CN114774772A - 一种耐腐蚀500hb马氏体耐磨钢板及其生产方法 - Google Patents

一种耐腐蚀500hb马氏体耐磨钢板及其生产方法 Download PDF

Info

Publication number
CN114774772A
CN114774772A CN202210215586.8A CN202210215586A CN114774772A CN 114774772 A CN114774772 A CN 114774772A CN 202210215586 A CN202210215586 A CN 202210215586A CN 114774772 A CN114774772 A CN 114774772A
Authority
CN
China
Prior art keywords
equal
resistant
steel plate
corrosion
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN202210215586.8A
Other languages
English (en)
Other versions
CN114774772B (zh
Inventor
刘俊
李曜
韩步强
武金明
杨洋
徐婷
芦莎
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Jiangyin Xingcheng Special Steel Works Co Ltd
Original Assignee
Jiangyin Xingcheng Special Steel Works Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jiangyin Xingcheng Special Steel Works Co Ltd filed Critical Jiangyin Xingcheng Special Steel Works Co Ltd
Priority to CN202210215586.8A priority Critical patent/CN114774772B/zh
Publication of CN114774772A publication Critical patent/CN114774772A/zh
Application granted granted Critical
Publication of CN114774772B publication Critical patent/CN114774772B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种耐腐蚀500HB马氏体耐磨钢板，化学成分按质量百分比计为C：0.25～0.30％，Si：0.10～0.40％，Mn：0.10～0.30％，Nb：0.010～0.040％，V：0.010～0.040％，Ti:0.010～0.040％，Al：0.02～0.05％，Cu：0.50～0.65％，Ni：1.50～2.00％，Cr：1.80～2.50％，Mo：0.50～1.00％，B：0.001～0.005％，Ca：0.0010～0.0050％，P：≤0.015％，S：≤0.0015％，O：≤0.0015％，N：≤0.0035％，H：≤0.0002％，余量为Fe及不可避免的杂质元素，且满足Ni/Cu≥3.0。显微组织为细小的马氏体组织；表面布氏硬度470‑530HB；抗拉强度≥1600MPa，延伸率≥10％，‑40℃夏比V型冲击功≥30J，表现出良好的低温韧性、强度。钢板在pH值为4.5‑6.5的酸性工况下，其抗腐蚀磨损性能可达同等硬度普通马氏体耐磨钢的1.5倍及以上。

Description

一种耐腐蚀500HB马氏体耐磨钢板及其生产方法
技术领域
本发明涉及一种铁基合金耐磨钢，属于铁基合金钢技术领域。
背景技术
马氏体耐磨钢具有良好的强韧性与焊接性，在工程机械、矿山机械及煤矿机械等领域得到了广泛的应用。但该种耐磨钢在湿态条件下的抗磨损能力不能得到很好的保证。比如，环卫车车斗用耐磨钢，由于垃圾液的存在，钢板表面很快腐蚀，导致磨损加重；煤矿机械采煤机中部槽，在潮湿矿井中呈弱酸性的恶劣工况下，钢板在腐蚀和磨损双重作用下很快失效，设备使用寿命大大降低。因此，有必要解决耐磨钢板在酸性湿态条件下的耐腐蚀磨损问题。
中国专利文献CN112159934A介绍了一种450HB级别的耐腐蚀耐磨钢。该发明添加了极高的Cr元素，含量在3.00％～6.00％。中国专利文献CN11549277A，Cr含量3.4％～4.0％。如此高的Cr含量一方面提高了钢板的耐腐蚀性，另一方面导致钢板碳当量大幅增加，焊接性能变差，同时大大增加了生产过程中的开裂倾向，其应用推广受到一定限制。
中国专利文献CN112267073A提供了一种低Cr解决方案，Cr含量为0.60～1.20％。为弥补低Cr带来的腐蚀性能下降的问题，该文献添加了0.06％～0.12％的Sb和0.02～0.10％的Sn。Sb和Sn虽然具有一定的耐腐蚀能力，但属于低熔点元素，很容易造成钢铁材料在连铸、轧钢或热处理过程中产生表面裂纹，因此常常被冶金工作者认为是非常规的有害元素而被限制加入。该发明实例硬度为372～476HB。同样，中国专利CN111575581A提供了一种低Cr(Cr：0.90％～1.3％)含Sb(Sb:0.08％～0.12％)450HB级耐蚀耐磨钢。
中国专利文献CN112195404A提供了一种含P含Sb耐蚀耐磨钢。为解决P和Sb带来的开裂问题，该文献创新性的添加了稀土元素铈(Ce：0.0020～0.0035％)。
综上所述，现有技术的耐腐蚀马氏体耐磨钢中，耐腐蚀性能的解决通常通过以下途径获得：(1)高Cr合金化：钢中Cr含量通常添加到3％以上；(2)Sb/Sn/P等非常规特殊合金元素的加入。高Cr、低熔点、低韧性等元素的加入，必然在源头上导致钢板制备及应用过程中韧性降低、极易产生裂纹，从而采用苛刻工艺，限制了该类产品的广泛应用。另外，现有发明的钢板硬度普遍在450HB及以下，属于低级别耐磨钢板。
随着耐磨设备的大型化，使用工况的进一步复杂化，开发500HB高级别低合金易加工耐腐蚀耐磨钢板势在必行，。
发明内容
本发明的目的在于提供一种500HB耐腐蚀耐磨钢板及其制造方法。该低合金耐磨钢板显微组织为细小的马氏体组织；表面布氏硬度470-530HB；抗拉强度≥1600MPa，延伸率≥10％，-40℃夏比V型冲击功≥30J，表现出良好的低温韧性、强度。钢板在pH值为4.5-6.5的酸性工况下，其抗腐蚀磨损性能可达同等硬度普通马氏体耐磨钢的1.5倍及以上。
本发明解决上述问题所采用的技术方案为：一种耐腐蚀500HB马氏体耐磨钢板，化学成分按质量百分比计为C：0.25～0.30％，Si：0.10～0.40％，Mn：0.10～0.30％，Nb：0.010～0.040％，V：0.010～0.040％，Ti:0.010～0.040％，Al：0.02～0.05％，Cu：0.50～0.65％，Ni：1.50～2.00％，Cr：1.80～2.50％，Mo：0.50～1.00％，B：0.001～0.005％，Ca：0.0010～0.0050％，P：≤0.015％，S：≤0.0015％，O：≤0.0015％，N：≤0.0035％，H：≤0.0002％，余量为Fe及不可避免的杂质元素，且满足Ni/Cu≥3.0。
本发明中钢成分的限定理由阐述如下：
C：碳含量决定了钢板的硬度。碳含量低，硬度低、韧性好、焊接性优良；碳含量高，淬火马氏体转变完全，强度高，硬度高，耐磨性好，但钢板塑韧性降低，焊接性差。基于钢板硬度、耐磨性和焊接性需要，本发明中碳含量控制为0.25～0.30％。
Si：硅固溶在铁素体和奥氏体中提高强度和硬度。含量过高会恶化马氏体钢的韧性，同时表面质量下降，控制在0.10～0.40％之间。
Cr：提高钢板耐腐蚀性能必须添加的元素，同时降低马氏体转变临界冷却速度，提高淬透性。Cr在钢中还可以形成多种碳化物，提高钢的强度、硬度和耐磨性，提高钢的高温回火抗力。但Cr含量过高会降低钢板的可焊接性，同时在淬火过程中易产生裂纹。故本发明采用中铬设计，含量控制在1.80％～2.50％。
Mn：增加奥氏体稳定性，提高钢的淬透性的有效元素。过高时有使晶粒粗化的倾向，同时会引起连铸坯偏析、韧性差和可焊性降低。而偏析形成的MnS会大幅减低酸性条件下钢板的抗腐蚀磨损能力。本发明采用超低Mn设计，限定锰含量加入量介于0.10～0.30％的范围内。主要原因有：(1)Mn易于氧化及偏析，对于钢板抗腐蚀能力十分不利；(2)本发明采用中Cr设计，淬透性很强，如继续采用中高Mn设计，钢板碳当量将大幅增加，钢板淬火过程中开裂风险很大，同时焊接性能将无法保证。
Cu：能够有效地降低钢的平均腐蚀深度和腐蚀速率,利于提高钢的耐腐蚀性能；同时也是有效提高钢的低温韧性的常用元素。但Cu含量过高，易于在晶界偏局导致星裂纹。为确保本发明钢板在耐腐蚀的同时，具有-40℃超低温冲击韧性，本发明限定Cu含量应介于0.50～0.65％。
Ni：抗腐蚀元素，有效提高钢的低温韧性的最常用元素，同时能与Cu相互固溶，降低Cu的热脆裂纹。由于本发明Cu含量相对较高，在连铸时有一定风险产生星形裂纹。为解决该问题，本发明采用Ni-Cu复合添加，限定Ni含量介于1.50～2.00％之间，同时要求Ni/Cu比≥3。
Nb/V/Ti：是强烈的C、N化物的形成元素，起到对奥氏体晶界的钉扎作用，在加热时抑制奥氏体晶粒的长大，并在轧制和回火过程中析出，显著提高钢的强度和韧性。由于V元素的增加不利于钢的焊接性能，本发明取消V的加入，采用Nb/Ti复合，规定Nb或Ti含量应介于0.010～0.040％范围内。
Al：强脱氧元素，同时与N有较强的亲和力，可以消除N元素造成的时效敏感性。N化物的析出起到细化奥氏体晶粒的效果，保护了B元素的淬透性作用。本发明中，规定Al含量应介于0.020～0.050％。
Mo：是提高钢淬透性的元素，有利于淬火时马氏体的形成。添加一定含量的Mo会提高钢板的强度，而不会影响钢板的低温冲击性能。Mo能增加钢板的回火抗性，可以使得钢板在较高的温度下不降低强度。本发明中Mo含量控制在0.50～1.00％。
B：本发明加入0.001～0.005％的微量B，其主要目的是提高钢板的淬透性，从而减少其他贵重金属的添加量，降低成本。超过0.005％的B很容易产生偏析，形成硼化物，严重恶化钢板韧性和降低淬透性。
Ca：Ca处理通常用来进行夹杂物变性处理，改变MnS等长条状夹杂物为CaS等球形夹杂物，降低钢板各向异性，提高钢板综合性能。本发明控制Ca含量0.0010～0.0050％。
P：有害元素，对材料塑性和韧性有不利影响。本发明追求超纯净钢，严格控制P含量≤0.015％。
S：钢中有害元素，对材料塑性和韧性有不利影响。S含量高，极易形成MnS等长条夹杂物，导致钢板各向异性，容易发生分层开裂。本发明要求S：≤0.0015％。
O、N、H：有害气体元素，含量高，夹杂物多，易产生白点，大大降低钢板塑性、韧性，产生切割延迟裂纹。本发明严格控制O含量不高于0.0015％；N含量不高于0.0035％；H含量≤0.0002％。
本发明另提供上述一种耐腐蚀500HB耐磨钢板的制备方法，具体工艺如下：
冶炼、连铸工艺：可选的：钢水冶炼涉及铁水预处理，采用电炉或转炉方式初炼，然后送入LF精炼炉进行精炼，并经过VD或RH真空处理。钢水脱气后进行微量Ca处理。连铸采用低过热度浇注，全程氩气保护浇注，以及动态轻压下控制。钢水过热度控制在5～25℃,中心偏析不高于C1.0级。
加热轧制工艺：加热优选将铸坯进入步进式加热炉，加热的温度为1150-1250℃，待心部温度到达表面温度时开始保温，保温时间不低于30min，使钢中的合金元素充分固溶以保证最终产品的成份及性能的均匀性。钢坯出炉后经高压水除鳞处理后进行粗轧+精轧两阶段控制轧制，细化晶粒，提高强度和韧性。粗轧的开轧温度介于1000-1100℃。待温厚度≥2H，其中H为成品厚度。精轧开轧温度介于820-920℃。为降低钢板内应力，降低延迟裂纹风险，钢板轧制后快速下线进行缓冷处理。缓冷开始温度≥100℃，缓冷时间≥24h。
淬火热处理工艺：钢板缓冷后进行离线淬火处理。淬火温度880-940℃，炉温到温后保温时间为30-60min，水淬。
回火热处理工艺：钢板淬火后，需要在200-250℃进行低温回火。钢板心部到温后，回火保温时间30-90min。
本申请与现有技术相比，具有如下特点和优势：
本发明采用超低Mn及中Cr设计，钢板合金含量低，在保证钢板耐腐蚀性能的同时，确保了钢板具有良好的焊接性能。
本发明采用Cu-Ni复合设计，Ni/Cu比≥3.0，在充分发挥Cu元素抗腐蚀性能的同时，降低了钢板裂纹产生的风险。同时，Ni-Cu的加入有利于钢板及焊接接头-40℃低温冲击性能的提高。
生产工艺上，本发明轧制后，快速下线进行缓冷处理。缓冷开始温度≥100℃，缓冷时间≥24h，降低了钢板延迟裂纹产生的风险。
产品性能上，本发明钢板表面布氏硬度470-530HB；抗拉强度≥1600MPa，延伸率≥10％，-40℃夏比V型冲击功≥30J，表现出良好的低温韧性和强度。钢板在PH值为4.5-6.5的酸性工况下，其抗腐蚀磨损性能可达同等硬度普通马氏体耐磨钢的1.5倍及以上。
本申请的耐腐蚀500HB耐磨钢板综合性能优良，相比现有钢种，合金含量低，添加元素均为常规元素，生产制造工艺控制简单，为社会经济和钢铁工业发展之必然趋势。
附图说明
图1是本发明实施例1的产品钢典型组织金相图片。
图2为本发明实施例1的产品与对比案例1、2产品的极化曲线。
具体实施方式
以下结合实施例对本发明作进一步详细描述，所述实施例是示例性的，旨在用于解释本发明，而不能理解为对本发明的限制。
本申请的耐腐蚀耐磨钢的生产工艺流程为：转炉炼钢->LF精炼->VD或RH高真空脱气->连铸->加热->轧制->缓冷->淬火->回火。
实施例1-2及对比例1-2的耐磨钢板的生产方法，包括如下步骤：
(1)冶炼：采用电炉或转炉方式冶炼，然后送入LF精炼炉进行精炼，并经过VD或RH真空处理。钢水脱气后进行微量Ca处理。钢水成分控制及对比例化学成分控制见表1。
(2)连铸：将冶炼的钢水浇铸成150mm厚的连铸坯。浇铸温度控制在液相线以上5-25℃。浇铸过程中实施动态轻压下，中心偏析不高于C1.0级。连铸工艺参数及板坯低倍控制见表2。
(3)轧制及缓冷：将步骤(2)所得连铸坯放入步进式加热炉，加热至1200℃，心部到温后开始保温，保温时间60分钟。钢坯出炉后经高压水除鳞处理后进行粗轧+精轧两阶段控制轧制。粗轧的开轧温度介于1000-1100℃，待温厚度≥2.0H；精轧开轧温度介于820-920℃。钢板轧制后快速下线进行缓冷处理。缓冷开始温度≥100℃，缓冷时间≥24h。具体相关工艺参数见表3。
(4)淬火：钢板淬火温度为900左右℃，保温时间为30-60min，水淬。
(5)回火：淬火钢板进入回火炉进行高温回火，回火温度200-250℃，保温时间30-90min。
具体成分、工艺参数见表1-表4。各实例样板对应的性能见表5。
图1给出了实施例1试验钢的微观组织照片。成品钢板的微观组织为均一的马氏体，晶粒细小，尺寸≤25um。
图2为本发明和对比例1、2钢板极化曲线对比。可见，本发明采用中Cr设计，钢板自腐蚀电位明显高于对比例1 0.81％低Cr钢板，略高于对比例2 4％高Cr钢板，表现了优越的耐腐蚀性能。
将实施例1和对比例1、2钢板试样放入盐雾箱进行盐雾加速腐蚀试验。试验按照国家标准GB/T10125-2012进行，溶液PH值5.5，实验周期240h，腐蚀失重检测结果见表6。可见，本发明腐蚀后失重最小，体现了良好的抗腐蚀能力。
表1实施例耐磨钢板的化学成分(wt％)
Figure BDA0003534427280000061
表2连铸工艺控制
实施例 过热度℃ 中心偏析
1 20 C1.0
2 15 C0.5
表3轧制工艺控制
Figure BDA0003534427280000062
表4热处理工艺控制
Figure BDA0003534427280000063
Figure BDA0003534427280000071
表5钢板力学性能
Figure BDA0003534427280000072
表6盐雾腐蚀实验
实验前质量，g 腐蚀酸洗后质量，g 失重比 相对耐腐蚀能力
实施例1 30.609 30.527 0.268％ 5.20
对比例1 29.155 28.479 1.393％ 1
对比例2 32.531 32.441 0.28％ 4.98
除上述实施例外，本发明还包括有其他实施方式，凡采用等同变换或者等效替换方式形成的技术方案，均应落入本发明权利要求的保护范围之内。

Claims (7)

1.一种耐腐蚀500HB马氏体耐磨钢板，其特征在于：化学成分按质量百分比计为C：0.25～0.30％，Si：0.10～0.40％，Mn：0.10～0.30％，Nb：0.010～0.040％，V：0.010～0.040％，Ti:0.010～0.040％，Al：0.02～0.05％，Cu：0.50～0.65％，Ni：1.50～2.00％，Cr：1.80～2.50％，Mo：0.50～1.00％，B：0.001～0.005％，Ca：0.0010～0.0050％，P：≤0.015％，S：≤0.0015％，O：≤0.0015％，N：≤0.0035％，H：≤0.0002％，余量为Fe及不可避免的杂质元素，且满足Ni/Cu≥3.0。
2.根据权利要求1所述的耐腐蚀500HB马氏体耐磨钢板，其特征在于：表面布氏硬度470-530HB；抗拉强度≥1600MPa，延伸率≥10％，-40℃夏比V型冲击功≥30J，马氏体组织的晶粒尺寸≤25um。
3.根据权利要求1所述的耐腐蚀500HB马氏体耐磨钢板，其特征在于：钢板的生产方法包括如下工艺：
冶炼、连铸工艺：获得符合化学成分的铸坯；
加热轧制工艺：铸坯入炉加热，使钢中的合金元素充分固溶，钢坯出炉后经高压水除鳞，之后进行粗轧+精轧两阶段控制轧制：粗轧的开轧温度介于1000-1100℃，待温厚度≥2H，H为成品厚度，精轧开轧温度介于820-920℃，钢板轧制后快速下线进行缓冷处理；
淬火热处理工艺：钢板缓冷后进行离线淬火处理，淬火温度880-940℃，炉温到温后保温30-60min，水淬；
回火热处理工艺：钢板淬火后，需要在200-250℃进行低温回火，钢板心部到温后，回火保温30-90min。
4.根据权利要求3所述的耐腐蚀500HB马氏体耐磨钢板，其特征在于：所述冶炼涉及：铁水预处理，采用电炉或转炉方式对钢水初炼，钢水精炼，钢水VD或RH真空处理，钢水脱气后进行微量Ca处理。
5.根据权利要求3所述的耐腐蚀500HB马氏体耐磨钢板，其特征在于：所述连铸采用低过热度浇注，全程氩气保护浇注，以及动态轻压下控制，钢水过热度控制在5～25℃，中心偏析不高于C1.0级。
6.根据权利要求3所述的耐腐蚀500HB马氏体耐磨钢板，其特征在于：加热轧制工艺中，将铸坯送入步进式加热炉，加热至1150-1250℃，待心部温度到达表面温度时开始保温，保温时间不低于30min。
7.根据权利要求3所述的耐腐蚀500HB马氏体耐磨钢板，其特征在于：加热轧制工艺中，轧制结束后的缓冷，缓冷开始温度≥100℃，缓冷时间≥24h。
CN202210215586.8A 2022-03-07 2022-03-07 一种耐腐蚀500hb马氏体耐磨钢板及其生产方法 Active CN114774772B (zh)