CN116855955A - 一种用于压铸铝合金的弱酸性清洗剂 - Google Patents
一种用于压铸铝合金的弱酸性清洗剂 Download PDFInfo
- Publication number
- CN116855955A CN116855955A CN202310673909.2A CN202310673909A CN116855955A CN 116855955 A CN116855955 A CN 116855955A CN 202310673909 A CN202310673909 A CN 202310673909A CN 116855955 A CN116855955 A CN 116855955A
- Authority
- CN
- China
- Prior art keywords
- die
- aluminum alloy
- cleaning agent
- weakly acidic
- acidic cleaning
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于压铸铝合金的弱酸性清洗剂，涉及压铸铝合金清洗剂技术领域，包括以下重量百分比的原料：弱酸25～40％、过氧化氢10～20％、铝盐10～20％、余量为水。本发明提供的用于压铸铝合金的弱酸性清洗剂能够能够有效地去除压铸铝合金材料表面的硅和还原金属成分，如铁、铜、锰、镁、锌和镍，在压铸铝合金材料的化学表面处理过程中，不会产生有毒物质，如对人体有害的氧化氮和氟化氢，另外还能溶解材料表面的残油。
Description
技术领域
本发明属于压铸铝合金清洗剂技术领域，具体涉及一种用于压铸铝合金的弱酸性清洗剂。
背景技术
铝合金是工业上应用最广泛的有色结构材料，己广泛应用于航空、航天、汽车、机械制造、造船、化工等行业。目前对压铸铝的表面进行去除氧化物和除油的过程中，大多数是采用酸性清洗的方式进行清洗。一方面，因为铝的化学性质较活泼，极易与常见的无机酸等发生剧烈的化学反应，在反应过程中，铝的基材很容易被腐蚀溶解到清洗剂中，但是因为压铸铝都存在一定的其他金属及非金属成分，这部分物质主要以硅元素、锰元素及铜元素为主，而这部分物质的化学性质较稳定，难与酸发生反应，因此经过酸性清洗后，这部分物质会以“黑灰”的形式出现在材质表面。由于无机酸酸性较强，极易造成压铸铝的表面的腐蚀。针对该缺陷，现有的技术中采用硝酸和氟化氢对压铸铝的表面的黑灰进行处理，虽然能够去除，但是会产生有毒物质，如对人体有害的氮氧化物和氟化氢。
发明内容
为了克服现有技术的不足，本发明的目的之一在于提供一种用于压铸铝合金的弱酸性清洗剂，能够有效地去除压铸铝合金材料表面的硅和还原金属成分，如铁、铜、锰、镁、锌和镍，在压铸铝合金材料的化学表面处理过程中，不会产生有毒物质，如对人体有害的氧化氮和氟化氢，另外还能溶解材料表面的残油。
本发明的目的之二在于提供一种用于压铸铝合金的弱酸性清洗剂的制备方法，制备方法简单，易于操作。
本发明的目的之三在于提供一种压铸铝合金表面处理方法，使用该表面处理方法能够有效地去除压铸铝合金材料表面的硅和还原金属成分，表面清洗比较干净。
本发明的目的之一采用如下技术方案实现：
一种用于压铸铝合金的弱酸性清洗剂，以下重量百分比的原料：弱酸25～40％、过氧化氢10～20％、铝盐10～20％、余量为水。
进一步地，所述弱酸为柠檬酸、醋酸、草酸中的一种或其混合物。
进一步地，所述铝盐为偏氢氧化铝、氢氧化铝中的一种。
进一步地，还包括重量百分比为5～10％表面活性剂。
进一步地，所述表面活性剂为阴离子表面活性剂，所述阴离子表面活性剂为十六烷基硫酸钠、硬脂酸钠、二辛基琥珀酸磺酸钠中的一种。
进一步地，还包括重量百分比为2～5％缓蚀剂。
进一步地，还包括重量百分比为1～2％铝离子螯合剂。
进一步地，所述铝离子螯合剂为乙二胺四醋酸、三乙醇胺、柠檬酸钠、葡萄糖酸钠中的一种或两种以上组合物。
进一步地，还包括重量百分比为1～2％铝离子螯合剂。
本发明的目的之二采用如下技术方案实现：
一种用于压铸铝合金的弱酸性清洗剂的制备方法，包括以下步骤：
S1、将所述弱酸和所述过氧化氢进行混合，得到混合液；
S2、将所述铝盐和水加入所述混合液中混合，得到所述用于压铸铝合金的弱酸性清洗剂。
本发明的目的之三采用如下技术方案实现：
一种压铸铝合金表面处理方法，将所述压铸铝合金浸入上述任一项所述的一种用于压铸铝合金的弱酸性清洗剂中以去除硅和还原金属元素。
相比现有技术，本发明的有益效果在于：
(1)本发明提供的一种用于压铸铝合金的弱酸性清洗剂，清洗剂在清洗过程中，其中的弱酸不会对压铸铝合金有腐蚀作用，并且提供酸性环境，能够溶解三氧化二铝及其他还原金属氧化物，且能提供电离氢离子，在过氧化氢的作用下，还原金属能够和过氧化氢发生反应，生成还原金属氧化物，更容易被弱酸去除；过氧化氢还能够溶解非金属硅，使硅被氧化成二氧化硅，二氧化硅在铝盐的吸附作用下能够被脱除，从而能够有效地去除压铸铝合金材料表面的硅和还原金属成分，如铁、铜、锰、镁、锌和镍，并且清洗后的压铸铝合金表面光滑。
(2)本发明提供的一种用于压铸铝合金的弱酸性清洗剂，在清除剂中添加阴离子表面活性剂能够有助于去除压铸铝合金表面的油污和污垢，而添加铝离子螯合剂能够使压铸铝合金表面的铝元素和铝离子螯合剂配位，防止局部清洗干净后，铝又被防止氧化和腐蚀，提高清洗的效率。
具体实施方式
下面结合具体实施例，对本发明做进一步描述，需要说明的是，在不相冲突的前提下，以下描述的各实施例之间或各技术特征之间可以任意组合形成新的实施例。
实施例1
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、余量为水。
本实施例中S1、将醋酸和过氧化氢进行混合，得到混合液；S2、将偏氢氧化铝和水加入混合液中混合，得到用于压铸铝合金的弱酸性清洗剂。
实施例2
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：柠檬酸30％、过氧化氢10％、氢氧化铝20％、余量为水。
实施例3
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：草酸40％、过氧化氢20％、偏氢氧化铝10％、余量为水。
实施例4
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、硬脂酸钠10％、余量为水。
实施例5
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、十六烷基硫酸钠8％、余量为水。
实施例6
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、二辛基琥珀酸磺酸钠5％、余量为水。
实施例7
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、硬脂酸钠10％、乙二胺四醋酸2％、余量为水。
实施例8
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、硬脂酸钠10％、三乙醇胺2％、余量为水。
实施例9
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、硬脂酸钠10％、柠檬酸钠1％、余量为水。
实施例10
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、硬脂酸钠10％、葡萄糖酸钠1％、余量为水。
实施例11
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、硬脂酸钠10％、三乙醇胺2％、5％缓蚀剂、余量为水。
实施例12
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、硬脂酸钠10％、三乙醇胺5％、5％缓蚀剂、余量为水。
实施例13
本实施例提供一种用于压铸铝合金的弱酸性清洗剂，包括以下重量百分比的原料：醋酸25％、过氧化氢15％、偏氢氧化铝12％、硬脂酸钠10％、三乙醇胺2％、3％缓蚀剂钼酸铵、余量为水。
对比例1
与实施例1～13不同的是，对比例1提供的一种用于压铸铝合金的弱酸性清洗剂中不包括过氧化氢组分，其它组分与实施例1相同。
对比例2
与实施例1～13不同的是，对比例2提供的一种用于压铸铝合金的弱酸性清洗剂中不包括铝盐组分，其它组分与实施例1相同。
对比例3
与实施例1～13不同的是，对比例3提供的一种用于压铸铝合金的弱酸性清洗剂中不包括过氧化氢、铝盐组分，其它组分与实施例1相同。
实施例14
本实施例一种压铸铝合金表面处理方法，将表面黑灰程度大致一样的压铸铝合金浸入实施例1～13和对比例1～3提供的一种用于压铸铝合金的弱酸性清洗剂中，浸泡时间30min，浸泡完成，用水冲洗干净，观察压铸铝合金表面的黑灰的清除效果，以压铸铝合金的干净光亮的程度进行比较分析，以未清洗的压铸铝合金的情况作为空白对照，实施例1～13以及对比例1～3的清洗效果如表1所示。
表1测试结果
通过表1可以看出，实施例1～13清洗效果均很好，压铸铝合金表面干净光亮，并且表面光滑，在清洗完成后，不会对压铸铝合金表面造成腐蚀；而未清洗的压铸铝合金的表面大面积黑灰，对比例1由于不添加过氧化氢组分，铝盐只对压铸铝合金的二氧化硅有吸附作用，表面大面积还是存在黑灰，对比例2由于不添加铝盐组分，过氧化氢能够清除压铸铝合金表面的还原性金属和非金属硅，表面只有局部区域有黑灰，比较干净光亮，对比例3由于不添加过氧化氢、铝盐组分，表面黑灰是少了点，黑灰的存在，表面依然粗糙。
上述实施方式仅为本发明的优选实施方式，不能以此来限定本发明保护的范围，本领域的技术人员在本发明的基础上所做的任何非实质性的变化及替换均属于本发明所要求保护的范围。
Claims (10)
1.一种用于压铸铝合金的弱酸性清洗剂，其特征在于，包括以下重量百分比的原料：弱酸25～40％、过氧化氢10～20％、铝盐10～20％、余量为水。
2.如权利要求1所述的一种用于压铸铝合金的弱酸性清洗剂，其特征在于，所述弱酸为柠檬酸、醋酸、草酸中的一种或其混合物。
3.如权利要求1所述的一种用于压铸铝合金的弱酸性清洗剂，其特征在于，所述铝盐为偏氢氧化铝、氢氧化铝中的一种。
4.如权利要求1所述的一种用于压铸铝合金的弱酸性清洗剂，其特征在于，还包括重量百分比为5～10％表面活性剂。
5.如权利要求4所述的一种用于压铸铝合金的弱酸性清洗剂，其特征在于，所述表面活性剂为阴离子表面活性剂，所述阴离子表面活性剂为十六烷基硫酸钠、硬脂酸钠、二辛基琥珀酸磺酸钠中的一种。
6.如权利要求1所述的一种用于压铸铝合金的弱酸性清洗剂，其特征在于，还包括重量百分比为2～5％缓蚀剂。
7.如权利要求1所述的一种用于压铸铝合金的弱酸性清洗剂，其特征在于，还包括重量百分比为1～2％铝离子螯合剂。
8.如权利要求1所述的一种用于压铸铝合金的弱酸性清洗剂，其特征在于，所述铝离子螯合剂为乙二胺四醋酸、三乙醇胺、柠檬酸钠、葡萄糖酸钠中的一种或两种以上组合物。
9.权利要求1～8任一项所述的一种用于压铸铝合金的弱酸性清洗剂的制备方法，其特征在于，包括以下步骤：
S1、将所述弱酸和所述过氧化氢进行混合，得到混合液；
S2、将所述铝盐和水加入所述混合液中混合，得到所述用于压铸铝合金的弱酸性清洗剂。
10.一种压铸铝合金表面处理方法，其特征在于，将所述压铸铝合金浸入权利要求1～8任一项所述的一种用于压铸铝合金的弱酸性清洗剂中以去除硅和还原金属元素。