CN115109484A - 一种水性多彩仿石漆的制作方法及施工工艺 - Google Patents
一种水性多彩仿石漆的制作方法及施工工艺 Download PDFInfo
- Publication number
- CN115109484A CN115109484A CN202210443254.5A CN202210443254A CN115109484A CN 115109484 A CN115109484 A CN 115109484A CN 202210443254 A CN202210443254 A CN 202210443254A CN 115109484 A CN115109484 A CN 115109484A
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- agent
- water
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种水性多彩仿石漆，包括软水、硅丙乳液、合成树脂和颜料，其组成的重量分数为：软水200‑350份、硅丙乳液250‑300份、彩色岩片150‑300份，合成树脂30‑40份、助溶剂1.5‑3份、乙二醇8‑12份、润湿剂1‑2.5份、颜料1.5‑4份、消泡剂2‑3份、抑菌剂8‑12份、分散剂2‑5份。本发明通过添加颜料，颜料可以为钛白、镉红、铬绿、奶光黄、铁蓝中的任意一种或几种混合的同质量的混合物，能根据实际使用得到想要的颜色，使得涂料变得多彩多样，然后通过添加硅丙乳液和合成树脂，能够提高涂料的耐久性，并且添加催干剂，能够加速涂料的风干，节约施工时间，还通过加入防结皮剂，能够防止涂料的表面起皮，并且不容易脱落，从而可以提高涂料表面的美观性和耐用性。
Description
技术领域
本发明涉及仿石漆技术领域，尤其涉及一种水性多彩仿石漆的制作方法及施工工艺。
背景技术
随着科技水平的提高和人民生活水平的上升，人们对涂料环保、装饰性以及保护功能的进一步认识,传统的外墙乳胶漆因其单调的装饰风格已经不能满足消费者的要求。
而如果采用有精美纹饰的大理石或者其他瓷砖对墙面进行装饰的话，不仅造价高，并且随着长时间的使用，大理石和瓷砖很容易从墙面上脱落，因此提高外墙漆的装饰性得到了越来越多人的重视。
发明内容
本发明针对现有技术存在的不足，提供了一种水性多彩仿石漆的制作方法及施工工艺，具体技术方案如下：
一种水性多彩仿石漆，包括软水、硅丙乳液、合成树脂和颜料，其组成的重量分数为：软水200-350份、硅丙乳液250-300份、彩色岩片150-300份，合成树脂30-40份、助溶剂1.5-3份、乙二醇8-12份、润湿剂1-2.5份、颜料1.5-4份、消泡剂2-3份、抑菌剂8-12份、分散剂2-5份、流平剂1-2.5份、成膜助剂15.5-20份、催干剂8-15份、防结皮剂15-30份。
作为上述技术方案的改进，所述颜料为钛白、镉红、铬绿、奶光黄、铁蓝中的任意一种或几种混合的同质量的混合物。
作为上述技术方案的改进，所述防结皮剂由甲乙酮肟和双戊烯混合而成，所述润湿剂是丁基禁磺酸钠盐。
作为上述技术方案的改进，其组成的重量分数为：软水350份、硅丙乳液300份、彩色岩片300份，合成树脂40份、助溶剂3份、乙二醇12份、润湿剂2.5份、颜料4份、消泡剂3份、抑菌剂12份、分散剂5份、流平剂2.5份、成膜助剂20份、催干剂15份、防结皮剂30份。
作为上述技术方案的改进，其组成的重量分数为：软水300份、硅丙乳液280份、彩色岩片200份，合成树脂35份、助溶剂2.5份、乙二醇10份、润湿剂2份、颜料3份、消泡剂2.5份、抑菌剂10份、分散剂3.5份、流平剂2份、成膜助剂17.5份、催干剂12份、防结皮剂25份。
一种水性多彩仿石漆的制作方法，包括以下步骤：
S1：制备A组分：将硅丙乳液加入软水中，用分散机高速搅拌，然后加入助溶剂、消泡剂和分散剂，搅拌直至混合均匀，然后依次添加彩色岩片和颜料，直至搅拌均匀，再添加抑菌剂，并搅拌混合均匀；
S2：制备B组分：将合成树脂加入软水中，用分散机中速搅拌，依次加入助溶剂、乙二醇、颜料、消泡剂和抑菌剂，直至混合均匀；
S3：制备A和B的混合物：将S1制备的A组分加入S2制备的B组分，搅拌均匀形成AB混合物，然后在AB混合物中依次加入润湿剂、消泡剂、流平剂、成膜助剂、催干剂和防结皮剂，搅拌均匀；
其中S1和S2可以任意顺序进行。
一种水性多彩仿石漆的施工工艺，包括以下步骤；
S1：墙体养护：新水泥墙面冬天的养护时间为28天，夏天的养护时间为14天；
S2：基面处理：用外墙找平腻子先对墙面进行修补，对墙面进行找平，将墙面中的缝隙和孔洞用腻子堵上，待腻子干燥后再进行打磨，使墙面保持平整；
S3：喷涂水性多彩仿石漆：通过喷涂对墙面喷涂水性多彩仿石漆，待第一层腻子完全干燥后，再喷涂第二遍水性多彩仿石漆，并通过砂纸对腻子表面凸起的颗粒进行轻轻打磨；
S4：涂刷罩面漆：在水性多彩仿石漆干燥24h后，采用涂刷将罩面漆涂在墙面上，待干燥后，即完成水性多彩仿石漆外墙漆的施工。
本发明的有益效果：
通过添加颜料，颜料可以为钛白、镉红、铬绿、奶光黄、铁蓝中的任意一种或几种混合的同质量的混合物，能够根据实际使用得到想要的颜色，使得涂料变得多彩多样，然后通过添加硅丙乳液和合成树脂，能够提高涂料的耐久性，并且添加催干剂，能够加速涂料的风干，节约施工时间，还通过加入防结皮剂，能够防止涂料的表面起皮，并且不容易脱落，从而可以提高涂料表面的美观性和耐用性。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例一：
一种水性多彩仿石漆，包括软水、硅丙乳液、合成树脂和颜料，其组成的重量分数为：软水200-350份、硅丙乳液250-300份、彩色岩片150-300份，合成树脂30-40份、助溶剂1.5-3份、乙二醇8-12份、润湿剂1-2.5份、颜料1.5-4份、消泡剂2-3份、抑菌剂8-12份、分散剂2-5份、流平剂1-2.5份、成膜助剂15.5-20份、催干剂8-15份、防结皮剂15-30份。
所述颜料为钛白、镉红、铬绿、奶光黄、铁蓝中的任意一种或几种混合的同质量的混合物。
所述防结皮剂由甲乙酮肟和双戊烯混合而成，所述润湿剂是丁基禁磺酸钠盐。
实施例二：
一种水性多彩仿石漆，其组成的重量分数为：软水350份、硅丙乳液300份、彩色岩片300份，合成树脂40份、助溶剂3份、乙二醇12份、润湿剂2.5份、颜料4份、消泡剂3份、抑菌剂12份、分散剂5份、流平剂2.5份、成膜助剂20份、催干剂15份、防结皮剂30份。
一种水性多彩仿石漆的制作方法，包括以下步骤：
S1：制备A组分：将硅丙乳液加入份软水中，用分散机高速搅拌，然后加入3助溶剂、消泡剂和分散剂，搅拌直至混合均匀，然后依次添加彩色岩片和颜料，直至搅拌均匀，再添加抑菌剂，并搅拌混合均匀；
S2：制备B组分：将合成树脂加入软水中，用分散机中速搅拌，依次加入助溶剂、乙二醇、颜料、消泡剂和抑菌剂，直至混合均匀；
S3：制备A和B的混合物：将S1制备的A组分加入S2制备的B组分，搅拌均匀形成AB混合物，然后在AB混合物中依次加入润湿剂、消泡剂、流平剂、成膜助剂、催干剂和防结皮剂，搅拌均匀；
其中S1和S2可以任意顺序进行。
实施例三：
一种水性多彩仿石漆，其组成的重量分数为：软水300份、硅丙乳液280份、彩色岩片200份，合成树脂35份、助溶剂2.5份、乙二醇10份、润湿剂2份、颜料3份、消泡剂2.5份、抑菌剂10份、分散剂3.5份、流平剂2份、成膜助剂17.5份、催干剂12份、防结皮剂25份。
一种水性多彩仿石漆的制作方法，包括以下步骤：
S1：制备A组分：将硅丙乳液加入份软水中，用分散机高速搅拌，然后加入3助溶剂、消泡剂和分散剂，搅拌直至混合均匀，然后依次添加彩色岩片和颜料，直至搅拌均匀，再添加抑菌剂，并搅拌混合均匀；
S2：制备B组分：将合成树脂加入软水中，用分散机中速搅拌，依次加入助溶剂、乙二醇、颜料、消泡剂和抑菌剂，直至混合均匀；
S3：制备A和B的混合物：将S1制备的A组分加入S2制备的B组分，搅拌均匀形成AB混合物，然后在AB混合物中依次加入润湿剂、消泡剂、流平剂、成膜助剂、催干剂和防结皮剂，搅拌均匀；
其中S1和S2可以任意顺序进行。
实施例四：
一种水性多彩仿石漆的施工工艺，包括以下步骤：
S1：墙体养护：新水泥墙面冬天的养护时间为28天，夏天的养护时间为14天；
S2：基面处理：用外墙找平腻子先对墙面进行修补，对墙面进行找平，将墙面中的缝隙和孔洞用腻子堵上，待腻子干燥后再进行打磨，使墙面保持平整；
S3：喷涂水性多彩仿石漆：通过喷涂对墙面喷涂水性多彩仿石漆，待第一层腻子完全干燥后，再喷涂第二遍水性多彩仿石漆，并通过砂纸对腻子表面凸起的颗粒进行轻轻打磨；
S4：涂刷罩面漆：在水性多彩仿石漆干燥24h后，采用涂刷将罩面漆涂在墙面上，待干燥后，即完成水性多彩仿石漆外墙漆的施工。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围。
Claims (7)
1.一种水性多彩仿石漆，包括软水、硅丙乳液、合成树脂和颜料，其特征在于：其组成的重量分数为：软水200-350份、硅丙乳液250-300份、彩色岩片150-300份，合成树脂30-40份、助溶剂1.5-3份、乙二醇8-12份、润湿剂1-2.5份、颜料1.5-4份、消泡剂2-3份、抑菌剂8-12份、分散剂2-5份、流平剂1-2.5份、成膜助剂15.5-20份、催干剂8-15份、防结皮剂15-30份。
2.根据权利要求1所述的一种水性多彩仿石漆，其特征在于：所述颜料为钛白、镉红、铬绿、奶光黄、铁蓝中的任意一种或几种混合的同质量的混合物。
3.根据权利要求1所述的一种水性多彩仿石漆，其特征在于：所述防结皮剂由甲乙酮肟和双戊烯混合而成，所述润湿剂是丁基禁磺酸钠盐。
4.根据权利要求1所述的一种水性多彩仿石漆，其特征在于：
其组成的重量分数为：软水350份、硅丙乳液300份、彩色岩片300份，合成树脂40份、助溶剂3份、乙二醇12份、润湿剂2.5份、颜料4份、消泡剂3份、抑菌剂12份、分散剂5份、流平剂2.5份、成膜助剂20份、催干剂15份、防结皮剂30份。
5.权利要求1所述的一种水性多彩仿石漆，其特征在于：
其组成的重量分数为：软水300份、硅丙乳液280份、彩色岩片200份，合成树脂35份、助溶剂2.5份、乙二醇10份、润湿剂2份、颜料3份、消泡剂2.5份、抑菌剂10份、分散剂3.5份、流平剂2份、成膜助剂17.5份、催干剂12份、防结皮剂25份。
6.根据权利要求1-5任意一项所述的一种水性多彩仿石漆的制作方法，其特征在于：包括以下步骤：
S1：制备A组分：将硅丙乳液加入软水中，用分散机高速搅拌，然后加入助溶剂、消泡剂和分散剂，搅拌直至混合均匀，然后依次添加彩色岩片和颜料，直至搅拌均匀，再添加抑菌剂，并搅拌混合均匀；
S2：制备B组分：将合成树脂加入软水中，用分散机中速搅拌，依次加入助溶剂、乙二醇、颜料、消泡剂和抑菌剂，直至混合均匀；
S3：制备A和B的混合物：将S1制备的A组分加入S2制备的B组分，搅拌均匀形成AB混合物，然后在AB混合物中依次加入润湿剂、消泡剂、流平剂、成膜助剂、催干剂和防结皮剂，搅拌均匀；
其中S1和S2可以任意顺序进行。
7.根据权利要求1-5任意一项所述的一种水性多彩仿石漆的施工工艺，其特征在于：包括以下步骤：
S1：墙体养护：新水泥墙面冬天的养护时间为28天，夏天的养护时间为14天；
S2：基面处理：用外墙找平腻子先对墙面进行修补，对墙面进行找平，将墙面中的缝隙和孔洞用腻子堵上，待腻子干燥后再进行打磨，使墙面保持平整；
S3：喷涂水性多彩仿石漆：通过喷涂对墙面喷涂水性多彩仿石漆，待第一层腻子完全干燥后，再喷涂第二遍水性多彩仿石漆，并通过砂纸对腻子表面凸起的颗粒进行轻轻打磨；
S4：涂刷罩面漆：在水性多彩仿石漆干燥24h后，采用涂刷将罩面漆涂在墙面上，待干燥后，即完成水性多彩仿石漆外墙漆的施工。