CN1162196C - Technology for making rod-shaped sports tool - Google Patents
Technology for making rod-shaped sports tool Download PDFInfo
- Publication number
- CN1162196C CN1162196C CNB021178321A CN02117832A CN1162196C CN 1162196 C CN1162196 C CN 1162196C CN B021178321 A CNB021178321 A CN B021178321A CN 02117832 A CN02117832 A CN 02117832A CN 1162196 C CN1162196 C CN 1162196C
- Authority
- CN
- China
- Prior art keywords
- embryo
- wooden
- wooden stick
- telescopic
- twill
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a method for making a wooden rod-shaped sports tool, which comprises the following steps: a wooden rod blank is prepared and sheathed with a telescopic twill fiber web sleeve; epoxy resin is added; the wooden rod is wound with a coating belt and is hardened at room temperature; the coating belt is removed; and the finished product is completed. The method has the advantages of hardening at room temperature, unchanged shape of the wooden rod blank, high qualified product rate, simple cutting, no longitudinal seam of the telescopic twill fiber web sleeve; in addition, the method is applicable for the rods with different diameters or in special shapes and has wide application range.
Description
Technical field
The present invention relates to a kind of manufacture method of wooden shaft-like sports requsites.
Background technology
The manufacture method of existing wooden billiard stick sees also Fig. 1 and Fig. 3, and its step is as follows:
1, makes wooden core bar 81: take a wooden core bar 91 with major axis and one first external diameter;
2, coat the made clad 82 of a fiber cloth by pre-soaked resin (Resin Dipped Cloth): cut earlier and be wound in this wooden core bar 91 again, and form a clad 92;
3, cover covers intermediary's material 83: intermediary's material 93 is wound in this clad outer rim;
4, add warm hardening 84: place in the heating furnace 94 and heat, make this carbon cloth hardened forming with 120 to 160 degree Celsius;
5, take off this intermediary's material 85;
6, finish finished product 86.
See also Fig. 2 and Fig. 4, the detailed manufacture process of the fiber cloth 92 of existing further this pre-soaked resin of labor, it is finished by the following step:
(1) sheet-like fiber cloth 821: obtain a sheet fiber cloth 921, fixed size can't elasticity widen;
(2) contain the curing agent 822 that resin pickup and high temperature just can react: this sheet-like fiber cloth 921 is contained resin pickup, and, add the curing agent 922 that high temperature just can react, so, just can not store, produce when selling or transporting hardening phenomenon;
(3) pre-soaked resin fiber cloth finished product 823: so, finish pre-soaked resin fiber cloth finished product, wait for and be sold to the buyer in the future;
(4) store/sell/transport 824: after manufacturing, to actual the use, all have first-class to treat the time, be statically placed in the warehouse or transport by lorry;
(5) be cut into trapezoidal 825: because general billiard stick is coniform, must be cut into one trapezoidally, the seam longitudinally 95 that it is intervolved behind this coniform wooden core bar 81 is smooth.
There is following shortcoming in above-mentioned prior art main:
[1] add warm hardening and cause wooden part bending, fraction defective is too high.Timber is natural material, and the orientation of fiber wherein, Density Distribution and inner slight void be uniformity fully all, and be particularly very responsive to temperature, in case heat to 45 to 60 degree Celsius when above, straight billiard stick can begin bending originally.Temperature is high more, and diastrophic situation is serious more, that is fraction defective improves.On the other hand, in order to enhance productivity, the high more then hardening of resin time of temperature is short more, and output is big more.So, if between 120 to 160 degree Celsius, add warm hardening in a conventional manner, produce in 20000 products, 10000 defective products (because of the hot bending distortion) are arranged approximately, fraction defective is about about 50%, though speed of production is fast, fraction defective is too high.
[2] must be cut into trapezoidally, formality is loaded down with trivial details, and only is applicable to single size, again can residual longitudinal seam.Because billiard stick is generally coniform, if outer surface will be coated, tapering is cut into trapezoidally according to this, and operation is loaded down with trivial details, and only is applicable to single size, if the diameter of another batch rod changes, then will be cut into another ladder type size.In addition, again can residual longitudinal seam 95 at joint, more not attractive in appearance.
[3] can't be applied to the special formed club of irregular surface.If external form such as the Fig. 8 or the club shape shown in Figure 9 of club then can't (or being difficult to) be cut out the pre-soaked resin fiber cloth, be of limited application.
So be necessary to research and develop new product to overcome above-mentioned shortcoming.
Summary of the invention
In order to overcome the above-mentioned shortcoming that existing wooden manufacture of ball-colliding rod exists, the invention provides a kind of manufacture method of wooden shaft-like sports requsites, it at room temperature hardens, and wooden stick's embryo is indeformable, and qualification rate is high.It cuts simple and easy, telescopic twill fiber net does not have longitudinal seam, is applicable to different-diameter or special external form, applied range are arranged.
The technical solution adopted for the present invention to solve the technical problems is:
A kind of manufacture method of wooden shaft-like sports requsites is characterized in that it comprises the following steps:
One, prepare wooden stick's embryo: processing car system one wooden stick's embryo, this wooden stick's embryo generally is the slightly straight round bar shape of tapering;
Two, put telescopic twill fiber net: a telescopic twill fleece cover is placed in the outer rim of this wooden stick's embryo, and this twill fiber net can tighten automatically fits, and afterwards, cuts redundance again;
Three, add epoxy resin: coating or immerse an epoxy resin liquid on wooden stick's embryo of this coating twill fiber net;
Four, twine one and coat band: the outer winding one of whole wooden stick embryo is coated band;
Five, room temperature vulcanizing:, under room temperature environment, harden through a predetermined firm time;
Six, take off this coating band;
Seven, finish finished product.
The manufacture method of aforesaid wooden shaft-like sports requsites, wherein telescopic twill fiber net can be sleeved on rule or the irregular wooden stick embryo of diameter between 5 millimeters to 100 millimeters.
The manufacture method of aforesaid wooden shaft-like sports requsites, wherein the outer surface of wooden stick's embryo has an irregular moulding portion, and this telescopic twill fiber net is can flexible distortion and fit fully.
The invention has the beneficial effects as follows that it at room temperature hardens, wooden stick's embryo is indeformable, and qualification rate is high.It cuts simple and easy, telescopic twill fiber net does not have longitudinal seam, is applicable to different-diameter or special external form, applied range are arranged.
Description of drawings
The present invention is further described below in conjunction with drawings and Examples.
Fig. 1 is the main flow chart of prior art
Fig. 2 is the less important flow chart of prior art
Fig. 3 is the main schematic flow sheet of prior art
Fig. 4 is the less important schematic flow sheet of prior art
Fig. 5 is a flow chart of the present invention
Fig. 6 is a schematic flow sheet of the present invention
Fig. 7 is the partial sectional view of finished product of the present invention
Fig. 8 is a second embodiment of the present invention schematic diagram
Fig. 9 is a third embodiment of the present invention schematic diagram
The figure number explanation:
Prepare wooden stick's embryo 11 and put telescopic twill fiber net 12
Add that epoxy resin 13 twines a coating and is with 14
Room temperature vulcanizing 15 takes off this coating and is with 16
Finish finished product 17 wooden stick's embryos 20
Telescopic twill fiber net 30 hardened layers 40
Epoxy resin liquid 41 coats is with 50
60 second moulding portions 70 of the first moulding portion
Make wooden core bar 81
The clad 82 that coating one is made by the fiber cloth of pre-soaked resin
Sheet-like fiber cloth 821 pre-soaked resin fiber cloth finished products 823
Contain the curing agent 822 that resin pickup and high temperature just react
Store/sell/transport 824 and be cut into trapezoidal 825
Cover covers intermediary's material 83 and adds warm hardening 84
Take off this intermediary's material 85 and finish finished product 86
Sheet-like fiber cloth 921 intermediary's materials 93
The specific embodiment
See also Fig. 5 to Fig. 7, the present invention is the manufacture method of relevant a kind of wooden shaft-like sports requsites, and it comprises the following steps:
1, prepare wooden stick's embryo 11: processing car system one wooden stick's embryo 20, this wooden stick's embryo 20 generally is the slightly straight round bar shape of tapering;
2, put telescopic twill fiber net 12: a telescopic twill fiber net 30 is enclosed within the outer rim of this wooden stick's embryo 20, and this twill fiber net 30 can tighten automatically fits, and afterwards, cuts redundance again;
3, add epoxy resin 13: coating or immerse an epoxy resin liquid 41 on wooden stick's embryo 20 of this coating twill fiber net 30;
4, twine a coating and be with 14: the 10 outer windings one of whole wooden stick embryo are coated be with 50;
5, room temperature vulcanizing 15: through a predetermined firm time, harden under room temperature environment, form a hardened layer 40;
6, be with 16 to take off this coating;
7, finish finished product 17.
Wherein, this telescopic twill fiber net 30 can be sleeved on rule or the irregular wooden stick embryo of diameter between 5 millimeters to 100 millimeters.
This telescopic twill fiber net 30 does not have the vertically seam of (axially) fully for intersecting twill, has several slits between its intersection twill, because it is the intersection twill, run into the bigger place of diameter and then can support automatically greatly, that is its elastically deformable is with automatic coating surface.
In addition, because resin of the present invention is to be coated with during fabrication or impregnation, the process that coats at once and harden afterwards, need not time of storing and transporting, so, in the resin as long as add the curing agent that room temperature can be reacted, therefore, as long as hardening temperature of the present invention is in room temperature, so, avoid natural wooden part Yin Gaowen fully and the shortcoming of being out of shape.
Secondly, see also Fig. 8, the second embodiment of the present invention, the outer surface of this wooden stick's embryo 20 has irregular first a moulding portion 60, and still, this telescopic twill fiber net 30 but can flexible distortion and fit fully, has no difficulty in the manufacturing.
In addition, see also Fig. 9, the third embodiment of the present invention, the outer surface of this wooden stick's embryo 20 has irregular second a moulding portion 70, in like manner, because this telescopic twill fiber net 30 can flexible distortion and applying fully, also has no difficulty in the manufacturing.
In sum, the present invention has following advantage and effect:
1, sclerosis at room temperature, wooden stick's embryo is indeformable, and qualification rate is high.Hardening process of the present invention at room temperature can be carried out, and therefore, wooden part can be out of shape, in case after the sclerosis, whole straight degree is splendid, fraction defective is extremely low.
2, cut simple and easyly, telescopic twill fiber net does not have longitudinal seam.The crop position of twill fiber net of the present invention is at two ends end to end, cuts simple and easyly, and do not have the problem of residual longitudinal seam.
3, applicable different-diameter or special external form person, applied range are arranged.Telescopic twill fiber net of the present invention is because can flexible support big, no matter tapering or diameter are slightly different, all applicable, in addition, have irregular special formedly for the surface, telescopic twill fiber net of the present invention also can be suitable for, and range of application is very extensive.
The above, it only is preferred embodiment of the present invention, be not that the present invention is done any pro forma restriction, every foundation technical spirit of the present invention all still belongs in the scope of technical solution of the present invention any simple modification, equivalent variations and modification that above embodiment did.
Claims (3)
1, a kind of manufacture method of wooden shaft-like sports requsites is characterized in that, it comprises the following steps:
One, prepare wooden stick's embryo: processing car system one wooden stick's embryo, this wooden stick's embryo generally is the slightly straight round bar shape of tapering;
Two, put telescopic twill fiber net: a telescopic twill fleece cover is placed in the outer rim of this wooden stick's embryo, and this twill fiber net can tighten automatically fits, and afterwards, cuts redundance again;
Three, add epoxy resin: coating or immerse an epoxy resin liquid on wooden stick's embryo of this coating twill fiber net;
Four, twine one and coat band: the outer winding one of whole wooden stick embryo is coated band;
Five, room temperature vulcanizing:, under room temperature environment, harden through a predetermined firm time;
Six, take off this coating band;
Seven, finish finished product.
2, the manufacture method of wooden shaft-like sports requsites according to claim 1 is characterized in that described telescopic twill fiber net can be sleeved on rule or the irregular wooden stick embryo of diameter between 5 millimeters to 100 millimeters.
3, the manufacture method of wooden shaft-like sports requsites according to claim 1, the outer surface that it is characterized in that described wooden stick embryo have an irregular moulding portion, and this telescopic twill fiber net is can flexible distortion and fit fully.