CN116535174A - 一种仿沥青快硬自密实窨井盖安装材料 - Google Patents
一种仿沥青快硬自密实窨井盖安装材料 Download PDFInfo
- Publication number
- CN116535174A CN116535174A CN202310535045.8A CN202310535045A CN116535174A CN 116535174 A CN116535174 A CN 116535174A CN 202310535045 A CN202310535045 A CN 202310535045A CN 116535174 A CN116535174 A CN 116535174A
- Authority
- CN
- China
- Prior art keywords
- percent
- asphalt
- inspection well
- well cover
- cover mounting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公布了一种仿沥青快硬自密实窨井盖安装材料，所述本安装材料以10‑30%的普通硅酸盐水泥、10‑30%的低碱度硫铝酸盐水泥、0‑20%的半水石膏或二水石膏、0‑20%的石粉、10‑40%的机制砂或河砂，0.5‑10%的氧化铁黑或炭黑为原料，外加占原料重量百分比为0.02%‑0.2%的减水剂、0.02%‑0.2%的消泡剂、0.02%‑0.2%的增稠剂、0.02%‑0.1%的缓凝剂、0.02%‑0.1%的早强剂，本发明不仅具有自密实施工简便的特点，而且材料颜色仿沥青，施工到路面时与原路面无色差，不影响城市道路的美观，同时材料早强快硬的特点能够在施工后一小时即可开放交通，有效缓解城市交通压力，提高了窨井设施维修改造的效率。
Description
技术领域
本发明属于市政窨井盖维修用安装材料，具体涉及一种仿沥青快硬自密实窨井盖安装材料。
背景技术
“小井盖关乎大民生”。窨井盖是城市基础设施的重要组成部分。井盖安全管理事关城市安全和群众生产生活有序运行。近年来，窨井盖安全管理工作取得一定成效，但一些地方仍存在窨井盖质量参差不齐以及容易破损、下陷、丢失等问题，人员坠井伤亡事故时有发生，严重危害人民群众生命财产安全，对窨井盖的加固改造已经刻不容缓。
在窨井设施维修改造过程中需要对窨井设施重新安装固定，传统的固定材料有沥青材料以及普通砂浆材料。沥青材料的优点是能做到改造后窨井设施周边的固定材料与原路面无色差，但是却有流动度差、难以保证密实度、分层施工反复夯实造成的施工繁琐、具有热塑性导致后期容易出现下陷移位等缺点；另一方面，普通砂浆固定材料也有其施工便捷的优点，但是普通砂浆的缺点也显而易见，包括开放交通时间长容易造成交通压力、窨井设施周边的砂浆固定材料与原路面色差严重、后期强度低且容易开裂等问题。
发明内容
本发明的目的在于提供一种仿沥青快硬自密实窨井盖安装材料，该种材料不仅具有自密实的特点，而且材料颜色仿沥青，施工到路面时与原路面无色差，不影响城市道路的美观，同时材料早强快硬的特点能够在施工后一小时即可开放交通，有效缓解城市交通压力，提高了窨井设施维修改造的效率。
为实现上述目的，本发明采用如下技术方案：
一种仿沥青快硬自密实窨井盖安装材料，本安装材料以10-30%的普通硅酸盐水泥、10-30%的低碱度硫铝酸盐水泥、0-20%的半水石膏或二水石膏、0-20%的石粉、10-40%的机制砂或河砂细骨料，0.5-10%的氧化铁黑或炭黑为原料，外加占原料重量百分比为0.02%-0.2%的减水剂、0.02%-0.2%的消泡剂、0.02%-0.2%的增稠剂、0.02%-0.1%的缓凝剂、0.02%-0.1%的早强剂。
优选的，所述普通硅酸盐水泥强度等级不低于42.5#。
优选的，所述低碱度硫铝酸盐水泥强度等级不低于42.5#。
优选的，所述半水石膏细度不大于0.2mm，半水石膏含量不低于80%，二水石膏含量应不高于4%。
优选的，所述石粉最大粒径不大于0.08mm。
优选的，所述细骨料可以为机制砂或河砂类材料，也可以为其他材质骨料，砂子级配为二区中砂，含粉量不大于5%。
优选的，所述颜料为氧化铁黑或炭黑，最大粒径不大于0.045mm。
优选的，所述减水剂为聚羧酸减水剂，减水率不应低于30%。
优选的，所述消泡剂为聚醚类消泡剂。
优选的，所述增稠剂为羟丙基甲基纤维素醚，粘度不宜高于400。
优选的，所述缓凝剂为酒石酸、无水柠檬酸、葡萄糖酸钠等。
优选的，所述早强剂为锂盐。
有益效果
与现有技术相比，本发明采用普通硅酸盐水泥与低碱度硫铝酸盐水泥复掺，并通过引入颜料的方式使制备出的仿沥青快硬自密实窨井盖安装材料，具有超早强高强、大流动度、色泽仿沥青等特点。既继承了传统安装材料施工便捷、与原路面无色差的优点，又克服了传统安装材料流动度差、早期强度低、易开裂、易下沉等缺点，具有广泛的应用前景。
实施方式
以下结合实施例对本发明的技术方案作进一步的详细介绍，但本发明的保护范围并不仅限于此。
实施例1
一种仿沥青快硬自密实窨井盖安装材料，本安装材料以10-30%的普通硅酸盐水泥、10-30%的低碱度硫铝酸盐水泥、0-20%的半水石膏或二水石膏、0-20%的石粉、10-40%的机制砂或河砂，0.5-10%的氧化铁黑或炭黑为原料，外加占原料重量百分比为0.02%-0.2%的减水剂、0.02%-0.2%的消泡剂、0.02%-0.2%的增稠剂、0.02%-0.1%的缓凝剂、0.02%-0.1%的早强剂。
实施例2
一种仿沥青快硬自密实窨井盖安装材料，本安装材料以10-30%的普通硅酸盐水泥、10-30%的低碱度硫铝酸盐水泥、0-20%的半水石膏或二水石膏、0-20%的石粉、10-40%的机制砂或河砂，0.5-10%的氧化铁黑或炭黑为原料，外加占原料重量百分比为0.02%-0.2%的减水剂、0.02%-0.2%的消泡剂、0.02%-0.2%的增稠剂、0.02%-0.1%的缓凝剂、0.02%-0.1%的早强剂。
所述普通硅酸盐水泥强度等级不低于42.5#，所述低碱度硫铝酸盐水泥强度等级不低于42.5#，所述半水石膏粒径≤0.2mm，半水石膏含量≥80%，二水石膏含量≤4%，所述石粉最大粒径≤0.08mm，所述细骨料为机制砂或河砂类材料，级配为二区中砂，含粉量≤5%，所述氧化铁黑或炭黑，粒径≤0.045mm。
所述减水剂为聚羧酸减水剂，减水率≥30%，所述消泡剂为聚醚类消泡剂，所述增稠剂为羟丙基甲基纤维素醚，粘度≤400，所述缓凝剂为酒石酸、无水柠檬酸、葡萄糖酸钠，所述早强剂为锂盐。
实施例1至2所述仿沥青快硬自密实窨井盖安装材料原料配比见下表1所示。
表1仿沥青快硬自密实窨井盖安装材料原料配比
实施例1至2所述仿沥青快硬自密实窨井盖安装材料性能指标及市售传统窨井盖安装材料的性能见下表2所示。
表2仿沥青快硬自密实窨井盖安装材料性能指标
由表2的数据可以看出，本发明的仿沥青快硬自密实窨井盖安装材料早期、后期强度较高而且具有良好的自密实、微膨胀特性，同时色泽仿沥青。本发明的仿沥青快硬自密实窨井盖安装材料既继承了传统安装材料施工便捷、与原路面无色差的优点，又克服了传统安装材料流动度差、早期强度低、易开裂、易下沉等缺点，应用前景非常广泛。
以上所述，仅是本发明的实施例而已，并非是对本发明作其它形式的限制，任何熟悉本专业的技术人员可能利用上述揭示的技术内容加以变更或改型为等同变化的等效实施例。但凡是未脱离本发明技术方案内容，依据本发明的技术实质对以上实施例所作的任何简单修改、等同变化与改型，仍属于本发明技术方案的保护范围。
Claims (3)
1.一种仿沥青快硬自密实窨井盖安装材料，其特征在于：本安装材料以10-30%的普通硅酸盐水泥、10-30%的低碱度硫铝酸盐水泥、0-20%的半水石膏或二水石膏、0-20%的石粉、10-40%的机制砂或河砂，0.5-10%的氧化铁黑或炭黑为原料，外加占原料重量百分比为0.02%-0.2%的减水剂、0.02%-0.2%的消泡剂、0.02%-0.2%的增稠剂、0.02%-0.1%的缓凝剂、0.02%-0.1%的早强剂。
2.根据权利要求1所述的一种仿沥青快硬自密实窨井盖安装材料，其特征在于：所述普通硅酸盐水泥强度等级不低于42.5#，所述低碱度硫铝酸盐水泥强度等级不低于42.5#，所述半水石膏粒径≤0.2mm，半水石膏含量≥80%，二水石膏含量≤4%，所述石粉最大粒径≤0.08mm，所述细骨料为机制砂或河砂类材料，级配为二区中砂，含粉量≤5%，所述氧化铁黑或炭黑，粒径≤0.045mm。
3.根据权利要求1所述的一种仿沥青快硬自密实窨井盖安装材料，其特征在于：所述减水剂为聚羧酸减水剂，减水率≥30%，所述消泡剂为聚醚类消泡剂，所述增稠剂为羟丙基甲基纤维素醚，粘度≤400，所述缓凝剂为酒石酸、无水柠檬酸、葡萄糖酸钠，所述早强剂为锂盐。