CN114836084A - 一种耐腐蚀聚合物水泥涂料及其制备方法 - Google Patents
一种耐腐蚀聚合物水泥涂料及其制备方法 Download PDFInfo
- Publication number
- CN114836084A CN114836084A CN202210704118.7A CN202210704118A CN114836084A CN 114836084 A CN114836084 A CN 114836084A CN 202210704118 A CN202210704118 A CN 202210704118A CN 114836084 A CN114836084 A CN 114836084A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber reinforced
- waste
- reinforced plastic
- resistant polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种耐腐蚀聚合物水泥涂料及其制备方法，该耐腐蚀聚合物水泥涂料按重量份数计包括以下原料组分：废弃纤维增强塑料粉40～50份、无机填料20～30份、水泥10～20份、聚合物乳液40～50份、成膜助剂1～5份、增塑剂1～3份、分散剂0.1～0.5份、消泡剂0.4～1份、水6～10份；所述废弃纤维增强塑料粉粒径不大于50μm，其通过对纤维增强塑料废弃物进行粉碎研磨获得。本发明利用废弃复合材料替代生产能耗高的水泥，即可消耗大量堆积的复合固废，变废为宝，利于环境保护和节能减排；废弃复合材料代替部分水泥还可降低原料成本；而且还可显著增强水泥涂料的力学强度、耐化学腐蚀性、抗渗性、粘结强度及柔韧性。
Description
技术领域
本发明属于节能环保建筑材料技术领域，具体涉及一种耐腐蚀聚合物水泥涂料及其制备方法。
背景技术
近年来，随着我国工业化、城市化进程的迅速发展，虽然各类建筑物给人们带来便利，但水汽、氯离子及二氧化碳等有害物质通过混凝土表面孔隙进入其内部，会对建筑物造成严重腐蚀。例如，建筑物墙体腐蚀造成建筑结构严重失稳，从而带来安全隐患；房屋因腐蚀造成的渗漏，给人们生活带来不变；水工建筑物因地下水的腐蚀危害建筑物的稳定和安全。因此，做好建筑物的防腐蚀工作尤为重要，可采用防腐涂料对建筑物进行防腐处理。
无机涂料具有环境污染小、技术经济性能优、材料种类丰富等优点，但具有耐腐蚀性能差、易开裂、粘接强度低等缺点。有机涂料具有弹性良好、防水性能好、粘接强度高等优点，但具有收缩系数大、耐火性差、透气性差等缺点。现有的防腐涂料大多以水泥为粉料，水泥生产的能耗大，不符合节能减排的趋势；且水泥涂料大多性能还需要进一步改进。例如公开号为CN106987187A的中国专利，其公开了一种水泥涂料，该水泥涂料具有优异的防霉、防潮及抗冻性，使用寿命也明显延长，且制备简单易生产。但该水泥涂料的拉伸强度不高，且涂层附着效果也欠佳。
发明内容
本发明的目的是提供一种利用废弃复合材料代替部分水泥的耐腐蚀聚合物水泥涂料及其制备方法，既可消耗大量的废弃复合材料，也可进一步提高水泥涂料的性能。
本发明的技术方案如下：
一种耐腐蚀聚合物水泥涂料，按重量份数计包括以下原料组分：
废弃纤维增强塑料粉40～50份、无机填料20～30份、水泥10～20份、聚合物乳液40～50份、成膜助剂1～5份、增塑剂1～3份、分散剂0.1～0.5份、消泡剂0.4～1份、水6～10份；
所述废弃纤维增强塑料粉粒径不大于50μm，其通过对纤维增强塑料废弃物进行粉碎研磨获得。
作为优选方案，本发明耐腐蚀聚合物水泥涂料，按重量份数计包括以下原料组分：
废弃纤维增强塑料粉40～50份、无机填料20～30份、水泥15份、聚合物乳液45份、成膜助剂1～3份、增塑剂2～3份、分散剂0.3～0.5份、消泡剂0.7～1份、水8份；
所述废弃纤维增强塑料粉粒径不大于50μm，其通过对纤维增强塑料废弃物进行粉碎研磨获得。
在一些具体实施方式中，水泥优选15份，聚合物乳液优选45份，成膜助剂优选1～3份，增塑剂优选2～3份、分散剂优选0.3～0.5份、消泡剂优选0.7～1份、水优选8份。
在一些具体实施方式中，纤维增强塑料废弃物为玻璃纤维增强塑料废弃物或碳纤维增强塑料废弃物。
在一些具体实施方式中，水泥采用普通硅酸盐水泥。
在一些具体实施方式中，无机填料采用由过400目筛所得的石英粉或膨润土。
在一些具体实施方式中，膨润土采用季铵型有机膨润土。
在一些具体实施方式中，聚合物乳液采用丙烯酸乳液或EVA乳液。
在一些具体实施方式中，成膜助剂采用乙二醇丁醚、乙二醇丁醚乙酸酯或丙二醇丁醚。
在一些具体实施方式中，增塑剂采用邻苯二甲酸二丁酯、邻苯二甲酸二辛酯或己二酸二辛酯。
在一些具体实施方式中，分散剂采用聚氧乙烯山梨醇酐单油酸酯。
在一些具体实施方式中，消泡剂采用有机硅型消泡剂或聚醚类消泡剂。
上述耐腐蚀聚合物水泥涂料的制备方法，包括：
(1)按前述重量份数取废弃纤维增强塑料粉、无机填料和水泥混合，经搅拌得干粉料；
(2)按前述重量份数取聚合物乳液、成膜助剂、增塑剂、分散剂、消泡剂和水混合，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌3～6min，制得耐腐蚀聚合物水泥涂料。
本发明中废弃纤维增强塑料粉通过对纤维增强塑料废弃物进行粉碎研磨获得，纤维增强塑料废弃物可以为玻璃纤维增强塑料废弃物或碳纤维增强塑料废弃物，进一步来说，玻璃纤维增强塑料废弃物可采用回收的废弃玻璃钢管道，碳纤维增强塑料废弃物可采用回收的废弃电子电器的电极板。玻璃纤维增强塑料更有利于提高水泥涂料的耐化学腐蚀性，而碳纤维增强塑料更有利于提高水泥涂料的耐久性。
无机填料采用石英粉或膨润土，石英粉更有利于提高水泥的水化度，增加水泥密实度，进而提高涂料强度；进一步来说，石英粉的加入可形成结晶中心，水泥水化时在石英粉结晶中心周围结晶并生长晶体，从而提高水泥密实度。而且石英粉具有强耐酸性，可制备耐酸性水泥涂料。此外，石英粉本身具有一定活性，可发生水化反应，从而填充涂料的毛细孔隙，降低涂料孔隙率，改善涂料整体性，使涂料不易被破坏。
膨润土具有吸附性，可使高分子聚合物一端吸附于膨润土颗粒表面，另一端溶于水使膨润土颗粒和水分子间产生间接联系，形成桥联作用，减少浆料中的自由水，从而提高水泥涂料性能。而膨润土的膨胀性可补偿涂料在硬化过程中的收缩值，避免涂料出现收缩开裂。
聚合物乳液可改善涂料的和易性，降低涂料渗透性，提高涂料附着力、抗化学腐蚀性、冻融风化以及碳化能力。一方面，聚合物与水泥间的物理作用，随着水泥水化和水泥凝胶化逐渐形成，聚合物颗粒包裹水泥凝胶颗粒表面，填充水泥凝胶孔隙。随着水分减少，聚合物逐渐被限制在毛细管孔隙中。涂料中较大的孔隙被聚合物填充，聚合物分子中的活性基团还可与水泥水化产物交联形成特殊的桥联，改善水泥涂料硬化体的物理结构，从而提高涂料密度。另一方面，聚合物与水泥间存在化学作用，由于连续水化作用，聚合物乳液水解液可与Ca(OH)2反应生成新的网络结构。这些交联网络结构产物覆盖水化产物和未水化颗粒，从而改善水泥砂浆的结构形态。
成膜助剂可促使乳胶粒子的塑性流动和弹性变形，改善其聚结性，软化乳液聚合物粒子，使它们融合在一起，降低涂料的最低成膜温度，因此，加入适量的成膜助剂能有效的提高其弹性和低温柔性。
在聚合物水泥涂料中加入适量的增塑剂，可削弱聚合物分子间的范德华力，从而增加聚合物分子链间的移动性，降低聚合物分子的结晶性，从而使聚合物分子链段变得柔顺，增加聚合物的弹塑性，进而增加聚合物水泥涂料的断裂延伸率、加强低温柔性。
在聚合物水涂料中加入适量的分散剂，由于分散剂能够提高粉料和填料的分散性，因此提高了聚合物水泥涂料的拉伸性能和降低了其涂料吸水率。
和现有技术相比，本发明具有如下优点和有益效果：
(1)利用废弃复合材料替代生产能耗高的水泥，即可消耗大量堆积的复合固废，变废为宝，利于环境保护和节能减排；废弃复合材料代替部分水泥还可降低原料成本。
(2)利用废弃复合材料替代部分水泥，可显著增强水泥涂料的力学强度、耐化学腐蚀性、抗渗性、粘结强度及柔韧性。
(3)工艺简单且废弃复合材料利用难度低，仅需将废弃复合材料粉碎研磨到一定细度即可，生产成本低。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，下面将进一步提供本发明的具体实施方式及实施例。应当理解，此处所描述的具体实施方式仅仅用以解释本发明，并不用于限定本发明。
以下结合具体实施例，对本发明技术方案作进一步说明。
在实施例和对比例中，所用原料来源如下：
废弃玻璃纤维增强塑料粉通过对回收的玻璃钢管道进行粉碎研磨获得，粒径不大于50μm，该玻璃钢管道主要成分为玻璃纤维增强环氧树脂；废弃碳纤维增强塑料粉通过对回收电子电器的电极板进行粉碎研磨获得，粒径不大于50μm，该电子电器的电极板主要成分为碳纤维增强酚醛树脂。
水泥：华新水泥的P.I42.5普通硅酸盐水泥；
膨润土：建平佳鑫矿业有限责任公司的季铵型有机膨润土；
石英粉：河南鸿树环保材料有限公司的石英粉；
丙烯酸乳液：新成化工有限公司，主要成份为丙烯酸类单体，固化量为49.5％，平均粒径为220nm；
EVA乳液：佛山今佳新材料科技有限公司，主要成份为醋酸乙烯单体，固含量为53.0％，平均粒径为225nm；
成膜助剂：麦克林试剂有限公司的乙二醇丁醚(化学式：C6H14O2，分析纯，纯度99.0％)、乙二醇丁醚乙酸酯(化学式：C8H16O3，分析纯，纯度98.0％)、丙二醇丁醚(化学式：C11H26O5，为分析纯，纯度99.5％)；
增塑剂：麦克林试剂有限公司的邻苯二甲酸二丁酯(化学式：C16H22O4，分析纯，纯度99.5％)、邻苯二甲酸二辛酯(化学式：C24H38O4，分析纯，纯度99.0％)、己二酸二辛酯(化学式：C22H42O4，分析纯，纯度99.0％)；
分散剂，麦克林试剂有限公司的吐温-80，成分为聚氧乙烯山梨醇酐单油酸酯，化学式：C24H44O6；
消泡剂：河北蓝凯节能科技有限公司的有机硅型消泡剂和聚醚类消泡剂，其中，有机硅型消泡剂主要成分为聚二甲基硅氧烷；聚醚类消泡剂为环氧乙烷和环氧丙烷的共聚物。
实施例1
本实施例耐腐蚀聚合物水泥涂料，按重量份数计包括以下原料组分：
废弃玻璃纤维增强塑料粉45份、膨润土25份、水泥15份、EVA乳液45份、乙二醇丁醚3份、邻苯二甲酸二丁酯2份、分散剂0.3份、聚醚类消泡剂0.7份、水8份。
本实施例耐腐蚀聚合物水泥涂料的制备步骤如下：
(1)取45份玻璃纤维增强环氧树脂、25份膨润土和15份水泥混合，经搅拌均匀得干粉料；
(2)取45份EVA乳液、3份乙二醇丁醚、2份邻苯二甲酸二丁酯、0.3份分散剂、0.7份聚醚类消泡剂和8份水混合，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌5min，制得耐腐蚀聚合物水泥涂料。
实施例2
本实施例耐腐蚀聚合物水泥涂料，按照重量份数计包括以下原料组分：
废弃玻璃纤维增强塑料粉40份、石英粉30份、水泥15份、EVA乳液45份、乙二醇丁醚3份、邻苯二甲酸二丁酯2份、分散剂0.3份、聚醚类消泡剂0.7份、水8份。
本实施例耐腐蚀聚合物水泥涂料的制备步骤如下：
(1)取40份玻璃纤维增强环氧树脂、30份石英粉和15份水泥混合，经搅拌均匀得干粉料；
(2)取45份EVA乳液、3份乙二醇丁醚、2份邻苯二甲酸二丁酯、0.3份分散剂、0.7份聚醚类消泡剂和8份水混合，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌5min，制得耐腐蚀聚合物水泥涂料。
实施例3
本实施例耐腐蚀聚合物水泥涂料，按照重量份数计包括以下原料组分：
废弃玻璃纤维增强塑料粉40份、膨润土30份、水泥15份、EVA乳液45份、乙二醇丁醚3份、邻苯二甲酸二丁酯2份、分散剂0.3份、聚醚类消泡剂0.7份、水8份。
本实施例耐腐蚀聚合物水泥涂料的制备步骤如下：
(1)取40份玻璃纤维增强环氧树脂、30份膨润土和15份水泥混合，经搅拌均匀得干粉料；
(2)取45份EVA乳液、3份乙二醇丁醚、2份邻苯二甲酸二丁酯、0.3份分散剂、0.7份聚醚类消泡剂，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌5min，制得耐腐蚀聚合物水泥涂料。
实施例4
本实施例耐腐蚀聚合物水泥涂料，按照重量份数计包括以下原料组分：
废弃玻璃纤维增强塑料粉50份、膨润土20份、水泥15份、EVA乳液45份、乙二醇丁醚3份、邻苯二甲酸二丁酯2份、分散剂0.3份、聚醚类消泡剂0.7份、水8份。
本实施例耐腐蚀聚合物水泥涂料的制备步骤如下：
(1)取50份玻璃纤维增强环氧树脂、20份膨润土和15份水泥混合，经搅拌均匀得干粉料；
(2)取45份EVA乳液、3份乙二醇丁醚、2份邻苯二甲酸二丁酯、0.3份分散剂、0.7份聚醚类消泡剂和8份水混合，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌5min，制得耐腐蚀聚合物水泥涂料。
实施例5
本实施例耐腐蚀聚合物水泥涂料，按照重量份数计包括以下原料组分：
废弃碳纤维增强塑料粉45份、石英粉25份、水泥10份、丙烯酸乳液50份、乙二醇丁醚3份、邻苯二甲酸二丁酯2份、分散剂0.3份、聚醚类消泡剂0.7份、水6份。
本实施例耐腐蚀聚合物水泥涂料的制备步骤如下：
(1)取45份碳纤维增强酚醛树脂、25份石英粉和10份水泥混合，经搅拌均匀得干粉料；
(2)取50份丙烯酸乳液、3份乙二醇丁醚、2份邻苯二甲酸二丁酯、0.3份分散剂、0.7份聚醚类消泡剂和6份水混合，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌5min，制得耐腐蚀聚合物水泥涂料。
实施例6
本实施例耐腐蚀聚合物水泥涂料，按照重量份数计包括以下原料组分：
废弃碳纤维增强塑料粉45份、石英粉25份、水泥20份、丙烯酸乳液40份、乙二醇丁醚乙酸酯3份、邻苯二甲酸二辛酯2份、分散剂0.3份、有机硅消泡剂0.7份、水10份。
本实施例耐腐蚀聚合物水泥涂料的制备步骤如下：
(1)取45份碳纤维增强酚醛树脂、25份石英粉和20份水泥混合，经搅拌均匀得干粉料；
(2)取40份丙烯酸乳液、3份乙二醇丁醚乙酸酯、2份邻苯二甲酸二辛酯、0.3份分散剂、0.7份有机硅消泡剂和10份水混合，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌5min，制得耐腐蚀聚合物水泥涂料。
实施例7
本实施例耐腐蚀聚合物水泥涂料，按照重量份数计包括以下原料组分：
废弃玻璃纤维增强塑料粉45份、膨润土25份、水泥15份、EVA乳液45份、乙二醇丁醚1份、邻苯二甲酸二丁酯3份、分散剂0.5份、聚醚类消泡剂1份、水8份。
本实施例耐腐蚀聚合物水泥涂料的制备步骤如下：
(1)取45份玻璃纤维增强环氧树脂、25份膨润土和15份水泥混合，经搅拌均匀得干粉料；
(2)取45份EVA乳液、1份乙二醇丁醚、3份邻苯二甲酸二丁酯、0.5份聚醚类消泡剂、1份聚醚类消泡剂和8份水混合，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌5min，制得耐腐蚀聚合物水泥涂料。
实施例8
本实施例耐腐蚀聚合物水泥涂料，按照重量份数计包括以下原料组分：
废弃玻璃纤维增强塑料粉45份、膨润土25份、水泥15份、EVA乳液45份、丙二醇丁醚5份、己二酸二辛酯1份、分散剂0.1份、有机硅消泡剂0.4份、水8份。
本实施例耐腐蚀聚合物水泥涂料的制备步骤如下：
(1)取45份玻璃纤维增强环氧树脂、25份膨润土和15份水泥混合，经搅拌均匀得干粉料；
(2)取45份EVA乳液、5份丙二醇丁醚、1份己二酸二辛酯、0.1份分散剂、0.4份有机硅消泡剂和8份水混合，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌5min，制得耐腐蚀聚合物水泥涂料。
对比例1
对比例1在实施例1的基础上，将实施例1中玻璃纤维增强环氧树脂采用等量的水泥替换，其他均不变。
对比例2
对比例2在实施例1的基础上，将实施例1中膨润土采用等量的水泥替换，其他均不变。
对比例3
对比例3在实施例1的基础上，将实施例1中EVA乳液采用等量的水替换，其他均不变。
对比例4
对比例4在实施例1的基础上，不添加成膜助剂，其他均不变。
对比例5
对比例5在实施例1的基础上，不添加分散剂，其他均不变。
对比例6
对比例6在实施例1的基础上，不添加增塑剂，其他均不变。
实施例1～8和对比例1～6的原料配方见表1和表2，其中，表1为实施例1～8的原料配方，表2为对比例1～6的原料配方。
表1实施例1～8的原料配方
表2对比例1～6的原料配方
对实施例1～8和对比例1～6所制备聚合物水泥涂料进行性能测试，根据GB/T16777-2008标准，测试聚合物水泥涂料分别在无处理、酸处理、碱处理下的拉伸强度和断裂伸长率、以及粘接强度、低温柔性。按照标准GB/T 528-2009要求截取哑铃I型试件，将无处理试件夹在拉伸试验机上，拉伸至断裂测试试件的拉伸强度和断裂伸长率。
裁取若干120mm×25mm大小的矩形试件，分别放在质量浓度为0.1％的600mL氢氧化钠水溶液和质量浓度为2％的600mL硫酸水溶液中，浸泡(168±1)h，取出擦干，再于(60±2)℃的电热鼓风烘箱中放置(6h±15)min，取出并在标准试验条件下放置(18±2)h，得到酸处理和碱处理后的试件。此处标准试验条件为：温度：(23±2)℃，相对湿度：(50±10)％。再按照标准GB/T 528-2009要求截取哑铃I型试件，将酸处理和碱处理的试件夹在拉伸试验机上，拉伸至断裂测试试件的拉伸强度和断裂伸长率。
将无处理试件安装在拉伸试验机上，保持试件表面垂直方向的中线与试验机夹具中心在一条线上，拉伸至试件破坏，记录最大拉力即试件的粘接强度。
将无处理试件和弯板或圆棒放入-10℃的冷冻液中，将温度计探头与试件置于同一水平位置，保持1h，然后在冷冻液中将试件绕圆棒或弯板在3s内弯曲180°，用肉眼观察试件表面有无裂纹。根据GB/T 23445-2009标准测试聚合物水泥涂料的抗渗性，将无处理试件放入渗透仪中，记录试件表面出现透水现象的水压(MPa)，水压值越大抗渗性越优。
所得性能测试数据见表3，其中无处理试件所对应数据为拉伸强度数据，酸处理和碱处理试件所对应数据为试件的拉伸强度保持率数据，即酸处理和碱处理后试件，其平均拉伸强度占无处理试件平均拉伸强度的百分率。
从表3可以看出，相较于对比例，实施例1～4及7的性能较好。实施例5中聚合物乳液用量略多，拉伸强度有降低；实施例6中聚合物乳液用量略少，断裂伸长率有降低。这是因为聚合物乳液用量多，水泥用量就少，影响拉伸强度。当聚合物乳液在体系中含量逐渐增加，使聚合物逐渐跃升为主要组分，而水泥为次要或改性成分，导致微观上水泥胶体链不完整，而聚合物的柔性链部分可完全包裹住水泥胶体颗粒，可提高体系的柔韧性，从而可增大断裂伸长率。对比例1中未添加废弃复合材料粉，对比例2中未添加无机填料，对比例3中未添加聚合物乳液，对比例4中未添加成膜助剂，对比例5中未添加分散剂，对比例6中未添加增塑剂，均对水泥涂料性能有显著影响。
表3实施例1～8和对比例1～6所制备聚合物水泥涂料的性能测试数据
本发明聚合物水泥涂料具有拉伸性能优、耐腐蚀性能优、抗渗性能优、粘结强度高、低温柔韧性好、价格低廉、绿色环保等优点，在降低成本的同时，还可以很好地改善建筑物表面易腐蚀、易开裂、易破损的问题。
上述本发明做了详细说明并且描述了实施例，但是对于本发明并不局限于此，本领域的普通技术人员，显然可以按照上述说明而做出各种形式上的改动和创新，只要不脱离本发明权利要求所保护的范围内，均受保护。
Claims (10)
1.一种耐腐蚀聚合物水泥涂料，其特征是：
按重量份数计包括以下原料组分：
废弃纤维增强塑料粉40～50份、无机填料20～30份、水泥10～20份、聚合物乳液40～50份、成膜助剂1～5份、增塑剂1～3份、分散剂0.1～0.5份、消泡剂0.4～1份、水6～10份；
所述废弃纤维增强塑料粉粒径不大于50μm，其通过对纤维增强塑料废弃物进行粉碎研磨获得。
2.如权利要求1所述的耐腐蚀聚合物水泥涂料，其特征是：
按重量份数计包括以下原料组分：
废弃纤维增强塑料粉40～50份、无机填料20～30份、水泥15份、聚合物乳液45份、成膜助剂1～3份、增塑剂2～3份、分散剂0.3～0.5份、消泡剂0.7～1份、水8份；
所述废弃纤维增强塑料粉粒径不大于50μm，其通过对纤维增强塑料废弃物进行粉碎研磨获得。
3.如权利要求1或2中任一项所述的耐腐蚀聚合物水泥涂料，其特征是：
所述纤维增强塑料废弃物为玻璃纤维增强塑料废弃物或碳纤维增强塑料废弃物。
4.如权利要求1或2中任一项所述的耐腐蚀聚合物水泥涂料，其特征是：
所述无机填料采用由过400目筛所得的石英粉或季铵型有机膨润土。
5.如权利要求1或2中任一项所述的耐腐蚀聚合物水泥涂料，其特征是：
所述聚合物乳液采用丙烯酸乳液或EVA乳液。
6.如权利要求1或2中任一项所述的耐腐蚀聚合物水泥涂料，其特征是：
所述成膜助剂采用乙二醇丁醚、乙二醇丁醚乙酸酯或丙二醇丁醚。
7.如权利要求1或2中任一项所述的耐腐蚀聚合物水泥涂料，其特征是：
所述增塑剂采用邻苯二甲酸二丁酯、邻苯二甲酸二辛酯或己二酸二辛酯。
8.如权利要求1或2中任一项所述的耐腐蚀聚合物水泥涂料，其特征是：
所述分散剂采用聚氧乙烯山梨醇酐单油酸酯。
9.如权利要求1或2中任一项所述的耐腐蚀聚合物水泥涂料，其特征是：
所述消泡剂采用有机硅型消泡剂或聚醚类消泡剂。
10.权利要求1或2中任一项所述耐腐蚀聚合物水泥涂料的制备方法，其特征是，包括：
(1)按重量份数取废弃纤维增强塑料粉、无机填料和水泥混合，经搅拌得干粉料；
(2)按重量份数取聚合物乳液、成膜助剂、增塑剂、分散剂、消泡剂和水混合，经过搅拌制得液料；
(3)将干粉料加入搅拌机，一边搅拌一边加入液料，待液料全部加完，再继续搅拌3～6min，制得耐腐蚀聚合物水泥涂料。