CN114854368A - 一种无醛阻燃防水胶及其制备方法 - Google Patents
一种无醛阻燃防水胶及其制备方法 Download PDFInfo
- Publication number
- CN114854368A CN114854368A CN202210423035.0A CN202210423035A CN114854368A CN 114854368 A CN114854368 A CN 114854368A CN 202210423035 A CN202210423035 A CN 202210423035A CN 114854368 A CN114854368 A CN 114854368A
- Authority
- CN
- China
- Prior art keywords
- parts
- formaldehyde
- flame
- retardant
- free flame
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明适用于防水胶技术领域,提供了一种无醛阻燃防水胶及其制备方法,以质量份数计,各组成成分及含量如下:生物质蛋白20~25份、水性高分子异氰酸酯5~12份、水玻璃3~8份、硼砂1~3份、聚硅氮烷3~5份、阻燃粉1~3份、防腐剂0.2~0.4份和增稠剂0.1~0.5份;本发明提供的一种无醛阻燃防水胶及其制备方法,可应用于各种人造板用胶合,实现零甲醛,具备阻燃、防水、防腐防霉等综合功效,成本低廉,比一般的MDI等无醛胶(不阻燃、不防水)成本低2/3,通过加入聚硅氮烷,利用聚硅氮烷具备的独特Si‑NH‑Si键,使得胶水具有良好结合力和良好的力学性能,固化后硬度高,而且具有抗醇类、酮类以及其他有机溶剂的功能。
Description
技术领域
本发明涉及防水胶技术领域,具体为一种无醛阻燃防水胶及其制备方法。
背景技术
近年来,甲醛的危害越来越受到重视,甲醛是一种无色易溶的刺激性气体,对人体有较大伤害,含有甲醛胶黏剂制作的木制品用于室内,甲醛释放期可长达15年,甲醛对人体健康的影响主要表现在嗅觉异常、刺激、过敏、肺功能异常、肝功能异常和免疫功能异常等方面,长期接触低剂量甲醛可引起慢性呼吸道疾病,引起鼻咽癌、结肠癌、脑瘤、月经紊乱、细胞核的基因突变,DNA单链内交连和DNA与蛋白质交连及抑制DNA损伤的修复、妊娠综合症,引起新生儿染色体异常、白血病,引起青少年记忆力和智力下降。在所有接触者中,儿童和孕妇对甲醛尤为敏感,危害也就更大,甲醛作为较高毒性的物质,在我国有毒化学品优先控制名单上甲醛高居第二位,甲醛已经被世界卫生组织确定为致癌和致畸形物质,是公认的变态反应源,也是潜在的强致突变物之一,而使用甲醛和尿素制作的脲醛胶是目前市场上大量销售的的人造板包括多层实木板、生态板、指接板、颗粒板、密度板、纤维板等的主要用胶。
目前市场上只允许销售甲醛含量E1级以上的板材,人造板主要包括胶合板、刨花板、细木工板和纤维板四大类,普通的脲醛胶难以满足上述要求,目前除了胶合板中的建筑模板是利用酚醛胶压制而成的外,其它都是利用脲醛胶或三聚氰胺改性脲醛胶压制成的,因此人造板的污染主要是粘合剂中甲醛的释放,要想彻底解决游离甲醛污染的问题,就必须研制开发新型绿色无醛粘合剂,据官方调查数据显示:近两年当中,随着国际市场竞争压力的增大,人造板环保等级的不断提升和全球公民对家居生活环保意识的不断增强,国内诸多人造板生产商已率先涉足环保产品的开发与推广,并占据了一定的市场地位,产品的环保等级已由E2级向E1级过渡,部分产品已符合E1级甚至接近于E0级的环保甲醛限量要求,但真正意义的实现无醛胶在中国人造板加工业的大范围普级推广,仍存在诸多工艺适用性差、成本过高、产品无竞争力等困难,使得生产商很难突破出口“瓶颈”,导致了我国板材加工业70-80%的企业处于停产、半停产的状态,生产前景堪忧。
现在市场上各类板材使用的脲醛胶、三聚氰胺改性脲醛胶、MDI胶防水性很差,遇潮湿会变形,遇水会散开、粉化,更重要的这些制品也都不阻燃,其制品的可燃、易燃性不仅没有改变,反而因为胶易燃,还会燃烧的更严重。
发明内容
本发明目的是提供一种无醛阻燃防水胶及其制备方法,以解决现有技术中,各类板材使用的脲醛胶、三聚氰胺改性脲醛胶、MDI胶防水性很差,遇潮湿会变形,遇水会散开、粉化,更重要的这些制品也都不阻燃,其制品的可燃、易燃性不仅没有改变,反而因为胶易燃,还会燃烧的更严重的问题。
为实现上述目的,本发明提供如下技术方案:一种无醛阻燃防水胶及其制备方法,包括以下组成成分:
生物质蛋白、水性高分子异氰酸酯、水玻璃、硼砂、聚硅氮烷、阻燃粉、防腐剂和增稠剂。
优选的,以质量份数计,各组成成分的含量如下:
生物质蛋白20~25份、水性高分子异氰酸酯5~12份、水玻璃3~8份、硼砂1~3份、聚硅氮烷3~5份、阻燃粉1~3份、防腐剂0.2~0.4份和增稠剂0.1~0.5份。
优选的,所述生物质蛋白的成分为明胶。
优选的,所述阻燃粉为铝类复合阻燃粉。
优选的,所述防腐剂为卡松防腐剂,所述增稠剂为丙烯酸增稠剂。
一种无醛阻燃防水胶的制备方法,包括以下步骤:
S1,将生物质蛋白和水性高分子异氰酸酯按比例倒入搅拌机中,高速搅拌10min,得到混合原料A;
S2,将硼砂破碎,磨成粉,然后加入水玻璃,混合研磨,得到混合原料B;
S3,将混合原料B倒入搅拌机中,与混合原料A进行混合,高速搅拌10min,然后依次按比例加入聚硅氮烷、阻燃粉、防腐剂和增稠剂,高速搅拌20min,制得产品。
本发明至少具备以下有益效果:
(1)本发明提供的一种无醛阻燃防水胶及其制备方法,可应用于各种人造板用胶合,实现零甲醛,具备阻燃、防水、防腐防霉等综合功效;
(2)本发明提供的一种无醛阻燃防水胶及其制备方法,成本低廉,比一般的MDI等无醛胶(不阻燃、不防水)成本低2/3;
(3)本发明提供的一种无醛阻燃防水胶及其制备方法,通过加入聚硅氮烷,利用聚硅氮烷具备的独特Si-NH-Si键,使得胶水具有良好结合力和良好的力学性能,固化后硬度高,而且具有抗醇类、酮类以及其他有机溶剂的功能。
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
实施例1
一种无醛阻燃防水胶,以质量份数计,各组成成分及含量如下:
生物质蛋白20份、水性高分子异氰酸酯5份、水玻璃3份、硼砂1份、聚硅氮烷3份、阻燃粉1份、防腐剂0.2份和增稠剂0.1份。
其中,生物质蛋白的成分为明胶;
其中,阻燃粉为铝类复合阻燃粉;
其中,防腐剂为卡松防腐剂,增稠剂为丙烯酸增稠剂。
实施例2
一种无醛阻燃防水胶,以质量份数计,各组成成分及含量如下:
生物质蛋白22份、水性高分子异氰酸酯7份、水玻璃6份、硼砂2份、聚硅氮烷3.5份、阻燃粉2.5份、防腐剂0.3份和增稠剂0.4份。
其中,生物质蛋白的成分为明胶;
其中,阻燃粉为铝类复合阻燃粉;
其中,防腐剂为卡松防腐剂,增稠剂为丙烯酸增稠剂。
实施例3
一种无醛阻燃防水胶,以质量份数计,各组成成分及含量如下:
生物质蛋白25份、水性高分子异氰酸酯12份、水玻璃8份、硼砂3份、聚硅氮烷5份、阻燃粉3份、防腐剂0.4份和增稠剂0.5份。
其中,生物质蛋白的成分为明胶;
其中,阻燃粉为铝类复合阻燃粉;
其中,防腐剂为卡松防腐剂,增稠剂为丙烯酸增稠剂。
以上实施例1~3提供的一种无醛阻燃防水胶的制备方法,包括以下步骤:
S1,将生物质蛋白和水性高分子异氰酸酯按比例倒入搅拌机中,高速搅拌10min,得到混合原料A;
S2,将硼砂破碎,磨成粉,然后加入水玻璃,混合研磨,得到混合原料B;
S3,将混合原料B倒入搅拌机中,与混合原料A进行混合,高速搅拌10min,然后依次按比例加入聚硅氮烷、阻燃粉、防腐剂和增稠剂,高速搅拌20min,制得产品。
本发明提供的一种无醛阻燃防水胶的制备方法,所得产品进行了一系列的性能测试,所得结果如下:
综上,本发明提供的一种无醛阻燃防水胶的制备方法所得到的产品具有良好的性能,零甲醛排放,力学性能好,阻燃等级高,具有广阔的应用前景。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点,对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
尽管已经示出和描述了本发明的实施例,对于本领域的普通技术人员而言,可以理解在不脱离本发明的原理和精神的情况下可以对这些实施例进行多种变化、修改、替换和变型,本发明的范围由所附权利要求及其等同物限定。
Claims (6)
1.一种无醛阻燃防水胶,其特征在于,包括以下组成成分:
生物质蛋白、水性高分子异氰酸酯、水玻璃、硼砂、聚硅氮烷、阻燃粉、防腐剂和增稠剂。
2.根据权利要求1所述的一种无醛阻燃防水胶,其特征在于,以质量份数计,各组成成分的含量如下:
生物质蛋白20~25份、水性高分子异氰酸酯5~12份、水玻璃3~8份、硼砂1~3份、聚硅氮烷3~5份、阻燃粉1~3份、防腐剂0.2~0.4份和增稠剂0.1~0.5份。
3.根据权利要求1所述的一种无醛阻燃防水胶,其特征在于,所述生物质蛋白的成分为明胶。
4.根据权利要求1所述的一种无醛阻燃防水胶,其特征在于,所述阻燃粉为铝类复合阻燃粉。
5.根据权利要求1所述的一种无醛阻燃防水胶,其特征在于,所述防腐剂为卡松防腐剂,所述增稠剂为丙烯酸增稠剂。
6.如权利要求1~5任一项所述的一种无醛阻燃防水胶的制备方法,其特征在于,包括以下步骤:
S1,将生物质蛋白和水性高分子异氰酸酯按比例倒入搅拌机中,高速搅拌10min,得到混合原料A;
S2,将硼砂破碎,磨成粉,然后加入水玻璃,混合研磨,得到混合原料B;
S3,将混合原料B倒入搅拌机中,与混合原料A进行混合,高速搅拌10min,然后依次按比例加入聚硅氮烷、阻燃粉、防腐剂和增稠剂,高速搅拌20min,制得产品。