CN116145300B - 一种具有负泊松比效应的电磁屏蔽功能弹性纱线 - Google Patents
一种具有负泊松比效应的电磁屏蔽功能弹性纱线 Download PDFInfo
- Publication number
- CN116145300B CN116145300B CN202310216251.2A CN202310216251A CN116145300B CN 116145300 B CN116145300 B CN 116145300B CN 202310216251 A CN202310216251 A CN 202310216251A CN 116145300 B CN116145300 B CN 116145300B
- Authority
- CN
- China
- Prior art keywords
- fiber
- yarn
- electromagnetic shielding
- modulus
- modulus fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种具有负泊松比效应的电磁屏蔽功能弹性纱线,得到的导电拉胀复合材料质轻、拉伸膨胀性稳定,不但实现了在拉伸作用下保持电磁屏蔽效能稳定,还提高了其对电磁波的吸收能力。当该纱线承受冲击载荷时,材料向冲击区域聚集变得更加致密,抵抗压痕的能力得到提高,因此本发明制备的电磁屏蔽纱线同时具有优异的机械性能如耐冲击性、抗断裂性能以及韧性,所制备的导电拉胀复合材料在可拉伸电磁屏蔽材料及吸波材料领域具有良好的应用前景。
Description
技术领域
本发明属于新材料技术领域,尤其涉及一种具有负泊松比效应的电磁屏蔽功能弹性纱线。
背景技术
自21世纪初以来,超材料已经逐渐发展成为新材料技术的一个重要分支。超材料是设计材料的内部结构,从而人为控制材料的各种属性以获得自然界没有的新材料。负泊松比(Negative Poisson's Ratio)材料是一种新型超材料,具体表现为在受到单轴压缩(拉伸)时在横向发生收缩(膨胀)变形。由于其独特的变形行为,负泊松比材料已被证实具有高比强度、高能量吸收率等性质,在航空航天、医疗卫生、日化用品等领域具有广阔的应用前景。
机械超材料是一种具有违反直觉力学性质的人造结构,其特殊的性能不是取决于材料本身的属性,而是源于对其单元结构进行创新设计。目前大多数负泊松比材料具有内凹多孔、旋转或剪纸等拓扑结构、多胞元结构等,其在单轴拉伸下能产生侧向膨胀。相关材料大多通过3D打印等高昂的制作方法制造,在航空航天领域已崭露头角,但因造价和工期等原因很难进行大规模应用。
电磁屏蔽材料是一种能屏蔽电磁波干扰的材料,主要包括三大类:1)金属类,如铍铜、不锈钢等;2)填充类,在不导电的基材中添加一定比例的导电填料从而使得材料导电;3)表面敷层和导电涂料类,对基材进行电镀,常用的制备方法包括化学镀金、真空喷镀、溅射、金属熔射以及贴金属箔等。电磁屏蔽材料作为电磁屏蔽技术的重要手段,能够对电子信息设备起到防护作用。随着电子信息设备的快速发展,对电磁屏蔽材料的可拉伸性等特性的要求也不断提高,如设备表面大量的气动曲面结构和部件之间的缝隙,使电磁屏蔽材料要有一定的曲面适应性和拉伸特性。
目前有技术人员做了一些研究。如中国专利CN202110738531.0将电磁性芯层与外包编织层通过编织工艺编织成夹心复合屏蔽绳。电磁性芯层通过原位聚合聚吡咯和喷涂纳米Fe3O4磁性粒子,实现电磁性;外包编织层选用镀银尼龙合股纱线,具有良好的导电性和耐磨性,但使用金属基屏蔽材料具有密度大、易腐蚀等缺点。中国专利CN202210202936.7将开孔泡沫浸入到导电填料分散液中,对该复合材料进行压缩并高温保温,冷却后得到所述的导电拉胀开孔泡沫复合材料。该发明将拉胀结构引入到电磁屏蔽材料中,制备得到的导电拉胀开孔泡沫复合材料质轻、拉伸膨胀性稳定、不但实现了在拉伸作用下保持电磁屏蔽效能稳定,还提高了其对电磁波的吸收能力,因为其构成方式采用拉胀开孔泡沫复合材料,无法改变其结构,适应不同环境,限制了其使用范围。中国专利CN201910061159.7采用不锈钢以短纤状态与涤纶短纤混纺而成,将不锈钢长丝束与涤纶生条共同以上下结构喂入并条机,喂入时不锈钢长丝束位于涤纶生条的上方且经并条机的后罗拉对的按压后嵌入在涤纶生条内,实现两种纤维的均匀混合,而后依次经粗纱、细纱得到所需的电磁屏蔽纱线,制备的导电材料在拉伸过程中普遍存在电导率下降进而导致电磁屏蔽效能下降的问题。因此提出本发明。
发明内容
为解决上述问题,本发明提供了一种具有负泊松比效应的电磁屏蔽功能弹性纱线,不同于现有技术,本发明的负泊松比结构中不设有同轴的弹性包芯纱,通过假捻及拉伸对纱线进行加弹处理,最终制成负泊松比纱线,且通过变形实现电磁屏蔽功能,不仅提高了对电磁波的吸收能力,而且纱线的形式更适宜更多场景中的应用。
本发明的第一个目的是提供一种具有负泊松比效应的电磁屏蔽功能弹性纱线的制备方法,包括以下步骤:
S1、在低模量纤维表面涂覆导电粒子溶液,再将高模量纤维螺旋缠绕抱合在低模量纤维表面;其中,所述低模量纤维具有导电性;
S2、将S1的复合纤维送入加弹机,经过假捻盘时将复合纤维两端握持,中间假捻;
S3、对S2加捻后的纱线进行热压牵伸,得到所述具有负泊松比效应的电磁屏蔽功能弹性纱线。
进一步地,所述高模量纤维选自聚乙烯纤维、镀镍碳纤维、氧化铝纤维中的一种或几种。
进一步地,所述低模量纤维为脂肪族聚酰胺纤维。
进一步地,所述高模量纤维与低模量纤维通过喷气式纺纱的方式进行螺旋缠绕抱合。
进一步地,高模量纤维与低模量纤维螺旋缠绕抱合过程中,高模量纤维的输出速度8~20m/min,低模量纤维的输出速度10~25m/min。
进一步地,所述导电粒子选自炭黑、碳纳米管、石墨烯、MXene中的至少一种。
进一步地,所述导电粒子溶液由导电粒子与分散剂混合得到,其中,分散剂为聚乙烯吡咯烷酮。
进一步地,在步骤S3中,热压牵伸的温度为80~150℃。
进一步地,所述低模量纤维和高模量纤维的半径比不小于2。
本发明的第二个目的是提供上述制备方法得到的电磁屏蔽功能弹性纱线。
本发明的有益效果:
(1)本发明的电磁屏蔽纱线结构采用两组不同模量的纱线一起假捻完成,纱线结构具有较好的稳定性,克服了现有技术中纱线结构表层纱线滑移、结构不稳定且捻度分布不匀以及拉伸时纱线表面凹凸不平等缺点,有利于改善结构的使用性能。该纱线采用结构加弹,具有更好的可加工性,扩大了纤维的适用范围。
(2)本发明的纱线结构可利用外部纤维环状结构,产生反向电磁场,来抵消原来的磁场,进一步提高电磁屏蔽效果,将拉胀结构引入电磁屏蔽材料中,制备得到的导电拉胀复合纱线材料质轻、拉伸膨胀性稳定、不但实现了在拉伸作用下保持电磁屏蔽效能稳定,还提高了其对电磁波的吸收能力。
(3)低模量纤维拉伸时把高模量纤维束缚或封锁住,增强纤维耐磨性,且使耐蠕变性得以提高,从而延长其使用寿命,在使用中不易出现退捻或者受力拉扯极易发生断裂的问题。该混纺纤维包缠平行导致气流纺纱外部纤维排列结构相对松散,具有一定的透气性。
附图说明
图1为本发明制备的电磁屏蔽纱线流程示意图;
图2为电磁屏蔽纱线结构受到轴向拉伸前的结构示意图;
图3为电磁屏蔽纱线结构受到轴向拉伸时的结构示意图;
图4为假捻盘正面结构示意图。
附图标记说明:
1-主纱工位,2-第一引导单元,3-第一牵伸装置,4-第一罗拉辊,5-第一喷嘴,6-辅纱工位,7-第二引导单元,8-第二牵伸装置,9-第二罗拉辊,10-第二喷嘴,11-纺纱单元,12-从动罗拉,13-假捻盘,14-加热牵伸辊,141-第一牵伸辊,142-第二牵伸辊,143-第三牵伸辊,15-高模量纤维,16-低模量纤维。
具体实施方式
下面结合附图和具体实施例对本发明作进一步说明,以使本领域的技术人员可以更好地理解本发明并能予以实施,但所举实施例不作为对本发明的限定。
本发明涉及的方案如下:
一种具有负泊松比效应的电磁屏蔽功能弹性纱线的制备方法,将高模量纤维与低模量纤维混纺,通过喷气式纺纱螺旋缠绕抱合的方式将纤维合为一体,在纤维扭转和卷曲变形时进行热定型,将其在蓬松状态固定下来。具体如下:
步骤一,利用主纱工位将主纱从主纱卷装中抽出、引导、变形并且牵拉,辅纱工位具有用于提供辅纱的辅纱卷装,利用引导单元将纱线送出。
步骤二,将高模量纤维引入于第一喷嘴,低模量纤维引入第二喷嘴,其中第一喷嘴输出速度为8~20m/min,压力为100~500kPa,第二喷嘴输出速度为10~25m/min,第二喷嘴压力为200~600kPa(低模量纤维半径:高模量纤维>2)。在低模量纤维表面涂覆导电粒子溶液,随后将高模量纤维螺旋缠绕抱合在低模量纤维表面,照预设时间规律周期性的改变螺距以正螺旋或者反螺旋抱合,在经过假捻盘将纱端两端握持,中间假捻,增加纤维间抱合力。
步骤三,把制得的复合纤维在扭转和卷曲变形时经过热辊进行热定型,热辊进行热定型时温度为80~150℃,牵伸时间为30-240s,牵伸倍数为2~10倍,进而获得弹力较好的弹力丝。
实施例1
利用主纱工位将主纱从主纱卷装中抽出、引导、变形并且牵拉,辅纱工位具有用于提供辅纱的辅纱卷装,利用引导单元将纱线送出,将超高分子量聚乙烯纤维(分子量150万-350万,下同)引入于第一喷嘴,输出速度为15m/min,第一喷嘴压力为254kPa。将聚酰胺纤维引入第二喷嘴,输出速度为16m/min,第二喷嘴压力为600kPa,将超高分子量聚乙烯螺旋缠绕抱合在脂肪族聚酰胺纤维表面,抱合前在聚酰胺纤维表面涂覆20wt%MXene溶液,分散剂为PVP。抱合纱线在经过假捻盘将纱端两端握持,中间假捻,增加纤维间抱合力。最后采取多级热压牵伸方式,达到高强、高模的特性,热压温度为100℃,控制前后牵伸辊:第一牵伸辊、第二牵伸辊和第三牵伸辊的速度比例为1:3:6,随着拉伸,大分子间由无序状向有序状,定向排列。
实施例2
利用主纱工位将主纱从主纱卷装中抽出、引导、变形并且牵拉,辅纱工位具有用于提供辅纱的辅纱卷装,利用引导单元将纱线送出,将超高分子量聚乙烯纤维引入于第一喷嘴,输出速度为20m/min,第一喷嘴压力为450kPa。将聚酰胺纤维引入第二喷嘴,输出速度为25m/min,第二喷嘴压力为450kPa,将超高分子量聚乙烯螺旋缠绕抱合在聚酰胺纤维表面,抱合前在聚酰胺纤维表面涂覆20wt%炭黑溶液,分散剂为PVP。抱合纱线在经过假捻盘将纱端两端握持,中间假捻,增加纤维间抱合力。在经过采取多级热压牵伸后,能达到高强、高模的特性,热压温度为120℃,控制前后牵伸辊速度比例为1:3:5。随着拉伸,大分子间由无序状向有序状,定向排列。
实施例3
利用主纱工位将主纱从主纱卷装中抽出、引导、变形并且牵拉,辅纱工位具有用于提供辅纱的辅纱卷装,利用引导单元将纱线送出,将超高分子量聚乙烯纤维引入于第一喷嘴,输出速度为18m/min,第一喷嘴压力为250kPa。将聚酰胺纤维引入第二喷嘴,输出速度为12m/min,第二喷嘴压力为500kPa,将超高分子量聚乙烯螺旋缠绕抱合在聚酰胺纤维表面,抱合前在聚酰胺纤维表面涂覆20wt%碳纳米管溶液,分散剂为PVP。抱合纱线在经过假捻盘将纱端两端握持,中间假捻,增加纤维间抱合力。在经过采取多级热压牵伸后,能达到高强、高模的特性,热压温度为80℃,控制前后牵伸辊速度比例为1:7:9。随着拉伸,大分子间由无序状向有序状,定向排列。
实施例4
将超高分子量聚乙烯纤维替换为镀镍碳纤维,其余同实施例3。
实施例5
将超高分子量聚乙烯纤维替换为氧化铝纤维,其余同实施例3。
对比例1
未进行假捻加弹,其余同实施例3。
对比例2
将超高分子量聚乙烯纤维、聚酰胺纤维分别送入加弹机进行加弹,并在聚酰胺纤维表面涂覆20wt%碳纳米管溶液,随后将加弹后的超高分子量聚乙烯纤维和聚酰胺纤维假捻,后进行多级热压牵伸,其余同实施例3。
测试例
为验证本发明所得的技术效果,分别对实施例1-5、对比例1-2所得复合纤维进行测试,具体结果如表1所示:
利用新拓三维XTDIC系统可对纤维材料强力伸长试验过程进行全场测量,测试弹性模量。采用微波网络矢量分析仪进行电磁屏蔽性能测试,测试频率范围(2-18GHz)。纱线在拉伸张力作用下发生结构反转导致纱线的直径由(2*d0+D0)向(2*D0+d0)变化,测试负泊松比系数。
表1各实施例与对比例的性能测试表
本发明中,相对于传统的负泊松比螺旋纱线,缩小了结构的尺寸,负泊松比材料更加接近材料本身的性质,将自由形状的表面包围起来包芯纱内部并不加捻,从工艺上来说没有模量的影响,较容易发生位置和状态的互换,实现结构相的快速可逆转变。对比例1中直接将两种纱线螺旋缠绕抱合,由于两种纱线模量差异大难混合做纱线,在拉伸过程中纱线并未发生位置和状态的互换,纱线中出现分离,不具有负泊松比效应,自然也无法实现电磁屏蔽的功能。对比例2中先将高模量纤维和低模量纤维加弹,再进行假捻,在假捻过程后,两种长丝均具有一定的弯曲结构,在拉伸过程中,并未发生位置的改变,因此负泊松比和电磁屏蔽效果较差。
显然,上述实施例仅仅是为清楚地说明所作的举例,并非对实施方式的限定。对于所属领域的普通技术人员来说,在上述说明的基础上还可以做出其它不同形式变化或变动。这里无需也无法对所有的实施方式予以穷举。而由此所引申出的显而易见的变化或变动仍处于本发明创造的保护范围之中。
Claims (4)
1.一种具有负泊松比效应的电磁屏蔽功能弹性纱线的制备方法,其特征在于,包括以下步骤:
S1、在低模量纤维表面涂覆导电粒子溶液,再将高模量纤维螺旋缠绕抱合在低模量纤维表面;其中,所述低模量纤维具有导电性,所述低模量纤维为脂肪族聚酰胺纤维,所述高模量纤维选自聚乙烯纤维、镀镍碳纤维、氧化铝纤维中的一种或几种,所述低模量纤维和高模量纤维的半径比不小于2,所述高模量纤维与低模量纤维通过喷气式纺纱的方式进行螺旋缠绕抱合,螺旋缠绕抱合过程中高模量纤维的输出速度8~20m/min,低模量纤维的输出速度10~25m/min;
S2、将S1的复合纤维送入加弹机,经过假捻盘时将复合纤维两端握持,中间假捻;
S3、对S2加捻后的纱线在纤维扭转和卷曲变形时进行热定型,将其在蓬松状态固定下来,热定型时温度为80~150℃,牵伸时间为30-240s,牵伸倍数为2~10倍,得到所述具有负泊松比效应的电磁屏蔽功能弹性纱线。
2.根据权利要求1所述的制备方法,其特征在于:所述导电粒子选自炭黑、碳纳米管、石墨烯、MXene中的至少一种。
3.根据权利要求1所述的制备方法,其特征在于:所述导电粒子溶液由导电粒子与分散剂混合得到,其中,分散剂为聚乙烯吡咯烷酮。
4.权利要求1-3任一项所述的制备方法得到的具有负泊松比效应的电磁屏蔽功能弹性纱线。