CN115960494B - 离子液体的应用、颜料及其制备方法 - Google Patents
离子液体的应用、颜料及其制备方法 Download PDFInfo
- Publication number
- CN115960494B CN115960494B CN202310160247.9A CN202310160247A CN115960494B CN 115960494 B CN115960494 B CN 115960494B CN 202310160247 A CN202310160247 A CN 202310160247A CN 115960494 B CN115960494 B CN 115960494B
- Authority
- CN
- China
- Prior art keywords
- gouache
- ionic liquid
- drying
- slow
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及美术颜料技术领域，具体而言，涉及离子液体的应用、颜料及其制备方法。本发明实施例将离子液体应用到水粉颜料中，继而有效的延长了水粉颜料室温下的干燥时间和表面的结皮时间，延长了水粉颜料的使用寿命，避免了颜料的资源的浪费。
Description
技术领域
本发明涉及美术颜料技术领域，具体而言，涉及离子液体的应用、颜料及其制备方法。
背景技术
水粉画颜料由于使用简便，调色简单，干湿色差小，绘画效率高，携带方便，广泛的应用于艺考和美术爱好者市场。
水粉颜料在绘画应用过程中，由于地域性差异，在中国北方气候干燥、空气中相对湿度较小，加之空调和暖气系统加快空气中水粉挥发，绘画所需求的水粉颜料需要有较长的干燥时间，否则水粉颜料未使用完就产生表面结皮，无法正常蘸取，不仅导致颜料浪费，同时给颜料使用者带来不好的使用体验，不利于水粉画爱好兴趣的推广。
鉴于此，特提出本发明。
发明内容
本发明的目的在于提供离子液体的应用、颜料及其制备方法。本发明实施例提供离子液体的新应用，将其应用到水粉颜料中，有效的延长了水粉颜料室温下的干燥时间和表面的结皮时间，延长了水粉颜料的使用寿命，避免了颜料的资源的浪费。
本发明是这样实现的：
第一方面，本发明提供一种离子液体在制备颜料中的应用。
在可选的实施方式中，所述颜料包括水粉颜料，优选为慢干型水粉颜料。
在可选的实施方式中，所述离子液体包括可以形成氢键的离子液体；
优选地，所述离子液体的阳离子部分包括N和O元素，阴离子部分包括F和O元素；
优选地，所述离子液体为N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐。
第二方面，本发明提供一种颜料，其原料包括离子液体。
在可选的实施方式中，按质量分数计，其原料组成为：
在可选的实施方式中，所述胶固剂的固含量为40～50％；
优选地，所述胶固剂的成分包括水和胶黏剂；
优选地，所述胶黏剂包括桃胶、阿拉伯胶、瓜尔胶、松香和糊精中的一种或几种。
在可选的实施方式中，所述颜料为水粉颜料，优选为慢干型水粉颜料；
更优选地，所述慢干型水粉颜料的细度≤50μm。
在可选的实施方式中，所述离子液体包括可以形成氢键的离子液体；
优选地，所述离子液体的阳离子部分包括N和O元素，阴离子部分包括F和O元素；
优选地，所述离子液体为N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐；
优选地，参照下述合成路径合成所述N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐：
第一步：C2H4OCl+C4H6N2→[C2mim]Cl
第二步：[C2mim]Cl+C3F7COONa→[C2mim]C3F7COO+NaCl；
其中，第一步的反应条件包括：N-甲基咪唑与甲氨基甲酰氯的摩尔比为1:1.0～1.05，反应温度为95-105℃；
第二步的反应条件包括：[C2mim]Cl与C3F7COONa的摩尔比为1：1.0～1.05。
在可选的实施方式中，所述颜料色粉包括钛白、铁红、铁黄、铁黑、中黄、大红、柠檬黄、酞青蓝、酞青绿、炭黑和永固紫中的至少一种；
优选地，所述填充粉料包括碳酸钙、硫酸钡、滑石粉、云母粉、高岭土、氢氧化铝、玻璃纤维和凹凸棒土中的至少一种；
优选地，所述黏度调节剂包括纤维素、气相二氧化硅和膨润土中的一种或几种；
优选地，所述的助剂包括分散剂、润湿剂、防腐剂和防霉剂中的一种或几种。
第三方面，本发明提供一种前述实施方式所述的颜料的制备方法，包括：添加离子液体；
优选地，包括：将水、胶固剂、助剂、颜料色粉和填充粉料混合得到混合浆料；将所述混合浆料与离子液体混合，而后根据浆料的粘度与黏度调节剂混合，而后研磨。
本发明具有以下有益效果：本发明实施例提供离子液体的一种新应用，其作为保湿的功能性助剂添加到颜料中，有助于锁住颜料中的水分，延缓水分挥发，达到颜料保湿长效耐用的目的。所制备的水粉颜料干燥时间上有明显的延长，非常适用于北方气候干燥的环境，延长颜料是使用寿命。同时颜料还具备优异的绘画性能、干湿色差小、绘画效率高、色彩饱和度好、绘画手感顺滑的，从而实现了绘画者多样性的绘画需求，改善了美术绘画者的绘画体验，有助于水粉颜料在市场的进一步普及。
附图说明
为了更清楚地说明本发明实施例的技术方案，下面将对实施例中所需要使用的附图作简单地介绍，应当理解，以下附图仅示出了本发明的某些实施例，因此不应被看作是对范围的限定，对于本领域普通技术人员来讲，在不付出创造性劳动的前提下，还可以根据这些附图获得其他相关的附图。
图1为本发明实施例提供的对比例1和实施例3的水粉颜料的实验结果；
图2和图3为发明实施例提供的对比例2和实施例4的水粉颜料的实验结果。
具体实施方式
为使本发明实施例的目的、技术方案和优点更加清楚，下面将对本发明实施例中的技术方案进行清楚、完整地描述。实施例中未注明具体条件者，按照常规条件或制造商建议的条件进行。所用试剂或仪器未注明生产厂商者，均为可以通过市售购买获得的常规产品。
水粉颜料在绘画应用过程中，由于地域性差异，北方气候干燥、空气湿度小，所需求的水粉颜料需要有较长的干燥时间，否则水粉颜料未使用完就产生表面结皮，无法正常蘸取，不仅导致颜料浪费，同时给颜料使用者带来不好的使用体验，不利于水粉画爱好兴趣的推广。因此，急需解决该问题。
离子液体(Ionic Liquid)又称室温离子液体、室温熔融盐或有机离子液体等，是由有机阳离子和无机或有机阴离子组成，在室温下呈液体状态的盐类。离子液体具有良好的吸湿性强，通常无色无味。发明人发现在水粉颜料中添加离子液体能够有效的延长了水粉颜料室温下的干燥时间和表面的结皮时间，延长了水粉颜料的使用寿命，避免了颜料的资源的浪费。因此，本发明实施例提供一种离子液体在制备颜料，特别是水粉颜料中的应用。
特别是采用能够形成分子间氢键的离子液体，更有利锁住颜料中的水粉，延缓水粉挥发，达到颜料保湿长效耐用的目的。例如，该离子液体的阳离子具备N和O元素，阴离子具备F和O元素，继而便于在微观结构上易形成分子内和分之间氢键。
将离子液体应用与颜料中，进一步扩大了离子液体的应用范围，也提升了颜料的使用。
进一步地，本发明实施例还提供一种适用于北方气候的慢干型水粉颜料，所制备得到的颜料既具备原有的调色简单，干湿色差小，绘画效率高等优点，还具备良好的缓慢干燥速率，非常适用于北方气候干燥的环境，延长颜料是使用寿命，改善了美术绘画者的绘画体验，有助于水粉颜料在市场的进一步推广。
具体地，颜料的原料包括前述实施方式所述的离子液体，将离子液体应用于水粉颜料中有效的延长了水粉颜料室温下的干燥时间和表面的结皮时间，延长了水粉颜料的使用寿命，避免了颜料的资源的浪费。
进一步地，按质量分数计，其原料组成为：
进一步具体地，颜料为水粉颜料，优选为慢干型水粉颜料；所述慢干型水粉颜料的细度≤50μm。
进一步地，离子液体包括可以形成氢键的离子液体；
优选地，所述离子液体的阳离子部分包括N和O元素，阴离子部分包括F和O元素；
例如，离子液体为N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐；
优选地，参照下述合成路径合成所述N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐：
第一步：C2H4OCl+C4H6N2→[C2mim]Cl
第二步：[C2mim]Cl+C3F7COONa→[C2mim]C3F7COO+NaCl；
其中，第一步的反应条件包括：N-甲基咪唑与甲氨基甲酰氯的摩尔比为1:1.0～1.05，反应温度为95-105℃；
第二步的反应条件包括：[C2mim]Cl与C3F7COONa的摩尔比为1：1.0～1.05。
进一步地，所述胶固剂的固含量为40～50％；
优选地，所述胶固剂的成分包括水和胶黏剂；
优选地，所述胶黏剂包括桃胶、阿拉伯胶、瓜尔胶、松香和糊精中的一种或几种。
颜料色粉包括但不限于钛白、铁红、铁黄、铁黑、中黄、大红、柠檬黄、酞青蓝、酞青绿、炭黑和永固紫中的至少一种；
优选地，所述填充粉料包括但不限于碳酸钙、硫酸钡、滑石粉、云母粉、高岭土、氢氧化铝、玻璃纤维和凹凸棒土中的至少一种；
优选地，所述黏度调节剂包括但不限于纤维素、气相二氧化硅和膨润土中的一种或几种；
优选地，所述的助剂包括但不限于分散剂、润湿剂、防腐剂和防霉剂中的一种或几种。
第三方面，本发明提供一种前述实施方式所述的颜料的制备方法，包括：添加离子液体；
优选地，包括：将水、胶固剂、助剂、颜料色粉和填充粉料混合得到混合浆料；将所述混合浆料与离子液体混合，而后根据浆料的粘度与黏度调节剂混合，而后研磨。
具体地，1)：按照配方计量，将水、胶固剂、助剂、颜料色粉和颜料填料依次加入容器中，室温、1000rpm条件下高速分散15～20分钟，得到混合浆料；
2)：向步骤1)中的混合浆料加入离子液体，在转速300～500rpm搅拌分散10～30min，再根据浆料黏度，通过添加黏度调节剂控制颜料黏度；
3)：将步骤2)中所得的混合浆料经过三辊研磨机研磨，重复研磨至细度≤50μm；
4)过滤灌装。
以下结合实施例对本发明的特征和性能作进一步的详细描述。
实施例1
本发明实施例提供N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐的制备方法，包括：
第一步：C2H4OCl+C4H6N2→[C2mim]Cl
将N-甲基咪唑与甲氨基甲酰氯按照摩尔比为1:1.0作为反应物，加入到含有适量溶剂醋酸丁酯的三口烧瓶中，在N2气保护和持续搅拌下，加热到100±3℃，冷凝回流48小时。待反应结束后采用旋转蒸发仪，并在60±2℃条件下持续抽真空12小时，除去溶剂和未参与反应的反应物。冷却至室温后，添加适量异丙醇，充分搅拌后继续采用旋转蒸发仪加热真空提纯，重复2～3次，经50±2℃真空干燥48小时后得到离子液体：N-甲基-N-甲氨基甲酰基咪唑氯盐。
第二步：[C2mim]Cl+C3F7COONa→[C2mim]C3F7COO+NaCl
将第一步反应所得的离子液体[C2mim]Cl加入到等摩尔量的C3F7COONa水溶液中，充分搅拌24小时后为浅黄色均相液体，室温下将混合液转移至分液漏斗中，分离出有机层。采用二氯甲烷对有机层进行多次萃取，并用水洗涤，直至有机层洗涤出的水相中滴加硝酸银溶液没有白色沉淀洗出为止。采用旋转蒸发仪对有机层在60±2℃条件下持续抽真空12小时，除去残余的水和萃取剂，最终得到[C2mim]C3F7COO即N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐。
实施例2
本实施例提供一种慢干型水粉颜料，按重量份计，其原料组成为：
其中，胶固剂为桃胶液，固含量50％，钛白色粉为细度1250目的金红石型钛白粉，重钙和硫酸钡细度均为1250目重钙，硫酸钡为沉淀硫酸钡，凹凸棒土细度为800目，分散剂为5040，润湿剂为Hydropalat875，消泡剂为A10，防腐防霉剂为GNCE5700-C1，膨润土为钠基膨润土。采用的离子液体为实施例1制备得到的N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐。
本实施例还提供一种上述慢干型水粉颜料的制备步骤：
1)混合：
按照配方计量，将去离子水、胶固剂、助剂、颜料色粉、填充料和功能填料依次加入容器中，室温、1000rpm条件下高速分散15～20分钟，得到混合浆料；
2)研磨：
向步骤1)中的混合浆料加入离子液体，在转速300～500rpm搅拌分散10～30min，再根据浆料黏度，通过添加黏度调节剂控制颜料黏度；
3)调浆：
将步骤2)中所得的混合浆料经过三辊研磨机研磨，重复研磨至细度≤50μm；
4)过滤灌装。
实施例3
本实施例提供一种慢干型水粉颜料，按重量份计，其原料组成为：
胶固剂为桃胶液，固含量50％，3132大红粉为苯基偶氮-2-羟基-3-萘甲酰苯胺，重钙和硫酸钡细度均为1250目重钙，硫酸钡为沉淀硫酸钡，凹凸棒土细度为800目，分散剂为5040，润湿剂为Hydropalat875，消泡剂为A10，防腐防霉剂为GNCE5700-C1，膨润土为钠基膨润土。采用的离子液体为实施例1制备得到的N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐。
本实施例还提供一种上述慢干型水粉颜料的制备步骤：
1)混合：
按照配方计量，将去离子水、胶固剂、助剂、颜料色粉、填充料和功能填料依次加入容器中，室温、1000rpm条件下高速分散15～20分钟，得到混合浆料；
2)研磨：
向步骤1)中的混合浆料加入离子液体，在转速300～500rpm搅拌分散10～30min，再根据浆料黏度，通过添加黏度调节剂控制颜料黏度；
3)调浆：
将步骤2)中所得的混合浆料经过三辊研磨机研磨，重复研磨至细度≤50μm；
4)过滤灌装。
实施例4
本实施例提供一种慢干型水粉颜料，按重量份计，其原料组成为：
胶固剂为桃胶液，固含量50％，群青色粉为市购463群青粉，重钙和硫酸钡细度均为1250目重钙，硫酸钡为沉淀硫酸钡，凹凸棒土细度为800目，分散剂为5040，润湿剂为Hydropalat875，消泡剂为A10，防腐防霉剂为GNCE5700-C1，膨润土为钠基膨润土。采用的离子液体为实施例1制备得到的N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐。
本实施例还提供一种上述慢干型水粉颜料的制备步骤：
1)混合：
按照配方计量，将去离子水、胶固剂、助剂、颜料色粉、填充料和功能填料依次加入容器中，室温、1000rpm条件下高速分散15～20分钟，得到混合浆料；
2)研磨：
向步骤1)中的混合浆料加入离子液体，在转速300～500rpm搅拌分散10～30min，再根据浆料黏度，通过添加黏度调节剂控制颜料黏度；
3)调浆：
将步骤2)中所得的混合浆料经过三辊研磨机研磨，重复研磨至细度≤50μm；
4)过滤灌装。
检测：
本发明实施例2制备得到的慢干型水粉颜料的绘画性能优异，其主要数据如下：
对比例1：参照实施例3提供的水粉颜料的制备方法制备该对比例的水粉颜料，区别在于未添加离子液体。
将实施例3和对比例1(即图1中的空白组)制备得到的水粉颜料同时在相同条件下敞口放置3天，而后拍照。结果参见图1，根据图1可知，添加离子液体的水粉颜料并未完全干燥，还可以正常使用，说明添加离子液体锁住颜料中的水粉，延缓水粉挥发，达到颜料保湿长效耐用的目的。
对比例2：参照实施例4提供的水粉颜料的制备方法制备该对比例的水粉颜料，区别在于未添加离子液体。
将实施例4和对比例2(即图2和3中的空白组)制备得到的水粉颜料在相同条件下涂抹在画纸上，而后观测二者干燥的时间，结果参见图2和图3，根据图2和图3可知，采用本发明实施例提供的水粉颜料，其干燥时间明显延长，说明离子液体的添加达到颜料保湿长效耐用的目的。
本发明创新的将离子液体应用到水粉颜料中，特别是从分子结构设计、分子氢键角度等选择能形成氢键的离子液体，实现锁住颜料中的水粉，延缓水粉挥发，达到颜料保湿长效耐用的目的。所制备的超级水粉颜料干燥时间上有明显的延长，非常适用于北方气候干燥的环境，延长颜料是使用寿命。同时颜料还具备优异的绘画性能、干湿色差小、绘画效率高、色彩饱和度好、绘画手感顺滑的，从而实现了绘画者多样性的绘画需求，改善了美术绘画者的绘画体验。
以上所述仅为本发明的优选实施例而已，并不用于限制本发明，对于本领域的技术人员来说，本发明可以有各种更改和变化。凡在本发明的精神和原则之内，所作的任何修改、等同替换、改进等，均应包含在本发明的保护范围之内。
Claims (9)
1.一种慢干型水粉颜料，其特征在于，按质量分数计，其原料组成为：
胶固剂30~50%；
离子液体0.5~2.0%；
颜料色粉5~15%；
填充粉料20~35%；
黏度调节剂5~10%；
助剂1~10%；
水余量；
其中，所述离子液体包括可以形成氢键的离子液体。
2.根据权利要求1所述的慢干型水粉颜料，其特征在于，所述胶固剂的固含量为40~50%。
3.根据权利要求2所述的慢干型水粉颜料，其特征在于，所述胶固剂的成分包括水和胶黏剂；
其中，所述胶黏剂包括桃胶、阿拉伯胶、瓜尔胶、松香和糊精中的一种或几种。
4.根据权利要求1所述的慢干型水粉颜料，其特征在于，
所述慢干型水粉颜料的细度≤50µm。
5.根据权利要求1所述的慢干型水粉颜料，其特征在于，
所述离子液体的阳离子部分包括N和O元素，阴离子部分包括F和O元素。
6.根据权利要求5所述的慢干型水粉颜料，其特征在于，
所述离子液体为N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐。
7.根据权利要求6所述的慢干型水粉颜料，其特征在于，
参照下述合成路径合成所述N-甲基-N-甲氨基甲酰基咪唑全氟丁酸盐：
第一步：C2H4OCl + C4H6N2→ [C2mim]Cl
第二步：[C2mim]Cl+C3F7COONa→ [C2mim]C3F7COO + NaCl；
其中，第一步的反应条件包括：N-甲基咪唑与甲氨基甲酰氯的摩尔比为1:1.0~1.05，反应温度为95-105℃；
第二步的反应条件包括：[C2mim]Cl与 C3F7COONa的摩尔比为1：1.0~1.05。
8.根据权利要求1-7任一项所述的慢干型水粉颜料，其特征在于，所述颜料色粉包括钛白、铁红、铁黄、铁黑、中黄、大红、柠檬黄、酞青蓝、酞青绿、炭黑和永固紫中的至少一种；
所述填充粉料包括碳酸钙、硫酸钡、滑石粉、云母粉、高岭土、氢氧化铝、玻璃纤维和凹凸棒土中的至少一种；
所述黏度调节剂包括纤维素、气相二氧化硅和膨润土中的一种或几种；
所述的助剂包括分散剂、润湿剂、防腐剂和防霉剂中的一种或几种。
9.一种权利要求1所述的慢干型水粉颜料的制备方法，其特征在于，包括：将水、胶固剂、助剂、颜料色粉和填充粉料混合得到混合浆料；将所述混合浆料与离子液体混合，而后根据浆料的粘度与黏度调节剂混合，而后研磨。