CN115262271A - 一种具有阻燃作用的装饰纸及其制备方法 - Google Patents
一种具有阻燃作用的装饰纸及其制备方法 Download PDFInfo
- Publication number
- CN115262271A CN115262271A CN202210527447.9A CN202210527447A CN115262271A CN 115262271 A CN115262271 A CN 115262271A CN 202210527447 A CN202210527447 A CN 202210527447A CN 115262271 A CN115262271 A CN 115262271A
- Authority
- CN
- China
- Prior art keywords
- decorative
- paper
- dipping
- decorative paper
- base paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种具有阻燃作用的装饰纸及其制备方法，所述制备方法包括：将聚磷酸铵(APP)、氢氧化铝、苯丙乳液和羟甲基纤维素按照一定比例混合，得到浸渍胶；将装饰原纸放入浸渍胶中浸渍不同时间，得到不同浸渍量的装饰原纸；利用热压机将浸渍后的装饰原纸与人造板贴合。本发明制备的阻燃装饰纸可以防止发烟、不产生滴下物、不产生有毒气体。并且，能够在纸张内部与表面形成有效的浸渍层，具有优异的阻燃性。
Description
技术领域
本发明涉及一种装饰纸，尤其是涉及一种具有阻燃作用的装饰纸及其制备方法。
背景技术
装饰纸是很多建材产品中必不可少的原料，如家具、橱柜用到的低压板、高压板，还有防火板、地板等，主要起提供花纹图案的装饰的作用和防止底层胶液渗现的覆盖的作用，装饰纸要求表面平滑，有良好吸收性和适应性，有底色的要求色调均匀，彩色的要求颜色鲜艳，现需要一种具有阻燃作用的装饰纸。
但是现有的装饰纸存在很多问题或缺陷，如传统的阻燃纸不具备良好的阻燃、保温隔热效果等。或者在表面平滑度、透胶性等方面表现较差。
发明内容
针对前述现有技术问题，本发明提供了一种具有阻燃作用的装饰纸及其制备方法，本发明的装饰纸具有优异的阻燃性能，并具有普通装饰纸的表面美观度。
本发明的具有阻燃作用的装饰纸的制备方法，包括以下步骤：
(1)浸渍胶的配制
将聚磷酸铵(APP)、氢氧化铝、苯丙乳液和羟甲基纤维素按照一定比例混合，得到浸渍胶。
(2)装饰原纸的浸渍
将装饰原纸放入浸渍胶中浸渍不同时间，得到不同浸渍量的装饰原纸。
(3)装饰纸的热压封装
利用热压机将浸渍后的装饰原纸与人造板贴合。
优选地，步骤(1)中，以质量比计聚磷酸铵相对于氢氧化铝的比例为1:1-1:5，最佳比例为1:3。
优选地，苯丙乳液占浸渍胶的5wt％-10wt％，最佳添加量为10wt％。
优选地，羧甲基纤维素占浸渍胶的0.2wt-0.6wt％，最佳添加量为0.5wt％。
优选地，聚磷酸铵聚合度为50DP，氢氧化铝可以采用纯度99％以上的氢氧化铝。
优选地，步骤(2)中浸渍时间可以为1～5min，浸渍量为3～7g/m2。
优选地，步骤(3)中热压机可以采用本领域常用的热压机，热压时采用特定的热压条件：温度为120℃，压力为150Pa，时间为3min。
本发明的另一方面提供了由前述制备方法制备的具有阻燃作用的装饰纸。
根据本发明的具有阻燃作用的装饰纸及其制备方法，本发明中采用的聚磷酸铵无毒无味，不产生腐蚀气体，吸湿性小，热稳定性高，是一种性能优良的非卤阻燃剂。本发明人发现其与氢氧化铝配合对于装饰纸的阻燃性和其他性能有明显的改进，氢氧化铝在装饰纸中不仅能阻燃，而且可以防止发烟、不产生滴下物、不产生有毒气体。
本发明制备的阻燃装饰纸能够在纸张内部与表面形成有效的浸渍层，具有优异的阻燃性。特别是特定比例(质量比1:3)的聚磷酸铵与氢氧化铝会产生协同凝聚作用，通过协同凝聚相阻燃作用，在受热后可在材料表面生成保护层，从而达到更优异的阻燃效果。
本发明选用特定比例的苯丙乳液和羟甲基纤维素作为胶粘剂，用于有效粘结聚磷酸铵和氢氧化铝，使其牢固地粘附在原纸上。
具体实施方式
本发明涉及一种具有阻燃作用的装饰纸的制备方法，其是通过浸渍的工艺将阻燃剂与装饰原纸复合，再通过热压成形的方式将其压封在人造板上，得到表面光滑的装饰纸。
本发明的具有阻燃作用的装饰纸的制备方法包括以下步骤：
(1)浸渍胶的配制
将聚磷酸铵(APP)、氢氧化铝、苯丙乳液和羟甲基纤维素按照一定比例混合，得到浸渍胶。
其中，以质量比计，聚磷酸铵(APP)相对于氢氧化铝的比例为10％-50％之间，最佳比例为30％，其在浸渍胶中的固含量在15-25％之间，最佳比例为20％；苯丙乳液占浸渍胶的5％-10％之间，最佳添加量为10％；羧甲基纤维素占浸渍胶的0.2-0.6％之间，最佳添加量为0.5％。
聚磷酸铵聚合度可以为40-80DP，优选为50DP，氢氧化铝可以采用纯度99％以上的氢氧化铝。
(2)装饰原纸的浸渍
将装饰原纸放入浸渍胶中浸渍不同时间，得到不同浸渍量的装饰原纸。
这里浸渍时间可以为1～5min，浸渍量为3～7g/m2。
(3)装饰纸的热压封装
利用热压机将浸渍后的装饰原纸与人造板贴合。
热压机可以采用本领域常用的热压机，热压时采用特定的热压条件：温度为120℃，压力为150Pa，时间为3min。这样得到的装饰纸表面更平滑，不发生透胶，与板材贴合效果更好。
下面结合具体实施例详细地说明本发明的具有阻燃作用的装饰纸的制备方法及制备的装饰纸。
实施例1
(1)配制浸渍胶
将聚磷酸铵(聚合度50DP)1kg、氢氧化铝1kg、苯丙乳液0.2kg和羟甲基纤维素0.01kg混合均匀，得到浸渍胶。
(2)浸渍装饰原纸
将装饰原纸垂直放入阻燃剂浸渍胶中，浸渍时间为1min。
(3)热压封装
将制备好的装饰原纸与人造板贴合，利用热压机(120℃、150Pa)热压3min得到浸渍热压装饰纸。
实施例2
(1)配制浸渍胶
将聚磷酸铵(聚合度50DP)1kg、氢氧化铝1kg、苯丙乳液0.2kg和羟甲基纤维素0.01kg混合均匀，得到浸渍胶。
(2)浸渍装饰原纸
将装饰原纸垂直放入阻燃剂浸渍胶中，浸渍时间为5min。
(3)热压封装
将制备的装饰原纸与人造板贴合，利用热压机(120℃、150Pa)热压3min得到浸渍热压装饰纸。
实施例3
(1)配制浸渍胶
将聚磷酸铵(聚合度50DP)1kg、氢氧化铝3kg、苯丙乳液0.4kg和羟甲基纤维素0.02kg混合均匀，得到浸渍胶。
(2)浸渍装饰原纸
将装饰原纸垂直放入阻燃剂浸渍胶中，浸渍时间为1min。
(3)热压封装
将制备的装饰原纸与人造板贴合，利用热压机(120℃、150Pa)热压3min得到浸渍热压装饰纸。
实施例4
(1)配制浸渍阻燃剂
将聚磷酸铵(聚合度50DP)1kg、氢氧化铝3kg、苯丙乳液0.4kg和羟甲基纤维素0.02kg混合均匀，得到浸渍胶。
(2)浸渍装饰原纸
将装饰原纸垂直放入阻燃剂浸渍胶中，浸渍时间为5min。
(3)热压封装
将制备的装饰原纸与人造板贴合，利用热压机(120℃、150Pa)热压3min得到浸渍热压装饰纸。
实施例5
(1)配制浸渍阻燃剂
将聚磷酸铵(聚合度50DP)1kg、氢氧化铝5kg、苯丙乳液0.6kg和羟甲基纤维素0.03kg混合均匀，得到浸渍胶。
(2)浸渍装饰原纸
将装饰原纸垂直放入阻燃剂中，浸渍时间为1min。
(3)热压封装
将制备的装饰原纸与人造板贴合，利用热压机(120℃、150Pa)热压3min得到浸渍热压装饰纸。
实施例6
(1)配制浸渍阻燃剂
将聚磷酸铵(聚合度50DP)1kg、氢氧化铝5kg、苯丙乳液0.6kg和羟甲基纤维素0.03kg混合均匀，得到浸渍胶。
(2)浸渍装饰原纸
将装饰原纸垂直放入阻燃剂中，浸渍时间为5min。
(3)热压封装
将制备的装饰原纸与人造板贴合，利用热压机(120℃、150Pa)热压3min得到浸渍热压装饰纸。
表1装饰纸性能评价
观察前述实施例1-6制备的装饰纸，表面平滑，没有发生透胶，与板材贴合效果良好。这是由于本发明采用了特定的热压条件：温度为120℃，压力为150Pa，时间为3min。本发明人分别改变温度、压力或时间做了大量的试验，得到的装饰纸存在表面凹凸不平、浸渍胶透出、贴合效果差等问题。本发明的热压条件实现了最佳的表观状态及热贴合效果。
由上述表1可知，实施例4的阻燃效果最佳，其极限氧指数为38.7％，热释放率为111.5KW·min·m-2，这是因为聚磷酸铵和氢氧化铝的添加减少了装饰纸中可燃物的含量，提高了装饰纸的比热容；另一方面，特定比例(质量比1:3)的聚磷酸铵与氢氧化铝会产生协同凝聚作用，通过协同凝聚相阻燃作用，在受热后可在材料表面生成保护层，从而达到更优异的阻燃效果，即当聚磷酸铵与氢氧化铝质量比为1:3时，与装饰原纸复合后得到的装饰纸当发生火灾时能够在表面形成有效的保护层，阻断火源，达到优异的阻燃效果。
以上所述之实施例，只是本发明的较佳实施例而已，仅仅用以解释本发明，并非限制本发明实施范围，对于本技术领域的技术人员来说，当然可根据本说明书中所公开的技术内容，通过置换或改变的方式轻易做出其它的实施方式，故凡在本发明的原理上所作的变化和改进等，均应包括于本发明申请专利范围内。
Claims (9)
1.一种具有阻燃作用的装饰纸的制备方法，其包括以下步骤：
(1)浸渍胶的配制
将聚磷酸铵(APP)、氢氧化铝、苯丙乳液和羟甲基纤维素按照一定比例混合，得到浸渍胶；
(2)装饰原纸的浸渍
将装饰原纸放入浸渍胶中浸渍不同时间，得到不同浸渍量的装饰原纸；
(3)装饰纸的热压封装
利用热压机将浸渍后的装饰原纸与人造板贴合。
2.根据权利要求1所述的装饰纸的制备方法，其中，步骤(1)中聚磷酸铵相对于氢氧化铝的质量比例为1:1-1:5。
3.根据权利要求1所述的装饰纸的制备方法，其中，聚磷酸铵相对于氢氧化铝的质量比例为1:3。
4.根据权利要求1所述的装饰纸的制备方法，其中，苯丙乳液占浸渍胶的5wt％-10wt％。
5.根据权利要求1所述的装饰纸的制备方法，其中，羧甲基纤维素占浸渍胶的0.2wt-0.6wt％。
6.根据权利要求1所述的装饰纸的制备方法，其中，聚磷酸铵聚合度为50DP，氢氧化铝可以采用纯度99％以上的氢氧化铝。
7.根据权利要求1所述的装饰纸的制备方法，其中，步骤(2)中浸渍时间可以为1～5min，浸渍量为3～7g/m2。
8.根据权利要求1所述的装饰纸的制备方法，其中，步骤(3)中热压时采用特定的热压条件：温度为120℃，压力为150Pa，时间为3min。
9.由前述权利要求1-8中任意一项所述的制备方法制备的具有阻燃作用的装饰纸。