CN114524642A - Wall material for geomagnetic functional house, preparation method and functional house - Google Patents
Wall material for geomagnetic functional house, preparation method and functional house Download PDFInfo
- Publication number
- CN114524642A CN114524642A CN202210186679.2A CN202210186679A CN114524642A CN 114524642 A CN114524642 A CN 114524642A CN 202210186679 A CN202210186679 A CN 202210186679A CN 114524642 A CN114524642 A CN 114524642A
- Authority
- CN
- China
- Prior art keywords
- powder
- wall material
- geomagnetic
- magnetic
- black
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a wall material for a geomagnetic functional house, a preparation method and the functional house, wherein the wall material comprises, by mass, 8-10 parts of black tourmaline, 8-10 parts of black magnetite, 3-5 parts of white jade, 3-5 parts of chestnut charcoal powder, 0.01-0.03 part of graphite powder, 0.005-0.01 part of citric acid powder and 63-65 parts of cement; the block-shaped magnetic wall material obtained by the preparation process has high compressive strength and good magnetic performance, and can be widely applied to wall building materials of geomagnetic functional rooms.
Description
Technical Field
The invention relates to the technical field of functional building materials, in particular to a wall material for a geomagnetic functional room, a preparation method and the functional room.
Background
The wall body is an important component of a building, the traditional wall body materials comprise natural stone, functional artificial stone slabs, functional wall surface coatings and the like, and different wall body materials play a key role in the external decoration effect and the internal environment of the building. With the continuous improvement of wall materials, more and more novel wall materials of different types gradually appear, and the wall materials often have excellent mechanical and chemical properties, such as various properties of heat preservation, heat insulation, water resistance, moisture preservation, sound insulation, noise reduction and the like.
At present, wall materials develop to be green, environment-friendly and multifunctional, and the research on functional wall materials is continuously and deeply carried out, but the research on the wall materials of special functional buildings is still less. The magnetic therapy mainly utilizes the action of a magnetic field to influence the current distribution and the motion of charged particles in a human body, change the physiology and biochemistry of human tissue cells, promote blood and lymph circulation and the like; the geomagnetic functional house mainly creates a living environment with a geomagnetic magnetotherapy function, and acts on a human body through a magnetic field to achieve a health care purpose, so that people in the original living environment can experience and enjoy a geomagnetic health care effect.
However, the application of the magnetic material to the wall material of the functional building is rarely reported, so how to prepare the magnetic wall material suitable for constructing the geomagnetic functional room and effectively apply the magnetic wall material to the functional building is an important technical basis for constructing a long-life health area, creating a geomagnetic functional health cell, improving the green, environment-friendly and healthy properties of modern house buildings and promoting the development of the national old health strategy.
Disclosure of Invention
In view of the above, the invention provides a wall material for a geomagnetic functional room, a preparation method thereof and a functional room.
The technical scheme of the invention is realized as follows:
the invention provides a wall material for a geomagnetic functional room, which comprises, by mass, 8-10 parts of black tourmaline, 8-10 parts of black magnetite, 3-5 parts of white jade, 3-5 parts of chestnut wood carbon powder, 0.01-0.03 part of graphite powder, 0.005-0.01 part of citric acid powder and 63-65 parts of cement.
More preferably, the stone material comprises, by mass, 9 parts of tourmaline, 9 parts of black magnetite, 4 parts of white jade, 4 parts of chestnut wood carbon powder, 0.02 part of graphite powder, 0.008 part of citric acid powder and 64 parts of cement.
A preparation method of a wall material for a geomagnetic functional room comprises the following steps:
step 1: the black tourmaline, the black magnet and the white jade are respectively ground into 400-450 meshes, 140-200 meshes and 250-300 meshes through a mechanical ball, and the crushed stone powder with the three-level particle size is obtained: tourmaline powder, black magnet powder and white jade powder;
step 2: burning chestnut branches to obtain chestnut carbon, and crushing to 400-450 meshes to obtain chestnut carbon powder;
and step 3: mixing the crushed stone powder obtained in the step 1 according to a ratio, adding the mixed powder into water with the volume of 2-2.5 times, standing and soaking the mixed powder for 25-35 min at a constant temperature of 30-40 ℃ to obtain a hydrated crushed stone mixed material;
and 4, step 4: adding graphite powder into the hydrated macadam mixed material, stirring for 10-15 min, and standing for 18-22 min to obtain an activated magnetic mixed material;
and 5: adding chestnut tree carbon powder into the activated magnetic mixed material, uniformly stirring, adding citric acid powder, continuously stirring for 20-25 min, and standing for 20-30 min to obtain a magnetic wall mixed base material;
step 6: mixing the magnetic wall mixed base material, adding cement according to a ratio, uniformly stirring, pouring into a mold, and drying and forming to obtain the massive magnetic wall material.
Further explaining, in the step 3, the crushed stone powder is mixed according to the proportion, added into water with the volume of 2 times, stirred for 8-10 min at the speed of 120r/min and then placed at the constant temperature of 35 ℃ for standing for 30min to obtain the hydrated crushed stone mixed material.
Further, in the step 4, the stirring speed for adding the graphite powder for activation is 100-120 r/min.
Further, in step 5, the citric acid powder is added and continuously stirred at a speed of 180-200 r/min.
Further explaining, in the step 5, after adding the citric acid powder, carrying out secondary heating, and heating to 30-35 ℃ for constant temperature and keeping when continuously stirring for 20-25 min; and standing for 20-30 min, and heating to 35-40 ℃ and keeping at a constant temperature.
Further, a groove of 0.8-1.2 mm is formed in the bottom surface of the block-shaped wall material of the geomagnetic functional room and used for arranging a temperature control line.
The utility model provides an insulating plank 2 that the function room that adopts the wall material of above-mentioned earth magnetism function room to establish and form, at insulating plank 1 fixed surface laying cubic magnetism wall material that function room wall body liftoff 2m department set up to cover honeycomb holes structure at cubic magnetism wall material's fixed surface.
Further, a temperature control line is arranged between the insulating wood board 1 and the magnetic block wall material and is installed and fixed in a groove on the bottom surface of the block magnetic wall material.
Compared with the prior art, the invention has the beneficial effects that:
(1) according to the invention, the combination of three magnetic stones, namely the black tourmaline, the black magnetite and the white jade, is used as a main magnetic material, and meanwhile, chestnut carbon powder, graphite powder and citric acid powder are added as auxiliary raw materials, so that the magnetic effect can be effectively enhanced, the conduction of magnetic residual charges in the magnetic stones to the space outside the bricks is effectively promoted, the stability of magnetic conduction to the outside is obviously improved, and the high-efficiency overflow effect of micro-electromagnetic stability is achieved.
(2) According to the invention, while the mobility of carriers is improved by using graphite powder, firstly, after the magnetic residual charge in the crushed stone powder is subjected to hydration conduction by using constant-temperature pure water liquid, citric acid is used as a stabilizer, and the stable and continuous conduction of micro-electromagnetism of the magnetic wall material is ensured under the combined adsorption and stabilization action of chestnut carbon powder and citric acid powder, so that the magnetic effect is enhanced, and meanwhile, the escape of negative charges in the wall is further accelerated by combining with secondary heating treatment, so that the good magnetic therapy effect on a human body is achieved.
(3) The invention adopts the combination and matching of the black tourmaline powder, the black magnet powder and the white jade powder with three levels of broken stone powders with different grain diameters, thereby not only effectively ensuring the compressive strength of the block-shaped magnetic wall body, but also obviously improving the magnetism of the wall body material; the wall material provided by the invention combines the honeycomb hole structure insulating wood board and the temperature control wire, and when the wall material is used in a functional room, a stable strong magnetic field environment can be formed, a certain magnetic function effect can be generated for people who receive health care exercise in the functional room, and a magnetic radiation effect can be generated for a residential area with the radius of 100 meters in the functional room, so that a health care effect is realized for people living in the radiation range.
Drawings
Fig. 1 is a magnetic wall material mounting structure of a functional room according to an embodiment of the present invention; wherein 1 is an insulating wood board, 2 is an insulating wood board with a honeycomb structure, and 3 is a block-shaped magnetic wall material.
Detailed Description
In order to better understand the technical content of the invention, specific examples are provided below to further illustrate the invention.
The experimental methods used in the examples of the present invention are all conventional methods unless otherwise specified.
The materials, reagents and the like used in the examples of the present invention can be obtained commercially without specific description.
Example 1
The utility model provides a wall material for earth magnetism function room, is according to the mass part ratio, including black apyrite 8 parts, black magnetite 8 parts, white jade 3 parts, 3 parts of chestnut wooden carbon powder, graphite powder 0.01 part, citric acid powder 0.01 part and cement 63 parts, and its preparation method includes the following step:
(1) respectively grinding the black tourmaline, the black magnetite and the white jade into 400 meshes, 140 meshes and 250 meshes by using a mechanical ball mill to obtain crushed stone powder with three-level particle size: tourmaline powder, black magnet powder and white jade powder;
(2) burning chestnut branches to obtain chestnut charcoal, and crushing to 400 meshes to obtain chestnut charcoal powder;
(3) mixing the crushed stone powder obtained in the step 1 according to a ratio, adding the mixture into water with 2.5 times of volume, standing and soaking at a constant temperature of 40 ℃ for 25min to obtain a hydrated crushed stone mixed material;
(4) adding graphite powder into the hydrated macadam mixed material, stirring at the speed of 120r/min for 10min, and standing for 22min to obtain an activated magnetic mixed material;
(5) adding chestnut tree carbon powder into the activated magnetic mixed material, uniformly stirring, adding citric acid powder, continuously stirring at the speed of 200r/min for 20min, and standing for 30min to obtain a magnetic wall mixed base material;
(6) mixing the magnetic wall mixed base material, adding cement according to a ratio, uniformly stirring, pouring into a mold, and drying and forming to obtain the massive magnetic wall material.
Example 2
The wall material for the geomagnetic functional room comprises, by mass, 10 parts of black tourmaline, 10 parts of black magnetite, 5 parts of white jade, 5 parts of chestnut wood carbon powder, 0.03 part of graphite powder, 0.005 part of citric acid powder and 65 parts of cement, and the preparation method comprises the following steps:
(1) respectively carrying out mechanical ball milling on the black tourmaline, the black magnetite and the white jade, and crushing to 450 meshes, 200 meshes and 300 meshes to obtain broken stone powder with three-level particle size: tourmaline powder, black magnet powder and white jade powder;
(2) burning chestnut branches to obtain chestnut charcoal, and crushing to 450 meshes to obtain chestnut charcoal powder;
(3) mixing the crushed stone powder obtained in the step 1 according to a ratio, adding the mixed powder into water with the volume being 2 times of that of the mixed powder, stirring the mixed powder at the speed of 100r/min for 10min, standing the mixed powder at the constant temperature of 30 ℃ and soaking the mixed powder for 35min to obtain a hydrated crushed stone mixed material;
(4) adding graphite powder into the hydrated macadam mixed material, stirring at the speed of 100r/min for 15min, and standing for 18min to obtain an activated magnetic mixed material;
(5) adding chestnut carbon powder into the activated magnetic mixed material, uniformly stirring, adding citric acid powder, continuously stirring at 1800r/min for 25min, and standing for 20min to obtain a magnetic wall mixed base material;
(6) mixing the magnetic wall mixed base material, adding cement according to a ratio, uniformly stirring, pouring into a mold, and drying and forming to obtain the massive magnetic wall material.
Example 3
A wall material for a geomagnetic functional room comprises, by mass, 9 parts of tourmaline, 9 parts of black magnetite, 4 parts of white jade, 4 parts of chestnut wood carbon powder, 0.02 part of graphite powder, 0.008 part of citric acid powder and 64 parts of cement, and the preparation method comprises the following steps:
(1) respectively grinding the black tourmaline, the black magnetite and the white jade into 400 meshes, 200 meshes and 300 meshes by using a mechanical ball mill to obtain crushed stone powder with three-level particle size: tourmaline powder, black magnet powder and white jade powder;
(2) burning chestnut branches to obtain chestnut charcoal, and crushing to 400 meshes to obtain chestnut charcoal powder;
(3) mixing the crushed stone powder obtained in the step 1 according to a ratio, adding the mixed powder into water with the volume being 2 times of that of the mixed powder, stirring the mixed powder at the speed of 120r/min for 8min, standing and soaking the mixed powder at the constant temperature of 35 ℃ for 30min to obtain a hydrated crushed stone mixed material;
(4) adding graphite powder into the hydrated macadam mixed material, stirring at the speed of 110r/min for 13min, and standing for 20min to obtain an activated magnetic mixed material;
(5) adding chestnut tree carbon powder into the activated magnetic mixed material, uniformly stirring, adding citric acid powder, continuously stirring at the speed of 190r/min for 23min, and standing for 25min to obtain a magnetic wall mixed base material;
(6) mixing the magnetic wall mixed base material, adding cement according to a ratio, uniformly stirring, pouring into a mold, and drying and forming to obtain the massive magnetic wall material.
Example 4
The formula and the preparation process of the wall material for the geomagnetic functional room as in example 3 are different in that: in the step 5, chestnut carbon powder is added into the activated magnetic mixed material, after uniform stirring, citric acid powder is added, the temperature is raised to 33 ℃ and kept constant, after continuous stirring is carried out for 23min at the speed of 190r/min, the temperature is raised to 38 ℃ and kept constant, standing is carried out for 25min, and the rest steps are the same as those in the embodiment 3.
Comparative example 1
The formula and the preparation process of the wall material for the geomagnetic functional room as in example 3 are different in that: the preparation process is different; and 3, mixing the crushed stone powder obtained in the step 1, adding the mixed powder into water with the volume being 2 times of that of the crushed stone powder, stirring the mixed powder at the speed of 120r/min for 8min, and standing and soaking the mixed powder in normal temperature for 30min to obtain a hydrated crushed stone mixed material.
Comparative example 2
The formula and the preparation process of the wall material for the geomagnetic functional room as in example 3 are different in that: the preparation process is different; step 3, mixing the crushed stone powder obtained in the step 1, adding the mixed crushed stone powder into water with the volume being 2 times that of the crushed stone powder, stirring the mixed crushed stone powder at the speed of 120r/min for 8min, and directly adding graphite powder for mixing and subsequent operation without standing; the remaining procedure was the same as in example 3.
Comparative example 3
The formula and the preparation process of the wall material for the geomagnetic functional room as in example 3 are different in that: the preparation process is different; in the step 1, the black tourmaline, the black magnetite and the white jade are respectively ground into the same crushed stone powder with the particle size of 200 meshes by a mechanical ball.
Comparative example 4
The formula and the preparation process of the wall material for the geomagnetic functional room as in example 3 are different in that: citric acid is not added; the other raw materials are the same as the raw materials in the example 3: 9 parts of black tourmaline, 9 parts of black magnetite, 4 parts of white jade, 4 parts of chestnut wood carbon powder, 0.02 part of graphite powder and 64 parts of cement;
in the preparation process, in the step 5, chestnut tree carbon powder is added into the activated magnetic mixed material, and after being uniformly stirred, the chestnut tree carbon powder is directly kept stand for 25min to obtain the magnetic wall mixed base material.
The sizes of the block-shaped magnetic wall materials prepared in the above examples and comparative examples are 80 × 80 × 15mm respectively; the magnetic performance test of different block magnetic wall materials of the above examples and comparative examples is carried out by using WT10A Tesla meter magnetic field detector test, and the measurement index ranges are as follows: the measurement results of 0-200 mT millitesla-2000 mT millitesla, 1mT millitesla ═ 10Gs gauss, and the mechanical properties of the compressive strength of the bulk magnetic wall material are as follows:
as can be seen from the above table, the bulk magnetic wall materials prepared in the embodiments 1 to 4 of the present invention have not only higher compressive strength, but also good magnetic properties, the residual magnetic induction strength can be above 0.58GS, and the compressive strength of the magnetic wall material is above 9.5 MPa. In example 4, the negative charges in the wall body escape outward is further accelerated by combining with the secondary temperature rise treatment when the wall body is fixed by citric acid powder, and the magnetic enhancement effect of the wall body material and the stability of the conduction of the magnetic residual charges to the space outside the brick are improved.
Compared with the comparative examples 1-2, the embodiment 3 has the advantages that the carrier mobility is improved by using the graphite powder, and the stability of outward magnetic conduction can be obviously improved by carrying out hydration conduction treatment on the magnetic residual charges in the crushed stone powder by using the constant-temperature pure water liquid, so that the high-efficiency overflow effect of micro-electromagnetic stability is achieved. Compared with the comparative examples 3-4, the method disclosed by the invention has the advantages that the combination and matching of the black tourmaline powder, the black magnet powder and the white jade powder with three levels of crushed stone powder with different particle sizes are adopted, so that the compressive strength and the magnetic performance of the block-shaped magnetic wall body are favorably improved; and citric acid is used as a stabilizer, so that the stable and continuous conduction of micro-electromagnetism of the magnetic wall material is ensured, and the magnetic effect is effectively enhanced.
Example 5
A functional house constructed by adopting the wall material of the geomagnetic functional house comprises the following specific construction methods:
the surface of an insulating wood board 1 fixedly arranged at a position 2m away from the ground of the functional house wall body is fixedly paved with a block-shaped magnetic wall material, the bottom surface of the block-shaped wall material is provided with a 1.0mm groove, and the surface of the block-shaped magnetic wall material is fixedly covered with an insulating wood board 2 with a honeycomb hole structure, wherein the structural schematic diagram is shown in fig. 1.
A 60 ℃ temperature control line is arranged between the insulating wood board 1 and the magnetic block wall material and is arranged and fixed in a groove on the bottom surface of the block magnetic wall material.
The above description is only for the purpose of illustrating the preferred embodiments of the present invention and is not to be construed as limiting the invention, and any modifications, equivalents, improvements and the like that fall within the spirit and principle of the present invention are intended to be included therein.
Claims (10)
1. The utility model provides a wall material for earth magnetism function room which characterized in that: the black tourmaline comprises, by mass, 8-10 parts of black tourmaline, 8-10 parts of black magnetite, 3-5 parts of white jade, 3-5 parts of chestnut charcoal powder, 0.01-0.03 part of graphite powder, 0.005-0.01 part of citric acid powder and 63-65 parts of cement.
2. The wall material for a geomagnetic functional room, according to claim 1, wherein: according to the mass portion ratio, the black tourmaline comprises 9 portions of black tourmaline, 9 portions of black magnetite, 4 portions of white jade, 4 portions of chestnut carbon powder, 0.02 portion of graphite powder, 0.008 portion of citric acid powder and 64 portions of cement.
3. A method for preparing a wall material for a geomagnetic functional room, as defined in claim 1 or 2, wherein: the method comprises the following steps:
step 1: the black tourmaline, the black magnet and the white jade are respectively ground into 400-450 meshes, 140-200 meshes and 250-300 meshes through a mechanical ball, and the crushed stone powder with the three-level particle size is obtained: tourmaline powder, black magnet powder and white jade powder;
step 2: burning chestnut branches to obtain chestnut carbon, and crushing to 400-450 meshes to obtain chestnut carbon powder;
and step 3: mixing the crushed stone powder obtained in the step 1 according to a ratio, adding the mixed powder into water with the volume of 2-2.5 times, standing and soaking the mixed powder for 25-35 min at a constant temperature of 30-40 ℃ to obtain a hydrated crushed stone mixed material;
and 4, step 4: adding graphite powder into the hydrated macadam mixed material, stirring for 10-15 min, and standing for 18-22 min to obtain an activated magnetic mixed material;
and 5: adding chestnut tree carbon powder into the activated magnetic mixed material, uniformly stirring, adding citric acid powder, continuously stirring for 20-25 min, and standing for 20-30 min to obtain a magnetic wall mixed base material;
and 6: mixing the magnetic wall mixed base material, adding cement according to a ratio, uniformly stirring, pouring into a mold, and drying and forming to obtain the massive magnetic wall material.
4. The method for preparing a wall material for a geomagnetic functional room, according to claim 3, wherein the method comprises the following steps: and 3, mixing the macadam powder according to a ratio, adding the macadam powder into water with the volume being 2 times of the macadam powder, stirring the mixture at the speed of 100-120r/min for 8-10 min, and standing the mixture at the constant temperature of 35 ℃ for 30min to obtain the hydrated macadam mixed material.
5. The method for preparing a wall material for a geomagnetic functional room, according to claim 3, wherein the method comprises the following steps: in the step 4, the stirring speed for adding the graphite powder for activation is 100-120 r/min.
6. The method for preparing a wall material for a geomagnetic functional room, as defined in claim 3, wherein the method comprises the following steps: in the step 5, the speed of adding the citric acid powder and continuously stirring is 180-200 r/min.
7. The method for preparing a wall material for a geomagnetic functional room, according to claim 3, wherein the method comprises the following steps: in the step 5, after adding citric acid powder, carrying out secondary heating, and heating to 30-35 ℃ for constant temperature holding when continuously stirring for 20-25 min; and standing for 20-30 min, and heating to 35-40 ℃ and keeping at a constant temperature.
8. The method for preparing a wall material for a geomagnetic functional room, according to claim 3, wherein the method comprises the following steps: the bottom surface of the blocky wall material is provided with a 0.8-1.2 mm groove for arranging a temperature control line.
9. A functional room constructed by using the wall material of the geomagnetic functional room as defined in any one of claims 1 and 2, wherein: and fixedly paving a block-shaped magnetic wall material on the surface of an insulating wood board 1 fixedly arranged at a position 2m away from the ground of the functional house wall, and fixedly covering the insulating wood board 2 with a honeycomb hole structure on the surface of the block-shaped magnetic wall material.
10. The functional room as claimed in claim 8, wherein the functional room is constructed by using wall materials of a geomagnetic functional room, and comprises: and a temperature control line is arranged between the insulating wood board 1 and the magnetic block wall material and is installed and fixed in a groove on the bottom surface of the block magnetic wall material.