CN116143470A - 一种石墨烯地暖专用砂浆的制造方法 - Google Patents
一种石墨烯地暖专用砂浆的制造方法 Download PDFInfo
- Publication number
- CN116143470A CN116143470A CN202310030405.9A CN202310030405A CN116143470A CN 116143470 A CN116143470 A CN 116143470A CN 202310030405 A CN202310030405 A CN 202310030405A CN 116143470 A CN116143470 A CN 116143470A
- Authority
- CN
- China
- Prior art keywords
- stirring
- parts
- graphene
- floor heating
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种石墨烯地暖专用砂浆，按照重量份数计，石墨烯地暖专用砂浆的组成和数量为：普通硅酸水泥为85～105份、细沙为15～25份、减水剂为0.5～1.5份、消泡剂为0.5～1份、水为20～30份、炉渣灰为10～20份、硅灰为10～20份、石墨烯1份和白炭黑1份，所述普通硅酸水泥的型号为PO32.5，所述减水剂为一种聚羧酸系高性能减水剂，所述消泡剂为一种有机硅类消泡剂。本发明结构巧妙，设计合理，能够提高石墨烯地暖产生热量的传导效率，同时能够增加降低使用时砂浆颗粒之中的缝隙，以来提高砂浆凝固后其抗压、抗折、抗渗、防腐、抗冲击及耐磨性能，而且能在砂浆混合中，在增加砂浆直中材料黏合性的同时，也能快速降低砂浆的水分。
Description
技术领域
本发明涉及石墨烯地暖用砂浆技术领域，尤其涉及一种石墨烯地暖专用砂浆的制造方法。
背景技术
石墨烯地暖的核心原材料就是石墨烯，此石墨烯并非你认知的石墨烯，1到10层碳原子构成的叫做石墨烯。石墨烯地暖的工作原理主要是靠温控器，可远程和直接在温控器上设置，在设定的温度范围内，随意调整室温，可做到单室可控，温高自动断电，温低石墨烯地暖开始工作。
将石墨烯放置完成后，需要在石墨烯上安装地砖，且在石墨烯与地砖之间填充有砂浆，市面上也有很多类型的砂浆，但是多数的砂浆在用于石墨烯地暖之上时，其温度传导的效率较低，在凝固后，其砂浆之间的缝隙较大，降低了其抗压、抗折、抗渗、防腐、抗冲击及耐磨性能，而且在对砂浆进行混合时，砂浆中的水分不能快速降低，存在一定的缺陷。
为此，我们提出一种石墨烯地暖专用砂浆的制造方法来解决上述问题。
发明内容
本发明的目的是为了解决现有技术中的问题，而提出的一种石墨烯地暖专用砂浆的制造方法。
为了实现上述目的，本发明采用了如下技术方案：一种石墨烯地暖专用砂浆，按照重量份数计，石墨烯地暖专用砂浆的组成和数量为：普通硅酸水泥为85～105份、细砂为15～25份、减水剂为0.5～1.5份、消泡剂为0.5～1份、水为20～30份、炉渣灰为10～20份、硅灰为10～20份、石墨烯1份和白炭黑1份。
在上述的石墨烯地暖专用砂浆中，所述普通硅酸水泥的型号为PO32.5。
在上述的石墨烯地暖专用砂浆中，所述减水剂为一种聚羧酸系高性能减水剂。
在上述的石墨烯地暖专用砂浆中，所述消泡剂为一种有机硅类消泡剂。
一种石墨烯地暖专用砂浆的制造方法，包括以下步骤：
S1、将85～105份普通硅酸水泥、15～25份细砂与10～20份炉渣灰加入搅拌设备之中，且进行升降式搅拌，将普通硅酸水泥与细沙搅拌均匀后，随即加入20～30份水加入搅拌设备之中，搅拌过程的转速为200～300转/分钟，搅拌的时间为10～20分钟，搅拌完成后，静置五分钟；
S2、静置后，在混合物之中加入0.5～1份消泡剂，随即进行搅拌，搅拌过程的转速为200～300转/分钟，搅拌时间为5～10分钟，完成搅拌后，搅拌完成后使用振荡机进振荡，振荡的时间为10～20分钟，完成后，进行静置；
S3、在静置五分钟后，将混合物中的泡沫消除后，随即在混合物加入减水剂0.5～1份与10～20份硅灰，再加入石墨烯1份和白炭黑1份，随即进行搅拌，搅拌过程的转速为400～500转/分钟，搅拌的时间为5～10分钟，搅拌完成过后，静置五分钟；
S4、静置后，便于混合完成后的材料在搅拌容器之中取出，进行使用。
在上述的石墨烯地暖专用砂浆的制造方法中，所述步骤中所使用的搅拌方式均为上下均匀搅动。
在上述的石墨烯地暖专用砂浆的制造方法中，所述步骤2中振荡设备处于搅拌容器底部。
与现有的技术相比，本发明的有益效果为：
1、该一种石墨烯地暖专用砂浆，通过将炉渣灰掺杂在用于地暖的砂浆之中，利用炉渣灰的保温导热性能，将石墨烯产生的热量导向地板砖，增加热量传导的效率。
2、该一种石墨烯地暖专用砂浆，通过将硅灰掺杂在用于地暖的砂浆之中，利用硅灰能够填充水泥颗粒间的孔隙，同时与水化产物生成凝胶体，以此来提高砂浆凝固后，其抗压、抗折、抗渗、防腐、抗冲击及耐磨性能。
3、该一种石墨烯地暖专用砂浆的制作方法，通过制作过程中，同时加入减水剂与硅灰，利用减水剂与硅灰相同作用，减水架在降低砂浆中水分的同时，其硅灰也与砂浆中的产生凝胶体，在增加砂浆直中材料黏合性的同时，也能快速降低砂浆的水分。
综上所述，本发明结构巧妙，设计合理，能够提高石墨烯地暖产生热量的传导效率，同时能够增加降低使用时砂浆颗粒之中的缝隙，以来提高砂浆凝固后其抗压、抗折、抗渗、防腐、抗冲击及耐磨性能，而且能在砂浆混合中，在增加砂浆直中材料黏合性的同时，也能快速降低砂浆的水分。
具体实施方式
以下实施例仅处于说明性目的，而不是想要限制本发明的范围。
实施例一
一种石墨烯地暖专用砂浆，按照重量份数计，石墨烯地暖专用砂浆的组成和数量为：普通硅酸水泥为85份、细沙为15份、减水剂为0.5份、消泡剂为0.5份、水为20份、炉渣灰为10份、硅灰为10份、石墨烯1份和白炭黑1份；
普通硅酸水泥的型号为PO42.5；
减水剂为一种聚羧酸系高性能减水剂；
消泡剂为一种有机硅类消泡剂
一种石墨烯地暖专用砂浆的制造方法，包括以下步骤：
S1、将85份普通硅酸水泥、15份细砂与10份炉渣灰加入搅拌设备之中，且进行升降式搅拌，将普通硅酸水泥与细沙搅拌均匀后，随即加入20份水加入搅拌设备之中，搅拌过程的转速为200转/分钟，搅拌的时间为10分钟，搅拌完成后，静置五分钟；
S2、静置后，在混合物之中加入0.5份消泡剂，随即进行搅拌，搅拌过程的转速为200转/分钟，搅拌时间为5分钟，完成搅拌后，搅拌完成后使用振荡机进振荡，振荡的时间为10分钟，完成后，进行静置；
S3、在静置五分钟后，将混合物中的泡沫消除后，随即在混合物加入减水剂0.5份与10份硅灰，再加入石墨烯1份和白炭黑1份，随即进行搅拌，搅拌过程的转速为400转/分钟，搅拌的时间为5分钟，搅拌完成过后，静置五分钟；
S4、静置后，便于混合完成后的材料在搅拌容器之中取出，进行使用。
步骤中所使用的搅拌方式均为上下均匀搅动，使得多种材料能够均匀混合，增加使用过程的稳定性，步骤2中振荡设备处于搅拌容器底部，与搅拌容器进行贴合，使得混合材料之中的间隙减小，减少其中气泡的产生。
实施例二
一种石墨烯地暖专用砂浆，按照重量份数计，石墨烯地暖专用砂浆的组成和数量为：普通硅酸水泥为105份、细砂为25份、减水剂为0.5份、消泡剂为0.5份、水为30份、炉渣灰为20份、硅灰为10份、、石墨烯1份和白炭黑1份；
普通硅酸水泥的型号为PO42.5；
减水剂为一种聚羧酸系高性能减水剂；
消泡剂为一种有机硅类消泡剂；
一种石墨烯地暖专用砂浆的制造方法，包括以下步骤：
S1、将105份普通硅酸水泥、25份细沙与20份炉渣灰加入搅拌设备之中，且进行升降式搅拌，将普通硅酸水泥与细沙搅拌均匀后，随即加入20份水加入搅拌设备之中，搅拌过程的转速为200转/分钟，搅拌的时间为10分钟，搅拌完成后，静置五分钟；
S2、静置后，在混合物之中加入0.5份消泡剂，随即进行搅拌，搅拌过程的转速为200转/分钟，搅拌时间为5分钟，完成搅拌后，搅拌完成后使用振荡机进振荡，振荡的时间为10分钟，完成后，进行静置；
S3、在静置五分钟后，将混合物中的泡沫消除后，随即在混合物加入减水剂0.5份与10份硅灰，再加入石墨烯1份和白炭黑1份，随即进行搅拌，搅拌过程的转速为400转/分钟，搅拌的时间为5分钟，搅拌完成过后，静置五分钟；
S4、静置后，便于混合完成后的材料在搅拌容器之中取出，进行使用。
步骤中所使用的搅拌方式均为上下均匀搅动，使得多种材料能够均匀混合，增加使用过程的稳定性，步骤2中振荡设备处于搅拌容器底部，与搅拌容器进行贴合，使得混合材料之中的间隙减小，减少其中气泡的产生。
实施例三
一种石墨烯地暖专用砂浆，按照重量份数计，石墨烯地暖专用砂浆的组成和数量为：普通硅酸水泥为85份、细砂为15份、减水剂为1份、消泡剂为1份、水为20份、炉渣灰为10份、硅灰为20份、石墨烯1份和白炭黑1份；
普通硅酸水泥的型号为PO42.5；
减水剂为一种聚羧酸系高性能减水剂；
消泡剂为一种有机硅类消泡剂；
一种石墨烯地暖专用砂浆的制造方法，包括以下步骤：
S1、将85份普通硅酸水泥、15份细沙与10份炉渣灰加入搅拌设备之中，且进行升降式搅拌，将普通硅酸水泥与细沙搅拌均匀后，随即加入20份水加入搅拌设备之中，搅拌过程的转速为200转/分钟，搅拌的时间为10分钟，搅拌完成后，静置五分钟；
S2、静置后，在混合物之中加入1份消泡剂，随即进行搅拌，搅拌过程的转速为200转/分钟，搅拌时间为5分钟，完成搅拌后，搅拌完成后使用振荡机进振荡，振荡的时间为10分钟，完成后，进行静置；
S3、在静置五分钟后，将混合物中的泡沫消除后，随即在混合物加入减水剂1份与20份硅灰，再加入石墨烯1份和白炭黑1份，随即进行搅拌，搅拌过程的转速为400转/分钟，搅拌的时间为5分钟，搅拌完成过后，静置五分钟；
S4、静置后，便于混合完成后的材料在搅拌容器之中取出，进行使用。
步骤中所使用的搅拌方式均为上下均匀搅动，使得多种材料能够均匀混合，增加使用过程的稳定性，步骤2中振荡设备处于搅拌容器底部，与搅拌容器进行贴合，使得混合材料之中的间隙减小，减少其中气泡的产生。
以上公开的本发明优选实施例只是用于帮助阐述本发明。优选实施例并没有详尽叙述所有的细节，也不限制该发明仅为所述的具体实施方式。显然，根据本说明书的内容，可作很多的修改和变化。本说明书选取并具体描述这些实施例，是为了更好地解释本发明的原理和实际应用，从而使所属技术领域技术人员能很好地理解和利用本发明。本发明仅受权利要求书及其全部范围和等效物的限制。
Claims (7)
1.一种石墨烯地暖专用砂浆，其特征在于：按照重量份数计，石墨烯地暖专用砂浆的组成和数量为：普通硅酸水泥为85～105份、细砂为15～25份、减水剂为0.5～1.5份、消泡剂为0.5～1份、水为20～30份、炉渣灰为10～20份、硅灰为10～20份、石墨烯1份和白炭黑1份。
2.根据权利要求1所述的一种石墨烯地暖专用砂浆，其特征在于：所述普通硅酸水泥的型号为PO42.5。
3.根据权利要求1所述的一种石墨烯地暖专用砂浆，其特征在于：所述减水剂为一种聚羧酸系高性能减水剂。
4.根据权利要求1所述的一种石墨烯地暖专用砂浆，其特征在于：所述消泡剂为一种有机硅类消泡剂。
5.根据权利要求1所述的一种石墨烯地暖专用砂浆的制造方法，其特征在于，包括以下步骤：
S1、将85～105份普通硅酸水泥、15～25份细砂与10～20份炉渣灰加入搅拌设备之中，且进行升降式搅拌，将普通硅酸水泥与细沙搅拌均匀后，随即加入20～30份水加入搅拌设备之中，搅拌过程的转速为200～300转/分钟，搅拌的时间为10～20分钟，搅拌完成后，静置五分钟；
S2、静置后，在混合物之中加入0.5～1份消泡剂，随即进行搅拌，搅拌过程的转速为200～300转/分钟，搅拌时间为5～10分钟，完成搅拌后，搅拌完成后使用振荡机进振荡，振荡的时间为10～20分钟，完成后，进行静置；
S3、在静置五分钟后，将混合物中的泡沫消除后，随即在混合物加入减水剂0.5～1份与10～20份硅灰，再加入石墨烯1份和白炭黑1份，随即进行搅拌，搅拌过程的转速为400～500转/分钟，搅拌的时间为5～10分钟，搅拌完成过后，静置五分钟；
S4、静置后，便于混合完成后的材料在搅拌容器之中取出，进行使用。
6.根据权利要求5所述的一种石墨烯地暖专用砂浆的制造方法，其特征在于：所述步骤中所使用的搅拌方式均为上下均匀搅动。
7.根据权利要求5所述的一种石墨烯地暖专用砂浆的制造方法，其特征在于：所述步骤2中振荡设备处于搅拌容器底部。