CN117062528A - 具有改进的抗菌和抗病毒性质的聚烯烃组合物 - Google Patents
具有改进的抗菌和抗病毒性质的聚烯烃组合物 Download PDFInfo
- Publication number
- CN117062528A CN117062528A CN202280024194.1A CN202280024194A CN117062528A CN 117062528 A CN117062528 A CN 117062528A CN 202280024194 A CN202280024194 A CN 202280024194A CN 117062528 A CN117062528 A CN 117062528A
- Authority
- CN
- China
- Prior art keywords
- composition
- weight
- moiety
- less
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及组合物，其包含：(a)聚烯烃；和(b)具有抗病毒和抗菌功能的化合物或配制物，其中这种组合物、优选聚乙烯组合物具有提高的针对H1N1的抗病毒率、针对新冠病毒的抗病毒率、针对大肠杆菌的抗菌率和/或针对金黄色葡萄球菌的抗菌率。
Description
本发明涉及具有改进的抗病毒和抗菌性质的聚烯烃组合物。本发明还涉及包含这种聚烯烃组合物的制品，特别是包含这种聚合物组合物的膜。
取决于病毒或细菌的性质，可导致发展某些病状的被病毒颗粒或细菌污染可经由各种路线发生。特别相关的一种方法是经由接触到作为病毒颗粒或细菌的载体的物体或表面。再次取决于病毒或细菌的性质，为了使病毒颗粒或细菌以造成病状的方式影响接受者(无论是动物还是人类)，接受者需要暴露于一定量的病毒或细菌颗粒。明显的是，病毒或细菌在这些物体或表面上的任何减少、特别是显著减少将有助于减少病状传播，由此提供社会迫切寻求实现的技术效果。
出于各种卫生和健康相关目的，需要确保各种制品中所用材料具有的构成使得它们作为病毒颗粒和细菌繁殖地的能力以及传播病毒颗粒或细菌的能力尽可能最低。可传播病毒颗粒或细菌的这类制品被称为污染物。
在许多应用和许多制品中，聚合物材料被用作构成这些制品或这些制品的元件的优选材料。因此，要理解这种聚合物材料具有使得病毒颗粒和/或细菌的传播降低到最大程度的性质。因此，正进行开发以提供具有所需的高抗病毒和/或抗菌性质的聚合物材料。
优选聚合物组合物具有抗病毒和/或抗微生物性质，使得使用聚合物组合物生产的物体实现对大肠杆菌(E.Coli)≥98.0％的抗菌率，对金黄色葡萄球菌(S.Aureus)≥98.0％的抗菌率，和/或对H1N1≥98.0％的抗病毒率。优选地，聚合物组合物实现对大肠杆菌≥98.0％的抗菌率，对金黄色葡萄球菌≥98.0％的抗菌率，和对H1N1≥98.0％的抗病毒率。认为这种聚合物组合物特别适合于其中某些卫生要求高的各种应用。
此外，意义重大的是使用安全、允许生产具有性质不低于产品通常所要求品质的产品，不影响生产这类制品的生产效率，并且可普及的组合物来实现这种抗病毒和抗菌效果。
根据本发明，本发明人现已提供这种组合物，其包含：
(a)聚烯烃；和
(b)具有抗病毒和抗菌功能的化合物或配制物。
在根据本发明的组合物中，(b)可例如包含根据式(I)的化合物或它们的混合物：
其中各R1、R2和R3单独地为羟基结构部分或根据式(II)的结构部分：
其中n为≥6且≤25的整数；
且其中R1、R2和R3中的至少一者为羟基结构部分。
组合物中的成分(b)可为例如包含一定量的具有式(I)、其中R1、R2和R3中的一者为羟基结构部分的化合物和一定量的具有式(I)、其中R1、R2和R3中的两者为羟基结构部分的化合物的混合物。优选地，组合物中的成分(b)是包含相对于组合物中的成分(b)的总重量计≥30.0重量％且≤95.0重量％的具有式(I)、其中R1、R2和R3中的一者为羟基结构部分的化合物和≥3.0重量％且≤70.0重量％的具有式(I)、其中R1、R2和R3中的两者为羟基结构部分的化合物的混合物。例如，组合物中的成分(b)可为包含相对于组合物中的成分(b)的总重量计≥35.0重量％且≤50.0重量％的具有式(I)、其中R1、R2和R3中的一者为羟基结构部分的化合物和≤65.0重量％的具有式(I)、其中R1、R2和R3中的两者为羟基结构部分的化合物的混合物。例如，组合物中的成分(b)可为包含相对于组合物中的成分(b)的总重量计≥55.0重量％且≤70.0重量％的具有式(I)、其中R1、R2和R3中的一者为羟基结构部分的化合物和≤45.0重量％的具有式(I)、其中R1、R2和R3中的两者为羟基结构部分的化合物的混合物。
在具有式(I)的化合物中，优选n为≥10且≤25、更优选≥15且≤25、甚至更优选≥15且≤20的整数。
成分(b)可包含单烷酸甘油酯，二烷酸甘油酯，或包含单烷酸甘油酯和二烷酸甘油酯的混合物。成分(b)可例如包含单烷酸甘油酯和二烷酸甘油酯的混合物，其中混合物包含≥30.0且≤95.0重量％的单烷酸甘油酯和优选≥3.0且≤70.0重量％的二烷酸甘油酯。成分(b)可例如包含单烷酸甘油酯和二烷酸甘油酯的混合物，其中混合物包含≥35.0且≤50.0重量％的单烷酸甘油酯和≤65.0重量％的二烷酸甘油酯。成分(b)可例如包含单烷酸甘油酯和二烷酸甘油酯的混合物，其中混合物包含≥55.0且≤70.0重量％的单烷酸甘油酯和≤45.0重量％的二烷酸甘油酯。
在如成分(b)中使用的具有式(I)的化合物或它们的混合物中，优选烷酸酯结构部分各自是相同的并且选自1-辛酸酯、1-壬酸酯、1-癸酸酯、1-十一烷酸酯、1-十二烷酸酯、1-十三烷酸酯、1-十四烷酸酯、1-十五烷酸酯、1-十六烷酸酯、1-十七烷酸酯、1-十八烷酸酯、1-十九烷酸酯、1-二十烷酸酯、1-二十一烷酸酯、1-二十二烷酸酯、1-二十三烷酸酯和1-二十四烷酸酯，优选其中烷酸酯结构部分选自1-十六烷酸酯、1-十八烷酸酯和1-二十烷酸酯。
成分(b)可例如包含单硬脂酸甘油酯，二硬脂酸甘油酯，或包含单硬脂酸甘油酯和二硬脂酸甘油酯的混合物。成分(b)可例如包含单硬脂酸甘油酯和二硬脂酸甘油酯的混合物，其中混合物包含≥30.0且≤95.0重量％的单硬脂酸甘油酯和优选≥3.0且≤70.0重量％的二硬脂酸甘油酯。成分(b)可例如包含单硬脂酸甘油酯和二硬脂酸甘油酯的混合物，其中混合物包含≥35.0且≤50.0重量％的单硬脂酸甘油酯和≤65.0重量％的二硬脂酸甘油酯。成分(b)可例如包含单硬脂酸甘油酯和二硬脂酸甘油酯的混合物，其中混合物包含≥55.0且≤70.0重量％的单硬脂酸甘油酯和≤45.0重量％的二硬脂酸甘油酯。
根据本发明的组合物优选包含相对于组合物的总重量计≥1.0且≤5.0重量％、优选>2.5且<4.0重量％的具有式(I)的化合物或它们的混合物。例如，组合物可包含≥1.0且≤5.0重量％、优选>2.5且<4.0重量％的单烷酸甘油酯和二烷酸甘油酯的混合物，其中混合物包含≥30.0且≤95.0重量％的单烷酸甘油酯和优选≥3.0且≤70.0重量％的二烷酸甘油酯。例如，组合物可包含≥1.0且≤5.0重量％、优选>2.5且<4.0重量％的单硬脂酸甘油酯和二硬脂酸甘油酯的混合物，其中混合物包含≥30.0且≤95.0重量％的单硬脂酸甘油酯和优选≥3.0且≤70.0重量％的二硬脂酸甘油酯。例如，组合物可包含≥1.0且≤5.0重量％、优选>2.5且<4.0重量％的单硬脂酸甘油酯。
在根据本发明的组合物中，(b)可例如包含二氧化钛。优选地，组合物包含相对于组合物的总重量计≥1.0且≤5.0重量％、更优选>2.5且<4.0重量％的二氧化钛。二氧化钛可例如具有≥100且≤1000nm、优选≥500且≤1000nm、更优选≥500且≤800nm的通过激光衍射干法试验在Malvern MASTERSIZER 3000上测定的定义为D50的平均粒度。
在本发明的某些实施方案中，成分(b)可包含1-羟基-2-吡啶硫酮锌盐，使得组合物包含相对于组合物的总重量计≥0.1且≤1.0重量％、优选≥0.1且≤0.5重量％的量的1-羟基-2-吡啶硫酮锌盐。
在另一个实施方案中，成分(b)可包含具有式(III)的化合物：
其中各R4、R5和R6单独地为烷基结构部分，优选直链烷基结构部分，优选具有5至25个碳原子的直链烷基结构部分；或烷氧基结构部分，优选具有1至10个碳原子的烷氧基结构部分；
其中R4、R5和R6中的至少一者为烷基结构部分，且优选其中R4、R5和R6中的至少另一者为烷氧基结构部分；
使得组合物包含相对于组合物的总重量计≥0.1且≤1.0重量％、优选≥0.1且≤0.6重量％的量的具有式(III)的化合物。
例如，具有式(III)的化合物可为双(2-羟乙基)十八烷基胺。
如在根据本发明的组合物中使用的聚烯烃可例如选自低密度聚乙烯、聚乙烯塑性体、聚乙烯弹性体、线性低密度聚乙烯、中密度聚乙烯、高密度聚乙烯或聚丙烯，或它们的组合。
在本发明的上下文中，低密度聚乙烯(也称为LDPE)可被理解为乙烯的均聚物或包含≥70.0％衍生自乙烯的结构部分的共聚物，其中LDPE是经由自由基聚合获得的聚合物。
LDPE可经由高压聚合，例如通过在管式反应器或高压釜反应器中聚合，在≥150MPA、更优选≥200MPa、诸如≥200且≤300MPa的压力下来生产。
LDPE可例如具有≥890且≤930kg/m3、优选≥905且≤925kg/m3的密度。LDPE可例如具有在190℃、2.16kg的载荷下测定的≥0.5且≤25.0g/10min、优选≥0.5且≤10.0g/10min、更优选≥1.0且≤5.0g/10min的熔体质量流动速率。
在本发明的上下文中，聚乙烯塑性体(也称为POP)可被理解为乙烯与选自丙烯、1-丁烯、1-己烯、4-甲基戊烯、1-辛烯和它们的混合物的α-烯烃共聚单体的共聚物。优选地，α-烯烃共聚单体可选自1-丁烯、1-己烯和1-辛烯。
POP可例如包含相对于POP的总重量计≥5.0且≤30.0重量％、优选≥10.0且≤20.0重量％的衍生自共聚单体的结构部分。POP可例如包含≥70.0且≤95.0重量％、优选≥80.0且≤90.0重量％的衍生自乙烯的结构部分。优选地，POP包含≥5.0且≤30.0重量％、优选≥10.0且≤20.0重量％的衍生自共聚单体的结构部分，和≥70.0且≤95.0重量％、优选≥80.0且≤90.0重量％的衍生自乙烯的结构部分，其中共聚单体选自1-丁烯、1-己烯和1-辛烯。
POP可例如具有≥850且≤875kg/m3、优选≥855且≤875kg/m3的密度。POP可例如具有在190℃、2.16kg的载荷下测定的≥0.5且≤25.0g/10min、优选≥0.5且≤10.0g/10min、更优选≥1.0且≤5.0g/10min的熔体质量流动速率。
在本发明的上下文中，聚乙烯弹性体(也称为POE)可被理解为乙烯与选自丙烯、1-丁烯、1-己烯、4-甲基戊烯、1-辛烯和它们的混合物的α-烯烃共聚单体的共聚物。优选地，α-烯烃共聚单体可选自1-丁烯、1-己烯和1-辛烯。
POE可例如包含相对于POE的总重量计≥5.0且≤30.0重量％、优选≥10.0且≤20.0重量％的衍生自共聚单体的结构部分。POE可例如包含≥70.0且≤95.0重量％、优选≥80.0且≤90.0重量％的衍生自乙烯的结构部分。优选地，POE包含≥5.0且≤30.0重量％、优选≥10.0且≤20.0重量％的衍生自共聚单体的结构部分，和≥70.0且≤95.0重量％、优选≥80.0且≤90.0重量％的衍生自乙烯的结构部分，其中共聚单体选自1-丁烯、1-己烯和1-辛烯。
POE可例如具有≥876且≤900kg/m3、优选≥885且≤900kg/m3的密度。POE可例如具有在190℃、2.16kg的载荷下测定的≥0.5且≤25.0g/10min、优选≥0.5且≤10.0g/10min、更优选≥1.0且≤5.0g/10min的熔体质量流动速率。
在本发明的上下文中，线性低密度聚乙烯(也称为LLDPE)可被理解为乙烯与选自丙烯、1-丁烯、1-己烯、4-甲基戊烯、1-辛烯和它们的混合物的α-烯烃共聚单体的共聚物。优选地，α-烯烃共聚单体可选自1-丁烯、1-己烯和1-辛烯。
LLDPE可例如包含相对于LLDPE的总重量计≥5.0且≤30.0重量％、优选≥10.0且≤20.0重量％的衍生自共聚单体的结构部分。LLDPE可例如包含≥70.0且≤95.0重量％、优选≥80.0且≤90.0重量％的衍生自乙烯的结构部分。优选地，LLDPE包含≥5.0且≤30.0重量％、优选≥10.0且≤20.0重量％的衍生自共聚单体的结构部分，和≥70.0且≤95.0重量％、优选≥80.0且≤90.0重量％的衍生自乙烯的结构部分，其中共聚单体选自1-丁烯、1-己烯和1-辛烯。
LLDPE可例如具有≥901且≤925kg/m3、优选≥910且≤925kg/m3的密度。LLDPE可例如具有在190℃、2.16kg的载荷下测定的≥0.5且≤25.0g/10min、优选≥0.5且≤10.0g/10min、更优选≥1.0且≤5.0g/10min的熔体质量流动速率。
在本发明的上下文中，中密度聚乙烯(也称为MDPE)可被理解为乙烯与选自丙烯、1-丁烯、1-己烯、4-甲基戊烯、1-辛烯和它们的混合物的α-烯烃共聚单体的共聚物。优选地，α-烯烃共聚单体可选自1-丁烯、1-己烯和1-辛烯。
MDPE可例如包含相对于MDPE的总重量计≥1.0且≤15.0重量％、优选≥2.0且≤10.0重量％的衍生自共聚单体的结构部分。MDPE可例如包含≥85.0且≤99.0重量％、优选≥90.0且≤98.0重量％的衍生自乙烯的结构部分。优选地，MDPE包含≥1.0且≤15.0重量％、优选≥2.0且≤10.0重量％的衍生自共聚单体的结构部分，和≥85.0且≤99.0重量％、优选≥90.0且≤98.0重量％的衍生自乙烯的结构部分，其中共聚单体选自1-丁烯、1-己烯和1-辛烯。
MDPE可例如具有≥926且≤940kg/m3、优选≥930且≤940kg/m3的密度。MDPE可例如具有在190℃、2.16kg的载荷下测定的≥0.5且≤25.0g/10min、优选≥0.5且≤10.0g/10min、更优选≥1.0且≤5.0g/10min的熔体质量流动速率。
在本发明的上下文中，高密度聚乙烯(也称为HDPE)可被理解为乙烯的均聚物或乙烯与选自丙烯、1-丁烯、1-己烯、4-甲基戊烯、1-辛烯和它们的混合物的α-烯烃共聚单体的共聚物。优选地，α-烯烃共聚单体可选自1-丁烯、1-己烯和1-辛烯。
HDPE可例如包含相对于HDPE的总重量计≥1.0且≤10.0重量％、优选≥2.0且≤5.0重量％的衍生自共聚单体的结构部分。HDPE可例如包含≥90.0且≤99.0重量％、优选≥95.0且≤98.0重量％的衍生自乙烯的结构部分。优选地，HDPE包含≥1.0且≤10.0重量％、优选≥2.0且≤5.0重量％的衍生自共聚单体的结构部分，和≥90.0且≤99.0重量％、优选≥95.0且≤98.0重量％的衍生自乙烯的结构部分，其中共聚单体选自1-丁烯、1-己烯和1-辛烯。
HDPE可例如具有≥941且≤975kg/m3、优选≥941且≤965kg/m3的密度。HDPE可例如具有在190℃、2.16kg的载荷下测定的≥0.5且≤25.0g/10min、优选≥0.5且≤10.0g/10min、更优选≥1.0且≤5.0g/10min的熔体质量流动速率。
在本发明的上下文中，聚丙烯(也称为PP)可被理解为丙烯均聚物、丙烯与α-烯烃的共聚物或多相丙烯共聚物。
优选地，聚丙烯选自丙烯均聚物和丙烯共聚物的组，丙烯共聚物包含衍生自丙烯以及选自乙烯和具有≥4且≤12个碳原子的α-烯烃的组的一种或多种共聚单体的结构部分。
优选地，丙烯共聚物包含基于丙烯共聚物计≤10重量％、例如≥1.0且≤7.0重量％的量的衍生自选自乙烯和具有≥4且≤12个碳原子的α-烯烃的组的一种或多种共聚单体的结构部分，其中重量％使用13C NMR测定。例如，丙烯共聚物包含衍生自选自乙烯、1-丁烯、1-戊烯、1-己烯、4-甲基-1-戊烯、1-庚烯、1-辛烯、1-癸烯和1-十二烯的组的一种或多种共聚单体的结构部分，优选衍生自乙烯的结构部分。
聚丙烯和合成聚丙烯的方法是已知的。丙烯均聚物通过在合适的聚合条件下使丙烯聚合获得。丙烯共聚物通过在合适的聚合条件下使丙烯与一种或多种其它共聚单体、例如乙烯共聚获得。
丙烯均聚物、丙烯共聚物和多相丙烯共聚物可通过任何已知的聚合技术以及利用任何已知的聚合催化剂体系来制得。关于技术，可提及淤浆聚合、溶液聚合或气相聚合；关于催化剂体系，可提及齐格勒-纳塔(Ziegler-Natta)、茂金属或单位点催化剂体系。全部是自身在本领域已知的。
优选地，聚丙烯具有根据ASTM D1238(2013)在230℃的温度在2.16kg的载荷下测定的≥0.50且≤8.0g/10min、更优选≥0.70且≤5.0g/10min、最优选≥1.0且≤4.0g/10min的熔体质量流动速率。
在本发明的上下文中，聚烯烃的密度可根据ASTM D792(2008)测定。熔体质量流动速率可根据ASTM D1238(2013)测定。重均分子量Mw和数均分子量Mn可根据ASTM D6474(2012)测定。共聚单体的含量和类型可使用13C核磁共振在配备有在125℃下运行的低温冷却探头的Bruker Avance 500谱仪上测定，其中样品在130℃下溶解于含有DBPC作为稳定剂的C2D2Cl4中。
组合物可例如包含相对于组合物的总重量计≥80.0重量％的聚烯烃，优选≥90.0重量％、更优选≥90.0且≤99.9重量％的聚烯烃。
在某些实施方案中，本发明还涉及包含组合物的制品，优选其中制品为膜、片材或模制物。
本发明还涉及根据式(I)的化合物或它们的混合物的用途，
其中：
各R1、R2和R3单独地为羟基结构部分或根据式(II)的结构部分：
其中n为≥6且≤25的整数；
且其中R1、R2和R3中的至少一者为羟基结构部分；
用来提高聚烯烃组合物、优选聚乙烯组合物针对H1N1的抗病毒率、针对新冠病毒(Sars-Cov-2)的抗病毒率、针对大肠杆菌的抗菌率和/或针对金黄色葡萄球菌的抗菌率。
本发明的另一个实施方案还涉及根据权利要求15的包含根据本发明的组合物的制品用来降低污染物的细菌和/或病毒传播能力的用途，优选用来降低H1N1传播能力、新冠病毒传播能力、大肠杆菌传播能力和/或金黄色葡萄球菌传播能力。
根据本发明的抗菌率或抗病毒率的测定可通过使用针对H1N1的ISO 21702(2019)的方法以及针对大肠杆菌和金黄色葡萄球菌的ISO 22196(2011)的方法来进行，其中抗病毒率或(c.q.)抗菌率经由下式测定：
其中AR为抗病毒率或抗菌率(视情况而定)，且其中R和At按照ISO21702或ISO22196的方法测定(视情况而定)。
现将通过以下非限制性实施例说明本发明。
在与本发明相关的工作中进行的实验中，使用如下表I中列举的材料。
表I：材料
使用上述材料，首先在双螺杆挤出机Coperion ZSK 26Mc上，利用以下温度分布，根据下表分配制备共混物。
| 区域1 | 区域2 | 区域3 | 区域4 | 区域5 | 区域6 | 区域7 |
| 20℃ | 40℃ | 160℃ | 160℃ | 170℃ | 170℃ | 180℃ |
| 区域8 | 区域9 | 区域10 | 区域11 | 口模温度 | 螺杆速度 | 通量 |
| 180℃ | 200℃ | 200℃ | 200℃ | 200℃ | 300rpm | 15kg/h |
使用Labtech LF400-COEX吹塑膜机，利用2mm模隙生产了厚度为50μm的单层膜。加工条件为210℃，吹胀比2.5，且输出为5kg/h，根据下表II中的配方。
表II：实验配方
| 实施例 | LLDPE | GMS40 | GMS100 | TiO2-A | TiO2-B | AS1800 | HPT-Zn |
| 1 | 100.0 | ||||||
| 2 | 94.0 | 3.5 | 2.5 | ||||
| 3 | 96.5 | 1.0 | 2.5 | ||||
| 4 | 96.8 | 0.7 | 2.5 | ||||
| 5 | 98.0 | 2.0 | |||||
| 6 | 96.5 | 3.5 | |||||
| 7 | 97.5 | 2.5 | |||||
| 8 | 96.5 | 3.5 | |||||
| 9 | 98.0 | 2.0 | |||||
| 10 | 96.5 | 3.5 | |||||
| 11 | 98.0 | 2.0 | |||||
| 12 | 95.5 | 2.0 | 2.5 | ||||
| 13 | 94.0 | 3.5 | 2.5 | ||||
| 14 | 97.0 | 2.5 | 0.5 | ||||
| 15 | 99.9 | 0.1 | |||||
| 16 | 99.7 | 0.3 |
表II中的值表示相对于配方总重量计的重量％。
使用按照上文表II的配方中每一者生产的膜，根据如上文所述方法测定抗病毒和抗菌性质。抗病毒和抗菌性质的测定结果呈现于下表III中。
表III：膜的抗病毒和抗菌性质
在上表中，如根据说明书中概述的方法测定，值表示抗病毒率或抗菌率AR，以％表示。
Claims (17)
1.组合物，其包含：
(a)聚烯烃；和
(b)具有抗病毒和抗菌功能的化合物或配制物。
2.根据权利要求1所述的组合物，其中(b)包含根据式(I)的化合物或它们的混合物：
其中各R1、R2和R3单独地为羟基结构部分或根据式(II)的结构部分：
其中n为≥6且≤25的整数；
且其中R1、R2和R3中的至少一者为羟基结构部分。
3.根据权利要求1-2中任一项所述的组合物，其中(b)包含单烷酸甘油酯，二烷酸甘油酯，或包含单烷酸甘油酯和二烷酸甘油酯的混合物。
4.根据权利要求3所述的组合物，其中所述烷酸酯结构部分各自是相同的并且选自1-辛酸酯、1-壬酸酯、1-癸酸酯、1-十一烷酸酯、1-十二烷酸酯、1-十三烷酸酯、1-十四烷酸酯、1-十五烷酸酯、1-十六烷酸酯、1-十七烷酸酯、1-十八烷酸酯、1-十九烷酸酯、1-二十烷酸酯、1-二十一烷酸酯、1-二十二烷酸酯、1-二十三烷酸酯和1-二十四烷酸酯，优选其中所述烷酸酯结构部分选自1-十六烷酸酯、1-十八烷酸酯和1-二十烷酸酯。
5.根据权利要求3-4所述的组合物，其中(b)包含单烷酸甘油酯和二烷酸甘油酯的混合物，其中所述混合物包含≥30.0且≤95.0重量％的所述单烷酸甘油酯和优选≥3.0且≤70.0重量％的所述二烷酸甘油酯。
6.根据权利要求2-5中任一项所述的组合物，其中所述组合物包含相对于所述组合物的总重量计≥1.0且≤5.0重量％、优选>2.5且<4.0重量％的具有式(I)的化合物或它们的混合物。
7.根据权利要求1-6中任一项所述的组合物，其中(b)包含二氧化钛。
8.根据权利要求7所述的组合物，其中所述组合物包含相对于所述组合物的总重量计≥1.0且≤5.0重量％、优选>2.5且<4.0重量％的所述二氧化钛。
9.根据权利要求7-8中任一项所述的组合物，其中所述二氧化钛具有通过激光衍射干法试验在Malvern MASTERSIZER 3000上测定的≥100且≤1000nm的定义为D50的平均粒度。
10.根据权利要求1-9中任一项所述的组合物，其中(b)包含1-羟基-2-吡啶硫酮锌盐，使得所述组合物包含相对于所述组合物的总重量计≥0.1且≤1.0重量％的量的1-羟基-2-吡啶硫酮锌盐。
11.根据权利要求1-10中任一项所述的组合物，其中(b)包含具有式(III)的化合物：
其中各R4、R5和R6单独地为烷基结构部分，优选直链烷基结构部分，优选具有5至25个碳原子的直链烷基结构部分；或烷氧基结构部分，优选具有1至10个碳原子的烷氧基结构部分；
其中R4、R5和R6中的至少一者为烷基结构部分，且优选其中R4、R5和R6中的至少另一者为烷氧基结构部分；
使得所述组合物包含相对于所述组合物的总重量计≥0.1且≤1.0重量％的量的所述具有式(III)的化合物。
12.根据权利要求11所述的组合物，其中所述具有式(III)的化合物为双(2-羟乙基)十八烷基胺。
13.根据权利要求1-12中任一项所述的组合物，其中所述聚烯烃选自低密度聚乙烯、聚乙烯塑性体、聚乙烯弹性体、线性低密度聚乙烯、中密度聚乙烯、高密度聚乙烯或聚丙烯，或它们的组合。
14.根据权利要求1-13中任一项所述的组合物，其中所述组合物包含相对于所述组合物的总重量计≥80.0重量％的所述聚烯烃，优选≥90.0重量％、更优选≥90.0且≤99.9重量％的所述聚烯烃。
15.包含根据权利要求1-14中任一项所述的组合物的制品，优选其中所述制品为膜、片材或模制物。
16.根据式(I)的化合物或它们的混合物的用途：
其中：
各R1、R2和R3单独地为羟基结构部分或根据式(II)的结构部分：
其中n为≥6且≤25的整数；
且其中R1、R2和R3中的至少一者为羟基结构部分；
用来提高聚烯烃组合物、优选聚乙烯组合物针对H1N1的抗病毒率、针对新冠病毒的抗病毒率、针对大肠杆菌的抗菌率和/或针对金黄色葡萄球菌的抗菌率。
17.根据权利要求15所述的制品用来降低污染物的细菌和/或病毒传播能力的用途，优选用来降低H1N1传播能力、新冠病毒传播能力、大肠杆菌传播能力和/或金黄色葡萄球菌传播能力。