CN115928492A - 一种三维立体特种防伪卡纸及其制备工艺 - Google Patents
一种三维立体特种防伪卡纸及其制备工艺 Download PDFInfo
- Publication number
- CN115928492A CN115928492A CN202211608147.XA CN202211608147A CN115928492A CN 115928492 A CN115928492 A CN 115928492A CN 202211608147 A CN202211608147 A CN 202211608147A CN 115928492 A CN115928492 A CN 115928492A
- Authority
- CN
- China
- Prior art keywords
- counterfeiting
- dimensional
- layer
- parts
- paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种三维立体特种防伪卡纸及其制备工艺，涉及防伪卡纸制备技术领域，包括依次叠加的底层、中间层、面纸层和面涂层，其中底层、中间层和面纸层至少有一层均匀分布三维立体防伪图案或字符，所述三维立体防伪图案或字符包括粘胶剂1‑50份、表面活性剂1‑50份、填充剂1‑20份、溶剂1‑50份、流变剂1‑15份、抗菌剂1‑15、耐磨剂1‑15份、植物油1‑20份，所述三维立体图案利用柔印油墨技术在中间层或底层预设完成图案或文字三维效果，本发明通过添加表面活性剂为聚山梨酯、脂肪酸双酰胺环氧氯丙烷，阳离子表面活性剂中的阳离子与带电负荷的限位结合，疏水基在限位外侧形成低能表面，使得特种防伪卡纸柔软不变形。
Description
技术领域
本发明涉及防伪卡纸制备技术领域，具体为一种三维立体特种防伪卡纸及其制备工艺。
背景技术
特种防伪卡纸是在纸张表面有隐藏标识或标记不易被仿造、改动的特种卡纸的统称，随着科学技术的不断发展，市面上防伪卡纸的种类不断增多，例如纤维纸、防伪全息纸、水印纸等等，纤维纸在造纸时将有色纤维参入纸浆中，在纸卡纸未定型前，进行紫外线照射使得有应该反射，使得卡纸中带有区别卡纸本身的有色纤维来辨别真伪，安全线防伪纸是在造纸时将金属丝埋入纸张内，达到简单区别其他纸张的特性，水印纸的表面有浮雕、透视以及触摸图像，同时水印纸不能被扫描器或者复印机复印的特性被广泛用于证件、书刊或者票据等。
纤维纸、安全线防伪纸以及水印纸通过特殊技术实现立体图案或文字，并依据各有的特性达到防伪的特性，然而在生产工艺技术等方面依然有很多不足之处，例如水印纸在印辊图案制作水印的设备进行改造，投入设备大，纤维纸在紫外光的照射下发出各种颜色的荧光，但生产使用时分布不均匀使得在纸面上经常出现一些有问题的纸张，降低了生产效率和生产质量，安全线防伪纸在生产时操作复杂且在使用时容易造成金属线因磨损导致金属丝脱落，使得安全线防伪纸不利于广泛使用。
发明内容
(一)解决的技术问题
针对现有技术的不足，本发明提供了一种三维立体特种防伪卡纸及其制备工艺，通过添加表面活性剂为聚山梨酯、脂肪酸双酰胺环氧氯丙烷，阳离子表面活性剂中的阳离子与带电负荷的限位结合，疏水基在限位外侧形成低能表面，使得三维立体特种防伪卡纸柔软不变形，通过添加有机溴化物和含有硫化物、氢硫基基团的有机化合物一种或两种以上，具有高效杀死细菌、对人体无危害、杀菌范围广，通过添加耐磨剂，让卡纸耐磨使用时间寿命更长，解决了背景技术卡纸不耐磨的问题。
(二)技术方案
为实现上述目的，本发明提供如下技术方案：一种三维立体特种防伪卡纸，包括依次叠加的底层、中间层、面纸层和面涂层，其中底层、中间层和面纸层至少有一层均匀分布三维立体防伪图案或字符。
所述底层和面涂层均设有多层耐磨防护膜，具体为聚氨酯树脂通过喷砂清洗后处理得到聚酯薄膜。
所述中间层设有由棉浆和麻浆按照1:9-9:1比例混合挤压、干燥而成。
所述面纸层由植物纤维表面嫁接纳米二氧化钛粒子组成，所述植物纤维为棉花、大豆、菜籽、花生中任意一种。
优选的，所述三维立体防伪图案或字符包括粘胶剂1-50份、表面活性剂1-50份、填充剂1-20份、溶剂1-50份、流变剂1-15份、抗菌剂1-15、耐磨剂1-15份、植物油1-20份。
优选的，所述三维立体图案利用柔印油墨技术在中间层或底层预设完成图案或文字三维效果。
优选的，所述粘胶剂为脲醛胶水、改性三胺胶水、苯丙乳液、聚乳酸、壳聚糖、纤维素或纤维素衍生物一种或两种以上混合物，所述表面活性剂为聚山梨酯、脂肪酸双酰胺环氧氯丙烷，阳离子表面活性剂中的阳离子与带电负荷的限位结合，疏水基在限位外侧形成低能表面，使得特种防伪卡纸柔软不变形。
优选的，所述填充剂为碳酸钙、高岭土、二氧化硅、吸水树脂、氧化铝一种或两种以上混合物，所述溶剂为丙酮、异丙醇、乙醇、二甲基甲酰胺或二甲基亚砜，所述流变剂为纤维素衍生物、聚氨酯、丙烯酸或硅藻土。
优选的，所述抗菌剂为有机溴化物和含有硫化物、氢硫基基团的有机化合物，具有高效杀死细菌、对人体无危害、杀菌范围广，所述耐磨剂为直链烷烃类，让卡纸耐磨使用时间寿命更长，所述植物油为大豆油、菜籽油、花生油或芝麻油。
优选的，遇水时该特征防伪卡纸表面会发生凸起且显现防伪三维立体文字或图案，干燥后防伪三维立体文字或图案消失。
优选的，具体按照如下步骤：
步骤10、配制涂料并制作浆料；
步骤20、将浆料捞出压制成型各层湿纸层；
步骤30、在面纸层和中间层或中间层和中间层进行喷淋，并控制纸机的运行速度，实现无色防伪图案或文字的稳定并进行压印；
步骤40、将无色防伪图案或文字的面、中间、底层纸复合后再干燥、UV柔印后再涂布、干燥、收卷打包获得三维立体特种防伪卡纸。
优选的，所述UV柔印利用UV柔印油墨印刷在无色卡纸的正面涂布，其涂布网纹辊线数为60-150L/cm。
优选的，所述特征防伪卡纸的三维立体文字或图案中含有硅胶粉末。
(三)有益效果
本发明提供了一种三维立体特种防伪卡纸及其制备工艺，具备以下有益效果：
(1)三维立体特种防伪卡纸，通过表面活性剂为聚山梨酯、脂肪酸双酰胺环氧氯丙烷，阳离子表面活性剂中的阳离子与带电负荷的限位结合，疏水基在限位外侧形成低能表面，使得特种防伪卡纸柔软不变形。
(2)三维立体特种防伪卡纸，通过抗菌剂为有机溴化物和含有硫化物、氢硫基基团的有机化合物，具有高效杀死细菌、对人体无危害、杀菌范围广，所述耐磨剂为直链烷烃类，让卡纸耐磨使用时间寿命更长。
具体实施方式
基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其他实施例，都属于本发明保护的范围。
实施例1
本发明提供一种技术方案：一种三维立体特种防伪卡纸，包括依次叠加的底层、中间层、面纸层和面涂层，其中底层、中间层和面纸层至少有一层均匀分布三维立体防伪图案或字符。
所述底层和面涂层均设有多层耐磨防护膜，具体为聚氨酯树脂通过喷砂清洗后处理得到聚酯薄膜。
所述中间层设有由棉浆和麻浆按照1:9-9:1比例混合挤压、干燥而成。
所述面纸层由植物纤维表面嫁接纳米二氧化钛粒子组成，所述植物纤维为棉花、大豆、菜籽、花生中任意一种。
其中三维立体防伪图案或字符包括粘胶剂25份、表面活性剂25份、填充剂10份、溶剂25份、流变剂8份、抗菌剂8、耐磨剂8份、植物油10份。
其中三维立体图案利用柔印油墨技术在中间层或底层预设完成图案或文字三维效果。
其中粘胶剂为脲醛胶水、改性三胺胶水、苯丙乳液、聚乳酸、壳聚糖、纤维素或纤维素衍生物一种或两种以上混合物，所述表面活性剂为聚山梨酯、脂肪酸双酰胺环氧氯丙烷。
其中填充剂为碳酸钙、高岭土、二氧化硅、吸水树脂、氧化铝一种或两种以上混合物，所述溶剂为丙酮、异丙醇、乙醇、二甲基甲酰胺或二甲基亚砜，所述流变剂为纤维素衍生物、聚氨酯、丙烯酸或硅藻土。
其中抗菌剂为有机溴化物和含有硫化物、氢硫基基团的有机化合物，所述耐磨剂为直链烷烃类，所述植物油为大豆油、菜籽油、花生油或芝麻油。
遇水时该特征防伪卡纸表面会发生凸起且显现防伪三维立体文字或图案，干燥后防伪三维立体文字或图案消失。
一种三维立体特种防伪卡纸的制备工艺，具体按照如下步骤：
步骤10、配制涂料并制作浆料；
步骤20、将浆料捞出压制成型各层湿纸层；
步骤30、在面纸层和中间层或中间层和中间层进行喷淋，并控制纸机的运行速度，实现无色防伪图案或文字的稳定并进行压印；
步骤40、将无色防伪图案或文字的面、中间、底层纸复合后再干燥、UV柔印后再涂布、干燥、收卷打包获得三维立体特种防伪卡纸。
其中UV柔印利用UV柔印油墨印刷在无色卡纸的正面涂布，其涂布网纹辊线数为60L/cm。
其中特征防伪卡纸的三维立体文字或图案中含有硅胶粉末。
实施例2
本发明提供一种技术方案：一种三维立体特种防伪卡纸，包括依次叠加的底层、中间层、面纸层和面涂层，其中底层、中间层和面纸层至少有一层均匀分布三维立体防伪图案或字符。
所述底层和面涂层均设有多层耐磨防护膜，具体为聚氨酯树脂通过喷砂清洗后处理得到聚酯薄膜。
所述中间层设有由棉浆和麻浆按照1:9-9:1比例混合挤压、干燥而成。
所述面纸层由植物纤维表面嫁接纳米二氧化钛粒子组成，所述植物纤维为棉花、大豆、菜籽、花生中任意一种。
其中三维立体防伪图案或字符包括粘胶剂50份、表面活性剂50份、填充剂20份、溶剂50份、流变剂15份、抗菌剂15、耐磨剂15份、植物油20份。
其中三维立体图案利用柔印油墨技术在中间层或底层预设完成图案或文字三维效果。
其中粘胶剂为脲醛胶水、改性三胺胶水、苯丙乳液、聚乳酸、壳聚糖、纤维素或纤维素衍生物一种或两种以上混合物，所述表面活性剂为聚山梨酯、脂肪酸双酰胺环氧氯丙烷。
其中填充剂为碳酸钙、高岭土、二氧化硅、吸水树脂、氧化铝一种或两种以上混合物，所述溶剂为丙酮、异丙醇、乙醇、二甲基甲酰胺或二甲基亚砜，所述流变剂为纤维素衍生物、聚氨酯、丙烯酸或硅藻土。
其中抗菌剂为有机溴化物和含有硫化物、氢硫基基团的有机化合物，，所述耐磨剂为直链烷烃类，所述植物油为大豆油、菜籽油、花生油或芝麻油。
遇水时该特征防伪卡纸表面会发生凸起且显现防伪三维立体文字或图案，干燥后防伪三维立体文字或图案消失。
一种三维立体特种防伪卡纸的制备工艺，具体按照如下步骤：
步骤10、配制涂料并制作浆料；
步骤20、将浆料捞出压制成型各层湿纸层；
步骤30、在面纸层和中间层或中间层和中间层进行喷淋，并控制纸机的运行速度，实现无色防伪图案或文字的稳定并进行压印；
步骤40、将无色防伪图案或文字的面、中间、底层纸复合后再干燥、UV柔印后再涂布、干燥、收卷打包获得三维立体特种防伪卡纸。
其中UV柔印利用UV柔印油墨印刷在无色卡纸的正面涂布，其涂布网纹辊线数为150L/cm。
其中特征防伪卡纸的三维立体文字或图案中含有硅胶粉末。
综上所述，该三维立体特种防伪卡纸，通过表面活性剂为聚山梨酯、脂肪酸双酰胺环氧氯丙烷，阳离子表面活性剂中的阳离子与带电负荷的限位结合，疏水基在限位外侧形成低能表面，使得特种防伪卡纸柔软不变形通过抗菌剂为有机溴化物和含有硫化物、氢硫基基团的有机化合物，具有高效杀死细菌、对人体无危害、杀菌范围广，所述耐磨剂为直链烷烃类，让卡纸耐磨使用时间寿命更长，解决了卡纸不耐磨的问题。
需要说明的是，在本文中，如若存在第一和第二等之类的关系术语仅仅用来将一个实体或者操作与另一个实体或操作区分开来，而不一定要求或者暗示这些实体或操作之间存在任何这种实际的关系或者顺序。而且，术语“包括”、“包含”或者其任何其他变体意在涵盖非排他性的包含，从而使得包括一系列要素的过程、方法、物品或者设备不仅包括那些要素，而且还包括没有明确列出的其他要素，或者是还包括为这种过程、方法、物品或者设备所固有的要素。在没有更多限制的情况下，由语句“包括一个……”限定的要素，并不排除在包括所述要素的过程、方法、物品或者设备中还存在另外的相同要素。
尽管已经示出和描述了本发明的实施例，对于本领域的普通技术人员而言，可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型，本发明的范围由所附权利要求及其等同物限定。
Claims (10)
1.一种三维立体特种防伪卡纸，其特征在于：包括依次叠加的底层、中间层、面纸层和面涂层，中底层、中间层和面纸层至少有一层均匀分布三维立体防伪图案或字符，
所述底层和面涂层均设有多层耐磨防护膜，具体为聚氨酯树脂通过喷砂清洗后处理得到聚酯薄膜，
所述中间层设有由棉浆和麻浆按照1:9-9:1比例混合挤压、干燥而成，
所述面纸层由植物纤维表面嫁接纳米二氧化钛粒子组成，所述植物纤维为棉花、大豆、菜籽、花生中任意一种。
2.根据权利要求1所述的一种三维立体特种防伪卡纸，其特征在于：所述三维立体防伪图案或字符包括粘胶剂1-50份、表面活性剂1-50份、填充剂1-20份、溶剂1-50份、流变剂1-15份、抗菌剂1-15、耐磨剂1-15份、植物油1-20份。
3.根据权利要求1所述的一种三维立体特种防伪卡纸，其特征在于：所述三维立体图案利用柔印油墨技术在中间层或底层预设完成图案或文字三维效果。
4.根据权利要求1所述的一种三维立体特种防伪卡纸及其制备工艺，其特征在于：所述粘胶剂为脲醛胶水、改性三胺胶水、苯丙乳液、聚乳酸、壳聚糖、纤维素或纤维素衍生物一种或两种以上混合物，所述表面活性剂为聚山梨酯、脂肪酸双酰胺环氧氯丙烷。
5.根据权利要求5所述的一种三维立体特种防伪卡纸，其特征在于：所述填充剂为碳酸钙、高岭土、二氧化硅、吸水树脂、氧化铝一种或两种以上混合物，所述溶剂为丙酮、异丙醇、乙醇、二甲基甲酰胺或二甲基亚砜，所述流变剂为纤维素衍生物、聚氨酯、丙烯酸或硅藻土。
6.根据权利要求1所述的一种三维立体特种防伪卡纸，其特征在于：所述抗菌剂为有机溴化物和含有硫化物、氢硫基基团的有机化合物，所述植物油为大豆油、菜籽油、花生油或芝麻油。
7.根据权利要求1-4任一项所述的一种三维立体特种防伪卡纸的制备工艺，其特征在于：所述三维立体防伪图案或字符遇水时该特征防伪卡纸表面会发生凸起且显现防伪三维立体文字或图案，干燥后防伪三维立体文字或图案消失。
8.根据权利要求7所述的一种三维立体特种防伪卡纸的制备工艺，其特征在于：具体按照如下步骤：
步骤10、配制涂料并制作浆料；
步骤20、将浆料捞出压制成型各层湿纸层；
步骤30、在面纸层和中间层或中间层和中间层进行喷淋，并控制纸机的运行速度，实现无色防伪图案或文字的稳定并进行压印；
步骤40、将无色防伪图案或文字的面、中间、底层纸复合后再干燥、UV柔印后再涂布、干燥、收卷打包获得三维立体特种防伪卡纸。
9.根据权利要求8所述的一种三维立体特种防伪卡纸的制备工艺，其特征在于：所述UV柔印利用UV柔印油墨印刷在无色卡纸的正面涂布，其涂布网纹辊线数为60-150L/cm。
10.根据权利要求7所述的一种三维立体特种防伪卡纸的制备工艺，其特征在于：所述特征防伪卡纸的三维立体文字或图案中含有硅胶粉末。