CN114933829A - 一种膨胀型防火涂料及其制备方法 - Google Patents
一种膨胀型防火涂料及其制备方法 Download PDFInfo
- Publication number
- CN114933829A CN114933829A CN202210462936.0A CN202210462936A CN114933829A CN 114933829 A CN114933829 A CN 114933829A CN 202210462936 A CN202210462936 A CN 202210462936A CN 114933829 A CN114933829 A CN 114933829A
- Authority
- CN
- China
- Prior art keywords
- intumescent
- retardant coating
- stirring
- parts
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种膨胀型防火涂料及其制备方法，属于防火涂料领域，它由下述重量份的原料组成：以质量份计，聚磷酸铵：10‑20；季戊四醇：2‑6；三聚氰胺：4‑6；石棉：15‑20；表面活性剂：3‑5；聚乙酸乙烯乳液：15‑20；氯化石蜡：2‑4；水：25‑30；金红石型钛白粉：5‑8；六偏磷酸钠：3‑5。发明制备出的膨胀型防火具有优异的防火性能，该制备方法具有操作简单、易于控制、成本低廉、能耗少、对环境污染小的优点。
Description
技术领域
本发明涉及防火涂料领域，更具体的涉及一种膨胀型防火涂料及其制备方法。
背景技术
膨胀超薄型防火涂料是由乙基纤维、氯化石腊、防火颜料、助剂、溶剂等组成的单组份自干涂料。主要用于涂覆在钢结构上，起到隔热和防火效果，避免建筑物构建在高温下失去载荷能力导致建筑物坍塌，给人们生命财产造成巨大损失。
目前，大多数膨胀超薄型防火涂料的改进在于阻燃助剂的选用以及无机填料的优化，极大的改善了膨胀型防火涂料的防火性能，但在乳液优化上仍然是一个短板，因此，在乳液上的创新，对于提升防火涂料的防火性能有极大意义。
发明内容
本发明的目的在于克服现有技术的不足，提供一种膨胀型防火涂料及其制备方法。
本发明的目的是通过以下技术方案来实现的：一种膨胀型防火涂料，它由下述重量份的原料组成：以质量份计，
本发明中聚乙酸乙烯乳液不仅能将各组分进行包裹、粘接，还能起到后期遇热碳化，将聚乙酸乙烯乳液与石棉复配，更利于在遭遇高温700℃环境下，形成更好的碳化层，起到更优异的防火性能。
具体来说，所述聚乙酸乙烯乳液的质量百分比为60％。即选择质量分数60％的聚乙酸乙烯乳液。
具体来说，六偏磷酸钠的质量百分比为10％。即选择质量分数10％的六偏磷酸钠。
具体来说，所述聚磷酸铵的聚合度在800-1000。该聚合度下的聚磷酸铵与其他原料复配，防火性能更好。
具体来说，表面活性剂选用十二烷基苯磺酸钠。
一种膨胀型防火涂料的制备方法，包括如下步骤：
S1.按照上述配方用量称重；
S2.将称取的聚磷酸铵、季戊四醇、三聚氰胺、表面活性剂、水混合高速搅拌；
S3.再添加石棉、聚乙酸乙烯乳液搅拌，混合；加入金红石型钛白粉搅拌，分散均匀；
S4.最后添加氯化石蜡和水，高速搅拌、稀释；
S5.脱水得到膨胀型防火涂料。
本发明的有益效果是：
1、本发明制备出的膨胀型防火具有优异的防火性能。
2、本发明采用的制备方法具有操作简单、易于控制、成本低廉、能耗少、对环境污染小的优点。
具体实施方式
下面详细描述本发明的技术方案，但本发明的保护范围不局限于以下所述。
实施例1
一种膨胀型防火涂料，它由下述重量份的原料组成：以质量份计，
一种膨胀型防火涂料的制备方法，包括以下步骤：
S1.按照上述配方用量称重；
S2.将称取的聚磷酸铵、季戊四醇、三聚氰胺、表面活性剂、水混合以1500-2000r/min的转速高速搅拌10min，生成反应物a；
S3.再添加石棉、聚乙酸乙烯乳液搅拌、混合，5min后使得聚乙酸乙烯乳液初步包裹反应物a与石棉，停止搅拌，加入金红石型钛白粉，高速分散剂以2000-2500r/min高速搅拌，分散均匀；
S4.最后添加氯化石蜡和水，高速分散剂以2000-2500r/min高速搅拌、稀释；
S5.脱水得到膨胀型防火涂料；
实施例2：
一种膨胀型防火涂料，它由下述重量份的原料组成：以质量份计，
一种膨胀型防火涂料的制备方法，包括以下步骤：
S1.按照上述配方用量称重；
S2.将称取的聚磷酸铵、季戊四醇、三聚氰胺、表面活性剂、水混合以1500-2000r/min的转速高速搅拌10min，生成反应物a；
S3.再添加石棉、聚乙酸乙烯乳液搅拌、混合，5min后使得聚乙酸乙烯乳液初步包裹反应物a与石棉，停止搅拌，加入金红石型钛白粉，高速分散剂以2000-2500r/min高速搅拌，分散均匀；
S4.最后添加氯化石蜡和水，高速分散剂以2000-2500r/min高速搅拌、稀释；
S5.脱水得到膨胀型防火涂料。
实施例3：
一种膨胀型防火涂料，它由下述重量份的原料组成：以质量份计，
一种膨胀型防火涂料的制备方法，包括以下步骤：
S1.按照上述配方用量称重；
S2.将称取的聚磷酸铵、季戊四醇、三聚氰胺、表面活性剂、水混合以1500-2000r/min的转速高速搅拌10min，生成反应物a；
S3.再添加石棉、聚乙酸乙烯乳液搅拌、混合，5min后使得聚乙酸乙烯乳液初步包裹反应物a与石棉，停止搅拌，加入金红石型钛白粉，高速分散剂以2000-2500r/min高速搅拌，分散均匀；
S4.最后添加氯化石蜡和水，高速分散剂以2000-2500r/min高速搅拌、稀释；
S5.脱水得到膨胀型防火涂料；。
以下通过性能测试实验说明本发明的有益效果；
测试对象：实施例1-3制备的膨胀型防火涂料；
测试项目：采用常规方法测试以下指标：容器中状态、初期干燥抗裂性、粘接强度、耐水性、施工性、低温储存稳定性、耐冷热循环性、高温耐火性能。
表1表示实施例1-3制备的膨胀型防火涂料各性能指标
不同实施例中膨胀型防火涂料性能检测结果由表1可知，采用本发明配方和方法制备的膨胀型防火涂料其耐高温性能优异，其余各项指标均满足国家标准。
以上所述仅是本发明的优选实施方式，应当理解本发明并非局限于本文所披露的形式，不应看作是对其他实施例的排除，而可用于各种其他组合、修改和环境，并能够在本文所述构想范围内，通过上述教导或相关领域的技术或知识进行改动。而本领域人员所进行的改动和变化不脱离本发明的精神和范围，则都应在本发明所附权利要求的保护范围。
Claims (6)
1.一种膨胀型防火涂料，其特征在于，它由下述重量份的原料组成：以质量份计，
2.根据权利要求1所述的一种膨胀型防火涂料，其特征在于，所述聚乙酸乙烯乳液的质量百分比为60％。
3.根据权利要求1所述的一种膨胀型防火涂料，其特征在于，所述聚磷酸铵的聚合度在800-1000。
4.根据权利要求1所述的一种膨胀型防火涂料，其特征在于，所述六偏磷酸钠的质量百分比为10％。
5.根据权利要求1所述的一种膨胀型防火涂料，其特征在于，所述表面活性剂选用十二烷基苯磺酸钠。
6.根据权利要求1至5中任一项所述一种膨胀型防火涂料的制备方法，其特征在于：包括如下步骤：
S1.按照配方用量称重；
S2.将称取的聚磷酸铵、季戊四醇、三聚氰胺、表面活性剂、水混合高速搅拌；
S3.再添加石棉、聚乙酸乙烯乳液搅拌，混合：加入金红石型钛白粉，分散均匀；
S4.最后添加氯化石蜡和水，高速搅拌、稀释；
S5.脱水得到膨胀型防火涂料。