CN116864560A - 一种光伏板基板 - Google Patents
一种光伏板基板 Download PDFInfo
- Publication number
- CN116864560A CN116864560A CN202310731616.5A CN202310731616A CN116864560A CN 116864560 A CN116864560 A CN 116864560A CN 202310731616 A CN202310731616 A CN 202310731616A CN 116864560 A CN116864560 A CN 116864560A
- Authority
- CN
- China
- Prior art keywords
- glass fiber
- polymer coating
- photovoltaic panel
- core layer
- panel substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明属于太阳能电池组件技术领域，具体公开了一种光伏板基板，其包括玻纤芯层，所述玻纤芯层的上表面喷涂有第一高分子聚合物涂层，所述玻纤芯层的下表面喷涂有第二高分子聚合物涂层；所述玻纤芯层包括两层玻璃纤维复合毡，两层所述玻璃纤维复合毡之间通过聚氨酯粘合剂连接；所述玻纤芯层、所述第一高分子聚合物涂层和所述第二高分子聚合物涂层通过模压发泡成型为一体结构。采用本发明，既能使得产品具有较高的韧性和弯曲性能，能够有效地避免光伏板在使用过程中产生破裂和开裂等问题，又能使得产品具有较高的强度和耐候性能，能够在各种恶劣环境下保持材料的稳定性能；并且，该光伏板基板的制作工艺简单，成本低廉，易于推广和应用。
Description
技术领域
本发明属于太阳能电池组件技术领域，具体涉及一种光伏板基板。
背景技术
随着科技的发展和进步，人类对于能源的需求也在急速地增长，太阳能作为一种可再生清洁能源受到广泛的关注和研究，关于太阳能电池和其发电组件的研究和发展也受到越来越多人的关注。太阳能电池组件是由太阳能电池片串并联，再使用钢化玻璃、封装胶膜和基板对其进行组装和保护。其中，基板位于太阳能电池组件背面的最外层，对电池片起到保护和支撑作用。为了使太阳能电池保持最佳的工作状态并维持最佳的使用寿命，基板应具有可靠的电气绝缘性、水汽阻隔性和良好的耐老化性，其中，优异的水汽阻隔性和耐水解性能是衡量基板性能好坏的重要指标。
目前聚对苯二甲酸乙二醇酯(PET)基板因其具有强度高、耐候性好、热稳定性强等优点成为现阶段市面上的主流基板。但PET也存在韧性及抗弯曲性能欠佳、水汽透过率高、耐水解、耐候性能差的缺点，从而光伏板在使用过程中产生破裂和开裂等问题，且在各种恶劣环境下难以保持材料的稳定性能。
发明内容
本发明的目的是提供一种既能满足基板使用的基本力学性能要求，又具备高韧性、高抗弯强度、高水汽阻隔性、耐水解性能、耐候性能的光伏板基板。
为了解决上述技术问题，本发明采用如下技术方案：
一种光伏板基板，其包括玻纤芯层，所述玻纤芯层的上表面喷涂有第一高分子聚合物涂层，所述玻纤芯层的下表面喷涂有第二高分子聚合物涂层；所述玻纤芯层包括两层玻璃纤维复合毡，两层所述玻璃纤维复合毡之间通过聚氨酯粘合剂连接；所述玻纤芯层、所述第一高分子聚合物涂层和所述第二高分子聚合物涂层通过模压发泡成型为一体结构。
作为本发明的优选方案，所述玻璃纤维复合毡的克重为250g/m2，所述聚氨酯粘合剂的克重为1200g/m2。
作为本发明的优选方案，所述玻璃纤维复合毡由玻璃纤维短切原丝毡和玻璃纤维连续原丝毡两种毡体有机复合而成。
作为本发明的优选方案，所述第一高分子聚合物涂层为聚酰亚胺(PI)、聚乙烯醇(PVA)或多元醇与异氰酸酯混合物；所述第二高分子聚合物涂层为聚酰亚胺(PI)、聚乙烯醇(PVA)或多元醇与异氰酸酯混合物。
作为本发明的优选方案，所述第一高分子聚合物涂层和所述第二高分子聚合物涂层均为多元醇与异氰酸酯混合物。
作为本发明的优选方案，所述多元醇与异氰酸酯混合物中的多元醇与异氰酸酯按照1:1.5的比例混合。
作为本发明的优选方案，所述第一高分子聚合物涂层的克重均为350g/m2～500g/m2；所述第二高分子聚合物涂层的克重为350g/m2～500g/m2。
作为本发明的优选方案，所述第一高分子聚合物涂层远离所述玻纤芯层的一面覆设有第一装饰层；所述第二高分子聚合物涂层远离所述玻纤芯层的一面覆设有第二装饰层。
作为本发明的优选方案，所述第一装饰层为柔性纤维PET类面料、柔性纤维PP类面料、或丙纶与玻纤混纺面料；所述第二装饰层为柔性纤维PET类面料、柔性纤维PP类面料、或丙纶与玻纤混纺面料。
作为本发明的优选方案，所述第一装饰层的厚度为0.3mm～2mm；所述第二装饰层的厚度为0.3mm～2mm。
实施本发明提供的一种光伏板基板，与现有技术相比，其有益效果在于：
本发明的光伏板基板通过玻纤芯层、第一高分子聚合物涂层和第二高分子聚合物涂层有机复合而成，既能使得产品具有较高的韧性和弯曲性能，能够有效地避免光伏板在使用过程中产生破裂和开裂等问题，又能使得产品具有较高的强度和耐候性能，能够在各种恶劣环境下保持材料的稳定性能；并且，该光伏板基板的制作工艺简单，成本低廉，易于推广和应用。
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例的附图作简单地介绍。
图1是本发明实施例的光伏板基板的结构示意图；
图2是本发明实施例的光伏板基板覆设装饰层后的结构示意图。
图中标记：
1、玻纤芯层；2、第一高分子聚合物涂层；3、第二高分子聚合物涂层；4、第一装饰层；5、第二装饰层；11、聚氨酯粘合剂；12、玻璃纤维复合毡。
具体实施方式
下面详细描述本发明的实施例，所述实施例的示例在附图中示出，其中自始至终相同或类似的标号表示相同或类似的元件或具有相同或类似功能的元件。下面通过参考附图描述的实施例是示例性的，仅用于解释本发明，而不能理解为对本发明的限制。
在本发明的描述中，需要理解的是，涉及到方位描述，例如上、下、前、后、左、右等指示的方位或位置关系为基于附图所示的方位或位置关系，仅是为了便于描述本发明和简化描述，而不是指示或暗示所指的装置或元件必须具有特定的方位、以特定的方位构造和操作，因此不能理解为对本发明的限制。
在本发明的描述中，若干的含义是一个或者多个，多个的含义是两个以上，大于、小于、超过等理解为不包括本数，以上、以下、以内等理解为包括本数。如果有描述到第一、第二只是用于区分技术特征为目的，而不能理解为指示或暗示相对重要性或者隐含指明所指示的技术特征的数量或者隐含指明所指示的技术特征的先后关系。
本发明的描述中，除非另有明确的限定，设置、安装、连接等词语应做广义理解，所属技术领域技术人员可以结合技术方案的具体内容合理确定上述词语在本发明中的具体含义。
如图1所示，本发明实施例的光伏板基板，其包括玻纤芯层1，所述玻纤芯层1的上表面喷涂有第一高分子聚合物涂层2，所述玻纤芯层1的下表面喷涂有第二高分子聚合物涂层3；所述玻纤芯层1包括两层玻璃纤维复合毡12，两层所述玻璃纤维复合毡12之间通过聚氨酯粘合剂11连接；所述玻纤芯层1、所述第一高分子聚合物涂层2和所述第二高分子聚合物涂层3通过模压发泡成型为一体结构。
本实施例中，所述玻璃纤维复合毡12由玻璃纤维短切原丝毡和玻璃纤维连续原丝毡两种毡体有机复合而成，使短切毡和连续毡的不同性能相互渗透，优势互补。
下面，针对本实施例玻纤芯层1的结构及克重配置，与不同复合结构及不同克重的对比实例进行机械性能验证，见下表一。
表一：本实施例与对比实例的机械性能数据
表一中，GF表示为玻璃纤维复合毡12，PU表示为聚氨酯粘合剂11，200gPU*2表示为200g聚氨酯粘合剂11分两次涂覆，200gPU*4表示为200g聚氨酯粘合剂11分四次涂覆。
从表一可以看出，当本实施例的玻纤芯层1采用250gGF+1200gPU+250gGF的配置，也即所述玻璃纤维复合毡12的克重优选为250g/m2，所述聚氨酯粘合剂11的克重为1200g/m2，其产生的机械性能的综合效果更佳，使得产品具有较高的韧性和弯曲性能，能够有效地避免光伏板在使用过程中产生破裂和开裂等问题。
并且，采用模压发泡成型工艺，将第一高分子聚合物涂层2和第二高分子聚合物涂层3复合到玻纤芯层1的上下表面形成为一体，能够进一步提高了产品的强度及韧性，同时使得产品具有较高的水汽阻隔性、耐腐蚀性和耐候性等优点，能够在各种恶劣环境下保持材料的稳定性能。
此外，本发明实施例的光伏板基板的制作工艺简单，成本低廉，易于推广和应用。
示例性的，所述第一高分子聚合物涂层2为聚酰亚胺(PI)、聚乙烯醇(PVA)或多元醇与异氰酸酯混合物；所述第二高分子聚合物涂层3为聚酰亚胺(PI)、聚乙烯醇(PVA)或多元醇与异氰酸酯混合物。优选地，所述第一高分子聚合物涂层2和所述第二高分子聚合物涂层3均为多元醇与异氰酸酯混合物；且多元醇与异氰酸酯按照1:1.5的比例混合。所述第一高分子聚合物涂层2的克重均为350g/m2～500g/m2；所述第二高分子聚合物涂层3的克重为350g/m2～500g/m2。
示例性的，如图2所示，为满足产品表面外观及防护的要求，所述第一高分子聚合物涂层2远离所述玻纤芯层1的一面覆设有第一装饰层4；所述第二高分子聚合物涂层3远离所述玻纤芯层1的一面覆设有第二装饰层5。本实施例中，所述第一装饰层4为柔性纤维PET类面料、柔性纤维PP类面料、或丙纶与玻纤混纺面料；所述第二装饰层5为柔性纤维PET类面料、柔性纤维PP类面料、或丙纶与玻纤混纺面料。进一步地，所述第一装饰层4的厚度为0.3mm～2mm；所述第二装饰层5的厚度为0.3mm～2mm。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和替换，这些改进和替换也应视为本发明的保护范围。
Claims (10)
1.一种光伏板基板，其特征在于，包括玻纤芯层，所述玻纤芯层的上表面喷涂有第一高分子聚合物涂层，所述玻纤芯层的下表面喷涂有第二高分子聚合物涂层；所述玻纤芯层包括两层玻璃纤维复合毡，两层所述玻璃纤维复合毡之间通过聚氨酯粘合剂连接；所述玻纤芯层、所述第一高分子聚合物涂层和所述第二高分子聚合物涂层通过模压发泡成型为一体结构。
2.如权利要求1所述的一种光伏板基板，其特征在于，所述玻璃纤维复合毡的克重为250g/m2，所述聚氨酯粘合剂的克重为1200g/m2。
3.如权利要求1所述的一种光伏板基板，其特征在于，所述玻璃纤维复合毡由玻璃纤维短切原丝毡和玻璃纤维连续原丝毡两种毡体有机复合而成。
4.如权利要求1所述的一种光伏板基板，其特征在于，所述第一高分子聚合物涂层为聚酰亚胺、聚乙烯醇或多元醇与异氰酸酯混合物；所述第二高分子聚合物涂层为聚酰亚胺、聚乙烯醇或多元醇与异氰酸酯混合物。
5.如权利要求4所述的一种光伏板基板，其特征在于，所述第一高分子聚合物涂层和所述第二高分子聚合物涂层均为多元醇与异氰酸酯混合物。
6.如权利要求5所述的一种光伏板基板，其特征在于，所述多元醇与异氰酸酯混合物中的多元醇与异氰酸酯按照1:1.5的比例混合。
7.如权利要求1所述的一种光伏板基板，其特征在于，所述第一高分子聚合物涂层的克重均为350g/m2～500g/m2；所述第二高分子聚合物涂层的克重为350g/m2～500g/m2。
8.如权利要求1至7所述的一种光伏板基板，其特征在于，所述第一高分子聚合物涂层远离所述玻纤芯层的一面覆设有第一装饰层；所述第二高分子聚合物涂层远离所述玻纤芯层的一面覆设有第二装饰层。
9.如权利要求8所述的一种光伏板基板，其特征在于，所述第一装饰层为柔性纤维PET类面料、柔性纤维PP类面料、或丙纶与玻纤混纺面料；所述第二装饰层为柔性纤维PET类面料、柔性纤维PP类面料、或丙纶与玻纤混纺面料。
10.如权利要求9所述的一种光伏板基板，其特征在于，所述第一装饰层的厚度为0.3mm～2mm；所述第二装饰层的厚度为0.3mm～2mm。