CN115008260A - Low-temperature baking label chromatography polishing process technology - Google Patents
Low-temperature baking label chromatography polishing process technology Download PDFInfo
- Publication number
- CN115008260A CN115008260A CN202210585777.3A CN202210585777A CN115008260A CN 115008260 A CN115008260 A CN 115008260A CN 202210585777 A CN202210585777 A CN 202210585777A CN 115008260 A CN115008260 A CN 115008260A
- Authority
- CN
- China
- Prior art keywords
- baking
- glaze
- labeling
- low
- process technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a low-temperature baking label chromatography polishing process technology, which comprises the following steps: s1: fitting the color difference of the trepanning on the glass blank; s2: curing, adhering and forming after baking; s3: tearing off the color block protective film of the prefabricated sheathing, and prefabricating the patterns and the characters into a sand blasting mark; s4: carrying out sand blasting treatment after labeling, airing and shielding, then soaking for half an hour and tearing off the sand blasting label to obtain the required pattern and shape; s5: prefabricating the glaze into a glaze mark block, adhering the glaze mark block to the surface of the color block in a water transfer labeling mode, and scraping to dry; s6: trimming redundant glaze on the pattern, and then baking and forming; s7: polishing treatment is carried out to improve the luster and achieve the brightening effect. The method changes high-temperature jacking into labeling jacking under the condition of keeping the original appearance effect, and realizes the purposes of changing the operating environment, reducing the production cost and lightening the labor intensity of the jacking process under the condition of keeping the appearance of the jacking attractive.
Description
Technical Field
The invention particularly relates to a low-temperature baking label chromatography polishing process technology.
Background
Along with the development of economy and social progress, the demand of people on the appearance package of the glass bottle is continuously improved, the glass batch is carved to be used as a traditional manual artistic product, transparent glass is carved by hands, colored patterns are reserved at the same time, the colored patterns are expressed by rich colors and patterns, the glass batch is popular with customers, and the glass batch occupies the top-level high-end market. The traditional handicraft set material carving has the advantages of bright color, rich content and higher collection value, but the reality that the manufacturing cost is high, the operation environment is severe and the working strength is high and is difficult to escape is realized. With the development of society and the change of consumption and employment concepts of people, technical personnel are aging, the production cost is continuously increased, more young people are reluctant to do hard material picking and nesting work, and meanwhile, the process has extremely low production efficiency and is not suitable for large-scale and batch production. The process of carving the trepanning tends to fade out the visual field of people gradually, and the process is also in an embarrassing situation.
Disclosure of Invention
The invention aims to provide a low-temperature label baking, color matching and polishing process technology aiming at the defects of the prior art, and the low-temperature label baking, color matching and polishing process technology can well solve the problems.
In order to meet the requirements, the technical scheme adopted by the invention is as follows: the low-temperature mark baking, color registering and polishing process technology comprises the following steps:
s1: fitting the color difference of the trepanning on the glass blank;
s2: curing, adhering and forming after baking;
s3: tearing off the color block protective film of the prefabricated sheathing, and prefabricating the patterns and the characters into a sand blasting mark;
s4: carrying out sand blasting treatment after labeling, airing and shielding, then soaking for half an hour and tearing off the sand blasting label to obtain the required pattern and shape;
s5: prefabricating the glaze into a glaze mark block, adhering the glaze mark block to the surface of the color block in a water transfer labeling mode, and scraping to dry;
s6: removing redundant glaze on the pattern, and then baking and forming;
s7: polishing treatment is carried out to improve the luster and achieve the brightening effect.
The low-temperature label baking, chromatography and polishing process technology has the advantages that:
the finished product has rich appearance effect of the trepanning, breaks through the technical limitation of a high-temperature trepanning process, has flexibility without being limited by production conditions, solves the unique mode of the trepanning production process effect and reduces the production cost in the production process. And has the operability of mass production. And can be popularized in batches.
Detailed Description
In order to make the objects, technical solutions and advantages of the present application more apparent, the present application is further described in detail with reference to specific embodiments below.
In the following description, references to "one embodiment", "an embodiment", "one example", "an example", etc., indicate that the embodiment or example so described may include a particular feature, structure, characteristic, property, element, or limitation, but not every embodiment or example necessarily includes the particular feature, structure, characteristic, property, element, or limitation. Moreover, repeated use of the phrase "in accordance with an embodiment of the present application" although it may possibly refer to the same embodiment, does not necessarily refer to the same embodiment.
Certain features that are well known to those skilled in the art have been omitted from the following description for the sake of simplicity.
According to an embodiment of the present application, a low-temperature baking label color-registering polishing process is provided, which includes the following steps:
s1: fitting the color difference of the trepanning on the glass blank;
s2: curing, adhering and forming after baking;
s3: tearing off the color block protective film of the prefabricated sheathing, and prefabricating the patterns and the characters into a sand blasting mark;
s4: carrying out sand blasting treatment after labeling, airing and shielding, then soaking for half an hour and tearing off the sand blasting label to obtain the required pattern and shape;
s5: prefabricating the glaze into a glaze mark block, adhering the glaze mark block to the surface of the color block in a water transfer labeling mode, and scraping to dry;
s6: trimming redundant glaze on the pattern, and then baking and forming;
s7: polishing treatment is carried out to improve the luster and achieve the brightening effect.
According to an embodiment of the present application, the temperature of the curing, adhering and forming process after baking in step S2 of the low-temperature baking, coloring and polishing process is 180 ℃.
According to an embodiment of the present application, the time for soaking in step S4 of the low-temperature baking, labeling, color-registering and polishing process is half an hour.
According to one embodiment of the application, when the excess glaze on the pattern is repaired by the low-temperature mark baking, color registering and polishing process technology, a manual blade repairing or laser repairing mode is adopted.
According to an embodiment of the present application, the temperature of the baking in step S6 of the low-temperature baking process is 180 ℃.
According to an embodiment of the present application, in step S7 of the low-temperature baking, color-registering and polishing process, rare earth polishing powder or polishing paste is used as a polishing treatment to enhance the gloss.
According to one embodiment of the application, the low-temperature label baking, color registering and polishing process technology adopts a water transfer labeling process to attach a color difference of a cover material to a glass blank, baking at 180 ℃ and then curing and attaching the cover material to form the cover material, tearing off a color block protective film of the prefabricated cover material, prefabricating a sand blasting label according to a desired pattern and characters, performing sand blasting treatment after labeling, airing and shielding, then tearing off the sand blasting label by soaking for half an hour or so to obtain a desired pattern and shape, prefabricating a glaze mark block from a glaze, attaching the glaze mark to the surface of the color block in a water transfer labeling mode, scraping the glaze to dry, then removing redundant glaze on the pattern by adopting a manual blade/laser, baking at 180 ℃ or so and forming. At the moment, the nesting effect is formed, and finally, rare earth polishing powder or grinding paste is adopted for polishing treatment to improve the luster, so that the brightening effect is achieved.
According to an embodiment of the application, the low-temperature label baking, color registering and polishing process technology aims at the defects of high manufacturing cost, severe operation environment and high workload intensity of the existing high-temperature nesting process technology, and the patent proposes that the high-temperature nesting is changed into the labeling and nesting process by changing the process route under the condition of keeping the original appearance effect, so that the purposes of changing the operation environment, reducing the production cost and reducing the labor intensity of the nesting process are realized under the condition of keeping the attractive appearance of the nesting.
According to one embodiment of the application, the finished product has rich appearance effect of the trepanning, breaks through the technical limitation of a high-temperature trepanning process, has flexibility without being limited by production conditions, solves the unique mode of the trepanning production process effect, and reduces the production cost. And has the operability of mass production. And can be popularized in batches.
The above-mentioned embodiments only show some embodiments of the present invention, and the description thereof is more specific and detailed, but should not be construed as limiting the scope of the present invention. It should be noted that, for a person skilled in the art, several variations and modifications can be made without departing from the inventive concept, which falls within the scope of the present invention. Therefore, the protection scope of the present invention should be subject to the claims.
Claims (6)
1. A low-temperature baking label chromatography polishing process technology is characterized by comprising the following steps:
s1: fitting the color difference of the trepanning on the glass blank;
s2: curing, adhering and molding after baking;
s3: tearing off the color block protective film of the prefabricated sheathing, and prefabricating the patterns and the characters into a sand blasting mark;
s4: carrying out sand blasting treatment after labeling, airing and shielding, then soaking for half an hour and tearing off the sand blasting label to obtain the required pattern and shape;
s5: prefabricating the glaze into a glaze mark block, adhering the glaze mark block to the surface of the color block in a water transfer labeling mode, and scraping to dry;
s6: trimming redundant glaze on the pattern, and then baking and forming;
s7: polishing treatment is carried out to improve the luster and achieve the brightening effect.
2. The low-temperature baking, labeling, color registering and polishing process technology as claimed in claim 1, wherein: the temperature at which the curing, adhesion and molding are performed after baking in step S2 is 180 ℃.
3. The low-temperature baking, labeling, color registering and polishing process technology as claimed in claim 1, wherein: the time for which the soaking in step S4 is performed is half an hour.
4. The low-temperature baking label chromatography polishing process technology according to claim 1, characterized in that: and when the redundant glaze on the pattern is repaired, a manual blade repairing or laser repairing mode is adopted.
5. The low-temperature baking, labeling, color registering and polishing process technology as claimed in claim 1, wherein: the baking temperature in step S6 was 180 ℃.
6. The low-temperature baking, labeling, color registering and polishing process technology as claimed in claim 1, wherein: in step S7, rare earth polishing powder or paste is used for polishing to improve the gloss.