CN114762533A - 一种卷烟滤棒的低温缓释加香颗粒及其制备方法和应用 - Google Patents
一种卷烟滤棒的低温缓释加香颗粒及其制备方法和应用 Download PDFInfo
- Publication number
- CN114762533A CN114762533A CN202110035728.8A CN202110035728A CN114762533A CN 114762533 A CN114762533 A CN 114762533A CN 202110035728 A CN202110035728 A CN 202110035728A CN 114762533 A CN114762533 A CN 114762533A
- Authority
- CN
- China
- Prior art keywords
- particles
- cigarette filter
- filter stick
- low
- temperature slow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种卷烟滤棒的低温缓释加香颗粒及其制备方法和应用，涉及滤嘴添加物技术领域，本发明将加热不燃烧抽吸品的相关技术与传统卷烟相结合，所制备的缓释颗粒中通过设置浸润了聚乳酸的增强型植物纤维，从而保证颗粒的强度，不易破碎掉渣，提高了成品率，其自身的强度也保证了在应用时可选择的方法多样化；同时本发明在颗粒外表喷洒纤维素溶液覆盖层，能够有效防止颗粒中的挥发性香味物质的流失，以及发烟剂发烟和润湿效果的降低；同时所述颗粒在烟气通过时能够释放含有香味物质和水蒸气的烟雾，具有烟雾量大，进入口腔的烟气温度低，口味多样化等优点，香料选择范围广，易于生产，消费者体验好。
Description
技术领域
本发明涉及烟油滤芯，例如过滤嘴、过滤插入物等技术领域，具体涉及一种卷烟滤棒的低温缓释加香颗粒及其制备方法和应用。
背景技术
香烟的口感和风味主要来源于烟草燃烧是释放的烟气，烟气的释放量、烟气的湿度大小，以及烟气中所携带的呈香物质，均会很大程度上影响香烟的口感和风味。其中，香味物质作为烟草添加剂，具有调香、增加甜润度、改善吸味、减轻刺激，提高烟草品质的作用；另外，香烟燃烧时所释放的烟气量越大，其内包含的呈香物质就越多，呈现的口感就越醇厚、香气也就更浓烈；并且烟气中的水分含量大，烟气的刺激性和不适感就会降低。
目前主流的评价烟用香味物质的主要指标有香韵、挥发性、持久性和稳定性。烟用香味物质大多具有沸点低，易挥发的特点，受外界因素的影响，其香味逐渐变淡，品质降低。其中，通过颗粒和爆珠来实现香烟口感和风味的调整是最为直接和成熟的方式，相关的技术十分丰富，但据一些相关机构的实验结果显示：爆珠香烟的爆珠使用以后，对于香烟物质的释放量有一定程度的影响，例如苯、巴豆醛、亚硝胺NNK 的释放量不稳定。
近年来，新型烟草，特别是加热不燃烧抽吸品，其有害成分释放量减少，显现了较大的市场潜力，但其烟气产生机制与传统卷烟不同，“加热不燃烧”抽吸品在烟气释放量、香味物质，以及烟气含水量的添加与控制方面均优于传统香烟，其技术改进的基础、范围和深度相对于传统香烟都更有优势。但“加热不燃烧”抽吸品法人技术门槛较高，各项参数的控制难度较高，并且核心技术多被技术壁垒所保护；同时，由于“加热不燃烧”抽吸品的作用机理和原材料均与常规香烟存在本质区别，还需要购置相应的使用设备，成本较高，导致很多消费者无论是无法接受口感、风味，还是成本因素考虑，都不选择“加热不燃烧”抽吸品，使其难以推广，而相关产品的发展与较为缓慢。
为克服以上问题，烟草企业在生产中将“加热不燃烧”抽吸品的中关于烟气参数控制的相关技术应用到传统香烟的制备中，不仅能够提升传统香烟的品质，降低技术门槛，还能使部分技术获得广泛应用，进而促进其发展。
发明内容
为解决现有技术中存在的问题，本发明提供了一种卷烟滤棒的低温缓释加香颗粒及其制备方法和应用，提高香气迁移效率，使其前后段均匀性和香味自然协调性更好，提高香料选择范围，降低生产难度，实现增加香气、保润以及增加烟雾量的目的，让消费体验更好。
本发明的目的之一，是提供一种卷烟滤棒的低温缓释加香颗粒，采用以下技术方案：一种卷烟滤棒的低温缓释加香颗粒，其特征在于，所述加香颗粒为多孔疏松结构，直径为0.3mm-1.0mm，采用天然香料、植物纤维、发烟剂、粘接剂混合制备。
所述天然香料包括植物类、动物类、矿物质类香料中的任意一种或任意两种及以上的混合物。
所述植物类天然香料包括芳香植物的花、果、叶、皮或地下茎、种籽及树脂分泌物。
所述动物类天然香料包括麝香、灵猫香、海狸香和龙涎香。
所述矿物质类天然香料为无毒性的矿石类中药材。
所述植物纤维采用植物的根、茎纤维干燥后粉碎至长度0.1-0.3mm，具体包括上述植物类天然香料的根、茎纤维，以及天然麻纤维、竹纤维中的任意一种或两种以上的混合物。
所述发烟剂为丙二醇、丙三醇、丁三醇、甘油任意一种或两种以上混合物，其余为水，比例为水：单一物质或混合物=1:2-3；所述混合物中各物质按相同比例均分。
所述粘接剂为所述粘接剂包括壳聚糖、瓜尔胶、卡拉胶、明胶、琼脂、阿拉伯胶、黄原胶、果胶中的任意一种。
本发明的目的之二，是提供一种卷烟滤棒的低温缓释加香颗粒的制备方法，采用以下技术方案：
一种卷烟滤棒的低温缓释加香颗粒的制备方法，其特征在于，包括以下步骤：
一、所述颗粒采用天然香料、植物纤维、发烟剂、粘接剂混合制备：
①选择植物类、动物类、矿物质类香料中的任意一种或任意两种及以上的混合物，进行晒干或者风干至水分含量≤15%，并将其粉碎至粒径0.05-0.1mm，按重量计，用量为40-80份；
②将植物纤维干燥后粉碎至长度0.1-0.3mm备用，按重量计为10-20份；
③将步骤②的植物纤维平均分为两份，其中的5-10份加入纤维素酶进行溶解，并用两倍的体积的蒸馏水混合制得纤维素溶液；
④将步骤③中平分的另外5-10份植物纤维浸入浓度为2-3%的聚乳酸溶液中混合，按重量计，植物纤维：聚乳酸溶液=1:5，所得混合物干燥后粉碎成粒径0.05-0.1mm的颗粒；
⑤将步骤①和步骤④所得的原料进行混合，然后加入发烟剂、粘接剂进行搅拌均匀，按重量计，所述发烟剂的用量为20-25份，所述粘接剂的用量不超过原料总重量的0.3%；
⑥将步骤⑤所得混合物进行造粒，并用流化床干燥至颗粒含水率为5-7%，之后进行筛分，保留直径为0.3mm-1.0mm的颗粒；
⑦将步骤③中所得纤维素溶液喷洒到步骤⑥得到的颗粒上，干燥后形成保护膜，之后控制颗粒含水率小于等于10%，得到颗粒。
优选的，在步骤⑤进行原料混合工序时，加入液态香精一起混合，液态香精的用量为混合原料总重量的5%-15%。
优选的，步骤⑦中采用顶喷方式喷洒。
本发明的目的之三，是提供上述卷烟滤棒的低温缓释加香颗粒在传统卷烟中的具体应用方式，采用以下技术方案：
将所述低温缓释加香颗粒按照常规方法应用在卷烟滤棒的制备中，即，将颗粒均匀分散在卷烟滤棒的醋酸纤维丝束中，或者将若干颗粒单独包裹在卷烟滤棒的下部靠近烟丝段的位置，制成二元滤棒；或者将若干颗粒单独包裹在卷烟滤棒中间部位，制成三元滤棒；或者将颗粒粘附在卷烟滤棒的接装纸或成型纸的内表面，然后包裹成型。
有益效果：
本发明将加热不燃烧抽吸品的相关技术与传统卷烟相结合，所制备的缓释颗粒中通过设置浸润了聚乳酸的增强型植物纤维，从而保证颗粒的强度，不易破碎掉渣，提高了成品率，其自身的强度也保证了在应用时可选择的方法多样化；同时本发明在颗粒外表喷洒纤维素溶液覆盖层，能够有效防止颗粒中的挥发性香味物质的流失，以及发烟剂发烟和润湿效果的降低。
本发明所述颗粒在烟气通过时能够释放含有香味物质和水蒸气的烟雾，具有烟雾量大，进入口腔的烟气温度低，口味多样化等优点；通过烟气温度加热发烟剂带动香料挥发起到增香目的，增香效率比爆珠或普通滤棒要高且更加自然；缓释颗粒中的发烟剂本身具有保湿作用，保证烟支和烟气水分含量，从而降低烟气干燥感，香味自然协调性好，香料选择范围广，易于生产，消费者体验好。
具体实施方式
下面对本发明所述技术方案进行进一步说明。
实施例1
本实施例所述的一种卷烟滤棒的低温缓释加香颗粒，为多孔疏松结构，直径为0.3mm-1.0mm，采用天然香料、植物纤维、发烟剂、粘接剂混合制备。
所述天然香料采用甘草；所述植物纤维采用天然麻纤维干燥后粉碎至长度0.1-0.3mm；所述发烟剂为丙二醇与水的混合物，水：丙二醇=1:2；粘接剂选用壳聚糖。
一种卷烟滤棒的低温缓释加香颗粒的制备方法，包括以下步骤：
一、所述颗粒采用甘草、天然麻纤维、丙二醇与水的混合物、以及壳聚糖混合制备：
①选择甘草进行晒干或者风干至水分含量≤15%，并将其粉碎至粒径0.05-0.1mm，按重量计，用量为70份；
②将天然麻纤维干燥后粉碎至长度0.1-0.3mm备用，按重量计为20份；
③将步骤②的天然麻纤维平均分为两份，其中的10份加入纤维素酶进行溶解，并用两倍的体积的蒸馏水混合制得纤维素溶液；
④将步骤③中平分的另外10份天然麻纤维浸入浓度为2-3%的聚乳酸溶液中混合，按重量计，天然麻纤维：聚乳酸溶液=1:5，所得混合物干燥后粉碎成粒径0.05-0.1mm的颗粒；
⑤将步骤①和步骤④所得的原料进行混合，然后加入丙二醇与水的混合物、壳聚糖进行搅拌均匀，按重量计，所述丙二醇与水的混合物的用量为20份，所述壳聚糖的用量为0.2份；
⑥将步骤⑤所得混合物进行造粒，并用流化床干燥至颗粒含水率为5-7%，之后进行筛分，保留直径为0.3mm-1.0mm的颗粒；
⑦将步骤③中所得纤维素溶液喷洒到步骤⑥得到的颗粒上，干燥形成保护膜，之后控制颗粒含水率小于等于10%，得到颗粒。
将上述制备好的低温缓释加香颗粒均匀分散在卷烟滤棒的醋酸纤维丝束中。
实施例2
本实施例所述的一种卷烟滤棒的低温缓释加香颗粒，采用柠檬叶80份、竹纤维10份、丙二醇+甘油与水的混合物25份、以及瓜尔胶0.3份混合制备，在进行原料混合工序时，加入薄荷精油6份一起混合；将上述制备好的低温缓释加香颗粒单独包裹在卷烟滤棒的下部靠近烟丝段的位置，制成二元滤棒。
实施例3
本实施例所述的一种卷烟滤棒的低温缓释加香颗粒，采用罗汉果40份、辣木纤维20份、丙二醇+丁三醇与水的混合物20份、以及明胶0.2份混合制备，在进行原料混合工序时，加入水溶性川贝提取物5份一起混合；将上述制备好的低温缓释加香颗粒单独包裹在卷烟滤棒中间部位，制成三元滤棒。
Claims (10)
1.一种卷烟滤棒的低温缓释加香颗粒，其特征在于，所述加香颗粒为多孔疏松结构，直径为0.3mm-1.0mm，采用天然香料、植物纤维、发烟剂、粘接剂混合制备。
2.根据权利要求1所述的一种卷烟滤棒的低温缓释加香颗粒，其特征在于，所述天然香料包括植物类、动物类、矿物质类香料中的任意一种或任意两种及以上的混合物；其中植物类天然香料包括芳香植物的花、果、叶、皮或地下茎、种籽及树脂分泌物；动物类天然香料包括麝香、灵猫香、海狸香和龙涎香；矿物质类天然香料为无毒性的矿石类中药材；
所述植物纤维采用植物的根、茎纤维干燥后粉碎至长度0.1-0.3mm，具体包括上述植物类天然香料的根、茎纤维，以及天然麻纤维、竹纤维中的任意一种或两种以上的混合物；
所述发烟剂为丙二醇、丙三醇、丁三醇、甘油任意一种或两种以上混合物，其余为水，比例为水：单一物质或混合物=1:2-3；所述混合物中各物质按相同比例均分；
所述粘接剂为所述粘接剂包括壳聚糖、瓜尔胶、卡拉胶、明胶、琼脂、阿拉伯胶、黄原胶、果胶中的任意一种。
3.一种卷烟滤棒的低温缓释加香颗粒的制备方法，其特征在于，包括以下步骤：
一、所述颗粒采用天然香料、植物纤维、发烟剂、粘接剂混合制备：
①选择植物类、动物类、矿物质类香料中的任意一种或任意两种及以上的混合物，进行晒干或者风干至水分含量≤15%，并将其粉碎至粒径0.05-0.1mm，按重量计，用量为40-80份；
②将植物纤维干燥后粉碎至至长度0.1-0.3mm备用，按重量计为10-20份；
③将步骤②的植物纤维平均分为两份，其中的5-10份加入纤维素酶进行溶解，并用两倍的体积的蒸馏水混合制得纤维素溶液；
④将步骤③中平分的另外5-10份植物纤维浸入浓度为2-3%的聚乳酸溶液中混合，按重量计，植物纤维：聚乳酸溶液=1:5，所得混合物干燥后粉碎成粒径0.05-0.1mm的颗粒；
⑤将步骤①和步骤④所得的原料进行混合，然后加入发烟剂、粘接剂进行搅拌均匀，按重量计，所述发烟剂的用量为20-25份，所述粘接剂的用量不超过原料总重量的0.3%；
⑥将步骤⑤所得混合物进行造粒，并用流化床干燥至颗粒含水率为5-7%，之后进行筛分，保留直径为0.3mm-1.0mm的颗粒；
⑦将步骤③中所得纤维素溶液喷洒到步骤⑥得到的颗粒上，干燥后形成保护膜，之后控制颗粒含水率小于等于10%，得到颗粒。
4.根据权利要求2所述的一种卷烟滤棒的低温缓释加香颗粒的制备方法，其特征在于，在步骤⑤进行原料混合工序时，加入液态香精一起混合，液态香精的用量为混合原料总重量的5%-15%。
5.根据权利要求2所述的一种卷烟滤棒的低温缓释加香颗粒的制备方法，其特征在于，步骤⑦中采用顶喷方式喷洒。
6.一种卷烟滤棒的低温缓释加香颗粒在传统卷烟中的应用。
7.根据权利要求6所述的一种卷烟滤棒的低温缓释加香颗粒在传统卷烟中的应用，其特征在于，将所述低温缓释加香颗粒均匀分散在卷烟滤棒的醋酸纤维丝束中。
8.根据权利要求6所述的一种卷烟滤棒的低温缓释加香颗粒在传统卷烟中的应用，其特征在于，将若干颗粒单独包裹在卷烟滤棒的下部靠近烟丝段的位置，制成二元滤棒。
9.根据权利要求6所述的一种卷烟滤棒的低温缓释加香颗粒在传统卷烟中的应用，其特征在于，将若干颗粒单独包裹在卷烟滤棒中间部位，制成三元滤棒。
10.根据权利要求6所述的一种卷烟滤棒的低温缓释加香颗粒在传统卷烟中的应用，其特征在于，将颗粒粘附在卷烟滤棒的接装纸或成型纸的内表面，然后包裹成型。