CN114853426A - 一种用于外墙外保温体系的轻质抹面胶浆 - Google Patents
一种用于外墙外保温体系的轻质抹面胶浆 Download PDFInfo
- Publication number
- CN114853426A CN114853426A CN202210631525.XA CN202210631525A CN114853426A CN 114853426 A CN114853426 A CN 114853426A CN 202210631525 A CN202210631525 A CN 202210631525A CN 114853426 A CN114853426 A CN 114853426A
- Authority
- CN
- China
- Prior art keywords
- percent
- light
- weight
- mortar
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种用于外墙外保温体系的轻质抹面胶浆，包括以下质量分数的组分配置而成：硅酸盐水泥15%～25%，级配砂石45%～65%，纤维素醚0.2%～1.0%份，胶粉2%～5%，聚苯颗粒0.5%～2.5%，重质碳酸钙粉20%～30%，憎水剂0.1%～0.5%，纤维0.1%～0.5%。本发明的产品具有轻质、耐冲击、单道施工厚度更高的特点；施工工艺更简单，大幅缩短施工所需时间，同时单位面积厚度下用量更低，性价比更高；具有优异的抗冲击性，为系统提供了更高的安全性。
Description
技术领域
本发明属于外墙涂料技术领域，具体涉及一种用于外墙外保温体系的轻质抹面胶浆。
背景技术
在外墙外保温施工中，有时会遇到由于模塑板基面平整度差或者墙面脚手架连接处修补等厚质抹灰的需求，在这种情况下，对于后续抹面层的施工厚度要求往往要求达到10mm以上。但是，目前一般外墙外保温用抹面胶浆单道施工厚度仅为3-5mm，当遇到厚层抹灰要求时，只能采用多道施工的工艺，相应的人工费、施工周期都会显著增加。
而一般目前市面上的可以满足厚层施工的产品大多为石膏基产品，并不能用于外墙系统中。或者只是满足普通抹灰砂浆标准，并不能满足外墙外保温抹面胶浆标准要求。
厚层施工的前提是降低砂浆的容重指标，一般采用膨胀珍珠岩、玻化微珠、聚苯颗粒作为轻质填料，使用这些材料配置的抹面砂浆在外墙外保温系统中会存在如下问题：
(1)膨胀珍珠岩：结构为多孔空腔结构，强度较低，无法满足抹面胶浆抗冲击要求，同时吸水量较大，会大幅提高抹面胶浆的吸水量指标，降低外墙外保温体系长期耐冻融性能。
(2)玻化微珠：结构为多孔空腔结构，强度较低，无法满足抹面胶浆抗冲击要求；同时吸水量取决于玻化率和破损率，会大幅加剧吸水量波动，降低外墙外保温体系长期耐冻融性能。
(3)聚苯颗粒：由可发性聚苯乙烯树脂珠粒为基础原料膨胀发泡制成，质量轻、吸水率低，是一种良好的轻质材料。但由于一般市面使用的聚苯颗粒粒径较大(1-5mm)，会直接导致砂浆孔隙率过大，使得水泥水化结构疏松，强度、抗冲击性都出现大幅下降，无法满足外保温抹面砂浆的要求。例如文献【李启强，张海波，等.废旧聚苯颗粒改性水泥砂浆力学性能研究[J].混凝土与水泥制品，2014，(3):P76-78.】就研究了废旧聚苯颗粒掺量对水泥砂浆静力学性能的影响，随着废旧聚苯颗粒掺量增加，抗折强度和抗压强度均呈下降趋势。
因此目前的市场现状就是并没有即可满足厚质抹灰要求同时可以达到外墙外保温抹面胶浆要求的产品。
发明内容
本发明的目的是提供一种用于外墙外保温体系的轻质抹面胶浆，以解决现有技术中抹面砂浆不能同时满足厚层施工和外墙外保温系统对于配套抹面胶浆耐冲击、低吸水的的要求。
本发明解决技术问题所采用的技术方案如下。
本发明的一种用于外墙外保温体系的轻质抹面胶浆，其特征在于，包括以下质量分数的组分配置而成：硅酸盐水泥15％～25％，级配砂石45％～65％，纤维素醚0.2％～1.0％份，胶粉2％～5％，聚苯颗粒0.5％～2.5％，重质碳酸钙粉20％～30％，憎水剂0.1％～0.5％，纤维0.1％～0.5％；
所述级配砂石为细度为30～120目的天然石英砂、天然河砂、机制石英砂中的一种或几种混合物；
所述纤维素醚为甲基纤维素醚、羟丙基甲基纤维素醚或者羟乙基甲基纤维素醚中的一种或几种，粘度20000～200000mpa·s；
所述胶粉为乙烯-醋酸乙烯共聚胶粉和/或建筑胶粉，优选为乙烯-醋酸乙烯共聚胶粉；
所述聚苯颗粒由可发性聚苯乙烯树脂珠粒为基础原料膨胀发泡制成；优选为母料的平均粒径为0.1～0.3mm、发泡后的平均粒径为0.5～2.0mm、容重为18～25kg/m3的聚苯颗粒；
所述重质碳酸钙粉的细度为200～400目；
所述憎水剂有机硅烷憎水剂或硬脂酸类憎水剂中的一种或几种混合物；所述纤维为聚丙烯纤维，长度为3～9mm。
本发明的一种用于外墙外保温体系的轻质抹面胶浆的制备方法，其特征在于，包括以下步骤：将所述硅酸盐水泥、级配砂石、纤维素醚、胶粉、憎水剂和PP纤维混合均匀；再添加所述聚苯颗粒；再添加所述重质碳酸钙粉，充分搅拌即可得到轻质抹面胶浆粉体。
本发明所述的轻质抹面胶浆，使用时与清水的质量比为(4～6)：1，优选的混合比例为(4.4～4.8)：1；先将适量水倒入搅拌桶，然后再将轻质抹面胶浆粉料慢慢倒入，并搅拌至均匀无颗粒，静置熟化3～5min再次搅拌，即可使用。
本发明的有益效果是：
本发明的轻质抹面胶浆具有轻质、耐冲击、单道施工厚度更高的特点；加入轻质的聚苯颗粒，使得抹面砂浆的容重更低，单道施工厚度从之前的3～5mm提高到10mm厚度，施工工艺更简单，大幅缩短施工所需时间，同时单位面积厚度下用量更低，性价比更高；通过原料的科学配比，使得轻质抹面胶浆在使用聚苯颗粒后仍旧具有优异的抗冲击性，为系统提供了更高的安全性。
具体实施方式
下面通过具体实施例，对本发明的技术方案作进一步的具体说明。
本发明中，若非特指，所采用的原料和设备等均可从市场购得或是本领域常用的。下述实施例中的方法，如无特别说明，均为本领域的常规方法。
实施例1
一种用于外墙外保温体系的轻质抹面胶浆，由以下质量分数的组分配置而成：普通硅酸盐水泥20％，级配砂石55％，粘度为20000mpa·s的羟丙基甲基纤维素醚0.3％，胶粉3％，粒径规格为0.5～2.0mm容重为18kg/m3的聚苯颗粒1％，细度为325目的重钙粉20％，憎水剂0.2％，长度为3mm的纤维0.5％；
将硅酸盐水泥、级配砂石、纤维素醚、胶粉、憎水剂和PP纤维混合均匀；再添加聚苯颗粒搅拌均匀；最后添加重钙粉，充分搅拌均匀，得到轻质抹面胶浆粉；
使用时，将轻质抹面胶浆粉与清水按照质量比4.7：1，先将适量水倒入搅拌桶，然后再将轻质抹面胶浆粉料慢慢倒入，并搅拌至均匀无颗粒，静置熟化3～5min再次搅拌，即可使用。施工时应在1.1～1.2m的宽度范围内由下至上将搅拌好的抹面胶浆均匀的涂抹到保温板上，及时地将玻纤网格布压入胶浆中，并将从网格中挤出的砂浆抹平。单层产品厚度可以满足10mm要求。
实施例2
一种用于外墙外保温体系的轻质抹面胶浆，由以下重量份的组分配置而成：普通硅酸盐水泥23％，级配砂石52％，粘度为40000mpa·s的羟丙基甲基纤维素醚0.25％，胶粉3％，粒径规格为0.5～2.0mm容重为18kg/m3的聚苯颗粒2％，细度为325目的重钙粉19％，憎水剂0.2％，长度为3mm的纤维0.55％；
将硅酸盐水泥、级配砂石、纤维素醚、胶粉、憎水剂和PP纤维混合均匀；再添加聚苯颗粒搅拌均匀；最后添加重钙粉，充分搅拌均匀，得到轻质抹面胶浆粉；
使用时，将轻质抹面胶浆粉与清水按照质量比4.7：1，先将适量水倒入搅拌桶，然后再将轻质抹面胶浆粉料慢慢倒入，并搅拌至均匀无颗粒，静置熟化3～5min再次搅拌，即可使用。施工时应在1.1～1.2m的宽度范围内由下至上将搅拌好的抹面胶浆均匀的涂抹到保温板上，及时地将玻纤网格布压入胶浆中，并将从网格中挤出的砂浆抹平。单道施工厚度可以由10mm提高到15mm。
实施例3
一种用于外墙外保温体系的轻质抹面胶浆，由以下重量份的组分配置而成：普通硅酸盐水泥25％，级配砂石50％，粘度为40000mpa·s的羟丙基甲基纤维素0.25％，胶粉3％，粒径规格为0.5～2.0mm容重为18kg/m3的聚苯颗粒2.5％，细度为325目的重钙粉18.4％，憎水剂0.2％，长度为3mm的纤维0.65％；
将硅酸盐水泥、级配砂石、纤维素醚、胶粉、憎水剂和PP纤维混合均匀；再添加聚苯颗粒搅拌均匀；最后添加重钙粉，充分搅拌均匀，得到轻质抹面胶浆粉；
使用时，将轻质抹面胶浆粉与清水按照质量比4.7：1，先将适量水倒入搅拌桶，然后再将轻质抹面胶浆粉料慢慢倒入，并搅拌至均匀无颗粒，静置熟化3～5min再次搅拌，即可使用。施工时应在1.1～1.2m的宽度范围内由下至上将搅拌好的抹面胶浆均匀的涂抹到保温板上，及时地将玻纤网格布压入胶浆中，并将从网格中挤出的砂浆抹平。单道施工厚度可以由10mm提高到20mm。
实施例4
本发明的实施例同实施例3，不同之处在于所述纤维替换为长度为6mm聚丙烯纤维。
按照GB/T 29906-2013《模塑聚苯板薄抹灰外墙外保温系统材料》要求，将实施例1～4的轻质抹面胶浆粉进行配置并检测，其各项性能指标如表1。表2则给出了实施例1的轻质抹面胶浆粉在不同外保温体系中的用量。
表1的性能检测结果
由表1可以看出，本发明的轻质抹面胶浆粉在满足外墙外保温抹面胶浆性能的前提下单道施工厚度提升到10mm，节约了外墙外保温厚层施工的工序时间，降低了施工工期。
表2实施例1在不同外保温体系中的用量测试结果
从表2可以看出，本发明的轻质抹面胶浆较普通抹面胶浆在不同外保温体系中用量都有所下降，其性价比更高。
在表1中同时对比了一款市售的玻化微珠抹面砂浆并根据GB/T29906-2013《模塑聚苯板薄抹灰外墙外保温系统材料》进行测试，与本发明的轻质抹面胶浆相比，对比的玻化微珠抹面胶浆吸水量、抗冲击性、不透水性、浸水拉拔强度都未能符合标准要求，本发明的轻质抹面胶浆在改善浸水性的同时优化了抗冲击性，提高了产品性能，同时也能满足厚层施工的要求，产品性能、施工性都优于市售玻化微珠抹面砂浆。
Claims (9)
1.一种用于外墙外保温体系的轻质抹面胶浆，其特征在于，包括以下质量分数的组分配置而成：硅酸盐水泥15%～25%，级配砂石45%～65%，纤维素醚0.2%～1.0%份，胶粉2%～5%，聚苯颗粒0.5%～2.5%，重质碳酸钙粉20%～30%，憎水剂0.1%～0.5%，纤维0.1%～0.5%。
2.根据权利要求1所述的的轻质抹面胶浆，其特征在于，所述级配砂石为细度为30～120目的天然石英砂、天然河砂、机制石英砂中的一种或几种混合物。
3.根据权利要求1所述的的轻质抹面胶浆，其特征在于，所述纤维素醚为甲基纤维素醚、羟丙基甲基纤维素醚或者羟乙基甲基纤维素醚中的一种或几种，粘度20000～200000mpa•s。
4.根据权利要求1所述的的轻质抹面胶浆，其特征在于，所述胶粉为乙烯-醋酸乙烯共聚胶粉和/或建筑胶粉。
5.根据权利要求1所述的的轻质抹面胶浆，其特征在于，所述聚苯颗粒由可发性聚苯乙烯树脂珠粒为基础原料膨胀发泡制成；母料的平均粒径为0.1～0.3mm、发泡后的平均粒径为0.5～2.0mm、容重为18～25kg/m3的聚苯颗粒。
6.根据权利要求1所述的的轻质抹面胶浆，其特征在于，所述重质碳酸钙粉的细度为200～400目；所述憎水剂有机硅烷憎水剂或硬脂酸类憎水剂中的一种或几种混合物；所述纤维为聚丙烯纤维，长度为3～9mm。
7.一种用于外墙外保温体系的轻质抹面胶浆的制备方法，其特征在于，包括以下步骤：将所述硅酸盐水泥、级配砂石、纤维素醚、胶粉、憎水剂和PP纤维混合均匀；再添加所述聚苯颗粒；再添加所述重质碳酸钙粉，充分搅拌即可得到轻质抹面胶浆粉体。
8.根据权利要求7所述的的轻质抹面胶浆得制备方法，其特征在于，所述轻质抹面胶浆，使用时与清水的质量比为（4～6）：1；先将适量水倒入搅拌桶，然后再将轻质抹面胶浆粉料慢慢倒入，并搅拌至均匀无颗粒，静置熟化3～5min再次搅拌，即可使用。
9.根据权利要求8所述的的轻质抹面胶浆得制备方法，其特征在于，所述轻质抹面胶浆，使用时与清水的质量比为（4.4～4.8）：1。