CN114656189A - 双组分早强型湿拌砌筑砂浆外加剂及其制备方法 - Google Patents
双组分早强型湿拌砌筑砂浆外加剂及其制备方法 Download PDFInfo
- Publication number
- CN114656189A CN114656189A CN202210337616.2A CN202210337616A CN114656189A CN 114656189 A CN114656189 A CN 114656189A CN 202210337616 A CN202210337616 A CN 202210337616A CN 114656189 A CN114656189 A CN 114656189A
- Authority
- CN
- China
- Prior art keywords
- water
- wet
- agent
- early
- mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种双组分早强型湿拌砌筑砂浆外加剂及其制备方法，外加剂由A料和B料组成，其中A料由以下重量份数的组分组成：减水剂：2％～8％，引气剂0.5％～2％，保水剂：0.5％～5％，早强剂：1％～5％，防腐剂：0.1％‑0.5％，乳化剂：0.05％～0.2％，余量为水；B料由以下重量份数的组分组成：缓凝剂：5％～15％，防腐剂：0.1％～0.5％，余量为水。本发明通过双组分的复合使用，使得砂浆具有良好的和易性和施工性能，能够根据施工需求有效调整砂浆的开放时间，提高砂浆的保水率，增加砂浆早期抗压强度和粘结强度，同时解决砂浆外加剂存放时间偏短的问题。
Description
技术领域
本发明涉及建筑材料技术领域，更具体地说，涉及一种双组分早强型湿拌砌筑砂浆外加剂及其制备方法。
背景技术
随着国家对工程质量和文明施工要求的不断提高，施工现场拌制砂浆的缺点和局限性日益突出，人们越来越重视工程砂浆的质量，预拌砂浆凭借其技术性能优良、使用方便、文明施工程度高，越来越受到社会各界的青睐。预拌砂浆有干混砂浆和湿拌砂浆两种，干混砂浆需要进行专门建厂生产，在生产过程中需要将各原材料烘干除水，一方面能耗较高，另一方面烘干除水基干混过程中产生粉尘对空气造成污染，并且在现场使用时需要加水拌和，也易产生扬尘；而湿拌砂浆生产过程中无需进行原材料烘干节省能源，混凝土搅拌站就可以进行生产，并且生产配比专门进行设计，生产过程中专业技术人员进行质量控制，其性能有很大保障，施工现场使用时无需进行再次加工，无粉尘污染。
湿拌砂浆经生产后运输至施工现场，并在一定的可操作时间内(保塑时间)保持良好的和易性和施工性能，硬化后力学性能及耐久性满足相关要求。湿拌砂浆优良性能需要性能优异的湿拌砂浆外加剂来实现。
发明内容
本发明要解决的技术问题在于，提供一种双组分早强型湿拌砌筑砂浆外加剂及其制备方法，外加剂性能稳定、存放时间长，用于湿拌砂浆生产，湿拌砂浆适应不同的施工条件，并且能够根据施工需要有效进行砂浆开放时间调整，砂浆早期强度高。
本发明解决其技术问题所采用的技术方案是：构造一种双组分早强型湿拌砌筑砂浆外加剂，由A料和B料组成，其中A料由以下重量份数的组分组成：减水剂：2％～8％，引气剂0.5％～2％，保水剂：0.5％～5％，早强剂：1％～5％，防腐剂：0.1％-0.5％，乳化剂：0.05％～0.2％，余量为水；B料由以下重量份数的组分组成：缓凝剂：5％～15％，防腐剂：0.1％～0.5％，余量为水。
按上述方案，所述减水剂为聚羧酸高性能减水剂。
按上述方案，所述引气剂为十二烷基苯磺酸钠、脂肪醇聚氧乙烯醚硫酸钠、α-烯基磺酸钠中的一种或多种。
按上述方案，所述保水剂为麦芽糊精或羟丙基甲基纤维素醚中的一种或两种。
按上述方案，所述早强剂为二乙醇胺、三乙醇胺、二乙醇单异丙醇胺、羟乙基二异丙醇胺中的一种或多种。
按上述方案，所述乳化剂为吐温80、辛苯昔醇中的一种或两种。
按上述方案，所述缓凝剂为白糖、柠檬酸、葡萄糖酸钠中的一种或多种。
按上述方案，所述防腐剂为亚硝酸钠。
按上述方案，采用复掺的方式将所述湿拌砌筑砂浆外加剂加入湿拌砂浆中，所述A料用量为砂浆中胶凝材料重量的1.5％-4％，所述B料用量为砂浆中胶凝材料重量的0.5％-3％
本发明还提供了一种所述双组分早强型湿拌砌筑砂浆外加剂的制备方法，A料的制作方法包括如下步骤：按照A料的配方，称取75％的水，升温至60-65℃，加入减水剂和早强剂搅拌3-5分钟，然后再加入保水剂搅拌至完全溶解，边搅拌边加入剩余的水，降温至常温，接着分别先后加入引气剂和防腐剂继续搅拌10-15分钟，最后加入乳化剂搅拌15-20分钟，使得溶液分散均匀；
B料的制作方法包括如下步骤：按照B料的配方，将水和缓凝剂先后加入，搅拌至缓凝剂完全溶解后再加入防腐剂继续搅拌5-8分钟。
实施本发明的双组分早强型湿拌砌筑砂浆外加剂及其制备方法，具有以下有益效果：
1、本发明的双组分早强型湿拌砌筑砂浆外加剂，A料作为调塑、保水、早强组分，B料作为缓凝组分，调整B料的用量即可得到不同开放时间的湿拌砂浆。
2、采用聚羧酸高性能减水剂，可以降低用水量，提升砂浆强度；采用十二烷基苯磺酸钠、脂肪醇聚氧乙烯醚硫酸钠或α-烯基磺酸钠作为引气剂，引气效率高、稳泡性能好，可以增加砂浆柔性，利于施工；采用麦芽糊精或羟丙基甲基纤维素醚作为保水剂，使得湿拌砂浆具有良好的保水性能；采用吐温80或辛苯昔醇作为乳化剂，可以使得溶液不分层、保存时间大大延长。
使用减水剂可以降低用水量，提升砂浆强度。采用聚羧酸高性能减水剂，在保证砂浆稠度符合要求的条件下降低砂浆用水量，使得水胶比降低从而提升砂浆强度。
引气剂在水泥-水-空气体系中，能够很快吸附在各相界面上，显著降低了体系的自由能，使得砂浆在搅拌过程中，能够引入大量微小的气泡，这些微小气泡被砂浆包裹并能稳定的存在于砂浆拌合物中。采用十二烷基苯磺酸钠、脂肪醇聚氧乙烯醚硫酸钠或α-烯基磺酸钠作为引气剂，引气效率高、稳泡性能好，可以增加砂浆柔性，利于施工，适量的引气剂与聚羧酸系减水剂复合使用，也可以增强聚羧酸系减水剂的减水效果。
麦芽糊精及纤维素醚分子结构中的羟基与水分子缔合成氢键，使游离水变成结合水，导致浆体中自由水变少，阻碍水分蒸发，使得湿拌砂浆具有良好的保水性能。
乳化剂一方面作为一种助溶剂，促进各成分的溶解；另一方面作为一种分子结构中既具有亲油性部分又有亲水性部分的表面活性剂，能够将自己与粒子表面结合，使难溶解于液体的无机、有机的固体及液体颗粒得到均匀分散，阻碍颗粒的沉降和团聚。砂浆外加剂放置时间过长时，A料中各成分易发生团聚、产生分层，对砂浆外加剂性能带来不利影响。采用吐温80或辛苯昔醇作为乳化剂，可以使得溶液不分层、保存时间大大延长。
3、本发明的双组分早强型湿拌砌筑砂浆外加剂，具有良好的储存稳定性，使用方便，性能优异。
具体实施方式
为了对本发明的技术特征、目的和效果有更加清楚的理解，现详细说明本发明的具体实施方式。
实施例一
1.配方(重量百分数)
A料：
B料：
白糖 10％
亚硝酸钠 0.2％
水 89.8
2.制备
A料制备：按照上述配方，将配方中75％的水加入三口烧瓶中，升温至60-65℃，加入聚羧酸减水剂和羟乙基二异丙醇胺搅拌5分钟，然后再加入麦芽糊精搅拌至完全溶解，边搅拌边加入剩余的水，降温至常温，接着分别先后加入α-烯基磺酸钠和亚硝酸钠继续搅拌10分钟，最后加入吐温80搅拌15分钟，使得溶液分散均匀，即得到A料；
B料制备：按照上述配方，将水加入烧瓶中，再加入白糖，搅拌至白糖完全溶解后再加入亚硝酸钠继续搅拌5分钟，即得到B料。
实施例二
1.配方(重量百分数)
A料：
B料：
2.制备
A料制备：按照上述配方，将配方中80％的水加入三口烧瓶中，升温至60-65℃，加入聚羧酸减水剂和三乙醇胺搅拌5分钟，然后再加入羟丙基甲基纤维素醚搅拌至完全溶解，边搅拌边加入剩余的水，降温至常温，接着分别先后加入α-烯基磺酸钠和亚硝酸钠继续搅拌10分钟，最后加入辛苯昔醇搅拌15分钟，使得溶液分散均匀，即得到A料；
B料制备：按照上述配方，将水加入烧瓶中，再加入白糖和葡萄糖酸钠，搅拌至白糖和葡萄糖酸钠完全溶解后再加入亚硝酸钠继续搅拌5分钟，即得到B料。
实施例三
1.配方(重量百分数)
A料：
B料：
白糖 10％
亚硝酸钠 0.2％
水 89.8
2.制备
制备方法与实施例2相同。
性能测试：
将实施例1-3中的A料和B料复合加入到湿拌砂浆的生产中，其中A料用于改善砂浆的和易性和施工性能、提升砂浆保水性，B料用于调节砂浆的开放时间，配制如下湿拌砂浆，同时测试湿拌砂浆的各项性能，湿拌砂浆的配方和性能检测结果见表1和表2。
表1性能检测结果
由表1可知，本发明A料的加入可以显著降低湿拌砂浆的用水量、提升湿拌砂浆的保水率、改善湿拌砂浆的施工性能，B料的加入可以显著降低湿拌砂浆的稠度损失，通过调整B料的用量可以有效调整湿拌砂浆的开放时间。
表2存放时间测试结果
| 存放时间 | 实施例1A料 | 实施例2A料 | 实施例3A料 |
| 1个月 | 未分层 | 未分层 | 未分层 |
| 2个月 | 未分层 | 未分层 | 未分层 |
| 3个月 | 未分层 | 未分层 | 未分层 |
由表2可知，本发明A料存放时间长、储存稳定性好。
上面对本发明的实施例进行了描述，但是本发明并不局限于上述的具体实施方式，上述的具体实施方式仅仅是示意性的，而不是限制性的，本领域的普通技术人员在本发明的启示下，在不脱离本发明宗旨和权利要求所保护的范围情况下，还可做出很多形式，这些均属于本发明的保护之内。
Claims (10)
1.一种双组分早强型湿拌砌筑砂浆外加剂，其特征在于，由A料和B料组成，其中A料由以下重量份数的组分组成：减水剂：2％～8％，引气剂0.5％～2％，保水剂：0.5％～5％，早强剂：1％～5％，防腐剂：0.1％-0.5％，乳化剂：0.05％～0.2％，余量为水；B料由以下重量份数的组分组成：缓凝剂：5％～15％，防腐剂：0.1％～0.5％，余量为水。
2.根据权利要求1所述的双组分早强型湿拌砌筑砂浆外加剂，其特征在于，所述减水剂为聚羧酸高性能减水剂。
3.根据权利要求1所述的双组分早强型湿拌砌筑砂浆外加剂，其特征在于，所述引气剂为十二烷基苯磺酸钠、脂肪醇聚氧乙烯醚硫酸钠、α-烯基磺酸钠中的一种或多种。
4.根据权利要求1所述的双组分早强型湿拌砌筑砂浆外加剂，其特征在于，所述保水剂为麦芽糊精或羟丙基甲基纤维素醚中的一种或两种。
5.根据权利要求1所述的双组分早强型湿拌砌筑砂浆外加剂，其特征在于，所述早强剂为二乙醇胺、三乙醇胺、二乙醇单异丙醇胺、羟乙基二异丙醇胺中的一种或多种。
6.根据权利要求1所述的双组分早强型湿拌砌筑砂浆外加剂，其特征在于，所述乳化剂为吐温80、辛苯昔醇中的一种或两种。
7.根据权利要求1所述的双组分早强型湿拌砌筑砂浆外加剂，其特征在于，所述缓凝剂为白糖、柠檬酸、葡萄糖酸钠中的一种或多种。
8.根据权利要求1所述的双组分早强型湿拌砌筑砂浆外加剂，其特征在于，所述防腐剂为亚硝酸钠。
9.根据权利要求1所述的双组分早强型湿拌砌筑砂浆外加剂，其特征在于，采用复掺的方式将所述湿拌砌筑砂浆外加剂加入湿拌砂浆中，所述A料用量为砂浆中胶凝材料重量的1.5％-4％，所述B料用量为砂浆中胶凝材料重量的0.5％-3％。
10.一种权利要求1所述双组分早强型湿拌砌筑砂浆外加剂的制备方法，其特征在于，A料的制作方法包括如下步骤：按照A料的配方，称取75％的水，升温至60-65℃，加入减水剂和早强剂搅拌3-5分钟，然后再加入保水剂搅拌至完全溶解，边搅拌边加入剩余的水，降温至常温，接着分别先后加入引气剂和防腐剂继续搅拌10-15分钟，最后加入乳化剂搅拌15-20分钟，使得溶液分散均匀；
B料的制作方法包括如下步骤：按照B料的配方，将水和缓凝剂先后加入，搅拌至缓凝剂完全溶解后再加入防腐剂继续搅拌5-8分钟。