CN115382509A - 一种绿色无毒的甲醛清除剂 - Google Patents
一种绿色无毒的甲醛清除剂 Download PDFInfo
- Publication number
- CN115382509A CN115382509A CN202210597511.0A CN202210597511A CN115382509A CN 115382509 A CN115382509 A CN 115382509A CN 202210597511 A CN202210597511 A CN 202210597511A CN 115382509 A CN115382509 A CN 115382509A
- Authority
- CN
- China
- Prior art keywords
- formaldehyde scavenger
- reaction kettle
- chemical reaction
- bentonite
- titanium dioxide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种绿色无毒的甲醛清除剂，属于空气净化技术领域，按重量百分比计，所述甲醛清除剂包括辅料11‑15％、活性炭纤维4‑6％、硅藻土2‑3％、改性纳米二氧化钛3‑7％、膨润土0.1‑0.5％、菠萝叶纤维1‑3％、其余为水，所述甲醛清除剂的pH在6.5‑8.5之间。本发明中，能够快速净化空气中的微量甲醛，净化深度小于0.1毫克每立方米，将改性纳米二氧化钛与载体备用料进行复合后再用于甲醛清除，能够延长甲醛清除剂的有效时间和清除效果，通过在甲醛清除剂中加入辅料、菠萝叶纤维、和膨润土能够提高上述复合料在甲醛清除剂中的分散效果，提高喷雾的效果。
Description
技术领域
本发明属于空气净化技术领域，尤其涉及一种绿色无毒的甲醛清除剂。
背景技术
背景技术：近年来家装安全日益受到人们的关注，家装污染物是导致家装安全事件的直接因素，甲醛对人身体健康所造成的影响被人们所广泛认识。
现有技术中已经有一些关于消除甲醛的技术，通常只能够起到暂时清除的效果，并不是从根本上消除，有效时间较短，吸附量小，达到平衡时间短，而且活性炭对于甲酵吸附性能较差，在环境条件变化之后，甲醛容易从活性炭中再次释放出来导致脱附现象发生。
基于此，本发明设计了一种绿色无毒的甲醛清除剂，以解决上述问题。
发明内容
本发明的目的在于：为了解决现有技术中已经有一些关于消除甲醛的技术，通常只能够起到暂时清除的效果，并不是从根本上消除，有效时间较短，吸附量小，达到平衡时间短，而且活性炭对于甲酵吸附性能较差，在环境条件变化之后，甲醛容易从活性炭中再次释放出来导致脱附现象发生的问题，而提出的一种绿色无毒的甲醛清除剂。
为了实现上述目的，本发明采用了如下技术方案：
一种绿色无毒的甲醛清除剂，按重量百分比计，所述甲醛清除剂包括辅料11-15％、活性炭纤维4-6％、硅藻土2-3％、改性纳米二氧化钛3-7％、膨润土0.1—0.5％、菠萝叶纤维1—3％、其余为水，所述甲醛清除剂的pH在6.5-8.5之间。
作为上述技术方案的进一步描述：
所述辅料包括天然海泡石、活性炭粉和可溶性特种金属盐，按重量百分比计，所述辅料包括天然海泡石10-20％、活性炭粉1-3％和可溶性特种金属盐1-2％。
作为上述技术方案的进一步描述：
所述辅料由以下方法制备而成：
将天然海泡石投放到球磨机中，球磨一段时间后过筛，获得天然海泡石粉；
在所获得的天然海泡石粉中加入活性炭粉，待活性炭粉和天然海泡石粉混合均匀后，加入可溶性特种金属盐，获得混合溶液；
使用捏合机对混合溶液进行捏合处理，然后使用挤出设备挤出成型，获得初级辅料；
将挤出成型后的初级辅料放入真空烘干机中烘干成型，将烘干成型后的初级辅料放入球磨机中，随后过筛处理，获得辅料。
作为上述技术方案的进一步描述：
所述活性炭纤维和硅藻土制备载体备用料，所述载体备用料的制备方法包括：
使用剪切设备将活性炭纤维剪切成条形小块；
将条形小块和硅藻土投放到盛放有去离子水的烧杯中，55-65℃水浴环境下浸泡1.2h；
然后将水浴浸泡后的条形小块和硅藻土放入真空烘干机中干燥2.5-3.3h，获得载体备用料。
作为上述技术方案的进一步描述：
所述改性纳米二氧化钛的制备方法包括：
将四氯化钛注入到配置有磁搅拌机构的化学反应釜中，注入一定量的蒸馏水搅拌混合；
待四氯化钛完全溶解后，于惰性气体环境下进行冷却降温处理，直至化学反应釜中不再有白色烟雾冒出；
向化学反应釜中加入尿素，并将化学反应釜置于55-63℃水浴环境下加热处理，待尿素完全溶解后，将化学反应釜由水浴环境中取出，冷却至室温；
向化学反应釜中加入一定量的活性氧化铝，搅拌30min后，将化学反应釜置于真空干燥箱内，100-110℃环境下干燥8-11h，获得改性纳米二氧化钛。
作为上述技术方案的进一步描述：
所述改性纳米二氧化钛与载体备用料的复合包括：
将改性纳米二氧化钛、无水乙醇、冰醋酸和去离子水注入到带有磁搅拌机构的化学反应釜中，充分混合形成混合溶液；
将载体备用料浸渍在混合溶液中，获得载体溶液；
超声仪中超声8-12min，使改性纳米二氧化钛负载在载体备用料上，提拉后在室内自然风干，然后将风干料放入马弗炉中，并在惰性气体环境下高温煅烧。
作为上述技术方案的进一步描述：
所述膨润土在使用前需进行预处理，所述膨润土的预处理包括：将膨润土浸泡在去离子水中，待膨润土充分分散后，向膨润土中加入盐酸溶液进行活化处理；
活化后抽滤漂洗至呈弱酸性，然后置于真空干燥箱中105-115℃环境下进行烘干处理。
一种绿色无毒的甲醛清除剂的制备方法，所述方法包括：
按重量比称量辅料、活性炭纤维、硅藻土、改性纳米二氧化钛、膨润土、菠萝叶纤维和去离子水；
将上述称量好的原料加入化学反应釜中，加入表面活化剂，在常温下搅拌，直至完全溶解；
静置后，获得透明的甲醛清除剂。
作为上述技术方案的进一步描述：
所述的表面活性剂是烷基硫酸酯钠、氨基磺酸钠、十二烷基硫酸酯钠、仲烷基硫酸钠中的一种。
作为上述技术方案的进一步描述：
所述常温下搅拌，直至完全溶解中的搅拌时长为30min；
所述静置后，获得透明的甲醛清除剂中的静置时长为30min。
综上所述，由于采用了上述技术方案，本发明的有益效果是：
本发明中，能够快速净化空气中的微量甲醛，净化深度小于0.1毫克每立方米，将改性纳米二氧化钛与载体备用料进行复合后再用于甲醛清除，能够延长甲醛清除剂的有效时间和清除效果，通过在甲醛清除剂中加入辅料、菠萝叶纤维、和膨润土能够提高上述复合料在甲醛清除剂中的分散效果，提高喷雾的效果。
具体实施方式
下面将结合本发明实施例，对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅仅是本发明一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有作出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
实施例一
一种绿色无毒的甲醛清除剂，按重量百分比计，所述甲醛清除剂包括辅料11％、活性炭纤维4％、硅藻土2％、改性纳米二氧化钛3％、膨润土0.1％、菠萝叶纤维1％、其余为水，所述甲醛清除剂的pH在6.5之间。
具体的，所述辅料包括天然海泡石、活性炭粉和可溶性特种金属盐，按重量百分比计，所述辅料包括天然海泡石10％、活性炭粉1％和可溶性特种金属盐1％。
具体的，所述辅料由以下方法制备而成：
将天然海泡石投放到球磨机中，球磨一段时间后过筛，获得天然海泡石粉；
在所获得的天然海泡石粉中加入活性炭粉，待活性炭粉和天然海泡石粉混合均匀后，加入可溶性特种金属盐，获得混合溶液；
使用捏合机对混合溶液进行捏合处理，然后使用挤出设备挤出成型，获得初级辅料；
将挤出成型后的初级辅料放入真空烘干机中烘干成型，将烘干成型后的初级辅料放入球磨机中，随后过筛处理，获得辅料。
具体的，所述活性炭纤维和硅藻土制备载体备用料，所述载体备用料的制备方法包括：
使用剪切设备将活性炭纤维剪切成条形小块；
将条形小块和硅藻土投放到盛放有去离子水的烧杯中，55℃水浴环境下浸泡1.2h；
然后将水浴浸泡后的条形小块和硅藻土放入真空烘干机中干燥2.5h，获得载体备用料。
具体的，所述改性纳米二氧化钛的制备方法包括：
将四氯化钛注入到配置有磁搅拌机构的化学反应釜中，注入一定量的蒸馏水搅拌混合；
待四氯化钛完全溶解后，于惰性气体环境下进行冷却降温处理，直至化学反应釜中不再有白色烟雾冒出；
向化学反应釜中加入尿素，并将化学反应釜置于55℃水浴环境下加热处理，待尿素完全溶解后，将化学反应釜由水浴环境中取出，冷却至室温；
向化学反应釜中加入一定量的活性氧化铝，搅拌30min后，将化学反应釜置于真空干燥箱内，100℃环境下干燥8h，获得改性纳米二氧化钛。
具体的，所述改性纳米二氧化钛与载体备用料的复合包括：
将改性纳米二氧化钛、无水乙醇、冰醋酸和去离子水注入到带有磁搅拌机构的化学反应釜中，充分混合形成混合溶液；
将载体备用料浸渍在混合溶液中，获得载体溶液；
超声仪中超声8min，使改性纳米二氧化钛负载在载体备用料上，提拉后在室内自然风干，然后将风干料放入马弗炉中，并在惰性气体环境下高温煅烧。
具体的，所述膨润土在使用前需进行预处理，所述膨润土的预处理包括：将膨润土浸泡在去离子水中，待膨润土充分分散后，向膨润土中加入盐酸溶液进行活化处理；
活化后抽滤漂洗至呈弱酸性，然后置于真空干燥箱中105-115℃环境下进行烘干处理。
一种绿色无毒的甲醛清除剂的制备方法，所述方法包括：
按重量比称量辅料、活性炭纤维、硅藻土、改性纳米二氧化钛、膨润土、菠萝叶纤维和去离子水；
将上述称量好的原料加入化学反应釜中，加入表面活化剂，在常温下搅拌，直至完全溶解；
静置后，获得透明的甲醛清除剂。
具体的，所述的表面活性剂是烷基硫酸酯钠、氨基磺酸钠、十二烷基硫酸酯钠、仲烷基硫酸钠中的一种。
具体的，所述常温下搅拌，直至完全溶解中的搅拌时长为30min；
所述静置后，获得透明的甲醛清除剂中的静置时长为30min。
实施例二
一种绿色无毒的甲醛清除剂，按重量百分比计，所述甲醛清除剂包括辅料15％、活性炭纤维6％、硅藻土3％、改性纳米二氧化钛7％、膨润土0.5％、菠萝叶纤维3％、其余为水，所述甲醛清除剂的pH在8.5之间。
具体的，所述辅料包括天然海泡石、活性炭粉和可溶性特种金属盐，按重量百分比计，所述辅料包括天然海泡石20％、活性炭粉3％和可溶性特种金属盐2％。
具体的，所述辅料由以下方法制备而成：
将天然海泡石投放到球磨机中，球磨一段时间后过筛，获得天然海泡石粉；
在所获得的天然海泡石粉中加入活性炭粉，待活性炭粉和天然海泡石粉混合均匀后，加入可溶性特种金属盐，获得混合溶液；
使用捏合机对混合溶液进行捏合处理，然后使用挤出设备挤出成型，获得初级辅料；
将挤出成型后的初级辅料放入真空烘干机中烘干成型，将烘干成型后的初级辅料放入球磨机中，随后过筛处理，获得辅料。
具体的，所述活性炭纤维和硅藻土制备载体备用料，所述载体备用料的制备方法包括：
使用剪切设备将活性炭纤维剪切成条形小块；
将条形小块和硅藻土投放到盛放有去离子水的烧杯中，65℃水浴环境下浸泡1.2h；
然后将水浴浸泡后的条形小块和硅藻土放入真空烘干机中干燥3.3h，获得载体备用料。
具体的，所述改性纳米二氧化钛的制备方法包括：
将四氯化钛注入到配置有磁搅拌机构的化学反应釜中，注入一定量的蒸馏水搅拌混合；
待四氯化钛完全溶解后，于惰性气体环境下进行冷却降温处理，直至化学反应釜中不再有白色烟雾冒出；
向化学反应釜中加入尿素，并将化学反应釜置于63℃水浴环境下加热处理，待尿素完全溶解后，将化学反应釜由水浴环境中取出，冷却至室温；
向化学反应釜中加入一定量的活性氧化铝，搅拌30min后，将化学反应釜置于真空干燥箱内，110℃环境下干燥11h，获得改性纳米二氧化钛。
具体的，所述改性纳米二氧化钛与载体备用料的复合包括：
将改性纳米二氧化钛、无水乙醇、冰醋酸和去离子水注入到带有磁搅拌机构的化学反应釜中，充分混合形成混合溶液；
将载体备用料浸渍在混合溶液中，获得载体溶液；
超声仪中超声12min，使改性纳米二氧化钛负载在载体备用料上，提拉后在室内自然风干，然后将风干料放入马弗炉中，并在惰性气体环境下高温煅烧。
具体的，所述膨润土在使用前需进行预处理，所述膨润土的预处理包括：将膨润土浸泡在去离子水中，待膨润土充分分散后，向膨润土中加入盐酸溶液进行活化处理；
活化后抽滤漂洗至呈弱酸性，然后置于真空干燥箱中105-115℃环境下进行烘干处理。
一种绿色无毒的甲醛清除剂的制备方法，所述方法包括：
按重量比称量辅料、活性炭纤维、硅藻土、改性纳米二氧化钛、膨润土、菠萝叶纤维和去离子水；
将上述称量好的原料加入化学反应釜中，加入表面活化剂，在常温下搅拌，直至完全溶解；
静置后，获得透明的甲醛清除剂。
具体的，所述的表面活性剂是烷基硫酸酯钠、氨基磺酸钠、十二烷基硫酸酯钠、仲烷基硫酸钠中的一种。
具体的，所述常温下搅拌，直至完全溶解中的搅拌时长为30min；
所述静置后，获得透明的甲醛清除剂中的静置时长为30min。
实施例三
一种绿色无毒的甲醛清除剂，按重量百分比计，所述甲醛清除剂包括辅料13％、活性炭纤维5％、硅藻土2.5％、改性纳米二氧化钛5％、膨润土0.3％、菠萝叶纤维2％、其余为水，所述甲醛清除剂的pH在7之间。
具体的，所述辅料包括天然海泡石、活性炭粉和可溶性特种金属盐，按重量百分比计，所述辅料包括天然海泡石15％、活性炭粉2％和可溶性特种金属盐1.5％。
具体的，所述辅料由以下方法制备而成：
将天然海泡石投放到球磨机中，球磨一段时间后过筛，获得天然海泡石粉；
在所获得的天然海泡石粉中加入活性炭粉，待活性炭粉和天然海泡石粉混合均匀后，加入可溶性特种金属盐，获得混合溶液；
使用捏合机对混合溶液进行捏合处理，然后使用挤出设备挤出成型，获得初级辅料；
将挤出成型后的初级辅料放入真空烘干机中烘干成型，将烘干成型后的初级辅料放入球磨机中，随后过筛处理，获得辅料。
具体的，所述活性炭纤维和硅藻土制备载体备用料，所述载体备用料的制备方法包括：
使用剪切设备将活性炭纤维剪切成条形小块；
将条形小块和硅藻土投放到盛放有去离子水的烧杯中，60℃水浴环境下浸泡1.2h；
然后将水浴浸泡后的条形小块和硅藻土放入真空烘干机中干燥2.8h，获得载体备用料。
具体的，所述改性纳米二氧化钛的制备方法包括：
将四氯化钛注入到配置有磁搅拌机构的化学反应釜中，注入一定量的蒸馏水搅拌混合；
待四氯化钛完全溶解后，于惰性气体环境下进行冷却降温处理，直至化学反应釜中不再有白色烟雾冒出；
向化学反应釜中加入尿素，并将化学反应釜置于59℃水浴环境下加热处理，待尿素完全溶解后，将化学反应釜由水浴环境中取出，冷却至室温；
向化学反应釜中加入一定量的活性氧化铝，搅拌30min后，将化学反应釜置于真空干燥箱内，105℃环境下干燥9h，获得改性纳米二氧化钛。
具体的，所述改性纳米二氧化钛与载体备用料的复合包括：
将改性纳米二氧化钛、无水乙醇、冰醋酸和去离子水注入到带有磁搅拌机构的化学反应釜中，充分混合形成混合溶液；
将载体备用料浸渍在混合溶液中，获得载体溶液；
超声仪中超声10min，使改性纳米二氧化钛负载在载体备用料上，提拉后在室内自然风干，然后将风干料放入马弗炉中，并在惰性气体环境下高温煅烧。
具体的，所述膨润土在使用前需进行预处理，所述膨润土的预处理包括：将膨润土浸泡在去离子水中，待膨润土充分分散后，向膨润土中加入盐酸溶液进行活化处理；
活化后抽滤漂洗至呈弱酸性，然后置于真空干燥箱中105-115℃环境下进行烘干处理。
一种绿色无毒的甲醛清除剂的制备方法，所述方法包括：
按重量比称量辅料、活性炭纤维、硅藻土、改性纳米二氧化钛、膨润土、菠萝叶纤维和去离子水；
将上述称量好的原料加入化学反应釜中，加入表面活化剂，在常温下搅拌，直至完全溶解；
静置后，获得透明的甲醛清除剂。
具体的，所述的表面活性剂是烷基硫酸酯钠、氨基磺酸钠、十二烷基硫酸酯钠、仲烷基硫酸钠中的一种。
具体的，所述常温下搅拌，直至完全溶解中的搅拌时长为30min；
所述静置后，获得透明的甲醛清除剂中的静置时长为30min。
以上所述，仅为本发明较佳的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本技术领域的技术人员在本发明揭露的技术范围内，根据本发明的技术方案及其发明构思加以等同替换或改变，都应涵盖在本发明的保护范围之内。
Claims (10)
1.一种绿色无毒的甲醛清除剂，其特征在于，按重量百分比计，所述甲醛清除剂包括辅料11-15％、活性炭纤维4-6％、硅藻土2-3％、改性纳米二氧化钛3-7％、膨润土0.1-0.5％、菠萝叶纤维1-3％、其余为水，所述甲醛清除剂的pH在6.5-8.5之间。
2.根据权利要求1所述的一种绿色无毒的甲醛清除剂，其特征在于，所述辅料包括天然海泡石、活性炭粉和可溶性特种金属盐，按重量百分比计，所述辅料包括天然海泡石10-20％、活性炭粉1-3％和可溶性特种金属盐1-2％。
3.根据权利要求1所述的一种绿色无毒的甲醛清除剂，其特征在于，所述辅料由以下方法制备而成：
将天然海泡石投放到球磨机中，球磨一段时间后过筛，获得天然海泡石粉；
在所获得的天然海泡石粉中加入活性炭粉，待活性炭粉和天然海泡石粉混合均匀后，加入可溶性特种金属盐，获得混合溶液；
使用捏合机对混合溶液进行捏合处理，然后使用挤出设备挤出成型，获得初级辅料；
将挤出成型后的初级辅料放入真空烘干机中烘干成型，将烘干成型后的初级辅料放入球磨机中，随后过筛处理，获得辅料。
4.根据权利要求1所述的一种绿色无毒的甲醛清除剂，其特征在于，所述活性炭纤维和硅藻土制备载体备用料，所述载体备用料的制备方法包括：
使用剪切设备将活性炭纤维剪切成条形小块；
将条形小块和硅藻土投放到盛放有去离子水的烧杯中，55-65℃水浴环境下浸泡1.2h；
然后将水浴浸泡后的条形小块和硅藻土放入真空烘干机中干燥2.5-3.3h，获得载体备用料。
5.根据权利要求4所述的一种绿色无毒的甲醛清除剂，其特征在于，所述改性纳米二氧化钛的制备方法包括：
将四氯化钛注入到配置有磁搅拌机构的化学反应釜中，注入一定量的蒸馏水搅拌混合；
待四氯化钛完全溶解后，于惰性气体环境下进行冷却降温处理，直至化学反应釜中不再有白色烟雾冒出；
向化学反应釜中加入尿素，并将化学反应釜置于55-63℃水浴环境下加热处理，待尿素完全溶解后，将化学反应釜由水浴环境中取出，冷却至室温；
向化学反应釜中加入一定量的活性氧化铝，搅拌30min后，将化学反应釜置于真空干燥箱内，100-110℃环境下干燥8-11h，获得改性纳米二氧化钛。
6.根据权利要求1所述的一种绿色无毒的甲醛清除剂，其特征在于，所述改性纳米二氧化钛与载体备用料的复合包括：
将改性纳米二氧化钛、无水乙醇、冰醋酸和去离子水注入到带有磁搅拌机构的化学反应釜中，充分混合形成混合溶液；
将载体备用料浸渍在混合溶液中，获得载体溶液；
超声仪中超声8-12min，使改性纳米二氧化钛负载在载体备用料上，提拉后在室内自然风干，然后将风干料放入马弗炉中，并在惰性气体环境下高温煅烧。
7.根据权利要求1所述的一种绿色无毒的甲醛清除剂，其特征在于，所述膨润土在使用前需进行预处理，所述膨润土的预处理包括：将膨润土浸泡在去离子水中，待膨润土充分分散后，向膨润土中加入盐酸溶液进行活化处理；
活化后抽滤漂洗至呈弱酸性，然后置于真空干燥箱中105-115℃环境下进行烘干处理。
8.一种根据权利要求1-7任意一项所述的绿色无毒的甲醛清除剂的制备方法，其特征在于，所述方法包括：
按重量比称量辅料、活性炭纤维、硅藻土、改性纳米二氧化钛、膨润土、菠萝叶纤维和去离子水；
将上述称量好的原料加入化学反应釜中，加入表面活化剂，在常温下搅拌，直至完全溶解；
静置后，获得透明的甲醛清除剂。
9.根据权利要求8所述的一种绿色无毒的甲醛清除剂的制备方法，其特征在于，所述的表面活性剂是烷基硫酸酯钠、氨基磺酸钠、十二烷基硫酸酯钠、仲烷基硫酸钠中的一种。
10.根据权利要求9所述的一种绿色无毒的甲醛清除剂的制备方法，其特征在于，所述常温下搅拌，直至完全溶解中的搅拌时长为30min；
所述静置后，获得透明的甲醛清除剂中的静置时长为30min。