CN114566307A - 一种防水中交电缆 - Google Patents
一种防水中交电缆 Download PDFInfo
- Publication number
- CN114566307A CN114566307A CN202210200853.4A CN202210200853A CN114566307A CN 114566307 A CN114566307 A CN 114566307A CN 202210200853 A CN202210200853 A CN 202210200853A CN 114566307 A CN114566307 A CN 114566307A
- Authority
- CN
- China
- Prior art keywords
- parts
- cable
- waterproof
- insulating layer
- pvc insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种防水中交电缆,设置有电缆芯体和包裹于电缆芯体外表面的防止铜锈PVC绝缘层。防铜锈PVC绝缘层含有聚合度为1000~1300的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡和防铜锈相容剂。所述防铜锈PVC绝缘层还设置有防水层和外护套层,所述防水层包覆于所述电缆芯体的外表面,所述外护套层包覆于所述防水层的外表面。本发明防水中交电缆的防铜锈PVC绝缘层含通过防铜锈相容剂,能防止电缆芯体的导体表面氧化,从而不会出现发黑现象,解决了电缆产品安全使用寿命长,降低了成本。
Description
技术领域
本发明涉及电缆技术领域,特别涉及一种防水中交电缆。
背景技术
电缆是由通常是由几根或几组导线(每组至少两根)绞合而成的类似绳索的电缆,每组导线之间相互绝缘,并常围绕着一根中心扭成,整个外面包有高度绝缘的覆盖层。电缆具有内通电,外绝缘的特征,电缆有电力电缆、控制电缆、补偿电缆、屏蔽电缆、高温电缆、计算机电缆、信号电缆、同轴电缆、耐火电缆、船用电缆、矿用电缆、铝合金电缆等等,它们都是由单股或多股导线和绝缘层组成,用来连接电路、电器等。目前在家用安装及周围潮湿环境中使用的电缆,铜制线缆导体容易出现发黑氧化现象,导体出现发黑氧化就会影响电缆产品安全使用寿命。
因此,针对现有技术不足,提供一种防铜锈PVC绝缘层及制备方法以解决现有技术不足甚为必要。
发明内容
本发明的目的在于避免现有技术的不足之处而提供一种防水中交电缆。该防水中交电缆的导体不氧化发黑,延长使用寿命。
本发明的上述目的通过以下技术措施实现:
提供一种防水中交电缆,设置有电缆芯体和包裹于电缆芯体外表面的防止铜锈PVC绝缘层。
所述防铜锈PVC绝缘层含有聚合度为1000~1300的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡和防铜锈相容剂。
优选的,上述防铜锈PVC绝缘层还设置有防水层和外护套层,所述防水层包覆于所述电缆芯体的外表面,所述外护套层包覆于所述防水层的外表面。
优选的,上述电缆芯体按照从中心到外部的顺序,依次设置有导体、绝缘屏蔽层和金属屏蔽层。
优选的,上述防止铜锈PVC绝缘层包覆于所述导体的外表面,所述防止铜锈PVC绝缘层包覆于所述绝缘屏蔽层的外表面,所述金属屏蔽层包覆于所述绝缘屏蔽层的外表面。
优选的,上述防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂。
优选的,上述防铜锈PVC绝缘层还含有改性陶土、纳米碳酸钙、抗氧化剂和色浆。
优选的,上述防铜锈PVC绝缘层以重量份计,
聚氯乙烯:30份~60份;
邻苯二甲酸二异壬酯:10份~30份;
环氧大豆油:1份~2份;
聚乙烯蜡:0.05份~0.5份;
改性陶土:1份~8份;
纳米碳酸钙:10份~30份;
防铜锈相容剂:1份~6份;
抗氧化剂:0.1份~1份;
色浆:0.5份~3份。
进一步优选的,上述防铜锈PVC绝缘层以重量份计,
聚氯乙烯:45份~50份;
邻苯二甲酸二异壬酯:19份~25份;
环氧大豆油:2份~3份;
聚乙烯蜡:0.1份~0.2份;
改性陶土:2份~6份;
纳米碳酸钙:19份~25份;
防铜锈相容剂:2份~4份;
抗氧化剂:0.2份~0.5份;
色浆:1份~2份。
以重量份计,所述防铜锈相容剂包含有20份~40份富勒烯、 10份~15份硫代二丙二月桂酯、20份~40份的2-苯基咪唑啉和 3份~10份硅烷偶联剂。
以重量份计,所述防铜锈相容剂包含有26份富勒烯、13.6 份硫代二丙二月桂酯、36份的2-苯基咪唑啉和6份硅烷偶联剂。
优选的,上述防铜锈PVC绝缘层抗氧化剂为四[3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯。
优选的,上述防铜锈PVC绝缘层防铜锈PVC绝缘层的制备步骤包括有:
步骤一、将聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆置于高速捏合机中加热并捏合搅拌,得到混合料;
步骤二、将混合料置于造粒机中进行挤出造粒,并进行切割、冷却,得到防铜锈PVC绝缘层。
本发明的防水中交电缆,设置有电缆芯体和包裹于电缆芯体外表面的防止铜锈PVC绝缘层。防铜锈PVC绝缘层含有聚合度为 1000~1300的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡和防铜锈相容剂。本发明防水中交电缆的防铜锈PVC绝缘层含通过防铜锈相容剂,能防止电缆芯体的导体表面氧化,从而不会出现发黑现象,解决了电缆产品安全使用寿命长,降低了成本。
具体实施方式
结合以下实施例对本发明的技术方案作进一步说明。
实施例1。
一种防水中交电缆,设置有电缆芯体和包裹于电缆芯体外表面的防止铜锈PVC绝缘层。
防铜锈PVC绝缘层含有聚合度为1000~1300的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆。
防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂。
本发明防铜锈相容剂的作用是防止铜导体氧化,在防铜锈相容剂中富勒烯和硫代二丙二月桂酯通过协同配合,产生抗氧化作用。而且硫代二丙二月桂酯和2-苯基咪唑啉中均含能与铜等原子配位络合的活性位,与金属表面形成强的作用力,硫代二丙二月桂酯和2-苯基咪唑啉能牢牢地地吸附在铜导体的表面,并同时本发明的硅烷偶联剂发生水解还能铜导体形成Si-O-Cu,而且2-苯基咪唑啉的苯基的形成π-π堆积作用,从而提高了Si-O-Cu的稳定度,形成比较致密的保护膜,因此在硫代二丙二月桂酯、2-苯基咪唑啉铜和硅烷偶联剂均能在导体的表面形成单分子吸附膜,该吸附膜能有效阻隔氧气金属表面进行氧化。本发明的富勒烯具体为 C60富勒烯。
本发明的苯二甲酸二壬酯、环氧大豆油作为增塑剂在增加聚氯乙烯的抗折、抗冲击等机械性能。而聚乙烯蜡能作为润滑剂增加与聚氯乙烯的相容性,同时本发明的富勒烯同时也起到润滑作用。纳米碳酸钙与环氧大豆油相作用增加本发明的稳定性。改性陶土具有补强作用,可提高绝缘料的定伸应力、硬度、强度和耐磨性。
以重量份计,
聚氯乙烯:30份~60份;
邻苯二甲酸二异壬酯:10份~30份;
环氧大豆油:1份~2份;
聚乙烯蜡:0.05份~0.5份;
改性陶土:1份~8份;
纳米碳酸钙:10份~30份;
防铜锈相容剂:1份~6份;
抗氧化剂:0.1份~1份;
色浆:0.5份~3份。
其中防铜锈相容剂包含有20份~40份富勒烯、10份~15份硫代二丙二月桂酯、20份~40份的2-苯基咪唑啉和3份~10份硅烷偶联剂。
抗氧化剂为四[3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯。
该防水中交电缆的防铜锈PVC绝缘层能防止电缆导体表面氧化,从而不会出现发黑现象,解决了电缆产品安全使用寿命长,降低了成本。
实施例2。
一种防铜锈PVC绝缘层,包括有:含有聚合度为1000~1300 的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆。
防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂
以重量份计,
聚氯乙烯:45份~50份;
邻苯二甲酸二异壬酯:19份~25份;
环氧大豆油:2份~3份;
聚乙烯蜡:0.1份~0.2份;
改性陶土:2份~6份;
纳米碳酸钙:19份~25份;
防铜锈相容剂:2份~4份;
抗氧化剂:0.2份~0.5份;
色浆:1份~2份。
防铜锈相容剂包含有25份~3份富勒烯、12份~14份硫代二丙二月桂酯、28份~32份的2-苯基咪唑啉、4份~7份硅烷偶联剂;抗氧化剂为四[3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯,其中四[3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯的cas号为 6683-19-8。
与实施例1相比,采用本实施例的防铜锈PVC绝缘层的铜导体的抑制发黑、氧化较实施例1的佳。
实施例3。
一种防铜锈PVC绝缘层,包括有:含有聚合度为1000~1300 的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆。
防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂
以重量份计,
聚氯乙烯:48.6份;
邻苯二甲酸二异壬酯:23.7份;
环氧大豆油:2.5份;
聚乙烯蜡:0.18份;
改性陶土:4份;
纳米碳酸钙:23份;
防铜锈相容剂:3.5份;
抗氧化剂:0.4份;
色浆:1.6份。
防铜锈相容剂包含有26份富勒烯、13.6份硫代二丙二月桂酯、36份的2-苯基咪唑啉和6份硅烷偶联剂;抗氧化剂为四 [3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯。
其中聚氯乙烯和环氧大豆油购自上海凯茵化工有限公司。邻苯二甲酸二异壬酯购自聊城市瑞邦塑料助剂有限公司。聚乙烯蜡购自扬州罗兰新材料有限公司。纳米碳酸钙购自中山市德远贸易有限公司。富勒烯购自湖北兴恒康化工科技有限公开。硫代二丙二月桂酯购自江苏裕坤生物科技术有限公司。2-苯基咪唑啉和四 [3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯均购自上海阿拉丁生化科技股份有限公司。硅烷偶联剂购自山东环正化工有限公司。
与实施例1相比,采用本实施例的防水中交电缆的铜导体的抑制发黑、氧化较实施例1的佳。
实施例4。
一种防铜锈PVC绝缘层,包括有:含有聚合度为1000~1300 的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆。
防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂
以重量份计,
聚氯乙烯:30份;
邻苯二甲酸二异壬酯:10份;
环氧大豆油:1份;
聚乙烯蜡:0.05份;
改性陶土:1份;
纳米碳酸钙:10份;
防铜锈相容剂:1份;
抗氧化剂:0.1份;
色浆:0.5份。
防铜锈相容剂包含有40份富勒烯、15份硫代二丙二月桂酯、 40份的2-苯基咪唑啉;抗氧化剂为四[3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯。
其中聚氯乙烯和环氧大豆油购自上海凯茵化工有限公司。邻苯二甲酸二异壬酯购自聊城市瑞邦塑料助剂有限公司。聚乙烯蜡购自扬州罗兰新材料有限公司。纳米碳酸钙购自中山市德远贸易有限公司。富勒烯购自湖北兴恒康化工科技有限公开。硫代二丙二月桂酯购自江苏裕坤生物科技术有限公司。2-苯基咪唑啉和四 [3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯均购自上海阿拉丁生化科技股份有限公司。硅烷偶联剂购自山东环正化工有限公司。
与实施例1相比,采用本实施例的防水中交电缆的铜导体的抑制发黑、氧化较实施例1的佳。
实施例5。
一种防铜锈PVC绝缘层,包括有:含有聚合度为1000~1300 的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆。
防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂
以重量份计,
聚氯乙烯:60份;
邻苯二甲酸二异壬酯:30份;
环氧大豆油:2份;
聚乙烯蜡:0.5份;
改性陶土:8份;
纳米碳酸钙:30份;
防铜锈相容剂:6份;
抗氧化剂:1份;
色浆:3份。
防铜锈相容剂包含有20份富勒烯、10份硫代二丙二月桂酯、 20份的2-苯基咪唑啉和3份硅烷偶联剂;抗氧化剂为四[3-3,5- 二叔丁基-4-羟苯基丙酸]季戊四醇酯。
其中聚氯乙烯和环氧大豆油购自上海凯茵化工有限公司。邻苯二甲酸二异壬酯购自聊城市瑞邦塑料助剂有限公司。聚乙烯蜡购自扬州罗兰新材料有限公司。纳米碳酸钙购自中山市德远贸易有限公司。富勒烯购自湖北兴恒康化工科技有限公开。硫代二丙二月桂酯购自江苏裕坤生物科技术有限公司。2-苯基咪唑啉和四 [3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯均购自上海阿拉丁生化科技股份有限公司。硅烷偶联剂购自山东环正化工有限公司。
与实施例1相比,采用本实施例的防水中交电缆的铜导体的抑制发黑、氧化较实施例1的佳。
实施例6。
一种防铜锈PVC绝缘层,包括有:含有聚合度为1300的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆。
防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂
以重量份计,
聚氯乙烯:45份;
邻苯二甲酸二异壬酯:19份;
环氧大豆油:2份;
聚乙烯蜡:0.1份;
改性陶土:2份;
纳米碳酸钙:19份;
防铜锈相容剂:2份;
抗氧化剂:0.2份;
色浆:1份。
防铜锈相容剂包含有25份富勒烯、17份硫代二丙二月桂酯和 26份的2-苯基咪唑啉;抗氧化剂为四[3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯。
其中聚氯乙烯和环氧大豆油购自上海凯茵化工有限公司。邻苯二甲酸二异壬酯购自聊城市瑞邦塑料助剂有限公司。聚乙烯蜡购自扬州罗兰新材料有限公司。纳米碳酸钙购自中山市德远贸易有限公司。富勒烯购自湖北兴恒康化工科技有限公开。硫代二丙二月桂酯购自江苏裕坤生物科技术有限公司。2-苯基咪唑啉和四 [3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯均购自上海阿拉丁生化科技股份有限公司。硅烷偶联剂购自山东环正化工有限公司。
与实施例1相比,采用本实施例的防水中交电缆的铜导体的抑制发黑、氧化较实施例1的佳。
实施例7。
一种防铜锈PVC绝缘层,包括有:含有聚合度为1000的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆。
防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂
以重量份计,
聚氯乙烯:50份;
邻苯二甲酸二异壬酯:25份;
环氧大豆油:3份;
聚乙烯蜡:0.2份;
改性陶土:6份;
纳米碳酸钙:25份;
防铜锈相容剂:4份;
抗氧化剂:0.5份;
色浆:2份。
防铜锈相容剂包含有23份富勒烯、11份硫代二丙二月桂酯、36份的2-苯基咪唑啉和10份硅烷偶联剂;抗氧化剂为四[3-3,5- 二叔丁基-4-羟苯基丙酸]季戊四醇酯。
其中聚氯乙烯和环氧大豆油购自上海凯茵化工有限公司。邻苯二甲酸二异壬酯购自聊城市瑞邦塑料助剂有限公司。聚乙烯蜡购自扬州罗兰新材料有限公司。纳米碳酸钙购自中山市德远贸易有限公司。富勒烯购自湖北兴恒康化工科技有限公开。硫代二丙二月桂酯购自江苏裕坤生物科技术有限公司。2-苯基咪唑啉和四 [3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯均购自上海阿拉丁生化科技股份有限公司。硅烷偶联剂购自山东环正化工有限公司。
与实施例1相比,采用本实施例的防水中交电缆的铜导体的抑制发黑、氧化较实施例1的佳。
实施例8。
一种防铜锈PVC绝缘层,包括有:含有聚合度为1230的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆。
防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂
以重量份计,
聚氯乙烯:47份;
邻苯二甲酸二异壬酯:21份;
环氧大豆油:2.3份;
聚乙烯蜡:0.15份;
改性陶土:3.5份;
纳米碳酸钙:23份;
防铜锈相容剂:2.6份;
抗氧化剂:0.41份;
色浆:1.7份。
防铜锈相容剂包含有23份富勒烯、11份硫代二丙二月桂酯、 36份的2-苯基咪唑啉和8份硅烷偶联剂;抗氧化剂为四[3-3,5- 二叔丁基-4-羟苯基丙酸]季戊四醇酯。
其中聚氯乙烯和环氧大豆油购自上海凯茵化工有限公司。邻苯二甲酸二异壬酯购自聊城市瑞邦塑料助剂有限公司。聚乙烯蜡购自扬州罗兰新材料有限公司。纳米碳酸钙购自中山市德远贸易有限公司。富勒烯购自湖北兴恒康化工科技有限公开。硫代二丙二月桂酯购自江苏裕坤生物科技术有限公司。2-苯基咪唑啉和四[3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯均购自上海阿拉丁生化科技股份有限公司。硅烷偶联剂购自山东环正化工有限公司。
与实施例1相比,采用本实施例的防水中交电缆的铜导体的抑制发黑、氧化较实施例1的佳。
实施例9。
一种防铜锈PVC绝缘层的制备方法,采用如实施例3至8任意防铜锈PVC绝缘层的原料配比,步骤包括有:步骤一、将聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆置于高速捏合机中加热至90℃~110℃,捏合搅拌8min~15min,得到混合料;
步骤二、将混合料置于造粒机中进行控制温度为140℃~170℃后挤出造粒,并进行切割、冷却,得到防铜锈PVC绝缘层。
通过该防铜锈PVC绝缘层的制备方法制备得到的防铜锈PVC 绝缘层,然后通过该防铜锈PVC绝缘层制备得到电缆导体不会出现发黑现象,解决了电缆产品安全使用寿命长,降低了成本。
实施例10。
一种防铜锈PVC绝缘层的制备方法,采用如实施例3至8任意防铜锈PVC绝缘层的原料配比,步骤包括有:步骤一、将聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆置于高速捏合机中加热至90℃,捏合搅拌8min,得到混合料;
步骤二、将混合料置于造粒机中进行控制温度为140℃后挤出造粒,并进行切割、冷却,得到防铜锈PVC绝缘层。
通过该防铜锈PVC绝缘层的制备方法制备得到的防铜锈PVC 绝缘层,然后通过该防铜锈PVC绝缘层制备得到电缆导体不会出现发黑现象,解决了电缆产品安全使用寿命长,降低了成本。
实施例11。
一种防铜锈PVC绝缘层的制备方法,采用如实施例3至8任意防铜锈PVC绝缘层的原料配比,步骤包括有:步骤一、将聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆置于高速捏合机中加热至110℃,捏合搅拌15min,得到混合料;
步骤二、将混合料置于造粒机中进行控制温度为170℃后挤出造粒,并进行切割、冷却,得到防铜锈PVC绝缘层。
通过该防铜锈PVC绝缘层的制备方法制备得到的防铜锈PVC 绝缘层,然后通过该防铜锈PVC绝缘层制备得到电缆导体不会出现发黑现象,解决了电缆产品安全使用寿命长,降低了成本。
实施例12。
一种防铜锈PVC绝缘层的制备方法,采用如实施例3至8任意防铜锈PVC绝缘层的原料配比,步骤包括有:步骤一、将聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆置于高速捏合机中加热至100℃,捏合搅拌12min,得到混合料;
步骤二、将混合料置于造粒机中进行控制温度为165℃后挤出造粒,并进行切割、冷却,得到防铜锈PVC绝缘层。
通过该防铜锈PVC绝缘层的制备方法制备得到的防铜锈PVC 绝缘层,然后通过该防铜锈PVC绝缘层制备得到电缆导体不会出现发黑现象,解决了电缆产品安全使用寿命长,降低了成本。
实施例13。
一种防水中交电缆,通过实施例3至8任意一种防铜锈PVC 绝缘层作为绝缘层,绝缘层包裹于导体的外表面。
需要说明的是,本发明的防水中交电缆也称为防水中压交联电缆,
本发明通过实施例3-8、实施例10-12得到防铜锈PVC绝缘层,的样品1-10表1,本发明同时分别将样品1-10制备成防水中交电缆。
表1、防铜锈PVC绝缘层
试验组 | 原料配比 | 制备方法 |
样品1 | 实施例3 | 实施例10 |
样品2 | 实施例4 | 实施例11 |
样品3 | 实施例5 | 实施例12 |
样品4 | 实施例6 | 实施例10 |
样品5 | 实施例7 | 实施例11 |
样品6 | 实施例3 | 实施例11 |
样品7 | 实施例4 | 实施例10 |
样品8 | 实施例5 | 实施例10 |
样品9 | 实施例6 | 实施例11 |
样品10 | 实施例3 | 实施例12 |
对比例1。
一种PVC绝缘料的制备方法,
步骤包括有:步骤一、将48.6份聚氯乙烯、23.7份邻苯二甲酸二异壬酯、2.5份环氧大豆油、0.18份聚乙烯蜡、3.5份稳定剂、 4份改性性陶土、23份纳米碳酸钙、0.4份抗氧化剂和1.6份色浆置于高速捏合机中加热至100℃,捏合搅拌12min,得到混合料,其中,稳定剂为硬脂酸锌;
步骤二、将混合料置于造粒机中进行控制温度为165℃后挤出造粒,并进行切割、冷却,得到PVC绝缘层。
对比例2。
一种PVC绝缘料的制备方法,
步骤包括有:步骤一、将48.6份聚氯乙烯、23.7份邻苯二甲酸二异壬酯、2.5份环氧大豆油、0.18份聚乙烯蜡、3.5份复合稳定剂、4份改性性陶土、23份纳米碳酸钙、0.4份抗氧化剂和1.6 份色浆置于高速捏合机中加热至100℃,捏合搅拌12min,得到混合料,其中,复合稳定剂为硬脂酸锌、硬脂酸镁和滑石粉混合物,且在复合稳定剂中的重量分为35份硬脂酸锌、45份硬脂酸镁和 20份滑石粉;
步骤二、将混合料置于造粒机中进行控制温度为165℃后挤出造粒,并进行切割、冷却,得到PVC绝缘层。
在其他实验条件相同的情况下,表2为将样品1-10防铜锈PVC 绝缘层、对比例1、2的P VC绝缘料进行性能测试,同时将样品 1-10、对比例1和对比例2制备成防水中交电缆进行测试破坏实验并把电线泡水后放老化箱7天进行老化测度,相关性能如表2:
表2、各项性能表
通过表2可知,本发明得到的防铜锈PVC绝缘层保证拉伸性能、电阻性能、低温及热稳定性。与对比例1和2相比,本发明采用防铜相容剂代替普通稳定剂,在老化测试结果明显优于对比例,样品1-10得到的防水中交电缆均没有不发黑不氧化现象。
最后应当说明的是,以上实施例仅用以说明本发明的技术方案而非对本发明保护范围的限制,尽管参照较佳实施例对本发明作了详细说明,本领域的普通技术人员应当理解,可以对本发明技术方案进行修改或者等同替换,而不脱离本发明技术方案的实质和范围。
Claims (10)
1.一种防水中交电缆,其特征在于:设置有电缆芯体和包裹于电缆芯体外表面的防止铜锈PVC绝缘层;
所述防铜锈PVC绝缘层含有聚合度为1000~1300的聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡和防铜锈相容剂。
2.根据权利要求1所述的防水中交电缆,其特征在于:所述防铜锈PVC绝缘层还设置有防水层和外护套层,所述防水层包覆于所述电缆芯体的外表面,所述外护套层包覆于所述防水层的外表面。
3.根据权利要求2所述的防水中交电缆,其特征在于:所述电缆芯体按照从中心到外部的顺序,依次设置有导体、绝缘屏蔽层和金属屏蔽层;
所述防止铜锈PVC绝缘层包覆于所述导体的外表面,所述防止铜锈PVC绝缘层包覆于所述绝缘屏蔽层的外表面,所述金属屏蔽层包覆于所述绝缘屏蔽层的外表面。
4.根据权利要求3所述的防水中交电缆,其特征在于:所述防铜锈相容剂包含有富勒烯、硫代二丙二月桂酯、2-苯基咪唑啉和硅烷偶联剂。
5.根据权利要求4所述的防水中交电缆,其特征在于:所述防铜锈PVC绝缘层还含有改性陶土、纳米碳酸钙、抗氧化剂和色浆。
6.根据权利要求5所述的防水中交电缆,其特征在于:所述防铜锈PVC绝缘层以重量份计,
聚氯乙烯:30份~60份;
邻苯二甲酸二异壬酯:10份~30份;
环氧大豆油:1份~2份;
聚乙烯蜡:0.05份~0.5份;
改性陶土:1份~8份;
纳米碳酸钙:10份~30份;
防铜锈相容剂:1份~6份;
抗氧化剂:0.1份~1份;
色浆:0.5份~3份。
7.根据权利要求4所述的防水中交电缆,其特征在于:所述防铜锈PVC绝缘层以重量份计,
聚氯乙烯:45份~50份;
邻苯二甲酸二异壬酯:19份~25份;
环氧大豆油:2份~3份;
聚乙烯蜡:0.1份~0.2份;
改性陶土:2份~6份;
纳米碳酸钙:19份~25份;
防铜锈相容剂:2份~4份;
抗氧化剂:0.2份~0.5份;
色浆:1份~2份。
8.根据权利要求7所述的防水中交电缆,其特征在于:以重量份计,所述防铜锈相容剂包含有20份~40份富勒烯、10份~15份硫代二丙二月桂酯、20份~40份的2-苯基咪唑啉和3份~10份硅烷偶联剂。
9.根据权利要求8所述的防水中交电缆,其特征在于:以重量份计,所述防铜锈相容剂包含有26份富勒烯、13.6份硫代二丙二月桂酯、36份的2-苯基咪唑啉和6份硅烷偶联剂;
所述抗氧化剂为四[3-3,5-二叔丁基-4-羟苯基丙酸]季戊四醇酯。
10.根据权利要求8所述的防水中交电缆,其特征在于:所述防铜锈PVC绝缘层的制备步骤包括有:
步骤一、将聚氯乙烯、邻苯二甲酸二异壬酯、环氧大豆油、聚乙烯蜡、防铜锈相容剂、改性陶土、纳米碳酸钙、抗氧化剂和色浆置于高速捏合机中加热并捏合搅拌,得到混合料;
步骤二、将混合料置于造粒机中进行挤出造粒,并进行切割、冷却,得到防铜锈PVC绝缘层。