CN117362942A - 一种旱作农业区专用全生物降解渗水地膜 - Google Patents
一种旱作农业区专用全生物降解渗水地膜 Download PDFInfo
- Publication number
- CN117362942A CN117362942A CN202311252107.0A CN202311252107A CN117362942A CN 117362942 A CN117362942 A CN 117362942A CN 202311252107 A CN202311252107 A CN 202311252107A CN 117362942 A CN117362942 A CN 117362942A
- Authority
- CN
- China
- Prior art keywords
- full
- mulching film
- parts
- film
- biodegradable water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本申请涉及地膜生产的技术领域,具体公开了一种旱作农业区专用全生物降解渗水地膜。一种旱作农业区专用全生物降解渗水地膜,所述地膜的原料包括如下重量份的组分:聚对苯二甲酸‑己二酸丁二醇酯50~70份、聚碳酸亚丙酯15~25份、海泡石10~20份、玻璃微珠5~15份、阳离子聚丙烯酰胺1~5份、相容剂1~5份、润滑剂1~5份、开口剂0.1~1份、扩链剂0.1~0.5份。本申请中阳离子聚丙烯酰胺使得海泡石、玻璃微珠均匀分散在地膜中,海泡石具有较多的孔隙结构,可以形成渗水通道,玻璃微珠具有较好的疏水性能,将雨水导入渗水通道中,且阳离子聚丙烯酰胺还能提高地膜整体的疏水性能,从而使得地膜具有较好的渗水性能。
Description
技术领域
本申请涉及地膜生产的技术领域,尤其是涉及一种旱作农业区专用全生物降解渗水地膜。
背景技术
地膜是地面覆盖薄膜,用于地面覆盖,提高土壤温度,保持土壤水分,维持土壤结构,防止害虫侵袭作物和某些微生物引起的病害等,可以促进植物的生长,通常用于地膜覆盖栽培。地膜覆盖栽培是一项成功的农业增产技术,是我国传统农业技术向现代化、集约化发展的重大技术改革。常用的地膜均为高分子化合物聚乙烯和聚氯乙烯,可以起到较好的保温效果,但是渗水性能较差,会影响作物的生长。
发明内容
为了提高制得地膜的渗水性能,本申请提供一种旱作农业区专用全生物降解渗水地膜。
第一方面,本申请提供的一种旱作农业区专用全生物降解渗水地膜,采用如下的技术方案:
一种旱作农业区专用全生物降解渗水地膜,所述地膜的原料包括如下重量份的组分:聚对苯二甲酸-己二酸丁二醇酯50~70份、聚碳酸亚丙酯15~25份、海泡石10~20份、玻璃微珠5~15份、阳离子聚丙烯酰胺1~5份、相容剂1~5份、润滑剂1~5份、开口剂0.1~1份、扩链剂0.1~0.5份。
通过采用上述技术方案,利用聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯以及其他助剂合成可全生物降解的地膜,阳离子聚丙烯酰胺使得海泡石、玻璃微珠均匀分散在地膜中,利用海泡石和玻璃微珠的配合,海泡石具有较多的孔隙结构,可以形成渗水通道,玻璃微珠具有较好的疏水性能,将雨水导入渗水通道中,且阳离子聚丙烯酰胺还能提高地膜整体的疏水性能,从而使得地膜具有较好的渗水性能;另外玻璃微珠的导热性能较差,从而提高了制得地膜的保温性能。
在一个具体的可实施方案中,所述相容剂包括溴化聚苯乙烯。
在一个具体的可实施方案中,所述润滑剂包括十八烷酸、顺-13-二十二碳烯酸酰胺中的一种或两者组成的混合物。
通过采用上述技术方案,利用溴化聚苯乙烯和润滑剂的配合,使得地膜原料中的各组分可以均匀分散,从而提高了制得地膜的性能。
在一个具体的可实施方案中,所述开口剂包括滑石粉、二氧化硅、油酸酰胺中的一种或多种。
在一个具体的可实施方案中,所述扩链剂包括乙二胺、丙二胺、环己二胺、N,N-二羟基(二异丙基)苯胺中的一种或多种。
通过采用上述技术方案,乙二胺、丙二胺、环己二胺、N,N-二羟基(二异丙基)苯胺的加入,方便原料的加工,且可以提高制得地膜的力学性能。
在一个具体的可实施方案中,所述地膜的原料还包括0.1~1重量份的硅油。
通过采用上述技术方案,硅油的加入,可以起到稀释和润滑作用,进一步提高制得地膜的性能,且还能提高地膜的光洁度。
第二方面,本申请提供的一种旱作农业区专用全生物降解渗水地膜的制备方法,采用如下的技术方案:
一种旱作农业区专用全生物降解渗水地膜的制备方法,包括以下步骤:
干燥:将聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯、海泡石、玻璃微珠、阳离子聚丙烯酰胺、相容剂、润滑剂、开口剂、扩链剂进行干燥;
挤出切粒:将干燥后的聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯、海泡石、玻璃微珠、阳离子聚丙烯酰胺、相容剂、润滑剂、开口剂、扩链剂搅拌混合均匀,接着加入硅油,搅拌混合均匀,得到混合料,将混合料进行挤出切粒,得到母粒;
吹膜:将母粒进行干燥,然后进行吹膜,得到全生物降解渗水地膜。
通过采用上述技术方案,先将原料进行干燥,接着混合挤出切粒,得到母粒,然后将母粒进行干燥,最后进行吹膜,得到渗水性能较好的地膜。
在一个具体的可实施方案中,所述吹膜步骤中,将母粒在70-80℃下干燥6-8h,然后进行吹膜,得到全生物降解渗水地膜。
通过采用上述技术方案,进一步限定了母粒的干燥温度与时间,方便进行对母粒进行吹膜。
综上所述,本申请包括以下至少一种有益技术效果:
1.本申请中利用聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯以及其他助剂合成可全生物降解的地膜,阳离子聚丙烯酰胺使得海泡石、玻璃微珠均匀分散在地膜中,利用海泡石和玻璃微珠的配合,海泡石具有较多的孔隙结构,可以形成渗水通道,玻璃微珠具有较好的疏水性能,将雨水导入渗水通道中,且阳离子聚丙烯酰胺还能提高地膜整体的疏水性能,从而使得地膜具有较好的渗水性能;另外玻璃微珠的导热性能较差,从而提高了制得地膜的保温性能;2.本申请中利用溴化聚苯乙烯和润滑剂的配合,使得地膜原料中的各组分可以均匀分散,从而提高了制得地膜的性能;
3.本申请中的方法,先将原料进行干燥,接着混合挤出切粒,得到母粒,然后将母粒进行干燥,最后进行吹膜,得到渗水性能较好的地膜。
具体实施方式
以下结合实施例对本申请作进一步详细说明。
实施例中所有原料均可通过市售获得。其中阳离子聚丙烯酰胺由苏州昊诺工贸有限公司提供;硅油CAS号:9006-65-9;润滑剂包括并不局限于如十八烷酸、顺-13-二十二碳烯酸酰胺中的一种或两者组成的混合物,本申请中优选为十八烷酸;开口剂包括并不局限于如滑石粉、二氧化硅、油酸酰胺中的一种或多种组成的混合物,本申请中优选为滑石粉和二氧化硅组成的混合物;扩链剂包括并不局限于如乙二胺、丙二胺、环己二胺、N,N-二羟基(二异丙基)苯胺中的一种或多种组成的混合物,本申请中优选丙二胺。
实施例
实施例1
实施例1提供了一种旱作农业区专用全生物降解渗水地膜的制备方法,包括以下步骤:
干燥:将50kg聚对苯二甲酸-己二酸丁二醇酯、15kg聚碳酸亚丙酯、10kg海泡石、5kg玻璃微珠、1kg阳离子聚丙烯酰胺、1kg相容剂、1kg润滑剂、0.1kg开口剂、0.1kg扩链剂进行干燥;其中相容剂为溴化聚苯乙烯;润滑剂为十八烷酸;开口剂为滑石粉和二氧化硅组成的混合物,且滑石粉、二氧化硅的重量比为1:1;扩链剂为丙二胺;
挤出切粒:将干燥后的聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯、海泡石、玻璃微珠、阳离子聚丙烯酰胺、相容剂、润滑剂、开口剂、扩链剂加入高混机中搅拌混合均匀,得到混合料,将混合料加入到双螺杆挤出机中进行熔融挤出,然后将挤出的物料冷却后加入到切粒机中进行切粒,得到母粒;其中挤出机长径比为:40:1,挤出机温度设置为:一区温度为100℃,二区温度为150℃,三区温度为170℃,四区温度为170℃,五区温度为165℃;
吹膜:将母粒在70℃下干燥8h,然后利用吹膜机进行吹膜,得到全生物降解渗水地膜。
实施例2
实施例2与实施例1的区别在于,干燥步骤中,将60kg聚对苯二甲酸-己二酸丁二醇酯、20kg聚碳酸亚丙酯、15kg海泡石、10kg玻璃微珠、3kg阳离子聚丙烯酰胺、3kg相容剂、3kg润滑剂、0.5kg开口剂、0.3kg扩链剂进行干燥;其余步骤与实施例1相一致。
实施例3
实施例3与实施例1的区别在于,干燥步骤中,将70kg聚对苯二甲酸-己二酸丁二醇酯、25kg聚碳酸亚丙酯、20kg海泡石、15kg玻璃微珠、5kg阳离子聚丙烯酰胺、5kg相容剂、5kg润滑剂、1kg开口剂、0.5kg扩链剂进行干燥;其余步骤与实施例1相一致。
实施例4
实施例4与实施例2的区别在于,挤出切粒步骤中,将干燥后的聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯、海泡石、玻璃微珠、阳离子聚丙烯酰胺、相容剂、润滑剂、开口剂、扩链剂搅拌混合均匀,接着加入0.5kg硅油,搅拌混合均匀,得到混合料,将混合料加入到双螺杆挤出机中进行熔融挤出,然后将挤出的物料冷却后加入到切粒机中进行切粒,得到母粒;其余步骤与实施例2相一致。
实施例5
实施例5与实施例4的区别在于,吹膜步骤中,将母粒在75℃下干燥7h,然后利用吹膜机进行吹膜,得到全生物降解渗水地膜;其余步骤与实施例4相一致。
实施例6
实施例6与实施例4的区别在于,吹膜步骤中,将母粒在80℃下干燥6h,然后利用吹膜机进行吹膜,得到全生物降解渗水地膜;其余步骤与实施例4相一致。
对比例
对比例1
对比例1与实施例1的区别在于,将66kg聚对苯二甲酸-己二酸丁二醇酯、15kg聚碳酸亚丙酯、1kg相容剂、1kg润滑剂、0.1kg开口剂、0.1kg扩链剂进行干燥;其中相容剂为溴化聚苯乙烯;润滑剂为十八烷酸;开口剂为滑石粉和二氧化硅组成的混合物,且滑石粉、二氧化硅的重量比为1:1;扩链剂为丙二胺;
将干燥后的聚对苯二甲酸-己二酸丁二醇酯、相容剂、润滑剂、开口剂、扩链剂加入高混机中搅拌混合均匀,得到混合料;其余步骤与实施例1相一致。
对比例2
对比例2与实施例1的区别在于,将51kg聚对苯二甲酸-己二酸丁二醇酯、15kg聚碳酸亚丙酯、10kg海泡石、5kg玻璃微珠、1kg相容剂、1kg润滑剂、0.1kg开口剂、0.1kg扩链剂进行干燥;其中相容剂为溴化聚苯乙烯;润滑剂为十八烷酸;开口剂为滑石粉和二氧化硅组成的混合物,且滑石粉、二氧化硅的重量比为1:1;扩链剂为丙二胺;
将干燥后的聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯、海泡石、玻璃微珠、相容剂、润滑剂、开口剂、扩链剂加入高混机中搅拌混合均匀,得到混合料;其余步骤与实施例1相一致。
对比例3
对比例3与实施例1的区别在于,将50kg聚对苯二甲酸-己二酸丁二醇酯、15kg聚碳酸亚丙酯、15kg海泡石、1kg阳离子聚丙烯酰胺、1kg相容剂、1kg润滑剂、0.1kg开口剂、0.1kg扩链剂进行干燥;其中相容剂为溴化聚苯乙烯;润滑剂为十八烷酸;开口剂为滑石粉和二氧化硅组成的混合物,且滑石粉、二氧化硅的重量比为1:1;扩链剂为丙二胺;
将干燥后的聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯、海泡石、阳离子聚丙烯酰胺、相容剂、润滑剂、开口剂、扩链剂加入高混机中搅拌混合均匀,得到混合料;其余步骤与实施例1相一致。
性能检测试验
1.生物分解率:按照GB/T 19277.1《受控堆肥条件下材料终须氧生物分解和崩解能力的测定》对各实施例中的地膜进行检测,得到生物分解率,生物分解率越高,地膜的降解效果越好。
2.渗水量:在室温23℃±2℃的条件下,将地膜平放在100mm的布氏漏斗芯上,加入计量好的100g蒸馏水,记录在1h内从布氏漏斗渗水烧杯中的质量,渗水量越高,地膜的渗水效果越好。
表1地膜的性能检测结果
样品 | 生物分解率(180h/%) | 渗水量(g) |
实施例1 | 90.8 | 44 |
实施例2 | 91.3 | 45 |
实施例3 | 91.0 | 45 |
实施例4 | 92.9 | 48 |
实施例5 | 93.5 | 50 |
实施例6 | 93.1 | 49 |
对比例1 | 88.9 | 10 |
对比例2 | 89.5 | 25 |
对比例3 | 90.1 | 30 |
结合实施例1和对比例1-3,实施例1中地膜的渗水效果最佳,可见在制备母粒时,向原料中加入海泡石、玻璃微珠、阳离子聚丙烯酰胺,利用三者的配合,阳离子聚丙烯酰胺使得海泡石、玻璃微珠均匀分散在地膜中,海泡石具有较多的孔隙结构,可以形成渗水通道,玻璃微珠具有较好的疏水性能,将雨水导入渗水通道中,因此提高了地膜的渗水性能。
结合实施例1-3,实施例1-3中地膜的生物分解率和渗水量均相差不大,可见在制备母粒时,提高原料的使用量,对制得地膜的性能影响不大。
结合实施例2和实施例4,实施例4中地膜的生物分解率和渗水量均较高,可见在制备母粒时,向原料中加入硅油,可以起到一定的稀释和润滑作用,因此可以进一步提高制得地膜的性能。
结合实施例4-6,实施例5中地膜的生物分解率和渗水量均较高,可见在吹膜前对母粒进行干燥时,实施例5中母粒的干燥条件最佳,从而实施例5中地膜的降解性能和渗水性能均最好。
本具体实施例仅仅是对本申请的解释,其并不是对本申请的限制,本领域技术人员在阅读完本说明书后可以根据需要对本实施例做出没有创造性贡献的修改,但只要在本申请的权利要求范围内都受到专利法的保护。
Claims (8)
1.一种旱作农业区专用全生物降解渗水地膜,其特征在于:所述地膜
的原料包括如下重量份的组分:聚对苯二甲酸-己二酸丁二醇酯50~70份、聚碳酸亚丙酯15~25份、海泡石10~20份、玻璃微珠5~15份、阳离子聚丙烯酰胺1~5份、相容剂1~5份、润滑剂1~5份、开口剂0.1~1份、扩链剂0.1~0.5份。
2.根据权利要求1所述的一种旱作农业区专用全生物降解渗水地膜,其特征在于:所述相容剂包括溴化聚苯乙烯。
3.根据权利要求1所述的一种旱作农业区专用全生物降解渗水地膜,其特征在于:所述润滑剂包括十八烷酸、顺-13-二十二碳烯酸酰胺中的一种或两者组成的混合物。
4.根据权利要求1所述的一种旱作农业区专用全生物降解渗水地膜,其特征在于:所述开口剂包括滑石粉、二氧化硅、油酸酰胺中的一种或多种。
5.根据权利要求1所述的一种旱作农业区专用全生物降解渗水地膜,其特征在于:所述扩链剂包括乙二胺、丙二胺、环己二胺、N,N-二羟基(二异丙基)苯胺中的一种或多种。
6.根据权利要求1所述的一种旱作农业区专用全生物降解渗水地膜,其特征在于:所述地膜的原料还包括0.1~1重量份的硅油。
7.一种如权利要求1-6任意一项所述的旱作农业区专用全生物降解渗水地膜的制备方法,其特征在于:包括以下步骤:
干燥:将聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯、海泡石、玻璃微珠、阳离子聚丙烯酰胺、相容剂、润滑剂、开口剂、扩链剂进行干燥;
挤出切粒:将干燥后的聚对苯二甲酸-己二酸丁二醇酯、聚碳酸亚丙酯、海泡石、玻璃微珠、阳离子聚丙烯酰胺、相容剂、润滑剂、开口剂、扩链剂搅拌混合均匀,接着加入硅油,搅拌混合均匀,得到混合料,将混合料进行挤出切粒,得到母粒;
吹膜:将母粒进行干燥,然后进行吹膜,得到全生物降解渗水地膜。
8.根据权利要求7所述的一种旱作农业区专用全生物降解渗水地膜的制备方法,其特征在于:所述吹膜步骤中,将母粒在70-80℃下干燥6-8h,然后进行吹膜,得到全生物降解渗水地膜。