CN1887076A - Rod for fishing rod and its making process - Google Patents
Rod for fishing rod and its making process Download PDFInfo
- Publication number
- CN1887076A CN1887076A CN 200610052553 CN200610052553A CN1887076A CN 1887076 A CN1887076 A CN 1887076A CN 200610052553 CN200610052553 CN 200610052553 CN 200610052553 A CN200610052553 A CN 200610052553A CN 1887076 A CN1887076 A CN 1887076A
- Authority
- CN
- China
- Prior art keywords
- material layer
- pole body
- fishing rod
- layer
- composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The making process of rod body for fishing rod includes winding one polymer material layer without superposing outside one compound material layer; spraying one extinction material layer to the surface of the polymer material layer; winding one layer of combining material of smelting point lower than that of the polymer material layer with partial superposing to the extinction material layer; sintering to form rod body core in complex layered structure; removing the rod body core from one mandrel and peeling off the combining material layer to form the rod body for fishing rod.
Description
Technical field
The invention relates to a kind of pole body of the usefulness of going fishing, be meant a kind of pole body and manufacture method thereof of fishing rod especially.
Background technology
Based on the convenience on carrying and collecting, fishing rod can install into its pole body the form of more piece hollow and caliber convergent, and, according to the pole body by extracting out in regular turn or continued access and be divided into " formula of shaking " and reach " and the formula that continues " two classes piecemeal.
The pole system method of present fishing rod, as Fig. 1,2, shown in 3, mainly be with the made reinforcement embryo cloth 91 of the interior impregnation synthetic resin of reinforcing fiber material (carbon fiber or glass fibre), after being cut into preliminary dimension earlier, cooperate again and consult the flow process 901 of Fig. 6 to flow process 907, and be wound on the thinner tubular axle 92 of a front end (flow process 901), then, again an OPP (biaxial stretched polypropylene) adhesive tape 93 is coated on this reinforcement embryo cloth 91 outer surfaces (flow process 902) with the form spooling that a helical form and a part overlap, make this reinforcement embryo cloth 91 can on this axle 92, obtain radially typing, then, whole again dislocation goes into to impose in the baking oven heat baking sintering (flow process 903), again this axle 92 is removed out after the sclerosis to be cooled, and this OPP adhesive tape 93 removed (flow process 904), to become as Fig. 4, a pole embryo 9 (flow process 907) of 5, last, again these pole embryo 9 two ends are cut into desire length, promptly become a pole body.
Consult Fig. 2,3,4, but this pole body is before sintering, its top layer is behind the spooling through OPP adhesive tape 93, the recess space 94 that can produce a step shape at its overlapping position, so, when this reinforcement embryo cloth 91 carries out sintering with OPP adhesive tape 93, this OPP adhesive tape 93 is radially brought together the power except meeting because of self material is subjected to thermal contraction that this reinforcement embryo cloth 91 is formed one, fibrous material in this reinforcement embryo cloth 91 also can enter in this recess space 94 along with flowing of synthetic resin, thus, consult Fig. 5, pole embryo 9 surfaces behind the sintering just can produce the lug boss 95 of plural loop shaped, and these lug bosses 95 have suitable height dimension drop, and cause the pole surface that scratch is arranged easily, the situation of damaging, and, the pole body is after removing this OPP adhesive tape 93, outer surface still can have the glossiness of metalloid, and under the irradiation of sunlight, the pole surface can produce strong reflect light and shouting pain fisherman's eye.
Consult Fig. 5,6, in order to overcome above-listed disappearance, the dealer imposes on pole embryo 9 surfaces of making to grind hacking (flow process 905) more at present, thick delustring lacquer (flow process 906) is gone up in spraying then, to reduce the concavo-convex class's drop of pole embryo 9 surperficial rings, and the light on elimination pole embryo 9 surfaces, but, pole embryo 9 is after process is ground hacking, can destroy (fibrous fracture) to the reinforcing fiber material production of a part virtually, cause the reduction of pole body intensity, in addition, thick and heavy delustring lacquer has also increased the weight of pole embryo 9, need light and handy and do not meet the pole body, the requirement that intensity is high, in addition, delustring lacquer only by spraying method attached on this pole embryo 9, also be easy to generate to peel off and come off.
Summary of the invention
Therefore, the present invention's purpose, promptly provide a kind of make the pole surface comparatively smooth, be difficult for scraping and damage, and can form the pole body of the fishing rod of not reflective, atomizing.
And, another object of the present invention, be at the pole body as yet not before the plasticizing forming, coat one deck macromolecular material prior to inside in advance, and spray an extinction material at this polymer material layer outer surface, make the pole body behind the sintering needn't be through grinding the hacking operation, and can improve fishing rod intensity, reduce electric conductivity, and the pole system making method of the incrust fishing rod of extinction material.
So the pole body of the present invention's fishing rod comprises a composite layer, a polymer material layer, and an extinction material layer.
This composite layer is to be included by the reinforcing fiber material that to be soaked with synthetic resin made.
This polymer material layer is according to a helical form and a mutual outer surface that is not wound on composite layer with not overlapping.
This extinction material layer is an outer surface of promptly not coating this bond material layer at the previous materials layer before the sintering.
And, the pole body and the manufacture method thereof of fishing rod of the present invention, this method comprises the following step:
A, take to include and be soaked with the made banded composite layer of synthetic resin by the reinforcing fiber material.
B, this composite layer is wound on the thinner axle outer surface of a front end.
C, with one by the made laminar polymer material layer of high molecular polymer, according to helical form and be not wound on an outer surface of this composite layer mutually with not overlapping.
D, on the outer surface of this polymer material layer the coating one extinction material.
E, a bond material layer is wound on the outer surface of this extinction material according to a helical form and a part with overlapping.
F, previous materials is imposed heat baking sintering, and the control temperature is not more than the melting temperature of this macromolecular material, to obtain a pole body core.
G, this pole body core is removed out on this axle, and divest this bond material layer, to obtain a fishing rod pole body.
Via above-mentioned explanation, compared to the pole body of existing fishing rod, the pole body of the present invention's fishing rod and manufacture method thereof have many effects and advantage in fact, conclude now as the back:
One, the pole body is before sintering, in advance at these composite layer 1 outer surface 11 these macromolecular materials of coating last layer (layer) 2, because this polymer material layer 2 is to adopt not overlap mode to make spooling, so its outer surface 11 is level and smooth shape, and the inboard recess space that does not also have step shape generates, so, the reinforcing fiber material of this composite layer 1 is subjected to the obstruct of polymer material layer 2, and can not protrude towards the pole external surface, make the pole surface become comparatively level and smooth, must not be difficult for producing scratch, damaging through grinding hacking yet.
Two, adopt the polymer material layer 2 of fluorine compounds to have low, the resistant to elevated temperatures characteristic of coefficient of friction, so, its material can not enter in these bond material layer 4 long-pending folded positions yet behind sintering, guarantee the level and smooth of these polymer material layer 2 outer surfaces 21, thus, delustring lacquer (extinction material layer) 3 amounts that sprayed significantly reduce, so can reduce the weight of pole body.
Three, the pole body is interior can improve the bulk strength of pole body through after twining this polymer material layer 2 in advance, and reduces electric conductivity.
Four, extinction material (extinction material layer 3) is not sinter into as yet at the pole body promptly to coat this polymer material layer 2 outer surfaces in advance, except the pole body is reached not reflective, the atomizing, and behind sintering, can increase the adhesion with polymer material layer 2, effectively prevent to peel off.
Description of drawings
Fig. 1 is a combination appearance figure, illustrates that an OPP adhesive tape is wound in one and is sheathed on the embryo cloth of an axle outer surface;
Fig. 2 is a combination section, and a kind of existing fishing rod is described;
Fig. 3 is the combination section after this existing fishing rod sintering processes;
Fig. 4 is an outside drawing of this existing fishing rod;
Fig. 5 is a partial enlarged drawing one of among Fig. 4;
Fig. 6 is the manufacturing step flow chart of existing fishing rod pole body;
Fig. 7 is a combination appearance figure, illustrates that one of the pole body of fishing rod of the present invention and the preferred embodiment of manufacture method thereof polymer material layer is not wound in one with overlapping mutually and is sheathed on the composite layer of an axle outer surface;
Fig. 8 is similar in one of Fig. 7 combination appearance figure, illustrates that bond material layer segment overlapping is wound in one of above-mentioned extinction material layer outer surface;
Fig. 9 is a combination section, illustrates that this polymer material layer and this bond material layer are wound on this composite layer in regular turn, and earlier an extinction material layer is sprayed at an outer surface of this polymer material layer before this bond material layer twines;
Figure 10 is another combination section, illustrates that the bond material layer with Fig. 9 removes from this extinction material layer outer surface;
Figure 11 is an outside drawing, and a pole body core is described;
Figure 12 is a partial enlarged drawing one of among Figure 11; And
Figure 13 is a flow chart of steps of above-mentioned preferred embodiment.
Embodiment
About addressing other technology contents, characteristics and effect before the present invention, in the following detailed description that cooperates with reference to one of a graphic preferred embodiment, can clearly present.
The primary clustering symbol description:
1 composite layer
11 outer surfaces
2 polymer material layers
21 outer surfaces
3 extinction material layers
31 outer surfaces
4 bond material layers
5 axles
100 pole body cores
101 flow processs
102 flow processs
103 flow processs
104 flow processs
105 flow processs
106 flow processs
107 flow processs
Consult Figure 10, the pole body and the manufacture method thereof of fishing rod of the present invention comprise a composite layer 1, a polymer material layer 2 and an extinction material layer 3.
Consult Fig. 9,10, this composite layer 1 is to be included by a reinforcing fiber material to be soaked with the made banded material of a synthetic resin, and this reinforcing fiber material can be combined by materials wherein a kind of or more than any such as carbon fiber, glass fibres.
Consult Fig. 7,9,10, this polymer material layer 2, be by made rectangular laminar of high molecular polymer, and be according to helical form and next-door neighbour but be not wound on an outer surface 11 of composite layer 1 mutually with not overlapping, to keep the smoothness of these polymer material layer 2 outer surfaces, and in present embodiment, this polymer material layer 2 is made of a fluorinated polymer (fluoropolymer) and the solid that is incorporated on its back side, wherein, the Teflon (Teflon ) that these fluorine compounds can adopt E.I.Du Pont Company to produce, solid then can adopt all kinds of pressure-sensing glue, the acryl glue of tack, PVA latex etc., and this polymer material layer 2 is to adopt into lighttight color (black) for best.
Consult Fig. 9, this extinction material layer 3 is outer surfaces of promptly not coating this polymer material layer 2 at the previous materials layer before the sintering.Extinction material can coat with lacquer with delustring.
Pole system making method as for fishing rod of the present invention includes the following step:
One, consults the flow process 101 of Figure 13, take to include and be soaked with synthetic resin and make this band shape composite layer 1 by the reinforcing fiber material.
Two, consult Fig. 7, this composite layer 1 is wound on the thinner axle of a front end 5 outer surfaces.
Three, consult Fig. 8,9 and the flow process 102 of Figure 13, with this polymer material layer 2 according to helical form and be not wound on an outer surface 11 of this composite layer 1 mutually with not overlapping.
Four, consult the flow process 103 of Fig. 9 and Figure 13, coating one black matt lacquer (extinction material layer 3) on an outer surface 21 of this polymer material layer 2.
Five, consult Fig. 8,9 and the flow process 104 of Figure 13, one bond material layer 4 is wound on the outer surface 31 of this extinction material layer 3 according to a helical form and a part with overlapping, closely to make this polymer material layer 2 envelope this composite layer 1, this bond material layer 4 is the fine sheets that adopt two extended polypropylene (OPP) materials to make.
Six,, the previous materials layer is imposed heat baking sintering, and the control temperature is not more than the melting temperature (about 120 ℃) of this polymer material layer 2, to obtain Figure 11, one of 12 pole body cores 100 as the flow process 105 of Figure 13.
Seven, as the flow process 106,107 of Figure 13, this pole body core 100 is removed out on these axle 5 (see figure 8)s, and divest these bond material layer 3 (see figure 10)s of outer surface.
Eight, these pole body core 100 two ends are cut into Len req to constitute the pole body of a fishing rod.
The above person of thought, only for the present invention's number preferred embodiment, when the scope that can not limit the invention process with this, promptly the simple equivalent of doing according to the present patent application claim and description generally changes and modifies, and all still belongs in the scope that patent of the present invention contains.
Claims (5)
1, a kind of pole body of fishing rod comprises: a composite layer (1) is to be included by the reinforcing fiber material that to be soaked with synthetic resin made; It is characterized in that:
One polymer material layer (2) is according to helical form and be not wound on the outer surface (11) of this composite layer (1) with not overlapping mutually, and this polymer material layer (2) has a smooth exterior surface face (21); And
One extinction material layer (3) is an outer surface (21) of promptly not coating this polymer material layer (2) at the previous materials layer before the sintering.
2, the pole body of fishing rod according to claim 1 is characterized in that wherein, and this reinforcing fiber material is combined by carbon fiber or glass fibre material wherein a kind of or more than any.
3, the pole body of fishing rod according to claim 1 is characterized in that wherein, and this polymer material layer (2) is that employing is high material than this composite layer (1) melting temperature.
4, the pole body of fishing rod according to claim 1 is characterized in that wherein, and this polymer material layer (2) is made of fluorinated polymer and the solid that is incorporated on its back side.
5, a kind of pole system making method of fishing rod is characterized in that comprising the following step:
A, take to include and be soaked with the made banded composite of synthetic resin by the reinforcing fiber material;
B, this composite is wound on the thinner axle outer surface of a front end;
C, with one by the made laminar macromolecular material of high molecular polymer, according to helical form and be not wound on the outer surface (11) of this composite mutually with not overlapping;
D, go up coating one extinction material at the outer surface (21) of this macromolecular material;
E, a bond material is wound on with overlapping the outer surface (31) of this extinction material layer (3) according to a helical form and a part;
F, previous materials is imposed heat baking sintering, and the control temperature is not more than the melting temperature of this macromolecular material, can obtains a pole body core (100); And
G, this pole body core (100) is removed out on this axle certainly, and divest this bond material layer, to obtain a fishing rod pole body.