CN114921152A - 高分子防腐涂料及其制作方法 - Google Patents
高分子防腐涂料及其制作方法 Download PDFInfo
- Publication number
- CN114921152A CN114921152A CN202210675299.5A CN202210675299A CN114921152A CN 114921152 A CN114921152 A CN 114921152A CN 202210675299 A CN202210675299 A CN 202210675299A CN 114921152 A CN114921152 A CN 114921152A
- Authority
- CN
- China
- Prior art keywords
- parts
- anticorrosive paint
- molecular
- polymer
- anticorrosive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种高分子防腐涂料，高分子纳米粉能够使得金属表面活性钝化，从而有效地隔绝腐蚀介质，将金属有效地保护起来。锆凝胶包裹的中空玻璃微珠一方面具有良好的隔热性能，另一方面具有优良的耐腐蚀性能。陶瓷树脂增加了高分子防腐涂料成膜的交联密度，提高了高分子防腐涂料的硬度、耐磨性、韧性以及耐热性。有机硅改性聚酯树脂进一步增加了高分子防腐涂料的耐热性能和耐候性。填料增加了高分子防腐涂料的耐热性能、化学稳定性以及硬度。玻璃鳞片可以增加高分子防腐涂料的化学稳定性、硬度以及耐热性。缓蚀剂可以增加高分子防腐涂料的耐腐蚀性能，防流淌剂可以增加高分子防腐涂料的成膜性，降低了高分子防腐涂料的施工难度。
Description
技术领域
本发明涉及涂料领域，特别是涉及一种高分子防腐涂料及其制作方法。
背景技术
防腐涂料，一般分为常规防腐涂料和重防腐涂料，是油漆涂料中必不可少的一种涂料。常规防腐涂料是在一般条件下，对金属等起到防腐蚀的作用，保护有色金属使用的寿命；重防腐涂料是指相对常规防腐涂料而言，能在相对苛刻腐蚀环境里应用，并具有能达到比常规防腐涂料更长保护期的一类防腐涂料。常规防腐涂料按照用途可分为：橡胶用防腐油漆、船舶用防腐油漆、金属用防腐油漆、汽车用防腐油漆、管道用防腐油漆、家具用防腐油漆、钢结构用防腐油漆。按树脂成膜分为：环氧防腐油漆、 过氯乙烯防腐油漆、氯化橡胶防腐油漆、聚氨酯防腐油漆、丙烯酸防腐油漆、 无机防腐油漆、高氯化聚乙烯防腐油漆。
市场上对于防腐涂料的要求也较为严格，一方面，要求防腐涂料能在苛刻条件下使用，并具有长效防腐寿命。另一方面，要求防腐涂料具有极强地附着性能，可以与待防腐物体的表面良好的结合在一起。传统的防腐涂料隔热性能不高，满足不了特定场合对防腐涂料的隔热性需求。
发明内容
基于此，有必要针对于传统的防腐涂料隔热性能不高，满足不了特定场合对防腐涂料的隔热性需求的技术问题，提供一种高分子防腐涂料及其制作方法。
一种高分子防腐涂料，该高分子防腐涂料包括如下质量份的各组分：高分子纳米粉1份至4份、锆凝胶包裹的中空玻璃微珠5份至10份、陶瓷树脂10份至15份、环氧树脂12份至24份、有机硅改性聚酯树脂8份至16份、填料14份至20份、玻璃鳞片4份至8份、防锈颜料2份至5份、稀释剂20份至30份、缓蚀剂0.2份至0.6份，防流淌剂2份至4份以及氨基硅烷偶联剂0.4份至0.8份。
在其中一个实施例中，所述高分子纳米粉包括如下质量份的各组分：聚吡咯纳米粉末30份至40份、聚苯胺纳米粉末30份至40份、羟乙基纤维素30份至40份。
在其中一个实施例中，所述填料包括如下质量份的各组分：云母粉20份至30份、滑石粉20份至30份、陶瓷粉20份至30份、高岭土20份至30份。
在其中一个实施例中，所述防流淌剂包括如下质量份的各组分：聚酰胺蜡30份至40份、气相二氧化硅30份至40份和有机膨润土30份至40份。
在其中一个实施例中，所述稀释剂的为聚丙二醇二缩水甘油醚。
在其中一个实施例中，缓蚀剂包括如下质量份的各组分：苯并三氮唑20份至30份、噻二唑衍生物20份至30份、咪唑衍生物20份至30份、巯基苯并噻唑20份至30份。
在其中一个实施例中，所述高分子防腐涂料还包括消泡剂0.2份至0.6份。
在其中一个实施例中，所述高分子防腐涂料还包括分散剂0.2份至0.6份。
在其中一个实施例中，所述高分子防腐涂料还包括固化剂3份至5份。
在其中一个实施例中，所述高分子防腐涂料还包括增塑剂2份至4份。
上述高分子防腐涂料中的高分子纳米粉能够使得金属表面活性钝化，从而有效地隔绝腐蚀介质，将金属有效地保护起来。锆凝胶包裹的中空玻璃微珠一方面具有良好的隔热性能，另一方面具有优良的耐腐蚀性能。陶瓷树脂增加了高分子防腐涂料成膜的交联密度，提高了高分子防腐涂料的硬度、耐磨性、韧性以及耐热性。有机硅改性聚酯树脂进一步增加了高分子防腐涂料的耐热性能和耐候性。填料增加了高分子防腐涂料的耐热性能、化学稳定性以及硬度。玻璃鳞片可以增加高分子防腐涂料的化学稳定性、硬度以及耐热性。缓蚀剂可以增加高分子防腐涂料的耐腐蚀性能，防流淌剂可以增加高分子防腐涂料的成膜性，降低了高分子防腐涂料的施工难度。氨基硅烷偶联剂可以增加高分子防腐涂料中各组分之间的结合稳定性。上述高分子防腐涂料具有良好的耐腐蚀性能的同时具有良好的隔热性和耐热性，成膜的硬度高、韧性高、不易开裂。
附图说明
图1为一个实施例中高分子防腐涂料的成分图；
图2为另一个实施例中高分子防腐涂料的成分图。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合附图及实施例，对本发明进行进一步详细说明。应当理解，此处描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
请参阅图1，本发明提供了一种高分子防腐涂料，该高分子防腐涂料包括如下质量份的各组分：高分子纳米粉1份至4份、锆凝胶包裹的中空玻璃微珠5份至10份、陶瓷树脂10份至15份、环氧树脂12份至24份、有机硅改性聚酯树脂8份至16份、填料14份至20份、玻璃鳞片4份至8份、防锈颜料2份至5份、稀释剂20份至30份、缓蚀剂0.2份至0.6份，防流淌剂2份至4份以及氨基硅烷偶联剂0.4份至0.8份。
上述高分子防腐涂料中的高分子纳米粉能够使得金属表面活性钝化，从而有效地隔绝腐蚀介质，将金属有效地保护起来。锆凝胶包裹的中空玻璃微珠一方面具有良好的隔热性能，另一方面具有优良的耐腐蚀性能。陶瓷树脂增加了高分子防腐涂料成膜的交联密度，提高了高分子防腐涂料的硬度、耐磨性、韧性以及耐热性。有机硅改性聚酯树脂进一步增加了高分子防腐涂料的耐热性能和耐候性。填料增加了高分子防腐涂料的耐热性能、化学稳定性以及硬度。玻璃鳞片可以增加高分子防腐涂料的化学稳定性、硬度以及耐热性。缓蚀剂可以增加高分子防腐涂料的耐腐蚀性能，防流淌剂可以增加高分子防腐涂料的成膜性，降低了高分子防腐涂料的施工难度。氨基硅烷偶联剂可以增加高分子防腐涂料中各组分之间的结合稳定性。上述高分子防腐涂料具有良好的耐腐蚀性能的同时具有良好的隔热性和耐热性，成膜的硬度高、韧性高、不易开裂。
为了进一步地增加高分子防腐涂料的耐腐蚀性能和导电性能，在其中一个实施例中，所述高分子纳米粉包括如下质量份的各组分：聚吡咯纳米粉末30份至40份、聚苯胺纳米粉末30份至40份、羟乙基纤维素30份至40份。聚吡咯和聚苯胺是一种导电聚合物，在增加保护膜导电性能，从而增加金属导电性能的同时可以对金属起到钝化和屏蔽的作用，可以提高金属的腐蚀电位，从而延缓了金属的腐蚀速度。羟乙基纤维素可以增加高分子防腐涂料的粘附性、成膜性以及化学稳定性以及耐候性。如此，高分子纳米粉进一步增加了高分子防腐涂料的耐腐蚀性能和导电性能。
为了进一步地增加高分子防腐涂料的耐热性能、化学稳定性以及硬度，在其中一个实施例中，所述填料包括如下质量份的各组分：云母粉20份至30份、滑石粉20份至30份、陶瓷粉20份至30份、高岭土20份至30份。由云母粉、滑石粉、陶瓷粉以及高岭土组成的填料作为高分子防腐涂料的主要成分之一，可以极大地增加高分子防腐涂料的耐热性能、化学稳定性以及硬度。
为了进一步地降低高分子防腐涂料的施工难度，在其中一个实施例中，所述防流淌剂包括如下质量份的各组分：聚酰胺蜡30份至40份、气相二氧化硅30份至40份和有机膨润土30份至40份。包含聚酰胺蜡、气相二氧化硅以及有机膨润土的防流淌剂，可以增加高分子防腐涂料的成膜性能，避免高分子防腐涂料流挂、流淌，从而进一步地降低了高分子防腐涂料的施工难度。
为了对高分子防腐涂料进行稀释，提高高分子防腐涂料的柔韧性，使得各成分可以有效地均匀地混合在一起，在其中一个实施例中，所述稀释剂的为聚丙二醇二缩水甘油醚。聚丙二醇二缩水甘油醚一方面可以将环氧树脂、陶瓷树脂以及有机硅改性聚酯树脂进行有效地稀释，另一方面可以增加环氧树脂、陶瓷树脂以及有机硅改性聚酯树脂的柔韧性、拉伸性以及抗冲击性。从而提高了高分子防腐涂料的柔韧性、拉伸性以及抗冲击性。
为了进一步地增加高分子防腐涂料的耐腐蚀性能，在其中一个实施例中，缓蚀剂包括如下质量份的各组分：苯并三氮唑20份至30份、噻二唑衍生物20份至30份、咪唑衍生物20份至30份、巯基苯并噻唑20份至30份。包含苯并三氮唑、噻二唑衍生物、咪唑衍生物以及巯基苯并噻唑的缓蚀剂具有优良的抗氧化性能，从而进一步地增加高分子防腐涂料的耐腐蚀性能，另外对环氧树脂可以起到一定的固化性能，可以提高高分子防腐涂料的柔韧性。
为了避免高分子防腐涂料中产生气泡在其中一个实施例中，所述高分子防腐涂料还包括消泡剂0.2份至0.6份。在本实施例中，消泡剂包括如下质量份的各组分：烃化油40份至60份、疏水性二氧化硅8份至16份、硬脂酸2份至4份、聚氧丙基甘油醚20份至30份、甲醇5份至10份以及聚丙烯酸甲酯5份至10份。为了提高高分子防腐涂料中各组分的混合均匀性，在其中一个实施例中，所述高分子防腐涂料还包括分散剂0.2份至0.6份。在本实施例中，分散剂包括如下质量份的各组分：丙烯酸10份至20份、乙二醇12份至18份、醋酸乙酯30份至40份、硬酯酸钙5份至15份、甲醇5份至10份以及硬酯酸镁5份至10份，余量为水。为了加快高分子防腐涂料的成膜速率，在其中一个实施例中，所述高分子防腐涂料还包括固化剂3份至5份。为了加快高分子防腐涂料的可塑性和强度，在其中一个实施例中，所述高分子防腐涂料还包括增塑剂2份至4份。
为了验证本申请中的高分子防腐涂料各项性能，对本申请中的高分子防腐涂料分别进行了粘度测试、细度测试、干燥时间测试(干透)、附着力测试、抗冲击测试、耐磨性测试、耐酸性测试、耐碱性测试、耐盐雾测试以及盐水测试，具体测试结果如下：
以上实施例的各技术特征可以进行任意的组合，为使描述简洁，未对上述实施例中的各个技术特征所有可能的组合都进行描述，然而，只要这些技术特征的组合不存在矛盾，都应当认为是本说明书记载的范围。
以上所述实施例仅表达了本发明的几种实施方式，其描述较为具体和详细，但并不能因此而理解为对发明专利范围的限制。应当指出的是，对于本领域的普通技术人员来说，在不脱离本发明构思的前提下，还可以做出若干变形和改进，这些都属于本发明的保护范围。因此，本发明专利的保护范围应以所附权利要求为准。
Claims (10)
1.一种高分子防腐涂料，其特征在于，包括如下质量份的各组分：高分子纳米粉1份至4份、锆凝胶包裹的中空玻璃微珠5份至10份、陶瓷树脂10份至15份、环氧树脂12份至24份、有机硅改性聚酯树脂8份至16份、填料14份至20份、玻璃鳞片4份至8份、防锈颜料2份至5份、稀释剂20份至30份、缓蚀剂0.2份至0.6份，防流淌剂2份至4份以及氨基硅烷偶联剂0.4份至0.8份。
2.根据权利要求1所述的高分子防腐涂料，其特征在于，所述高分子纳米粉包括如下质量份的各组分：聚吡咯纳米粉末30份至40份、聚苯胺纳米粉末30份至40份、羟乙基纤维素30份至40份。
3.根据权利要求1所述的高分子防腐涂料，其特征在于，所述填料包括如下质量份的各组分：云母粉20份至30份、滑石粉20份至30份、陶瓷粉20份至30份、高岭土20份至30份。
4.根据权利要求1所述的高分子防腐涂料，其特征在于，所述防流淌剂包括如下质量份的各组分：聚酰胺蜡30份至40份、气相二氧化硅30份至40份和有机膨润土30份至40份。
5.根据权利要求1所述的高分子防腐涂料，其特征在于，所述稀释剂的为聚丙二醇二缩水甘油醚。
6.根据权利要求1所述的高分子防腐涂料，其特征在于，缓蚀剂包括如下质量份的各组分：苯并三氮唑20份至30份、噻二唑衍生物20份至30份、咪唑衍生物20份至30份、巯基苯并噻唑20份至30份。
7.根据权利要求1所述的高分子防腐涂料，其特征在于，所述高分子防腐涂料还包括消泡剂0.2份至0.6份。
8.根据权利要求1所述的高分子防腐涂料，其特征在于，所述高分子防腐涂料还包括分散剂0.2份至0.6份。
9.根据权利要求1所述的高分子防腐涂料，其特征在于，所述高分子防腐涂料还包括固化剂3份至5份。
10.根据权利要求1所述的高分子防腐涂料，所述高分子防腐涂料还包括增塑剂2份至4份。