CN115584170A - 一种具有天然气孔艺术效果的墙面微水泥及其制备方法 - Google Patents
一种具有天然气孔艺术效果的墙面微水泥及其制备方法 Download PDFInfo
- Publication number
- CN115584170A CN115584170A CN202211233891.6A CN202211233891A CN115584170A CN 115584170 A CN115584170 A CN 115584170A CN 202211233891 A CN202211233891 A CN 202211233891A CN 115584170 A CN115584170 A CN 115584170A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- micro
- water
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明属于墙面微水泥领域，尤其是一种具有天然气孔艺术效果的墙面微水泥及其制备方法，其墙面微水泥包括粉料和液料，粉料包括以下重量份的原料：52.5白水泥20‑60份，20‑325目石英砂40‑80份，滑石粉0‑10份，高岭土0‑10份，其制备方法，包括以下几个步骤：S1、液料混合；S2、固料混合；本发明不同目数的石英砂级配，还可以使涂层形成光滑细腻或粗糙的纹理效果，还可加入色浆调出各种颜色，满足不同消费需求；天然气孔效果在批刮面层微水泥时采用特殊施工工艺得到，而非配方中加入物理或化学发泡剂制的，避免微水泥表面的气孔、蜂窝和麻面等缺陷，提高微水泥的密实度，从而提高墙面强度。
Description
技术领域
本发明涉及墙面微水泥领域，尤其涉及一种具有天然气孔艺术效果的墙面微水泥及其制备方法。
背景技术
现有的墙面微水泥在使用过程中存在硬度、粘结力、抗压强度较低的缺陷；普通水泥的环保级别不够，若配方比例不当，使用久了容易起灰起沙，此外，普通水泥的收缩性不佳，容易开裂形成裂纹，并且耐磨性较差；
目前市面上墙面微水泥艺术涂料施工时是用抹刀平批，施工后侘祭风艺术效果比较单调，其艺术效果与清水混凝土差别不大。
发明内容
本发明的目的是为了解决现有技术中存在墙面微水泥艺术涂料施工时是用抹刀平批，施工后侘祭风艺术效果比较单调，其艺术效果与清水混凝土差别不大的缺点，而提出的一种具有天然气孔艺术效果的墙面微水泥及其制备方法。
本发明提出的一种具有天然气孔艺术效果的墙面微水泥，包括粉料和液料，粉料包括以下重量份的原料：52.5白水泥20-60份，20-325目石英砂40-80份，滑石粉0-10份，高岭土0-10份；白色铝酸盐水泥0-5份，缓凝剂0-3份，保水剂0-0.5份，淀粉醚0-0.5份，粉末消泡剂0-0.5份，减水剂0-0.3份，液料包括以下重量份的原料：丙烯酸乳液40-60份，成膜助剂0-5份，液体消泡剂0-0.5份，抗菌剂0-0.5份，水40-60份，粉料和液料质量比为100：20-40。
优选的，所述丙烯酸乳液为苯丙或纯丙中的一种或两种，消泡剂为矿物油类消泡剂、有机硅类消泡剂中的一种或几种的组合。
优选的，所述抗菌剂为1,2-苯并异噻唑啉-3-酮/2-甲基-4异噻唑啉。
优选的，所述白水泥为阿尔博牌52.5白水泥；石英砂为白度≥90，SiO2含量≥99％的石英砂，其目数为20-40目、40-80目、80-120目、120-180目、200目和325目中的一种或几种。
优选的，所述滑石粉目数为400目；白色铝酸盐水泥为塞卡CA70铝酸盐水泥；缓凝剂为柠檬酸钠；减水剂为聚羧酸类减水剂；保水剂为羟丙基甲基纤维素醚，分子量为4-6万；淀粉醚为改性马铃薯淀粉醚；粉末消泡剂为矿物油型或有机硅消泡剂中的一种或几种。
本发明还提出了一种具有天然气孔艺术效果的墙面微水泥的制备方法，包括以下几个步骤：
S1、液料混合：取丙烯酸乳液50份，水50份，消泡剂0.5份，抗菌剂0.3份，加入混合釜中，打开搅拌电机对液体原料进行搅拌混合，搅拌30min，得到液体混合原料；
S2、固料混合：取水泥35份，20-40目石英砂10份，40-80目石英砂30份，325目石英砂高15份，岭土5份，滑石粉5份，铝酸盐水泥3份，缓凝剂1份，保水剂0.2份，纤维素醚0.2份，减水剂0.2份，消泡剂0.2份，加入密封干粉混料机中，打开搅拌电机对固体原料进行均匀的搅拌混合，得到固体混合原料；
S3、现场应用：取100份固体混合原料与30份液体混合原料，根据需要加入水性色浆进行调色，混合搅拌均匀；
S4、天然气孔艺术效果的制备。
优选的，所述S4中，天然气孔艺术效果的制备：
4.1、将水性墙面涂料搅拌均匀后在批刮在墙面上；
4.2、批完后用带把手的一定面积平面工具摁压后提起，快速重复该动作以形成一定高度的不规则凸起；
4.3、然后用度塑料布覆盖，再用带把手的一定面积平面工具压平；
4.4、最后待物料完全干燥后去除塑料布，并用80-120目砂纸打磨，即可得到天然气孔艺术效果。
优选的，所述4.1中，批刮厚度为2-5mm，厚度根据需要形成的气孔深度决定，深度越深，批刮厚度越厚，4.2和4.3中一定面积平面工具，是一定面积的带把手的平面不锈钢、一定面积的带把手的平面塑料或者一定面积的带把手的平面木板，4.3中压平的力度会影响气孔的深度及大小，力度越大，气孔深度越浅，面积越大。
本发明的有益效果是：
(1)视觉效果丰富，艺术性好：不同目数的石英砂级配，还可以使涂层形成光滑细腻或粗糙的纹理效果，还可加入色浆调出各种颜色，满足不同消费需求；天然气孔效果在批刮面层微水泥时采用特殊施工工艺得到，而非配方中加入物理或化学发泡剂制的，避免微水泥表面的气孔、蜂窝和麻面等缺陷，提高微水泥的密实度，从而提高墙面强度。
(2)柔韧性好，涂层中含有有机水性丙烯酸乳液，可使涂层具有良好的柔韧性，涂层不易开裂。
(3)涂层防潮防霉，且防水性能好，水中浸泡不会起皱起皮及脱落，不渗水，不变色；
(4)无甲醛等有机物释放，绿色环保：本发明所用装饰涂层以水泥基无机胶凝材料为主，涂层中有机物含量在10％以下，而且所用的有机物为水性丙烯酸乳液，符合GB18582-2020建筑用墙面涂料中有害物质限量标准要求。
具体实施方式
下面结合具体实施例对本发明作进一步解说。
实施例一
本发明提出了一种具有天然气孔艺术效果的墙面微水泥，包括以下重量份的原料：包括粉料和液料，粉料包括以下重量份的原料：52.5白水泥20份，20目石英砂40份，滑石粉1份，高岭土1份；白色铝酸盐水泥1份，缓凝剂1份，保水剂0.1份，淀粉醚0.1份，粉末消泡剂0.1份，减水剂0.1份，液料包括以下重量份的原料：丙烯酸乳液40份，成膜助剂1份，液体消泡剂0.1份，抗菌剂0.1份，水40份，粉料和液料质量比为100：20。
本实施例中，丙烯酸乳液为苯丙或纯丙中的一种或两种，消泡剂为矿物油类消泡剂、有机硅类消泡剂中的一种或几种的组合。
本实施例中，抗菌剂为1,2-苯并异噻唑啉-3-酮/2-甲基-4异噻唑啉。
本实施例中，白水泥为阿尔博牌52.5白水泥；石英砂为白度≥90，SiO2含量≥99％的石英砂，其目数为20目、40目、80目、120目、200目和325目中的一种或几种。
本实施例中，滑石粉目数为400目；白色铝酸盐水泥为塞卡CA70铝酸盐水泥；缓凝剂为柠檬酸钠；减水剂为聚羧酸类减水剂；保水剂为羟丙基甲基纤维素醚，分子量为4万；淀粉醚为改性马铃薯淀粉醚；粉末消泡剂为矿物油型或有机硅消泡剂中的一种或几种。
本实施例还提出了一种具有天然气孔艺术效果的墙面微水泥的制备方法，包括以下几个步骤：
S1、液料混合：取丙烯酸乳液，水，消泡剂，抗菌剂，加入混合釜中，打开搅拌电机对液体原料进行搅拌混合，搅拌30min，得到液体混合原料；
S2、固料混合：取水泥，20目石英砂，40目石英砂，325目石英砂高，岭土，滑石粉，铝酸盐水泥，缓凝剂，保水剂，纤维素醚，减水剂，消泡剂，加入密封干粉混料机中，打开搅拌电机对固体原料进行均匀的搅拌混合，得到固体混合原料；
S3、现场应用：取100份固体混合原料与20份液体混合原料，根据需要加入水性色浆进行调色，混合搅拌均匀。
S4、天然气孔艺术效果的制备。
本实施例中，S4中，天然气孔艺术效果的制备：
4.1、将水性墙面涂料搅拌均匀后在批刮在墙面上；
4.2、批完后用带把手的一定面积平面工具摁压后提起，快速重复该动作以形成一定高度的不规则凸起；
4.3、然后用度塑料布覆盖，再用带把手的一定面积平面工具压平；
4.4、最后待物料完全干燥后去除塑料布，并用80目砂纸打磨，即可得到天然气孔艺术效果。
本实施例中，4.1中，批刮厚度为2mm，厚度根据需要形成的气孔深度决定，深度越深，批刮厚度越厚，4.2和4.3中一定面积平面工具，是一定面积的带把手的平面不锈钢、一定面积的带把手的平面塑料或者一定面积的带把手的平面木板，4.3中压平的力度会影响气孔的深度及大小，力度越大，气孔深度越浅，面积越大。
实施例二
本发明提出了一种具有天然气孔艺术效果的墙面微水泥，包括以下原料：包括粉料和液料，粉料包括以下原料：52.5白水泥，目石英砂，滑石粉，高岭土；白色铝酸盐水泥，缓凝剂，保水剂，淀粉醚，粉末消泡剂，减水剂，液料包括以下原料：丙烯酸乳液份，成膜助剂份，液体消泡剂份，抗菌剂，水，粉料和液料质量比为100：30。
本实施例中，丙烯酸乳液为苯丙或纯丙中的一种或两种，消泡剂为矿物油类消泡剂、有机硅类消泡剂中的一种或几种的组合。
本实施例中，抗菌剂为1,2-苯并异噻唑啉-3-酮/2-甲基-4异噻唑啉。
本实施例中，白水泥为阿尔博牌52.5白水泥；石英砂为白度≥90，SiO2含量≥99％的石英砂，其目数为30目、60目、100目、150目、200目和325目中的一种或几种。
本实施例中，滑石粉目数为400目；白色铝酸盐水泥为塞卡CA70铝酸盐水泥；缓凝剂为柠檬酸钠；减水剂为聚羧酸类减水剂；保水剂为羟丙基甲基纤维素醚，分子量为5万；淀粉醚为改性马铃薯淀粉醚；粉末消泡剂为矿物油型或有机硅消泡剂中的一种或几种。
本实施例还提出了一种具有天然气孔艺术效果的墙面微水泥的制备方法，包括以下几个步骤：
S1、液料混合：取丙烯酸乳液50份，水50份，消泡剂0.5份，抗菌剂0.3份，加入混合釜中，打开搅拌电机对液体原料进行搅拌混合，搅拌30min，得到液体混合原料；
S2、固料混合：取水泥35份，30目石英砂10份，60目石英砂30份，325目石英砂高15份，岭土5份，滑石粉5份，铝酸盐水泥3份，缓凝剂1份，保水剂0.2份，纤维素醚0.2份，减水剂0.2份，消泡剂0.2份，加入密封干粉混料机中，打开搅拌电机对固体原料进行均匀的搅拌混合，得到固体混合原料；
S3、现场应用：取100份固体混合原料与30份液体混合原料，根据需要加入水性色浆进行调色，混合搅拌均匀。
S4、天然气孔艺术效果的制备。
本实施例中，S4中，天然气孔艺术效果的制备：
4.1、将水性墙面涂料搅拌均匀后在批刮在墙面上；
4.2、批完后用带把手的一定面积平面工具摁压后提起，快速重复该动作以形成一定高度的不规则凸起；
4.3、然后用度塑料布覆盖，再用带把手的一定面积平面工具压平；
4.4、最后待物料完全干燥后去除塑料布，并用100目砂纸打磨，即可得到天然气孔艺术效果。
本实施例中，4.1中，批刮厚度为3mm，厚度根据需要形成的气孔深度决定，深度越深，批刮厚度越厚，4.2和4.3中一定面积平面工具，是一定面积的带把手的平面不锈钢、一定面积的带把手的平面塑料或者一定面积的带把手的平面木板，4.3中压平的力度会影响气孔的深度及大小，力度越大，气孔深度越浅，面积越大。
本发明不同目数的石英砂级配，还可以使涂层形成光滑细腻或粗糙的纹理效果，还可加入色浆调出各种颜色，满足不同消费需求；天然气孔效果在批刮面层微水泥时采用特殊施工工艺得到，而非配方中加入物理或化学发泡剂制的，避免微水泥表面的气孔、蜂窝和麻面等缺陷，提高微水泥的密实度，从而提高墙面强度，同时视觉效果丰富，艺术性好。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (8)
1.一种具有天然气孔艺术效果的墙面微水泥，其特征在于，包括粉料和液料，粉料包括以下重量份的原料：52.5白水泥20-60份，20-325目石英砂40-80份，滑石粉0-10份，高岭土0-10份；白色铝酸盐水泥0-5份，缓凝剂0-3份，保水剂0-0.5份，淀粉醚0-0.5份，粉末消泡剂0-0.5份，减水剂0-0.3份，液料包括以下重量份的原料：丙烯酸乳液40-60份，成膜助剂0-5份，液体消泡剂0-0.5份，抗菌剂0-0.5份，水40-60份，粉料和液料质量比为100：20-40。
2.根据权利要求1所述的一种具有天然气孔艺术效果的墙面微水泥，其特征在于，所述丙烯酸乳液为苯丙或纯丙中的一种或两种，消泡剂为矿物油类消泡剂、有机硅类消泡剂中的一种或几种的组合。
3.根据权利要求2所述的一种具有天然气孔艺术效果的墙面微水泥，其特征在于，所述抗菌剂为1,2-苯并异噻唑啉-3-酮/2-甲基-4异噻唑啉。
4.根据权利要求3所述的一种具有天然气孔艺术效果的墙面微水泥，其特征在于，所述白水泥为阿尔博牌52.5白水泥；石英砂为白度≥90，SiO2含量≥99％的石英砂，其目数为20-40目、40-80目、80-120目、120-180目、200目和325目中的一种或几种。
5.根据权利要求4所述的一种具有天然气孔艺术效果的墙面微水泥，其特征在于，所述滑石粉目数为400目；白色铝酸盐水泥为塞卡CA70铝酸盐水泥；缓凝剂为柠檬酸钠；减水剂为聚羧酸类减水剂；保水剂为羟丙基甲基纤维素醚，分子量为4-6万；淀粉醚为改性马铃薯淀粉醚；粉末消泡剂为矿物油型或有机硅消泡剂中的一种或几种。
6.一种具有天然气孔艺术效果的墙面微水泥的制备方法，其特征在于，包括以下几个步骤：
S1、液料混合：取丙烯酸乳液50份，水50份，消泡剂0.5份，抗菌剂0.3份，加入混合釜中，打开搅拌电机对液体原料进行搅拌混合，搅拌30min，得到液体混合原料；
S2、固料混合：取水泥35份，20-40目石英砂10份，40-80目石英砂30份，325目石英砂高15份，岭土5份，滑石粉5份，铝酸盐水泥3份，缓凝剂1份，保水剂0.2份，纤维素醚0.2份，减水剂0.2份，消泡剂0.2份，加入密封干粉混料机中，打开搅拌电机对固体原料进行均匀的搅拌混合，得到固体混合原料；
S3、现场应用：取100份固体混合原料与30份液体混合原料，根据需要加入水性色浆进行调色，混合搅拌均匀；
S4、天然气孔艺术效果的制备。
7.根据权利要求6所述的一种具有天然气孔艺术效果的墙面微水泥的制备方法，其特征在于，所述S4中，天然气孔艺术效果的制备：
4.1、将水性墙面涂料搅拌均匀后在批刮在墙面上；
4.2、批完后用带把手的一定面积平面工具摁压后提起，快速重复该动作以形成一定高度的不规则凸起；
4.3、然后用度塑料布覆盖，再用带把手的一定面积平面工具压平；
4.4、最后待物料完全干燥后去除塑料布，并用80-120目砂纸打磨，即可得到天然气孔艺术效果。
8.根据权利要求7所述的一种具有天然气孔艺术效果的墙面微水泥的制备方法，其特征在于，所述4.1中，批刮厚度为2-5mm，厚度根据需要形成的气孔深度决定，深度越深，批刮厚度越厚，4.2和4.3中一定面积平面工具，是一定面积的带把手的平面不锈钢、一定面积的带把手的平面塑料或者一定面积的带把手的平面木板，4.3中压平的力度会影响气孔的深度及大小，力度越大，气孔深度越浅，面积越大。