CN1172398C - 在铅蓄电池中使用的无硅胶体电解液 - Google Patents
在铅蓄电池中使用的无硅胶体电解液 Download PDFInfo
- Publication number
- CN1172398C CN1172398C CNB021209227A CN02120922A CN1172398C CN 1172398 C CN1172398 C CN 1172398C CN B021209227 A CNB021209227 A CN B021209227A CN 02120922 A CN02120922 A CN 02120922A CN 1172398 C CN1172398 C CN 1172398C
- Authority
- CN
- China
- Prior art keywords
- silicon
- electrolyte
- present
- sulfuric acid
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开一种在铅蓄电池中使用的无硅胶体电解液，包括消泡剂、分散剂、稳定剂和硫酸，其特征是采用聚乙烯二醇和聚乙烯醇凝胶剂，丙二醇稳定剂阳树脂分散剂，磷酸三丁酯消泡剂，各成份按重量计配比范围为聚乙烯二醇1-8%，聚乙烯醇0.3-3.5%，丙二醇0.1-2.5%，硫酸72-78%，阳树脂15-25%，磷酸三丁酯1%，全部成份重量之和为100%。本发明利用高分子聚合物具有很强的凝胶性，并利用这些物质分子中同时存在着对吸附剂有强烈的亲和性、对分散介质有很好的相溶性形成稳定的胶体，利用分散剂使有效成份分散到介质中，使得本发明的电解液为胶体状且其中不含硅元素，内阻很小，内耗小，输出电流大，寿命长。
Description
技术领域
本发明涉及一种蓄电池用电解液，特别涉及一种在铅蓄电池中使用的无硅胶体电解液。
背景技术
我国“八五”科技攻关项目阀控式密封铅酸蓄电池已被电力、通讯、交通、国防、能源等行业广泛采用，但它的使用寿命只有5年左右，而德国和美国生产的蓄电池使用寿命是10-15年，并且在质量上国产蓄电池还有一定的差距，究其原因，就是国产蓄电池的电解液技术还有待提高，德国和美国生产的蓄电池使用的是胶体电解液；国内曾经研制过胶体电解液，但在研制过程中，都使用二氧化硅和硅酸钠反应生成的凝胶物质作胶体，而硅元素会使蓄电池内阻增大，充放电性能下降，损耗增加。
本发明内容
有鉴于此，如何能提供一种电解液，采用胶体电解液，但其中不含硅元素，内阻尽可能低，正是本发明研创动机所在。
本发明设计人凭借多年从事各类电化学技术研究生产加工等领域的实际经验，在反复研究论证的基础上，做一全新设计构成，终得本发明的产生。
针对现有技术的不足，本发明的目的是提供一种无硅胶体电解液，采用高分子聚合物作为凝胶剂，实现不含硅，低阻抗的高效能电解液。
本发明的目的可以按下述方式实现：一种在铅蓄电池中使用的无硅胶体电解液，包括消泡剂、分散剂、稳定剂和硫酸，其特征在于采用的凝胶剂为聚乙烯二醇和聚乙烯醇，稳定剂为丙二醇，分散剂为阳树脂，消泡剂为磷酸三丁酯，其中各成份按重量配比范围为聚乙烯二醇1-8％，聚乙烯醇0.3-3.5％，丙二醇0.1-2.5％，硫酸72-78％，阳树脂15-25％，磷酸三丁酯1％，全部成份重量之和为100％。
较佳优选方法是按重量成份比例范围为聚乙烯二醇2-3％，聚乙烯醇1-2％，丙二醇1％，硫酸75％，阳树脂19％，磷酸三丁酯1％，全部成份之和为100％。
更佳优选方法是按重量比聚乙烯二醇2％，聚乙烯醇1％，丙二醇1％，硫酸75％，阳树脂20％，磷酸三丁酯1％。
本发明利用高分子聚合物具有很强的凝胶性，并利用这些物质分子中同时存在着对吸附剂有强烈的亲和性、对分散介质有很好的相溶性形成稳定的胶体，利用分散剂使有效成份分散到介质中，使得本发明的电解液为胶体状且其中不含硅元素，内阻很小，内耗小，输出电流大，寿命长。
本发明具体实施方式
本发明包括消泡剂、分散剂、稳定剂和硫酸，采用的凝胶剂为：聚乙烯二醇、聚乙烯醇，稳定剂采用丙二醇；分散剂采用阳树脂，消泡剂为磷酸三丁酯，阳树脂也称阳离子交换树脂，其具有两种功能：一是利用其高度的化学稳定性和机械稳定性，几乎不溶于一切有机、无机溶剂，对溶于硫酸中或水中的阴、阳离子能有效的吸附。二是将其制成15mμm-30mμm的粉粒，起分散介质的作用，同时调整粘度。
具体实施例为按重量聚乙烯二醇2％，聚乙烯醇1％，丙二醇1％，硫酸75％，阳树脂20％，磷酸三丁酯1％，按此成份组成的电解液呈胶体状，不含硅元素，内阻很小。
采用本发明所说的凝胶剂成份，并在所述重量范围内组合得到的在铅蓄电池中使用的无硅胶体电解液均，其均具有电解液呈胶体状，不含硅元素，内阻很小的特性，并且所有凝胶剂成份的组合均不产生降低凝胶的效果。
综上所述，本发明采用不含硅元素的凝胶剂作胶体，有效地延长蓄电池寿命和增大输出电流。显然本发明为一种新颖、进步并深具实用性的新设计。以上所述乃是本发明的具体实施例及所运用的技术原理，若依本发明的构想所作的等效改变，其所产生的功能作用仍未超出说明书及附图所涵盖的精神时，均应在本发明的范围内，特此说明。
Claims (3)
1、一种在铅蓄电池中使用的无硅胶体电解液，包括消泡剂、分散剂、稳定剂和硫酸，其特征在于采用的凝胶剂为聚乙烯二醇和聚乙烯醇，稳定剂为丙二醇，分散剂为阳树脂，消泡剂为磷酸三丁酯，其中各成份按重量计配比范围为聚乙烯二醇1-8％，聚乙烯醇0.3-3.5％，丙二醇0.1-2.5％，硫酸72-78％，阳树脂15-25％，磷酸三丁酯1％，全部成份重量之和为100％。
2、根据权利要求1所述的无硅胶体电解液，其特征在于各成份按重量计配比范围为聚乙烯二醇2-3％，聚乙烯醇1-2％，丙二醇1％，硫酸75％，阳树脂19％，磷酸三丁酯1％，全部成份重量之和为100％。
3、根据权利要求1所述的无硅胶体电解液，其特征在于按重量计聚乙烯二醇2％，聚乙烯醇1％，丙二醇1％，硫酸75％，阳树脂20％，磷酸三丁酯1％。