CN114762534A - 一种低温缓释微晶颗粒及其制备方法和应用 - Google Patents
一种低温缓释微晶颗粒及其制备方法和应用 Download PDFInfo
- Publication number
- CN114762534A CN114762534A CN202110036068.5A CN202110036068A CN114762534A CN 114762534 A CN114762534 A CN 114762534A CN 202110036068 A CN202110036068 A CN 202110036068A CN 114762534 A CN114762534 A CN 114762534A
- Authority
- CN
- China
- Prior art keywords
- release
- low
- microcrystalline
- particles
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种低温缓释微晶颗粒，涉及滤嘴添加物技术领域，本发明将加热不燃烧抽吸品的相关技术与传统卷烟相结合，所制备的低温缓释微晶颗粒设置为三层结构，其中主要的赋香物质为添加在内核中的固态香精和液态香精，通过羧甲基纤维素钠和粉状微晶纤维素作为水溶性的缓释载体，羧甲基淀粉钠作为粘接剂，首先能够保证内核的强度，不易破碎，提高了成品率；同时本发明在颗粒外表喷洒纤维素溶液覆盖层，能够有效防止颗粒中的挥发性香味物质的流失，以及发烟剂发烟和润湿效果的降低；所述颗粒在烟气通过时能够释放含有香味物质和水蒸气的烟雾，具有烟雾量大，进入口腔的烟气温度低，口味多样化等优点。
Description
技术领域
本发明涉及烟油滤芯，例如过滤嘴、过滤插入物等技术领域，具体涉及一种低温缓释微晶颗粒。
背景技术
香烟的口感和风味主要来源于烟草燃烧是释放的烟气，烟气的释放量、烟气的湿度大小，以及烟气中所携带的呈香物质，均会很大程度上影响香烟的口感和风味。其中，香味物质作为烟草添加剂，具有调香、增加甜润度、改善吸味、减轻刺激，提高烟草品质的作用；另外，香烟燃烧时所释放的烟气量越大，其内包含的呈香物质就越多，呈现的口感就越醇厚、香气也就更浓烈；并且烟气中的水分含量大，烟气的刺激性和不适感就会降低。
目前主流的评价烟用香味物质的主要指标有香韵、挥发性、持久性和稳定性。烟用香味物质大多具有沸点低，易挥发的特点，受外界因素的影响，其香味逐渐变淡，品质降低。其中，通过颗粒和爆珠来实现香烟口感和风味的调整是最为直接和成熟的方式，相关的技术十分丰富，但据一些相关机构的实验结果显示：爆珠香烟的爆珠使用以后，对于香烟物质的释放量有一定程度的影响，例如苯、巴豆醛、亚硝胺NNK 的释放量不稳定。
“CN102835736B-一种卷烟滤棒用颗粒材料及其制备方法”，公开了一种卷烟滤棒用颗粒材料及其制备方法，该颗粒材料由脱胶麻纤维粉、微晶纤维素、纳米碳酸钙、水溶性壳聚糖和烟草提取物通过物料混合、颗粒成型、干燥、配制烟草提取物以及颗粒载香五个步骤制备而成。其利用了麻纤维中空结构具有的孔道效应，以及微晶纤维素较高的比表面积，显著地提高了颗粒材料对卷烟烟气的吸附量，从而实现选择性吸附，最终达到优化卷烟吸味、减害降焦方面的需求，对于增香保润效果不明显，也并未提及。
近年来，新型烟草，特别是加热不燃烧抽吸品，其有害成分释放量减少，显现了较大的市场潜力，但其烟气产生机制与传统卷烟不同，“加热不燃烧”抽吸品在烟气释放量、香味物质，以及烟气含水量的添加与控制方面均优于传统香烟，其技术改进的基础、范围和深度相对于传统香烟都更有优势。但“加热不燃烧”抽吸品法人技术门槛较高，各项参数的控制难度较高，并且核心技术多被技术壁垒所保护；同时，由于“加热不燃烧”抽吸品的作用机理和原材料均与常规香烟存在本质区别，还需要购置相应的使用设备，成本较高，导致很多消费者无论是无法接受口感、风味，还是成本因素考虑，都不选择“加热不燃烧”抽吸品，使其难以推广，而相关产品的发展与较为缓慢。
为克服以上问题，烟草企业在生产中将“加热不燃烧”抽吸品的中关于烟气参数控制的相关技术应用到传统香烟的制备中，不仅能够提升传统香烟的品质，降低技术门槛，还能使部分技术获得广泛应用，进而促进其发展。
发明内容
为解决现有技术中存在的问题，本发明提供了一种低温缓释微晶颗粒，提高香气迁移效率，使其前后段均匀性和香味自然协调性更好，提高香料选择范围，降低生产难度，实现增加香气、保润以及增加烟雾量的目的，让消费体验更好。
本发明的目的是提供一种低温缓释微晶颗粒，采用以下技术方案：
一种低温缓释微晶颗粒，其特征在于，所述颗粒为三层结构，即内核、包裹所述内核的壳体，以及外层缓释膜层，其整体直径为0.5mm-1.5mm；所述颗粒采用天然香料、植物纤维、发烟剂、粘接剂、香精、粉状微晶纤维素、羧甲基纤维素钠、羧甲基淀粉钠分次进行制备。
所述天然香料包括植物类、动物类、矿物质类香料中的任意一种或任意两种及以上的混合物；所述植物类天然香料包括芳香植物的花、果、叶、皮或地下茎、种籽及树脂分泌物；所述动物类天然香料包括麝香、灵猫香、海狸香和龙涎香；所述矿物质类天然香料为无毒性的矿石类中药材。
所述植物纤维采用植物的根、茎纤维干燥后粉碎至长度0.1-0.3mm，具体包括上述植物类天然香料的根、茎纤维，以及天然麻纤维、竹纤维中的任意一种或两种以上的混合物。
所述发烟剂为丙二醇、丙三醇、丁三醇、甘油任意一种或两种以上混合物，其余为水，比例为水：单一物质或混合物=1:2-3；所述混合物中各物质按相同比例均分。
所述粘接剂为所述粘接剂包括壳聚糖、瓜尔胶、卡拉胶、明胶、琼脂、阿拉伯胶、黄原胶、果胶中的任意一种。
上述一种低温缓释微晶颗粒的制备方法，采用以下技术方案：
一种低温缓释微晶颗粒的制备方法，其特征在于，包括以下步骤：
一、内核的制备，采用固态香精或液态香精、粉状微晶纤维素、羧甲基纤维素钠、羧甲基淀粉钠制备，具体步骤如下：
称取0.5-1份固态或液态香精、5-10份羧甲基纤维素钠、0.1-0.5份羧甲基淀粉钠、1-2份粉状微晶纤维素混合均匀，加入0.5-1份水搅拌均匀，通过50-20目的筛盘成粒，室温下干燥24小时，即为内核、备用。
二、壳体的制备，采用天然香料、植物纤维、发烟剂、粘接剂混合制备：
①选择植物类、动物类、矿物质类香料中的任意一种或任意两种及以上的混合物，进行晒干或者风干至水分含量≤15%，并将其粉碎至粒径0.05-0.1mm，按重量计，用量为40-80份；
②在步骤①所得的原料进行混合，然后加入发烟剂、粘接剂进行搅拌均匀，按重量计，所述发烟剂的用量为20-25份，所述粘接剂的用量不超过原料总重量的0.3%；
③将步骤②所得混合物与内核通过圆盘造粒机进行造粒，并干燥至颗粒含水率为5-7%，之后进行筛分，保留直径为0.5-1.5的微粒；
三、缓释膜层的制备：
①将植物纤维干燥后粉碎至长度0.1-0.3mm备用，按重量计为10-20份；
②将粉碎好的植物纤维加入水混合搅拌成浆状，然后用1mol/L的冰醋酸调节pH值至5.0-6.0，然后加入纤维素酶和聚木糖酶，纤维素酶的用量3U/g，聚木糖酶的用量为150U/g，调整混合物的浓度为10%，将容器置于水浴锅中进行处理，温度保持在50-70℃，不断进行搅拌，处理时间2-3小时，处理完成后，用200目的筛网过滤点未溶解在植物纤维，制得纤维素溶液；
③将步骤②中所得纤维素溶液通过顶喷方式喷洒到步骤二.③得到的微粒上，干燥后形成保护膜，之后控制微粒含水率小于等于10%，最终得到低温缓释微晶颗粒。
本发明的目的之三，是提供上述低温缓释微晶颗粒在传统卷烟中的具体应用方式，采用以下技术方案：
将所述低温缓释微晶颗粒按照常规方法应用在卷烟滤棒的制备中，即：
将颗粒均匀分散在卷烟滤棒的醋酸纤维丝束中；
或者将若干颗粒单独包裹在卷烟滤棒的下部靠近烟丝段的位置，制成二元滤棒；
或者将若干颗粒单独包裹在卷烟滤棒中间部位，制成三元滤棒；
或者将颗粒粘附在卷烟滤棒的接装纸或成型纸的内表面，然后包裹成型。
有益效果：
本发明将加热不燃烧抽吸品的相关技术与传统卷烟相结合，所制备的低温缓释微晶颗粒设置为三层结构，其中主要的赋香物质为添加在内核中的固态香精和液态香精，通过羧甲基纤维素钠和粉状微晶纤维素作为水溶性的缓释载体，羧甲基淀粉钠作为粘接剂，首先能够保证内核的强度，不易破碎，提高了成品率；同时本发明在颗粒外表喷洒纤维素溶液覆盖层，能够有效防止颗粒中的挥发性香味物质的流失，以及发烟剂发烟和润湿效果的降低。
本发明所述颗粒在烟气通过时能够释放含有香味物质和水蒸气的烟雾，具有烟雾量大，进入口腔的烟气温度低，口味多样化等优点；通过烟气温度加热发烟剂带动香料挥发起到增香目的，增香效率比爆珠或普通滤棒要高且更加自然；缓释颗粒中的发烟剂本身具有保湿作用，保证烟支和烟气水分含量，从而降低烟气干燥感，香味自然协调性好，香料选择范围广，易于生产，消费者体验好。
具体实施方式
下面对本发明所述技术方案进行进一步说明。
实施例1
本实施例所述的本发明的目的是提供一种低温缓释微晶颗粒，采用三层结构，即内核、包裹所述内核的壳体，以及外层缓释膜层，其整体直径为0.5mm-1.5mm；所述颗粒采用天然香料、植物纤维、发烟剂、粘接剂、香精、粉状微晶纤维素、羧甲基纤维素钠、羧甲基淀粉钠分次进行制备；采用甘草；所述植物纤维采用天然麻纤维干燥后粉碎至长度0.1-0.3mm；所述发烟剂为丙二醇与水的混合物，水：丙二醇=1:2；粘接剂选用壳聚糖。
上述一种低温缓释微晶颗粒的制备方法，采用以下技术方案：
一、内核的制备，采用香精与香精、粉状微晶纤维素、羧甲基纤维素钠、羧甲基淀粉钠制备，具体步骤如下：
称取0.5-1份薄荷液态香精、5-10份羧甲基纤维素钠、0.1-0.5份羧甲基淀粉钠、1-2份粉状微晶纤维素混合均匀，加入0.5-1份水搅拌均匀，通过50-20目的筛盘成粒，室温下干燥24小时，即为内核、备用。
二、壳体的制备，采用天然香料、植物纤维、发烟剂、粘接剂混合制备：
①选择甘草进行晒干或者风干至水分含量≤15%，并将其粉碎至粒径0.05-0.1mm，按重量计，用量为40-80份；
②在步骤①所得的原料进行混合，然后加入丙二醇与水的混合物、壳聚糖进行搅拌均匀，按重量计，所述丙二醇与水的混合物的用量为20-25份，所述壳聚糖的用量不超过原料总重量的0.3%；
③将步骤②所得混合物与内核通过圆盘造粒机进行造粒，并干燥至颗粒含水率为5-7%，之后进行筛分，保留直径为0.5-1.5的微粒；
三、缓释膜层的制备：
①将植物纤维干燥后粉碎至长度0.1-0.3mm备用，按重量计为10-20份；
②将粉碎好的植物纤维加入水混合搅拌成浆状，然后用1mol/L的冰醋酸调节pH值至5.0-6.0，然后加入纤维素酶和聚木糖酶，纤维素酶的用量3U/g，聚木糖酶的用量为150U/g，调整混合物的浓度为10%，将容器置于水浴锅中进行处理，温度保持在50-70℃，不断进行搅拌，处理时间2-3小时，处理完成后，用200目的筛网过滤点未溶解在植物纤维，制得纤维素溶液；
③将步骤②中所得纤维素溶液通过顶喷方式喷洒到步骤二.③得到的微粒上，干燥后形成保护膜，之后控制微粒含水率小于等于10%，最终得到低温缓释微晶颗粒；将颗粒均匀分散在卷烟滤棒的醋酸纤维丝束中。
实施例2
本实施例所述的一种低温缓释微晶颗粒，采用柠檬叶80份、竹纤维10份、丙二醇+甘油与水的混合物25份、以及瓜尔胶0.3份混合制备，在制作内核时加入水溶性川贝提取物1份；将上述制备好的低温缓释微晶颗粒单独包裹在卷烟滤棒的下部靠近烟丝段的位置，制成二元滤棒。
实施例3
本实施例所述的一种低温缓释微晶颗粒，采用罗汉果40份、辣木纤维20份、丙二醇+丁三醇与水的混合物20份、以及明胶0.2份混合制备，在制作内核时加入柠檬香精；将上述制备好的低温缓释微晶颗粒单独包裹在卷烟滤棒中间部位，制成三元滤棒。
实施例4
本实施例所述的一种低温缓释微晶颗粒，采用香樟40份、檀香木20份、丙二醇+丁三醇与水的混合物20份、以及卡拉胶0.2份混合制备，在制作内核时加入菊花粉末香精；将上述制备好的低温缓释微晶颗粒粘附在卷烟滤棒的接装纸或成型纸的内表面，然后包裹成型。
Claims (10)
1.一种低温缓释微晶颗粒，其特征在于，所述颗粒为三层结构，即内核、包裹所述内核的壳体，以及外层缓释膜层，其整体直径为0.5mm-1.5mm；所述颗粒采用天然香料、植物纤维、发烟剂、粘接剂、香精、粉状微晶纤维素、羧甲基纤维素钠、羧甲基淀粉钠分次进行制备。
2.根据权利要求1所述的一种低温缓释微晶颗粒，其特征在于，所述天然香料包括植物类、动物类、矿物质类香料中的任意一种或任意两种及以上的混合物；所述植物类天然香料包括芳香植物的花、果、叶、皮或地下茎、种籽及树脂分泌物；所述动物类天然香料包括麝香、灵猫香、海狸香和龙涎香；所述矿物质类天然香料为无毒性的矿石类中药材。
3.根据权利要求1所述的一种低温缓释微晶颗粒，其特征在于，所述植物纤维采用植物的根、茎纤维干燥后粉碎至长度0.1-0.3mm，具体包括上述植物类天然香料的根、茎纤维，以及天然麻纤维、竹纤维中的任意一种或两种以上的混合物。
4.根据权利要求1所述的一种低温缓释微晶颗粒，其特征在于，所述发烟剂为丙二醇、丙三醇、丁三醇、甘油任意一种或两种以上混合物，其余为水，比例为水：单一物质或混合物=1:2-3；所述混合物中各物质按相同比例均分。
5.根据权利要求1所述的一种低温缓释微晶颗粒，其特征在于，所述粘接剂为所述粘接剂包括壳聚糖、瓜尔胶、卡拉胶、明胶、琼脂、阿拉伯胶、黄原胶、果胶中的任意一种。
6.上述一种低温缓释微晶颗粒的制备方法，采用以下技术方案：
一种低温缓释微晶颗粒的制备方法，其特征在于，包括以下步骤：
一、内核的制备，采用固态香精或液态香精、粉状微晶纤维素、羧甲基纤维素钠、羧甲基淀粉钠制备，具体步骤如下：
称取0.5-1份固态或液态香精、5-10份羧甲基纤维素钠、0.1-0.5份羧甲基淀粉钠、1-2份粉状微晶纤维素混合均匀，加入0.5-1份水搅拌均匀，通过50-20目的筛盘成粒，室温下干燥24小时，即为内核、备用；
二、壳体的制备，采用天然香料、植物纤维、发烟剂、粘接剂混合制备：
①选择植物类、动物类、矿物质类香料中的任意一种或任意两种及以上的混合物，进行晒干或者风干至水分含量≤15%，并将其粉碎至粒径0.05-0.1mm，按重量计，用量为40-80份；
②在步骤①所得的原料进行混合，然后加入发烟剂、粘接剂进行搅拌均匀，按重量计，所述发烟剂的用量为20-25份，所述粘接剂的用量不超过原料总重量的0.3%；
③将步骤②所得混合物与内核通过圆盘造粒机进行造粒，并干燥至颗粒含水率为5-7%，之后进行筛分，保留直径为0.5-1.5的微粒；
三、缓释膜层的制备：
①将植物纤维干燥后粉碎至长度0.1-0.3mm备用，按重量计为10-20份；
②将粉碎好的植物纤维加入水混合搅拌成浆状，然后用1mol/L的冰醋酸调节pH值至5.0-6.0，然后加入纤维素酶和聚木糖酶，纤维素酶的用量3U/g，聚木糖酶的用量为150U/g，调整混合物的浓度为10%，将容器置于水浴锅中进行处理，温度保持在50-70℃，不断进行搅拌，处理时间2-3小时，处理完成后，用200目的筛网过滤点未溶解在植物纤维，制得纤维素溶液；
③将步骤②中所得纤维素溶液通过顶喷方式喷洒到步骤二.③得到的微粒上，干燥后形成保护膜，之后控制微粒含水率小于等于10%，最终得到低温缓释微晶颗粒。
7.一种低温缓释微晶颗粒在传统卷烟中的应用。
8.根据权利要求7所述的一种低温缓释微晶颗粒在传统卷烟中的应用，其特征在于，将所述低温缓释微晶颗粒按照常规方法应用在卷烟滤棒的制备中，即：将颗粒均匀分散在卷烟滤棒的醋酸纤维丝束中。
9.根据权利要求7所述的一种低温缓释微晶颗粒在传统卷烟中的应用，其特征在于，将若干颗粒单独包裹在卷烟滤棒的下部靠近烟丝段的位置，制成二元滤棒；或者将若干颗粒单独包裹在卷烟滤棒中间部位，制成三元滤棒。
10.根据权利要求7所述的一种低温缓释微晶颗粒在传统卷烟中的应用，其特征在于，将颗粒粘附在卷烟滤棒的接装纸或成型纸的内表面，然后包裹成型。