CN114561184A - 一种全固含光固化绝缘胶及其制备工艺 - Google Patents
一种全固含光固化绝缘胶及其制备工艺 Download PDFInfo
- Publication number
- CN114561184A CN114561184A CN202210167486.2A CN202210167486A CN114561184A CN 114561184 A CN114561184 A CN 114561184A CN 202210167486 A CN202210167486 A CN 202210167486A CN 114561184 A CN114561184 A CN 114561184A
- Authority
- CN
- China
- Prior art keywords
- acrylate
- solid
- parts
- agent
- insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种全固含光固化绝缘胶及其制备工艺,涉及电子材料技术领域,为解决固化过程中使用多种溶剂并进行烘烤,溶剂挥发造成环境污染,且绝缘胶热形变性能不佳的问题。其原料包括光固化树脂、活性单体、光引发剂、附着力促进剂、绝缘填料、颜料和助剂,其中光固化树脂20‑40份,活性单体5‑40份,光引发剂0.5‑5份,附着力促进剂0.5‑5份,绝缘填料10‑40份,颜料0.5‑5份,助剂1‑10份,所述助剂包括流平剂、分散剂、消泡剂和防沉剂。
Description
技术领域
本发明涉及电子材料技术领域,具体为一种全固含光固化绝缘胶及其制备工艺。
背景技术
绝缘胶具有良好电绝缘性能的多组分复合胶,电子产品的轻薄化,便携化,新的场景应用对电子应用功能型高分子材料提出了更高的要求,优秀的功能体现,物理性能,环保高效是本产品的优点所在。全固含光固化绝缘材料可用计算机键盘线路,柔性线路,电器薄膜开关,RFID天线及印刷电极,属功能型新兴材料,具有环保无溶剂,高效,功能稳定等优点,终端产品可应用航空航天,军工,民用电器,等各种柔性线路上。
目前,全固含光固化绝缘胶的全固含性不佳,在使用时柔性化、高度绝缘和苛刻物性相对下降,固化过程中使用多种溶剂并进行烘烤,溶剂挥发造成环境污染,且绝缘胶热形变性能不佳,不能满足使用需求,因此市场上急需一种全固含光固化绝缘胶及其制备工艺来解决这些问题。
发明内容
本发明的目的在于提供一种全固含光固化绝缘胶及其制备工艺,以解决上述背景技术中提出的固化过程中使用多种溶剂并进行烘烤,溶剂挥发造成环境污染,且绝缘胶热形变性能不佳的问题。
为实现上述目的,本发明提供如下技术方案:一种全固含光固化绝缘胶,其原料包括光固化树脂、活性单体、光引发剂、附着力促进剂、绝缘填料、颜料和助剂,其中光固化树脂20-40份,活性单体5-40份,光引发剂0.5-5份,附着力促进剂0.5-5份,绝缘填料10-40份,颜料0.5-5份,助剂1-10份,所述助剂包括流平剂、分散剂、消泡剂和防沉剂。
优选的,所述光固化树脂为脂肪族聚氨酯二丙烯酸酯、脂肪族聚氨酯、脂肪族聚氨酯六丙烯酸酯、胺改性丙烯酸酯、双官能团丙烯酸酯、四官能团丙烯酸酯、六官能团丙烯酸酯、聚酯内烯酸酯的一种或多种复配物。
优选的,所述活性单体为丙烯酸异冰片酯、丙烯酰吗啉、四氢呋喃丙烯酸酯、乙氧基乙氧乙基丙烯酸酯、2-苯氧基乙基丙烯酸酯、环脂肪族丙烯酸酯、环脂肪族丙烯酸酯、二缩三丙二醇二丙烯酸酯、二环戊烯基氧基乙基丙烯酸酯、1,6-己二醇二丙烯酸酯、(3)乙氧化三羟甲基丙丙烯酸酯、乙氧基乙氧基乙基丙烯酸酯、丙烯酸月桂酯、(5)乙氧基化季戊四醇四丙烯酸酯、季戊四醇三丙烯酸酯、二季戊四醇六丙烯酸酯的一种或多种复配物。
优选的,所述光引发剂为2-羟基-2-甲基-1-苯基-1-丙酮、1-羟基环己基苯基甲酮、邻苯甲酰苯甲酸甲酯、二苯甲酮、安息香双甲醚、2,4,6-三甲基苯甲酰基-二苯基氧化膦、异丙基硫杂蒽酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮、2-苯基苄-2-二甲基胺-1-(4-吗啉苄苯基)丁酮、双(1-(2,4-二氟苯基)-3-吡咯基)二茂钛、2,4-二乙基硫杂蒽酮的一种或多种复配物。
优选的,所述附着力促进剂为2-羟乙基甲基丙烯酸酯磷酸酯、γ-缩水甘油醚丙基三甲氧基硅烷、甲基丙烯酰氧基丙基甲基二甲氧基硅烷、氨乙基氨丙基三甲氧基硅烷、3-氨丙基三甲氧基硅烷的一种或多种复配物。
优选的,所述绝缘填料为滑石粉、氧化镁粉、二氧化硅、聚丙烯微粉、聚酰胺微粉、聚四氟乙烯蜡粉、聚乙烯蜡粉的一种或多种复配物。
优选的,所述颜料为苯并咪挫酮黄、酞青蓝、二酮吡咯并吡咯、异吲哚啉酮、永固洋红中的一种或多种复配物。
优选的,所述流平剂为固体环氧树脂为载体的固态流平剂,所述分散剂为三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、古尔胶、脂肪酸聚乙二醇酯中的一种或多种复配物,所述消泡剂为高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷中的一种或多种复配物,所述防沉剂为聚烯烃蜡微粒。
一种全固含光固化绝缘胶的制备工艺,包括以下步骤:
步骤1:取光固化树脂、活性单体、光引发剂、附着力促进剂和助剂将其添加到真空搅拌器中,真空搅拌器以500-1000r/min搅拌30min至完全混合溶解均匀;
步骤2:在搅拌状态下将绝缘填料添加到真空搅拌器中,以500-1000r/min分散30min并控制温度50℃下;
步骤3:将颜料与助剂、光固化树脂,活性单体按需调配比率混合搅拌均匀,再使用纳米砂磨机研磨细度至5μ以下制备成低卤素色浆;
步骤4:将制备的低卤素色浆按着色要求加入助剂混合物中以500-1000r/min搅拌分散均匀;
步骤5:搅拌分散均匀后搅拌速度调至500-1000r/min在真空0.1~0.2MPa条件下搅拌30min去除物料中的空气泡沫,出料得到均匀一致的全固含、低卤素、胶粘剂分散体;
步骤6:对制备的分散体进行物性技术指标检测,所述检测包括附着力、耐水性、耐酒精、抗冲击、漆膜弯曲、铅笔硬度、耐湿性、耐寒性、耐热性、耐酸性、耐清洁剂性和耐溶剂性检测。
与现有技术相比,本发明的有益效果是:
1.该发明通过光固化树脂、活性单体和光引发剂的设置,光固化树脂和活性单体作为绝缘胶的全固含光主体,在光引发剂的作用下使得制备出的全固含光固化绝缘胶性能更加稳定。解决了制备出来的全固含光固化绝缘胶性能不佳的问题。
2.该发明通过真空搅拌分散混合法和纳米砂磨机的设置,采用真空搅拌分散混合法可以减少空气渗透,可以最大限度的将物料中的空气泡沫去除,确保制备物料的质量,纳米砂磨机可以对混合物研磨,使得后续制备的低卤素色浆颗粒分布均匀,间接的提高了绝缘胶性能。解决了研磨的颗粒细度不达标降低低卤素色浆质量的问题
3.该发明通过附着力、耐水性、耐酒精、抗冲击、漆膜弯曲、铅笔硬度、耐湿性、耐寒性、耐热性、耐酸性、耐清洁剂性和耐溶剂性检测的设置,制备后的胶粘剂分散体进行多项物性技术指标检测,根据检测结果可以获得绝缘胶指标数据,确保了绝缘胶使用效果,便于后续对绝缘胶进行改进。解决了制备后的绝缘胶料没有进行彻底的物性技术指标检测,存在缺陷的问题
具体实施方式
下面对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅仅是本发明一部分实施例,而不是全部的实施例。
实施例1:一种全固含光固化绝缘胶,其原料包括光固化树脂、活性单体、光引发剂、附着力促进剂、绝缘填料、颜料和助剂,其中光固化树脂20份,活性单体5份,光引发剂0.5份,附着力促进剂0.5份,绝缘填料10份,颜料0.5份,助剂1份,助剂包括流平剂、分散剂、消泡剂和防沉剂。
进一步,光固化树脂为脂肪族聚氨酯二丙烯酸酯、脂肪族聚氨酯、脂肪族聚氨酯六丙烯酸酯、胺改性丙烯酸酯、双官能团丙烯酸酯、四官能团丙烯酸酯、六官能团丙烯酸酯、聚酯内烯酸酯的一种或多种复配物,通过使用光固化树脂作为绝缘胶主体,光固化树脂化学粘接固位,固位力强。
进一步,活性单体为丙烯酸异冰片酯、丙烯酰吗啉、四氢呋喃丙烯酸酯、乙氧基乙氧乙基丙烯酸酯、2-苯氧基乙基丙烯酸酯、环脂肪族丙烯酸酯、环脂肪族丙烯酸酯、二缩三丙二醇二丙烯酸酯、二环戊烯基氧基乙基丙烯酸酯、1,6-己二醇二丙烯酸酯、(3)乙氧化三羟甲基丙丙烯酸酯、乙氧基乙氧基乙基丙烯酸酯、丙烯酸月桂酯、(5)乙氧基化季戊四醇四丙烯酸酯、季戊四醇三丙烯酸酯、二季戊四醇六丙烯酸酯的一种或多种复配物,活性单体可以降低粘度,调节体系的固化速度,控制到达完全固化所需要的时间,还能增加交联密度,提高了全固含光固化绝缘胶性能。
进一步,光引发剂为2-羟基-2-甲基-1-苯基-1-丙酮、1-羟基环己基苯基甲酮、邻苯甲酰苯甲酸甲酯、二苯甲酮、安息香双甲醚、2,4,6-三甲基苯甲酰基-二苯基氧化膦、异丙基硫杂蒽酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮、2-苯基苄-2-二甲基胺-1-(4-吗啉苄苯基)丁酮、双(1-(2,4-二氟苯基)-3-吡咯基)二茂钛、2,4-二乙基硫杂蒽酮的一种或多种复配物,通过光引发剂能在紫外光区或可见光区吸收一定波长的能量,产生自由基、阳离子等,从而引发单体聚合交联固化。
进一步,附着力促进剂为2-羟乙基甲基丙烯酸酯磷酸酯、γ-缩水甘油醚丙基三甲氧基硅烷、甲基丙烯酰氧基丙基甲基二甲氧基硅烷、氨乙基氨丙基三甲氧基硅烷、3-氨丙基三甲氧基硅烷的一种或多种复配物,通过附着力促进剂增进绝缘胶与基材之间的附着力,提高了绝缘胶的使用效果。
进一步,绝缘填料为滑石粉、氧化镁粉、二氧化硅、聚丙烯微粉、聚酰胺微粉、聚四氟乙烯蜡粉、聚乙烯蜡粉的一种或多种复配物,通过绝缘填料可以增加了绝缘胶的绝缘性能,提高了绝缘胶的使用安全性能。
进一步,颜料为苯并咪挫酮黄、酞青蓝、二酮吡咯并吡咯、异吲哚啉酮、永固洋红中的一种或多种复配物,通过颜料可以对绝缘胶进行上色,从而使得绝缘胶具备相应的颜色,满足不同使用需求。
进一步,流平剂为固体环氧树脂为载体的固态流平剂,分散剂为三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、古尔胶、脂肪酸聚乙二醇酯中的一种或多种复配物,消泡剂为高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷中的一种或多种复配物,防沉剂为聚烯烃蜡微粒。
步骤1:取光固化树脂、活性单体、光引发剂、附着力促进剂和助剂将其添加到真空搅拌器中,真空搅拌器以500r/min搅拌30min至完全混合溶解均匀;
步骤2:在搅拌状态下将绝缘填料添加到真空搅拌器中,以500r/min分散30min并控制温度50℃下;
步骤3:将颜料与助剂、光固化树脂,活性单体按需调配比率混合搅拌均匀,再使用纳米砂磨机研磨细度至5μ以下制备成低卤素色浆;
步骤4:将制备的低卤素色浆按着色要求加入助剂混合物中以500r/min搅拌分散均匀;
步骤5:搅拌分散均匀后搅拌速度调至500r/min在真空0.1MPa条件下搅拌30min去除物料中的空气泡沫,出料得到均匀一致的全固含、低卤素、胶粘剂分散体;
步骤6:对制备的分散体进行物性技术指标检测,检测包括附着力、耐水性、耐酒精、抗冲击、漆膜弯曲、铅笔硬度、耐湿性、耐寒性、耐热性、耐酸性、耐清洁剂性和耐溶剂性检测。
实施例2:一种全固含光固化绝缘胶,其原料包括光固化树脂、活性单体、光引发剂、附着力促进剂、绝缘填料、颜料和助剂,其中光固化树脂30份,活性单体25份,光引发剂2.5份,附着力促进剂2.5份,绝缘填料20份,颜料2.5份,助剂5份,助剂包括流平剂、分散剂、消泡剂和防沉剂。
进一步,光固化树脂为脂肪族聚氨酯二丙烯酸酯、脂肪族聚氨酯、脂肪族聚氨酯六丙烯酸酯、胺改性丙烯酸酯、双官能团丙烯酸酯、四官能团丙烯酸酯、六官能团丙烯酸酯、聚酯内烯酸酯的一种或多种复配物,通过使用光固化树脂作为绝缘胶主体,光固化树脂化学粘接固位,固位力强。
进一步,活性单体为丙烯酸异冰片酯、丙烯酰吗啉、四氢呋喃丙烯酸酯、乙氧基乙氧乙基丙烯酸酯、2-苯氧基乙基丙烯酸酯、环脂肪族丙烯酸酯、环脂肪族丙烯酸酯、二缩三丙二醇二丙烯酸酯、二环戊烯基氧基乙基丙烯酸酯、1,6-己二醇二丙烯酸酯、(3)乙氧化三羟甲基丙丙烯酸酯、乙氧基乙氧基乙基丙烯酸酯、丙烯酸月桂酯、(5)乙氧基化季戊四醇四丙烯酸酯、季戊四醇三丙烯酸酯、二季戊四醇六丙烯酸酯的一种或多种复配物,活性单体可以降低粘度,调节体系的固化速度,控制到达完全固化所需要的时间,还能增加交联密度,提高了全固含光固化绝缘胶性能。
进一步,光引发剂为2-羟基-2-甲基-1-苯基-1-丙酮、1-羟基环己基苯基甲酮、邻苯甲酰苯甲酸甲酯、二苯甲酮、安息香双甲醚、2,4,6-三甲基苯甲酰基-二苯基氧化膦、异丙基硫杂蒽酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮、2-苯基苄-2-二甲基胺-1-(4-吗啉苄苯基)丁酮、双(1-(2,4-二氟苯基)-3-吡咯基)二茂钛、2,4-二乙基硫杂蒽酮的一种或多种复配物,通过光引发剂能在紫外光区或可见光区吸收一定波长的能量,产生自由基、阳离子等,从而引发单体聚合交联固化。
进一步,附着力促进剂为2-羟乙基甲基丙烯酸酯磷酸酯、γ-缩水甘油醚丙基三甲氧基硅烷、甲基丙烯酰氧基丙基甲基二甲氧基硅烷、氨乙基氨丙基三甲氧基硅烷、3-氨丙基三甲氧基硅烷的一种或多种复配物,通过附着力促进剂增进绝缘胶与基材之间的附着力,提高了绝缘胶的使用效果。
进一步,绝缘填料为滑石粉、氧化镁粉、二氧化硅、聚丙烯微粉、聚酰胺微粉、聚四氟乙烯蜡粉、聚乙烯蜡粉的一种或多种复配物,通过绝缘填料可以增加了绝缘胶的绝缘性能,提高了绝缘胶的使用安全性能。
进一步,颜料为苯并咪挫酮黄、酞青蓝、二酮吡咯并吡咯、异吲哚啉酮、永固洋红中的一种或多种复配物,通过颜料可以对绝缘胶进行上色,从而使得绝缘胶具备相应的颜色,满足不同使用需求。
进一步,流平剂为固体环氧树脂为载体的固态流平剂,分散剂为三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、古尔胶、脂肪酸聚乙二醇酯中的一种或多种复配物,消泡剂为高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷中的一种或多种复配物,防沉剂为聚烯烃蜡微粒
步骤1:取光固化树脂、活性单体、光引发剂、附着力促进剂和助剂将其添加到真空搅拌器中,真空搅拌器以800/min搅拌30min至完全混合溶解均匀;
步骤2:在搅拌状态下将20份绝缘填料添加到真空搅拌器中,以800r/min分散30min并控制温度50℃下;
步骤3:将颜料与助剂、光固化树脂,活性单体按需调配比率混合搅拌均匀,再使用纳米砂磨机研磨细度至5μ以下制备成低卤素色浆;
步骤4:将制备的低卤素色浆按着色要求加入助剂混合物中以800r/min搅拌分散均匀;
步骤5:搅拌分散均匀后搅拌速度调至800r/min在真空0.15MPa条件下搅拌30min去除物料中的空气泡沫,出料得到均匀一致的全固含、低卤素、胶粘剂分散体;
步骤6:对制备的分散体进行物性技术指标检测,检测包括附着力、耐水性、耐酒精、抗冲击、漆膜弯曲、铅笔硬度、耐湿性、耐寒性、耐热性、耐酸性、耐清洁剂性和耐溶剂性检测。
实施例3:一种全固含光固化绝缘胶,其原料包括光固化树脂、活性单体、光引发剂、附着力促进剂、绝缘填料、颜料和助剂,其中光固化树脂40份,活性单体40份,光引发剂5份,附着力促进剂5份,绝缘填料40份,颜料5份,助剂10份,助剂包括流平剂、分散剂、消泡剂和防沉剂。
进一步,光固化树脂为脂肪族聚氨酯二丙烯酸酯、脂肪族聚氨酯、脂肪族聚氨酯六丙烯酸酯、胺改性丙烯酸酯、双官能团丙烯酸酯、四官能团丙烯酸酯、六官能团丙烯酸酯、聚酯内烯酸酯的一种或多种复配物,通过使用光固化树脂作为绝缘胶主体,光固化树脂化学粘接固位,固位力强。
进一步,活性单体为丙烯酸异冰片酯、丙烯酰吗啉、四氢呋喃丙烯酸酯、乙氧基乙氧乙基丙烯酸酯、2-苯氧基乙基丙烯酸酯、环脂肪族丙烯酸酯、环脂肪族丙烯酸酯、二缩三丙二醇二丙烯酸酯、二环戊烯基氧基乙基丙烯酸酯、1,6-己二醇二丙烯酸酯、(3)乙氧化三羟甲基丙丙烯酸酯、乙氧基乙氧基乙基丙烯酸酯、丙烯酸月桂酯、(5)乙氧基化季戊四醇四丙烯酸酯、季戊四醇三丙烯酸酯、二季戊四醇六丙烯酸酯的一种或多种复配物,活性单体可以降低粘度,调节体系的固化速度,控制到达完全固化所需要的时间,还能增加交联密度,提高了全固含光固化绝缘胶性能。
进一步,光引发剂为2-羟基-2-甲基-1-苯基-1-丙酮、1-羟基环己基苯基甲酮、邻苯甲酰苯甲酸甲酯、二苯甲酮、安息香双甲醚、2,4,6-三甲基苯甲酰基-二苯基氧化膦、异丙基硫杂蒽酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮、2-苯基苄-2-二甲基胺-1-(4-吗啉苄苯基)丁酮、双(1-(2,4-二氟苯基)-3-吡咯基)二茂钛、2,4-二乙基硫杂蒽酮的一种或多种复配物,通过光引发剂能在紫外光区或可见光区吸收一定波长的能量,产生自由基、阳离子等,从而引发单体聚合交联固化。
进一步,附着力促进剂为2-羟乙基甲基丙烯酸酯磷酸酯、γ-缩水甘油醚丙基三甲氧基硅烷、甲基丙烯酰氧基丙基甲基二甲氧基硅烷、氨乙基氨丙基三甲氧基硅烷、3-氨丙基三甲氧基硅烷的一种或多种复配物,通过附着力促进剂增进绝缘胶与基材之间的附着力,提高了绝缘胶的使用效果。
进一步,绝缘填料为滑石粉、氧化镁粉、二氧化硅、聚丙烯微粉、聚酰胺微粉、聚四氟乙烯蜡粉、聚乙烯蜡粉的一种或多种复配物,通过绝缘填料可以增加了绝缘胶的绝缘性能,提高了绝缘胶的使用安全性能。
进一步,颜料为苯并咪挫酮黄、酞青蓝、二酮吡咯并吡咯、异吲哚啉酮、永固洋红中的一种或多种复配物,通过颜料可以对绝缘胶进行上色,从而使得绝缘胶具备相应的颜色,满足不同使用需求。
进一步,流平剂为固体环氧树脂为载体的固态流平剂,分散剂为三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、古尔胶、脂肪酸聚乙二醇酯中的一种或多种复配物,消泡剂为高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷中的一种或多种复配物,防沉剂为聚烯烃蜡微粒
步骤1:取光固化树脂、活性单体、光引发剂、附着力促进剂和助剂将其添加到真空搅拌器中,真空搅拌器以1000r/min搅拌30min至完全混合溶解均匀;
步骤2:在搅拌状态下将绝缘填料添加到真空搅拌器中,以1000r/min分散30min并控制温度50℃下;
步骤3:将颜料与助剂、光固化树脂,活性单体按需调配比率混合搅拌均匀,再使用纳米砂磨机研磨细度至5μ以下制备成低卤素色浆;
步骤4:将制备的低卤素色浆按着色要求加入助剂混合物中以1000r/min搅拌分散均匀;
步骤5:搅拌分散均匀后搅拌速度调至1000r/min在真空0.2MPa条件下搅拌30min去除物料中的空气泡沫,出料得到均匀一致的全固含、低卤素、胶粘剂分散体;
步骤6:对制备的分散体进行物性技术指标检测,检测包括附着力、耐水性、耐酒精、抗冲击、漆膜弯曲、铅笔硬度、耐湿性、耐寒性、耐热性、耐酸性、耐清洁剂性和耐溶剂性检测。
附着力检测采用十字错纹胶带剥离实验,浸泡自来水24小时无异常表示耐水性达标,用99.5%的酒精磨擦50次无异常表示耐酒精达标,杜邦式冲击实验φ12.6500g20cm无异常表示抗冲击达标,折曲实验2mmφ、180℃折曲无异常表示漆膜弯曲达标,使用硬度H中华铅笔负荷1kg砝码无异常表示铅笔硬度达标,60℃状态下95%RH240小时无异常表示耐湿性达标,-25℃状态下240小时无异常表示耐寒性达标,70℃状态下240小时无异常表示耐热性达标,在5%HCl里浸泡24小时无异常表示耐酸性达标,用清洗剂磨擦50次无异常表示耐清洁剂性达标,用MEK溶剂磨擦50次无异常表示耐溶剂性达标。
对于本领域技术人员而言,显然本发明不限于上述示范性实施例的细节,而且在不背离本发明的精神或基本特征的情况下,能够以其他的具体形式实现本发明。因此,无论从哪一点来看,均应将实施例看作是示范性的,而且是非限制性的,本发明的范围由所附权利要求而不是上述说明限定,因此旨在将落在权利要求的等同要件的含义和范围内的所有变化囊括在本发明内。
Claims (9)
1.一种全固含光固化绝缘胶,其特征在于,其原料包括光固化树脂、活性单体、光引发剂、附着力促进剂、绝缘填料、颜料和助剂,其中光固化树脂20-40份,活性单体5-40份,光引发剂0.5-5份,附着力促进剂0.5-5份,绝缘填料10-40份,颜料0.5-5份,助剂1-10份,所述助剂包括流平剂、分散剂、消泡剂和防沉剂。
2.根据权利要求1所述的一种全固含光固化绝缘胶,其特征在于,所述光固化树脂为脂肪族聚氨酯二丙烯酸酯、脂肪族聚氨酯、脂肪族聚氨酯六丙烯酸酯、胺改性丙烯酸酯、双官能团丙烯酸酯、四官能团丙烯酸酯、六官能团丙烯酸酯、聚酯内烯酸酯的一种或多种复配物。
3.根据权利要求1所述的一种全固含光固化绝缘胶,其特征在于,所述活性单体为丙烯酸异冰片酯、丙烯酰吗啉、四氢呋喃丙烯酸酯、乙氧基乙氧乙基丙烯酸酯、2-苯氧基乙基丙烯酸酯、环脂肪族丙烯酸酯、环脂肪族丙烯酸酯、二缩三丙二醇二丙烯酸酯、二环戊烯基氧基乙基丙烯酸酯、1,6-己二醇二丙烯酸酯、(3)乙氧化三羟甲基丙丙烯酸酯、乙氧基乙氧基乙基丙烯酸酯、丙烯酸月桂酯、(5)乙氧基化季戊四醇四丙烯酸酯、季戊四醇三丙烯酸酯、二季戊四醇六丙烯酸酯的一种或多种复配物。
4.根据权利要求1所述的一种全固含光固化绝缘胶,其特征在于,所述光引发剂为2-羟基-2-甲基-1-苯基-1-丙酮、1-羟基环己基苯基甲酮、邻苯甲酰苯甲酸甲酯、二苯甲酮、安息香双甲醚、2,4,6-三甲基苯甲酰基-二苯基氧化膦、异丙基硫杂蒽酮、2-甲基-2-(4-吗啉基)-1-[4-(甲硫基)苯基]-1-丙酮、2-苯基苄-2-二甲基胺-1-(4-吗啉苄苯基)丁酮、双(1-(2,4-二氟苯基)-3-吡咯基)二茂钛、2,4-二乙基硫杂蒽酮的一种或多种复配物。
5.根据权利要求1所述的一种全固含光固化绝缘胶,其特征在于,所述附着力促进剂为2-羟乙基甲基丙烯酸酯磷酸酯、γ-缩水甘油醚丙基三甲氧基硅烷、甲基丙烯酰氧基丙基甲基二甲氧基硅烷、氨乙基氨丙基三甲氧基硅烷、3-氨丙基三甲氧基硅烷的一种或多种复配物。
6.根据权利要求1所述的一种全固含光固化绝缘胶,其特征在于,所述绝缘填料为滑石粉、氧化镁粉、二氧化硅、聚丙烯微粉、聚酰胺微粉、聚四氟乙烯蜡粉、聚乙烯蜡粉的一种或多种复配物。
7.根据权利要求1所述的一种全固含光固化绝缘胶,其特征在于,所述颜料为苯并咪挫酮黄、酞青蓝、二酮吡咯并吡咯、异吲哚啉酮、永固洋红中的一种或多种复配物。
8.根据权利要求1所述的一种全固含光固化绝缘胶,其特征在于,所述流平剂为固体环氧树脂为载体的固态流平剂,所述分散剂为三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、古尔胶、脂肪酸聚乙二醇酯中的一种或多种复配物,所述消泡剂为高碳醇脂肪酸酯复合物、聚氧乙烯聚氧丙烯季戊四醇醚、聚氧乙烯聚氧丙醇胺醚、聚氧丙烯甘油醚和聚氧丙烯聚氧乙烯甘油醚、聚二甲基硅氧烷中的一种或多种复配物,所述防沉剂为聚烯烃蜡微粒。
9.基于权利要求1-8任意一项所述的一种全固含光固化绝缘胶的制备工艺,其特征在于,包括以下步骤:
步骤1:取光固化树脂、活性单体、光引发剂、附着力促进剂和助剂将其添加到真空搅拌器中,真空搅拌器以500-1000r/min搅拌30min至完全混合溶解均匀;
步骤2:在搅拌状态下将绝缘填料添加到真空搅拌器中,以500-1000r/min分散30min并控制温度50℃下;
步骤3:将颜料与助剂、光固化树脂,活性单体按需调配比率混合搅拌均匀,再使用纳米砂磨机研磨细度至5μ以下制备成低卤素色浆;
步骤4:将制备的低卤素色浆按着色要求加入助剂混合物中以500-1000r/min搅拌分散均匀;
步骤5:搅拌分散均匀后搅拌速度调至500-1000r/min在真空0.1~0.2MPa条件下搅拌30min去除物料中的空气泡沫,出料得到均匀一致的全固含、低卤素、胶粘剂分散体;
步骤6:对制备的分散体进行物性技术指标检测,所述检测包括附着力、耐水性、耐酒精、抗冲击、漆膜弯曲、铅笔硬度、耐湿性、耐寒性、耐热性、耐酸性、耐清洁剂性和耐溶剂性检测。