备原料中添加了贝壳粉的能增加保温隔热成品艺术漆的硬度,加大耐磕碰性能。
优选地,所述艺术漆色彩层的制备原料包括按重量份数计的如下组分:水性丙烯酸乳液40-55份(例如42份、44份、46份、48份、50份、52份或54份等)、聚四氟乙烯乳液15-25份(例如16份、17份、18份、19份、20份、21份、22份、23份或24份等)、钛白粉5-10份(例如5.5份、6份、6.5份、7份、7.5份、8份、8.5份、9份或9.5份等)、高岭土5-15份(例如6份、7份、8份、9份、10份、11份、12份、13份或14份等)和水性色浆1-3份(例如1.2份、1.4份、1.6份、18份、2份、2.2份、2.4份、2.6份或2.8份等)。
本发明中,所述艺术漆色彩层通过采用水性色浆融入浆料式喷涂,非表层喷涂颜色,色泽更饱满、耐掉色、耐退色。
需要说明的是,在本发明对水性色浆的颜色选择不做特殊限制,本领域技术人员可根据实际情况进行调整。
优选地,所述保温隔热层的厚度为0.5-0.8mm,例如0.55mm、0.58mm、0.6mm、0.62mm、0.65mm、0.68mm、0.7mm、0.62mm、0.75mm或0.78mm等。
本发明中,所述保温隔热层的厚度为0.5-0.8mm,若保温隔热层的厚度过大,则制得的保温隔热成品艺术漆过厚,将不易将其平整牢固的粘贴在墙面上,影响施工效果;若厚度过小,则保温隔热的效果下降。
优选地,所述无纺布层的厚度为0.05-1mm,例如0.1mm、0.2mm、0.3mm、0.4mm、0.5mm、0.6mm、0.7mm、0.8mm或0.9mm等。
优选地,所述防护层的厚度为0.05-0.5mm,例如0.08mm、0.1mm、0.15mm、0.2mm、0.25mm、0.3mm、0.35mm、0.4mm或0.45mm等。
优选地,所述艺术漆基础层的厚度为0.1-0.5mm,例如0.15mm、0.2mm、0.25mm、0.3mm、0.35mm、0.4mm或0.45mm等。
优选地,所述艺术漆色彩层的厚度为0.1-1mm,例如0.2mm、0.3mm、0.4mm、0.5mm、0.6mm、0.7mm、0.8mm或0.9mm等。
优选地,所述艺术漆纹理层的厚度为0.1-1mm,例如0.2mm、0.3mm、0.4mm、0.5mm、0.6mm、0.7mm、0.8mm或0.9mm等。
优选地,所述疏水保护层的厚度为0.01-0.5mm,例如0.1mm、0.15mm、0.2mm、0.25mm、0.3mm、0.35mm、0.4mm或0.45mm等。
第二方面,本发明提供一种如第一方面所述的保温隔热成品艺术漆的制备方法,所述制备方法包括如下步骤:在无纺布层一侧复合保温隔热层,在无纺布层另一侧依次复合防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层,得到所述保温隔热成品艺术漆。
优选地,所述制备方法具体包括如下步骤:在无纺布层一侧刮涂保温隔热层的制备原料,干燥形成保温隔热层,冷却,在无纺布层另一侧喷涂防护层的制备原料,干燥,冷却,再喷涂艺术漆基础层的制备原料,干燥,冷却,喷涂艺术漆色彩层的制备原料,干燥,冷却,喷涂压花艺术漆纹理层的制备原料,干燥,冷却,最后喷涂疏水保护层的制备原料,得到所述保温隔热成品艺术漆;上述制备方法中,所述干燥包括80-140℃(例如85℃、90℃、95℃、100℃、105℃、110℃、115℃、120℃、125℃、130℃或135℃等)逐级烘干,所述冷却包括90-25℃(例如85℃、80℃、75℃、70℃、65℃、60℃、55℃、50℃、45℃、40℃、35℃或30℃等)逐级冷却。
第三方面,本发明提供一种如第一方面所述的保温隔热成品艺术漆在家居墙面装饰材料中的应用。
相对于现有技术,本发明具有以下有益效果:
(1)本发明提供的保温隔热成品艺术漆包括依次设置的保温隔热层、无纺布层、防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层;通过上述多层结构设计,使得到保温隔热成品艺术漆具有保温、隔热、抗开裂、防水、防污、可擦洗效果和耐候性的特点;同时还具有优异的附着性和阻燃性,能达到B1级阻燃。所述保温隔热成品艺术漆的热阻值为0.364-1.133m2·K/W,优选情况下,热阻值为0.863-0.995m2·K/W。
(2)本发明提供的保温隔热成品艺术漆在使用时可以有效降低人工操作的出错率,提高施工效率,将艺术漆提前生产成为保温隔热成品艺术漆,施工时只需要将保温隔热成品艺术漆粘贴墙面即可。
附图说明
图1为实施例1提供的保温隔热成品艺术漆的剖面结构示意图;
其中,1-保温隔热层;2-无纺布层;3-防护层;4-艺术漆基础层;5-艺术漆色彩层;6-艺术漆纹理层;7-疏水保护层。
具体实施方式
下面通过具体实施方式来进一步说明本发明的技术方案。本领域技术人员应该明了,所述实施例仅仅是帮助理解本发明,不应视为对本发明的具体限制。
实施例1
本实施例提供一种保温隔热成品艺术漆及其制备方法,所述保温隔热成品艺术漆包括依次层叠设置的保温隔热层1、无纺布层2、防护层3、艺术漆基础层4、艺术漆色彩层5、艺术漆纹理层6和疏水保护层7。
所述保温隔热层1的厚度为0.7mm。
所述无纺布层2的材质为水刺无纺布,厚度为0.5mm。
所述防护层3的材质为纳米活性炭,厚度为0.25mm。
所述艺术漆基础层4的厚度为0.25mm。
所述艺术漆色彩层5的厚度为0.5mm。
所述艺术漆纹理层6的厚度为0.5mm。
所述疏水保护层7的材质为疏水性材料,厚度为0.25mm。
所述保温隔热成品艺术漆的制备方法如下:
保温隔热层的制备原料的制备:将水性树脂(水性丙烯酸树脂,固含量40%,粘度8000mpa.s)40重量份、气凝胶(二氧化硅气凝胶)8重量份、隔热填料(空心玻璃微珠)4重量份、助剂(十二碳醇酯)3重量份和水35重量份混合,得到所述保温隔热层的制备原料;
艺术漆基础层的制备原料的制备:将水性丙烯酸乳液(水性丙烯酸树脂,固含量为40%,粘度8000mpa.s)20重量份、聚四氟乙烯乳液(固含量为60%,粘度10000mpa.s)8重量份、贝壳粉15重量份、水8重量份、和高岭土8重量份混合,得到所述艺术漆基础层的制备原料。
艺术漆色彩层的制备原料的制备:将水性丙烯酸乳液(水性丙烯酸树脂,固含量为40%,粘度8000mpa.s)45重量份、聚四氟乙烯乳液(固含量为60%,粘度10000mpa.s)20重量份、钛白粉8重量份、高岭土8重量份和水性色浆(厂家:泰升颜料,型号中黄Y1074)2重量份混合,得到所述艺术漆色彩层的制备原料。
艺术漆纹理层的制备原料的制备:将水性丙烯酸乳液(水性丙烯酸树脂,固含量为40%,粘度8000mpa.s)20重量份、聚四氟乙烯乳液(固含量为60%,粘度10000mpa.s)8重量份、贝壳粉15重量份、水8重量份和高岭土10重量份混合,得到所述艺术漆基础层的制备原料。
将在水刺无纺布一侧刮涂上述保温隔热层的制备原料,干燥形成保温隔热层,冷却,在水刺无纺布另一侧喷涂纳米活性炭,干燥,冷却,再喷涂上述艺术漆基础层的制备原料,干燥,冷却,喷涂上述艺术漆色彩层的制备原料,干燥,冷却,喷涂上述压花艺术漆纹理层的制备原料,用模具滚轴压花工艺制作纹理,干燥,冷却,最后喷涂疏水性材料(厂家:金桥,型号:SF30),得到所述保温隔热成品艺术漆;上述制备方法中,所述干燥为80℃、100℃、120℃、140℃逐级烘干,所述冷却为90℃、75℃、50℃、25℃逐级冷却。
实施例2
本实施例提供一种保温隔热成品艺术漆及其制备方法,所述保温隔热成品艺术漆包括依次层叠设置的保温隔热层、无纺布层、防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层。
所述保温隔热层的厚度为0.5mm。
所述无纺布层的材质为水刺无纺布,厚度为0.05mm。
所述防护层的材质为纳米活性炭,厚度为0.05mm。
所述艺术漆基础层的厚度为0.1mm。
所述艺术漆色彩层的厚度为0.1mm。
所述艺术漆纹理层的厚度为0.1mm。
所述疏水保护层的材质为疏水性材料,厚度为0.01mm。
所述保温隔热成品艺术漆采用如下方法制备得到:
保温隔热层的制备原料的制备:将水性树脂(水性丙烯酸树脂,固含量40%,粘度7000mpa.s)30重量份、气凝胶(二氧化硅气凝胶)5重量份、隔热填料(空心玻璃微珠)3重量份、助剂(十二碳醇酯)2重量份和水30重量份混合,得到所述保温隔热层的制备原料;
艺术漆基础层的制备原料的制备:将水性丙烯酸乳液(水性丙烯酸树脂,固含量40%,粘度7000mpa.s)10重量份、聚四氟乙烯乳液(固含量为60%,粘度15000mpa.s)5重量份、贝壳粉5重量份、水5重量份和钛白粉5重量份混合,得到所述艺术漆基础层的制备原料。
艺术漆色彩层的制备原料的制备:将水性丙烯酸乳液(水性丙烯酸树脂,固含量40%,粘度7000mpa.s)40重量份、聚四氟乙烯乳液(固含量为60%,粘度15000mpa.s)15重量份、钛白粉5重量份、高岭土5重量份和水性色浆(厂家:泰升颜料,型号桔橙O3013)1重量份混合,得到所述艺术漆色彩层的制备原料。
艺术漆纹理层的制备原料的制备:将水性丙烯酸乳液(水性丙烯酸树脂,固含量为40%,粘度7000mpa.s)10重量份、聚四氟乙烯乳液(固含量为60%,粘度15000mpa.s)5重量份、贝壳粉5重量份、水5重量份和钛白粉5重量份混合,得到所述艺术漆基础层的制备原料。
将在水刺无纺布一侧刮涂上述保温隔热层的制备原料,干燥形成保温隔热层,冷却,在水刺无纺布另一侧喷涂纳米活性炭,干燥,冷却,再喷涂上述艺术漆基础层的制备原料,干燥,冷却,喷涂上述艺术漆色彩层的制备原料,干燥,冷却,喷涂上述压花艺术漆纹理层的制备原料,用模具滚轴压花工艺制作纹理,干燥,冷却,最后喷涂疏水性材料(厂家:金桥,型号:SF30),得到所述保温隔热成品艺术漆;上述制备方法中,所述干燥为80℃、100℃、120℃、140℃逐级烘干,所述冷却为90℃、75℃、50℃、25℃逐级冷却。
实施例3
本实施例提供一种保温隔热成品艺术漆及其制备方法,所述保温隔热成品艺术漆包括依次层叠设置的保温隔热层、无纺布层、防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层。
所述保温隔热层的厚度为0.8mm。
所述无纺布层的材质为水刺无纺布,厚度为1mm。
所述防护层的材质为纳米活性炭,厚度为0.5mm。
所述艺术漆基础层的厚度为0.5mm。
所述艺术漆色彩层的厚度为1mm。
所述艺术漆纹理层的厚度为1mm。
所述疏水保护层的材质为疏水性材料,厚度为0.5mm。
所述保温隔热成品艺术漆的制备方法如下:
保温隔热层的制备原料的制备:将水性树脂(水性丙烯酸树脂,固含量40%,粘度8000mpa.s)45重量份、气凝胶(二氧化硅气凝胶)10重量份、隔热填料(空心玻璃微珠)5重量份、助剂(十二碳醇酯)5重量份和水30重量份混合,得到所述保温隔热层的制备原料;
艺术漆基础层的制备原料的制备:将水性丙烯酸乳液(水性丙烯酸树脂,固含量为40%,粘度8000mpa.s)10重量份、聚四氟乙烯乳液(固含量为60%,粘度10000mpa.s)5重量份、贝壳粉5重量份、水5重量份和滑石粉10重量份混合,得到所述艺术漆基础层的制备原料。
艺术漆色彩层的制备原料的制备:将水性丙烯酸乳液(水性丙烯酸树脂,固含量为40%,粘度8000mpa.s)55重量份、聚四氟乙烯乳液(固含量为60%,粘度10000mpa.s)25重量份、钛白粉10重量份、高岭土10重量份和水性色浆(厂家:泰升颜料,型号中黄Y1074)3重量份混合,得到所述艺术漆色彩层的制备原料。
艺术漆纹理层的制备原料的制备:将水性丙烯酸乳液(水性丙烯酸树脂,固含量为40%,粘度8000mpa.s)25重量份、聚四氟乙烯(固含量为60%,粘度10000mpa.s)10重量份、贝壳粉20重量份、水10重量份和滑石粉10重量份混合,得到所述艺术漆基础层的制备原料。
将在水刺无纺布一侧刮涂上述保温隔热层的制备原料,干燥形成保温隔热层,冷却,在水刺无纺布另一侧喷涂纳米活性炭,干燥,冷却,再喷涂上述艺术漆基础层的制备原料,干燥,冷却,喷涂上述艺术漆色彩层的制备原料,干燥,冷却,喷涂上述压花艺术漆纹理层的制备原料,用模具滚轴压花工艺制作纹理,干燥,冷却,最后喷涂疏水性材料(厂家:金桥,型号:SF30),得到所述保温隔热成品艺术漆;上述制备方法中,所述干燥为80℃、100℃、120℃、140℃逐级烘干,所述冷却为90℃、75℃、50℃、25℃逐级冷却。
实施例4
本实施例提供一种保温隔热成品艺术漆及其制备方法,其与实施例1的区别仅在于,将保温隔热层的制备原料中气凝胶的质量份数调整为3份,其他与实施例1相同。
实施例5
本实施例提供一种保温隔热成品艺术漆及其制备方法,其与实施例1的区别仅在于,将保温隔热层的制备原料中气凝胶的质量份数调整为13份,其他与实施例1相同。
实施例6
本实施例提供一种保温隔热成品艺术漆及其制备方法,其与实施例1的区别仅在于,将保温隔热层的厚度调整为0.3mm,其他与实施例1相同。
实施例7
本实施例提供一种保温隔热成品艺术漆及其制备方法,其与实施例1的区别仅在于,将保温隔热层的厚度调整为1mm,其他与实施例1相同。
对比例1
本对比例提供一种保温隔热成品艺术漆及其制备方法,其与实施例1的区别仅在于,所述保温隔热成品艺术漆不包括保温隔热层,所述保温隔热成品艺术漆包括依次层叠设置的无纺布层、防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层。
所述保温隔热成品艺术漆的制备方法中,不包括在水刺无纺布一侧刮涂上述保温隔热层的制备原料,干燥形成保温隔热层,冷却的步骤。
其他与实施例1相同。
对实施例和对比例提供的保温隔热成品艺术漆进行如下性能测试。
(1)防水性:将保温隔热成品艺术漆泡在水中,观察起皱时间。
(2)防污性:测试非油性污迹是否可清洗干净。
(3)硬度:参照《GB6739-86涂膜硬度铅笔测定法》提供的测试方法进行测试。
(4)附着性能:参照《GB/T9286-88》提供的测试方法进行测试。
(5)抗开裂:手撕保温隔热成品艺术漆,观察是否开裂。
(6)热阻值:参照GB/T 35762-2017热传递性能提供的测试方法进行测试。
(7)施工性能:将保温隔热成品艺术漆粘贴在阳角的直角墙面,观察呈直角或圆角。
(8)阻燃性能:参照GB/8624-2012建筑材料及制品燃烧性能分级。
测试结果如表1所示。
表1
根据表1测试结果可知,实施例1-7提供的保温隔热成品艺术漆24h不起皱,防水性好,非油性污迹能可清洗干净,防污性能好,附着性能为0级,附着性好,热阻值0.364-1.133m2·K/W,保温隔热效果好。实施例1-3提供的保温隔热成品艺术漆的热阻值0.863-0.995m2·K/W。
与实施例1对比可知,若保温隔热层的制备原料中气凝胶的质量份数过小(实施例4),则热阻值降低,保温隔热效果下降;若保温隔热层的制备原料中气凝胶的质量份数过大(实施例5),则保温隔热层易开裂,热阻值降低,保温隔热效果下降,证明保温隔热层的制备原料中气凝胶的质量份数在特定范围内制得的保温隔热成品艺术漆性能更佳。
与实施例1对比可知,若保温隔热层的厚度过小(实施例6),则热阻值降低,保温隔热效果下降;若保温隔热层的厚度过大(实施例7),则施工性能下降,粘贴阳角处呈圆角,证明保温隔热层的厚度在特定范围内制得的保温隔热成品艺术漆性能更佳。
与实施例1对比可知,若所述保温隔热成品艺术漆不包括保温隔热层(对比例1),则保温隔热性能下降。
申请人声明,本发明通过上述实施例来说明本发明的工艺方法,但本发明并不局限于上述工艺步骤,即不意味着本发明必须依赖上述工艺步骤才能实施。所属技术领域的技术人员应该明了,对本发明的任何改进,对本发明所选用原料的等效替换及辅助成分的添加、具体方式的选择等,均落在本发明的保护范围和公开范围之内。
Claims (10)
1.一种保温隔热成品艺术漆,其特征在于,所述保温隔热成品艺术漆包括依次层叠设置的保温隔热层、无纺布层、防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层。
2.根据权利要求1所述的保温隔热成品艺术漆,其特征在于,所述保温隔热层的制备原料包括水性树脂、气凝胶、隔热填料、助剂和水;
优选地,所述保温隔热层的制备原料包括按重量份数计的如下组分:水性树脂30-45份、气凝胶5-10份、隔热填料3-5份、助剂2-5份和水30-42份;
优选地,所述水性树脂包括水性丙烯酸树脂;
优选地,所述气凝胶包括二氧化硅气凝胶;
优选地,所述隔热填料包括空心玻璃微珠;
优选地,所述助剂包括十二碳醇酯。
3.根据权利要求1或2所述的保温隔热成品艺术漆,其特征在于,所述无纺布层包括水刺无纺布。
4.根据权利要求1-3任一项所述的保温隔热成品艺术漆,其特征在于,所述防护层的制备原料包括纳米活性炭。
5.根据权利要求1-4任一项所述的保温隔热成品艺术漆,其特征在于,所述保温隔热层的厚度为0.5-0.8mm。
6.根据权利要求1-5任一项所述的保温隔热成品艺术漆,其特征在于,所述无纺布层的厚度为0.05-1mm。
7.根据权利要求1-6任一项所述的保温隔热成品艺术漆,其特征在于,所述防护层的厚度为0.05-0.5mm;
优选地,所述艺术漆基础层的厚度为0.1-0.5mm。
8.根据权利要求1-7任一项所述的保温隔热成品艺术漆,其特征在于,所述艺术漆色彩层的厚度为0.1-1mm;
优选地,所述艺术漆纹理层的厚度为0.1-1mm;
优选地,所述疏水保护层的厚度为0.01-0.5mm。
9.一种如权利要求1-8任一项所述的保温隔热成品艺术漆的制备方法,其特征在于,所述制备方法包括如下步骤:在无纺布层一侧复合保温隔热层,在无纺布层另一侧依次复合防护层、艺术漆基础层、艺术漆色彩层、艺术漆纹理层和疏水保护层,得到所述保温隔热成品艺术漆。
10.一种如权利要求1-8任一项所述的保温隔热成品艺术漆在家居墙面装饰材料中的应用。